CATHODE ACTIVE MATERIAL FOR SODIUM-ION BATTERIES, AND PREPARATION METHOD THEREFORE AND APPLICATION THEREOF

20240234711 ยท 2024-07-11

    Inventors

    Cpc classification

    International classification

    Abstract

    Disclosed are a cathode active material for sodium-ion batteries and a preparation method therefor and an application thereof. The cathode active material has a chemical formula of Na.sub.xNi.sub.yFe.sub.zMn.sub.gM.sub.hA.sub.mO.sub.2, where M is selected from the group consisting of Ti, Al, Mg, Ca, Zr, Y, Zn, Nb, W and combinations thereof, A is selected from the group consisting of B, P, C and combinations thereof, 0.80?x?1.40, 0.05?y?0.95, 0.05?z?0.95, 0.05?g?0.95, 0.01?h?0.50, and 0.01?m?0.30. By adding M and A elements to the ternary iron-manganese-nickel cathode active material for sodium-ion batteries, and controlling the ratio of all elements, the present disclosure can achieve the formation of a perfect layered single-crystal structure of the cathode active material for sodium-ion batteries, with large particles, ultimately achieving the stability of the active material, and when used in sodium-ion batteries, it can significantly improve the cycling performance at high temperatures while ensuring high gram capacity.

    Claims

    1. A cathode active material for sodium-ion batteries, wherein, the cathode active material has a chemical formula of Na.sub.xNi.sub.yFe.sub.zMn.sub.gM.sub.hA.sub.mO.sub.2, wherein M is selected from the group consisting of Ti, Al, Mg, Ca, Zr, Y, Zn, Nb, W and combinations thereof, A is selected from the group consisting of B, P, C and combinations thereof, 0.80?x?1.40, 0.05?y?0.95, 0.05?z?0.95, 0.05?g?0.95, 0.01?h?0.50, and 0.01?m?0.30.

    2. The cathode active material for sodium-ion batteries according to claim 1, wherein, in the chemical formula Na.sub.xNi.sub.yFe.sub.zMn.sub.gM.sub.hA.sub.mO.sub.2, 0.90?x?1.20, and 1.2?(y+z+g+h)?0.

    3. The cathode active material for sodium-ion batteries according to claim 1, wherein, in the chemical formula Na.sub.xNi.sub.yFe.sub.zMn.sub.gM.sub.hA.sub.mO.sub.2, 0.95?x?1.05, 0.1?y?0.5, 0.1?z?0.6, 0.1?g?0.5, 0.01?h?0.3, and 0.01?m?0.2.

    4. The cathode active material for sodium-ion batteries according to claim 1, wherein, in the chemical formula Na.sub.xNi.sub.yFe.sub.zMn.sub.gM.sub.hA.sub.mO.sub.2, 0.98?x?1.03, 0.1?y?0.4, 0.2?z?0.5, 0.1?g?0.4, 0.01?h?0.2, and 0.01?m?0.1.

    5. The cathode active material for sodium-ion batteries according to claim 1, wherein, M is selected from the group consisting of Ti, Mg, Ca and combinations thereof, A is selected from combinations of two or three of B, P and C.

    6. The cathode active material for sodium-ion batteries according to claim 1, wherein, the cathode active material has a layered single-crystal structure, with an average particle size of 1-30 microns.

    7. The cathode active material for sodium-ion batteries according to claim 1, wherein, the cathode active material has a tap density of 1.33-2.5 g/cm.sup.3, and a pH of below 12.6.

    8. A method for preparing the cathode active material for sodium-ion batteries according to claim 1, wherein, the method comprises the following steps: 1) reacting a nickel salt, a manganese salt, and a hydroxide in the presence of a complexing agent to form nickel-manganese hydroxide; 2) adding water to the nickel-manganese hydroxide, an iron source, a compound containing M element, a compound containing A element, and a sodium source to make a slurry, and sand grinding to give a mixed slurry; 3) drying and sintering the mixed slurry to give a cathode active material for sodium-ion batteries.

    9. The method for preparing a cathode active material for sodium-ion batteries according to claim 8, wherein, the chemical formula of the nickel-manganese hydroxide in step 1) is Ni.sub.aMn.sub.b(OH).sub.2, where 0.05?a?0.95, 0.05?b?0.95, and 1?a?b?0; and/or, in step 2), a ratio of the total molar amount of nickel and manganese in the nickel-manganese hydroxide, iron in the iron source, M element in the compound containing M element and A element in the compound containing A element to the molar amount of sodium in the sodium source is 1:(0.90-1.20).

    10. The method for preparing a cathode active material for sodium-ion batteries according to claim 8, wherein, in step 1), the nickel salt is selected from the group consisting of nickel sulfate, nickel chloride, nickel nitrate and combinations thereof, the manganese salt is selected from the group consisting of manganese sulfate, manganese chloride, and manganese nitrate and combinations thereof, the hydroxide is selected from the group consisting of sodium hydroxide, potassium hydroxide and combinations thereof, and the complexing agent is selected from the group consisting of ethylenediamine, ethylenediamine tetraacetic acid, tartaric acid, citric acid, oxalic acid, ammonia and combinations thereof; and/or, in step 2), the iron source is selected from the group consisting of ferrous oxide, ferric oxide, ferroferric oxide and combinations thereof; the sodium source is selected from the group consisting of sodium carbonate, sodium hydroxide and combinations thereof.

    11. The method for preparing a cathode active material for sodium-ion batteries according to claim 8, wherein, in step 1), the nickel salt and the manganese salt are prepared into a metal salt solution, which is then mixed with an aqueous solution of the hydroxide and the complexing agent to obtain a mixed solution, and the mixed solution is then reacted at pH 9-12 and 40-70? C. and stirring to give the nickel-manganese hydroxide.

    12. The method for preparing a cathode active material for sodium-ion batteries according to claim 11, wherein, the total concentration of nickel and manganese ions in the metal salt solution is 0.5-2 mol/L.

    13. (canceled)

    14. The method for preparing a cathode active material for sodium-ion batteries according to claim 8, wherein, in step 2), the compound containing M element is selected from the group consisting of titanium dioxide, aluminum oxide, magnesium oxide, calcium oxide, calcium carbonate, zirconia, yttrium oxide, zinc oxide, niobium oxide, tungsten oxide and combinations thereof; the compound containing A element is selected from the group consisting of boric acid, boron oxide, sodium tetraborate, phosphorus pentoxide, phosphoric acid, sodium phosphate, sodium hypophosphite, glucose, sucrose, polyethylene glycol, polyvinyl alcohol and combinations thereof.

    15. (canceled)

    16. The method for preparing a cathode active material for sodium-ion batteries according to claim 8, wherein, in step 2), the sand grinding time is 0.5-8 h, the grinding body is zirconia balls with particle sizes of 0.1-0.8 mm, and the sand grinding speed is 800-3000 rpm.

    17. The method for preparing a cathode active material for sodium-ion batteries according to claim 8, wherein, the median particle size of the particles in the mixed slurry is 20-800 nm, and the solid content of the mixed slurry is 10%-60%.

    18. The method for preparing a cathode active material for sodium-ion batteries according to claim 8, wherein, in step 3), the drying is spray drying, and in the spray drying equipment, the rotational speed of the atomizing disc is 1000-3000 rpm, the inlet air temperature is 150-300? C., and the outlet air temperature is 80-120? C.

    19. The method for preparing a cathode active material for sodium-ion batteries according to claim 8, wherein, in step 3), the sintering is carried out in air, with a sintering temperature of 750-1000? C. and a sintering time of 5-25 h.

    20. (canceled)

    21. A cathode material for sodium-ion batteries comprising a cathode active material, an adhesive and a conductive agent, wherein, the cathode active material comprises the cathode active material for sodium-ion batteries according to claim 1.

    22. (canceled)

    23. (canceled)

    24. The cathode active material for sodium-ion batteries according to claim 1, wherein, A is combinations of three of B, P and C, and the molar ratio of B, P and C is (2-4):(0.1-1.5):(0.1-1.5).

    25. The cathode active material for sodium-ion batteries according to claim 1, wherein, A is combinations of two of B and P, and the molar ratio of B and P is (2-4):(0.1-1.5).

    Description

    BRIEF DESCRIPTION OF THE DRAWINGS

    [0044] FIG. 1 is a scanning electron microscope image of NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ti.sub.0.05B.sub.0.05O.sub.2 prepared in Embodiment 1;

    [0045] FIG. 2 is a XRD (X-Ray Diffraction) pattern of NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ti.sub.0.05B.sub.0.05O.sub.2 prepared in Embodiment 1;

    [0046] FIG. 3 is a charge-discharge curve of NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ti.sub.0.05B.sub.0.05O.sub.2 prepared in Embodiment 1;

    [0047] FIG. 4 is a high-temperature (60? C.) cycling diagram of NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ti.sub.0.05B.sub.0.05O.sub.2 prepared in Embodiment 1 at 2.0-4.0 V/1 C;

    [0048] FIG. 5 is a scanning electron microscope image of NaNi.sub.0.25Fe.sub.0.40Mn.sub.0.25Ti.sub.0.03B.sub.0.05P.sub.0.02O.sub.2 prepared in Embodiment 2;

    [0049] FIG. 6 is a XRD pattern of NaNi.sub.0.25Fe.sub.0.40Mn.sub.0.25Ti.sub.0.03B.sub.0.05P.sub.0.02O.sub.2 prepared in Embodiment 2;

    [0050] FIG. 7 is a charge-discharge curve of NaNi.sub.0.25Fe.sub.0.40Mn.sub.0.25Ti.sub.0.03B.sub.0.05P.sub.0.02O.sub.2 prepared in Embodiment 2;

    [0051] FIG. 8 is a high-temperature (60? C.) cycling diagram of NaNi.sub.0.25Fe.sub.0.40Mn.sub.0.25Ti.sub.0.03B.sub.0.05P.sub.0.02O.sub.2 prepared in Embodiment 2 at 2.0-4.0 V/1 C;

    [0052] FIG. 9 is a scanning electron microscope image of NaNi.sub.0.25Fe.sub.0.45Mn.sub.0.25Ti.sub.0.05O.sub.2 prepared in Comparative example 1;

    [0053] FIG. 10 is a XRD pattern of NaNi.sub.0.25Fe.sub.0.45Mn.sub.0.25Ti.sub.0.05O.sub.2 prepared in Comparative example 1;

    [0054] FIG. 11 is a charge-discharge curve of NaNi.sub.0.25Fe.sub.0.45Mn.sub.0.25Ti.sub.0.05O.sub.2 prepared in Comparative example 1;

    [0055] FIG. 12 is a high-temperature (60? C.) cycling diagram of NaNi.sub.0.25Fe.sub.0.45Mn.sub.0.25Ti.sub.0.05O.sub.2 prepared in Comparative example 1 at 2.0-4.0 V/1 C.

    DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS

    [0056] To better understand the present disclosure, it is further explained below combining with specific embodiments and the accompanying drawings. It should be understood that these embodiments are intended only for the further description of the present disclosure and are not intended to limit the scope of the present disclosure. Furthermore it should be understood that after reading the contents of the present disclosure, various improvements and adjustments made to the present disclosure by those skilled in the art, without departing from the principles of the present disclosure, still fall within the scope of protection of the present disclosure. In the following, all raw materials were obtained commercially if not otherwise specified.

    [0057] In the following embodiments and comparative examples, the charge-discharge curves and high-temperature cycling performance were tested using the following method: first, preparing a sodium-ion battery: 20 g of prepared cathode active material was weighed, 0.64 g of conductive agent SP and 0.64 g of PVDF dissolved in NMP were added, mixed evenly, and coated on aluminum foil to make an electrode plate. In a glove box in argon atmosphere, a button cell was assembled with a metal sodium sheet as the anode, Celgard2700 as the diaphragm, and 1 mol/L NaPF.sub.6+EC:DEC (1:1)+5% FEC as the electrolyte. Then, the charge-discharge curve was tested at a voltage range of 2.0-4.0 V, a charge discharge rate of 0.1 C, a current of 13 mA, and a test temperature of 25?2? C., and the cycling performance was tested for 100 cycles at a voltage range of 2.0-4.0 V, a charge discharge rate of 1 C, a current of 130 mA, and 60? C.

    Embodiment 1

    [0058] This embodiment provides a cathode active material for sodium-ion batteries, the chemical formula thereof is NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ti.sub.0.05B.sub.0.05O.sub.2, and the preparation method comprises the following steps: [0059] (1) Nickel sulfate and manganese sulfate was added to pure water in a Ni:Mn molar ratio of 1:1 to prepare a solution with a total concentration of metallic elements of 1.3 mol/L; [0060] (2) A 4.0 mol/L solution of sodium hydroxide and a 5.0 mol/L solution of ammonia were prepared; [0061] (3) The metal salt solution obtained in step (1) and the sodium hydroxide solution and ammonia solution obtained in step (2) were added to a reactor at a rate of 2.5 L/h, 1.5 L/h, and 0.2 L/h, respectively, and a precursor was prepared by controlling the reaction temperature to 50? C., reaction pH to 11.5, stirring speed to 650 rpm, and reacting time to 12 h; [0062] (4) The precursor was washed with pure water, filtered, and dried to give Ni.sub.0.5Mn.sub.0.5(OH).sub.2; [0063] (5) 2.0 mol of Ni.sub.0.5Mn.sub.0.5(OH).sub.2, 0.8 mol of Fe.sub.2O.sub.3, 0.2 mol of TiO.sub.2, 0.2 mol of H.sub.3BO.sub.3, 2.0 mol of Na.sub.2CO.sub.3 were added into 3.5 L of water to prepare a slurry; [0064] (6) The slurry obtained in step (5) was added to a sand grinder, and ground for 3 h, with the grinding body being zirconia balls with a particle size of 0.2 mm, and a sand grinding speed of 2500 rpm, to give a mixed slurry with an average particle size of about 350 nm; [0065] (7) The mixed slurry prepared in step (6) was transferred into a mixing drum, stirred thoroughly, and mixed with pure water to form a slurry with a solid content of 30?1%, spray dried under the conditions of spray drying equipment with an atomization frequency of 35 Hz, an inlet air temperature of 190? C. and an outlet air temperature of 85? C., the dried product was sintered at 850-940? C. for 12 h in an air-atmosphere furnace, cooled to below 80? C., jaw broken, rolled, and crushed to give a cathode active material for sodium-ion batteries, named as NFM242-TB.

    [0066] The scanning electron microscope image of NFM242-TB is shown in FIG. 1, and it can be seen that the material has a single crystal morphology. The XRD pattern of NFM242-TB is shown in FIG. 2, and it can be seen that the material is ?-NaFeO.sub.2 type pure phase layered structure. The charge-discharge curve of NFM242-TB is shown in FIG. 3, and it can be seen that within the voltage window of 2.0-4.0 V, the discharge grain capacity at a rate of 0.1 C is 124.8 mAh/g. The high-temperature cycling diagram of NFM242-TB is shown in FIG. 4, and it can be seen that at 60? C., within the voltage window of 2.0-4.0 V, the capacity retention rate is 89.04% after 100 cycles at a rate of 1 C.

    Embodiment 2

    [0067] The chemical formula of the cathode active material for sodium-ion batteries of this embodiment is NaNi.sub.0.25Fe.sub.0.40Mn.sub.0.25Ti.sub.0.03B.sub.0.05P.sub.0.02O.sub.2.

    [0068] The preparation method was basically the same as that in Embodiment 1, except that step (5) was replaced by: 2.0 mol of Ni.sub.0.5Mn.sub.0.5 (OH).sub.2, 0.8 mol of Fe.sub.2O.sub.3, 0.12 mol of TiO.sub.2, 0.2 mol of H.sub.3B.sub.0.3, 0.08 mol of H.sub.3PO.sub.4, 2.0 mol of Na.sub.3CO.sub.3 were added into 3.5 L of water to prepare a slurry. The sample was named NFM242-TBP.

    [0069] The scanning electron microscope image of NFM242-TBP is shown in FIG. 5, and it can be seen that the material has a single crystal morphology. The XRD pattern of NFM242-TBP is shown in FIG. 6, and it can be seen that the material is ?-NaFeO.sub.2 type pure phase layered structure. The charge-discharge curve of NFM242-TBP is shown in FIG. 7, and it can be seen that within the voltage window of 2.0-4.0V, the specific discharge capacity at a rate of 0.1 C is 125 mAh/g. The high-temperature cycling diagram of NFM242-TBP is shown in FIG. 8, and it can be seen that at 60? C., within the voltage window of 2.0-4.0 V, the capacity retention rate is 93.31% after 100 cycles at a rate of 1 C.

    Embodiment 3

    [0070] The chemical formula of the cathode active material for sodium-ion batteries of this embodiment is NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ti.sub.0.05P.sub.0.05O.sub.2.

    [0071] The preparation method was basically the same as that in Embodiment 1, except that step (5) was replaced by: 2.0 mol of Ni.sub.0.5Mn.sub.0.5(OH).sub.2, 0.8 mol of Fe.sub.2O.sub.3, 0.20 mol of TiO.sub.2, 0.2 mol of H.sub.3PO.sub.4 and 2.0 mol of Na.sub.2CO.sub.3 were added into 3.5 L of water to prepare a slurry. After sand grinding, spray drying, sintering, jaw breaking, rolling, and crushing, the final obtained cathode active material for sodium-ion batteries was NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ti.sub.0.05P.sub.0.05O.sub.2, named NFM242-TP.

    Embodiment 4

    [0072] The chemical formula of the cathode active material for sodium-ion batteries of this embodiment is NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ca.sub.0.05B.sub.0.05O.sub.2.

    [0073] The preparation method was basically the same as that in Embodiment 1, except that step (5) was replaced by: 2.0 mol of Ni.sub.0.5Mn.sub.0.5(OH).sub.2, 0.8 mol of Fe.sub.2O.sub.3, 0.2 mol of CaCO.sub.3, 0.2 mol of H.sub.3B.sub.0.3 and 2.0 mol of Na.sub.2CO.sub.3 were added into 3.5 L of water to prepare a slurry. After sand grinding, spray drying, sintering, jaw breaking, rolling, and crushing, the final obtained cathode active material for sodium-ion batteries was NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ca.sub.0.05B.sub.0.05O.sub.2, named NFM242-CaB.

    Embodiment 5

    [0074] The chemical formula of the cathode active material for sodium-ion batteries of this embodiment is NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ca.sub.0.05P.sub.0.05O.sub.2.

    [0075] The preparation method was basically the same as that in Embodiment 1, except that step (5) was replaced by: 2.0 mol of Ni.sub.0.5Mn.sub.0.5(OH).sub.2, 0.8 mol of Fe.sub.2O.sub.3, 0.2 mol of CaCO.sub.3, 0.2 mol of H.sub.3PO.sub.4 and 2.0 mol of Na.sub.2CO.sub.3 were added into 3.5 L of water to prepare a slurry. After sand grinding, spray drying, sintering, jaw breaking, rolling, and crushing, the final obtained cathode active material for sodium-ion batteries was NaNi.sub.0.25Fe.sub.0.4Mn.sub.0.25Ca.sub.0.05P.sub.0.05O.sub.2, named NFM242-CaP.

    Embodiment 6

    [0076] The chemical formula of the cathode active material for sodium-ion batteries of this embodiment is NaNi.sub.0.25Fe.sub.0.40Mn.sub.0.25Ca.sub.0.03B.sub.0.05P.sub.0.02O.sub.2.

    [0077] The preparation method was basically the same as that in Embodiment 1, except that step (5) was replaced by: 2.0 mol of Ni.sub.0.5Mn.sub.0.5(OH).sub.2, 0.8 mol of Fe.sub.2O.sub.3, 0.2 mol of CaCO.sub.3, 0.2 mol of H.sub.3B.sub.0.3, 0.08 mol of H.sub.3PO.sub.4 and 2.0 mol of Na.sub.2CO.sub.3 were added into 3.5 L of water to prepare a slurry. After sand grinding, spray drying, sintering, jaw breaking, rolling, and crushing, the final obtained cathode active material for sodium-ion batteries was NaNi.sub.0.25Fe.sub.0.40Mn.sub.0.25Ca.sub.0.03B.sub.0.05P.sub.0.02O.sub.2, named NFM242-CaBP.

    Comparative Example 1

    [0078] It was basically the same as Embodiment 1, except that step (5) was replaced by: 2.0 mol of Ni.sub.0.5Mn.sub.0.5 (OH).sub.2, 0.9 mol of Fe.sub.2O.sub.3, 0.2 mol of TiO.sub.2 and 2.0 mol of Na.sub.2CO.sub.3 were added into 3.5 L of water to prepare a slurry. After sand grinding, spray drying, sintering, jaw breaking, rolling, and crushing, the final obtained cathode active material for sodium-ion batteries was NaNi.sub.0.25Fe.sub.0.45Mn.sub.0.25Ti.sub.0.05O.sub.2, named NFM242-T.

    [0079] The scanning electron microscope image of NFM242-T is shown in FIG. 9, and it can be seen that the material is a loose spherical structure formed by the aggregation of fine primary particles, which cannot form a single-crystal structure. The XRD pattern of NFM242-T is shown in FIG. 10, and it can be seen that the material is ?-NaFeO.sub.2 type pure phase layered structure. The charge-discharge curve of NFM242-T is shown in FIG. 11, and it can be seen that within the voltage window of 2.0-4.0V, the discharge grain capacity at a rate of 0.1 C is 126.6 mAh/g. The high-temperature cycling diagram of NFM242-T is shown in FIG. 12, and it can be seen that at 60? C., within the voltage window of 2.0-4.0 V, the capacity retention rate is 82.8% after 100 cycles at a rate of 1 C.

    Comparative Example 2

    [0080] It was basically the same as Embodiment 1, except that step (5) was replaced by: 2.0 mol of Ni.sub.0.5Mn.sub.0.5(OH).sub.2, 0.9 mol of Fe.sub.2O.sub.3, 0.2 mol of CaCO.sub.3 and 2.0 mol of Na.sub.2CO.sub.3 were added into 3.5 L of water to prepare a slurry. After sand grinding, spray drying, sintering, jaw breaking, rolling, and crushing, the final obtained cathode active material for sodium-ion batteries was NaNi.sub.0.25Fe.sub.0.45Mn.sub.0.25Ca.sub.0.05O.sub.2, named NFM242-Ca.

    Comparative Example 3

    [0081] It was basically the same as Embodiment 1, except that step (5) was replaced by: 2.0 mol of Ni.sub.0.5Mn.sub.0.5 (OH).sub.2, 1.0 mol of Fe.sub.2O.sub.3 and 2.0 mol of Na.sub.3CO.sub.3 were added into 3.5 L of water to prepare a slurry. After sand grinding, spray drying, sintering, jaw breaking, rolling, and crushing, the final obtained cathode active material for sodium-ion batteries was NaNi.sub.0.25Fe.sub.0.50Mn.sub.0.25O.sub.2, named NFM252.

    Performance Testing

    [0082] The physicochemical properties of the cathode active materials prepared in the above Embodiments 1 to 7 and Comparative examples 1 to 3 were tested, and the pH test method was: weighing 5 g of the prepared layered oxide cathode material and dispersing it into 50 mL of deionized water, stirring in a magnetic stirrer for 5 min, then standing at 25? C. for 30 min, filtering the mixed solution, and testing the pH of the filtrate with a pH meter. The physicochemical property results are shown in Table 1.

    TABLE-US-00001 TABLE 1 Physicochemical properties of cathode active materials Specific Tap surface Sample D10/ D50/ D90/ density area No. name ?m ?m ?m (g/cm.sup.3) (m.sup.2/g) pH Embodiment NFM242- 2.08 7.72 17.87 1.98 0.59 12.25 1 TB Embodiment NFM242- 3.02 7.24 18.54 2.06 0.54 12.07 2 TBP Embodiment NFM242- 1.18 4.43 13.19 1.37 1.31 12.43 3 TP Embodiment NFM242- 1.41 7.92 19.78 1.94 0.62 12.30 4 CaB Embodiment NFM242- 1.48 4.36 15.24 1.33 1.47 12.45 5 CaP Embodiment NFM242- 2.08 7.04 20.24 2.01 0.56 12.19 6 CaBP Comparative NFM242- 1.70 3.85 10.42 1.35 1.55 12.82 example 1 T Comparative NFM242- 1.20 4.66 11.92 1.40 1.53 12.90 example 2 Ca Comparative NFM252 0.32 3.65 21.59 1.28 1.60 12.88 example 3

    [0083] The performance of sodium-ion batteries used the cathode active materials prepared in the above Embodiments 1 to 7 and Comparative examples 1 to 3 was tested, and the method for preparing a sodium-ion battery was: 20 g of prepared cathode active material was weighed, 0.64 g of conductive agent SP and 0.64 g of PVDF dissolved in NMP were added, mixed evenly, and coated on aluminum foil to make an electrode plate. In a glove box in argon atmosphere, a button cell was assembled with a metal sodium sheet as the anode, Celgard2700 as the diaphragm, and 1 mol/L NaPF.sub.6+EC:DEC (1:1)+5% FEC as the electrolyte. Then, the charge-discharge curve was tested at a voltage range of 2.0-4.0 V, a charge discharge rate of 0.1 C, a current of 13 mA, and a test temperature of 25?2? C., and the cycling performance was tested for 100 cycles at a voltage range of 2.0-4.0 V, a charge discharge rate of 1 C, a current of 130 mA, and 60? C. The test results are shown in Table 2 below.

    TABLE-US-00002 TABLE 2 Performance of sodium-ion batteries Initial discharge Discharge gram Discharge gram gram capacity capacity after 1 capacity after 100 (mAh/g) cycle (mAh/g) cycles (mAh/g) Retention after No. Sample name 0.1 C, 25? C. 1 C, 60? C. 1 C, 60? C. 100 cycles (%) Embodiment 1 NFM242-TB 124.8 117.6 104.7 89.04% Embodiment 2 NFM242-TBP 125.0 119.8 111.8 93.31% Embodiment 3 NFM242-TP 125.3 118.6 102.6 86.50% Embodiment 4 NFM242-CaB 126.1 119.4 105.7 88.56% Embodiment 5 NFM242-CaP 125.6 118.0 99.4 84.26% Embodiment 6 NFM242-CaBP 125.1 117.4 108.6 92.47% Comparative NFM242-T 126.6 120.0 99.3 82.80% example 1 Comparative NFM242-Ca 127.3 120.5 96.7 80.29% example 2 Comparative NFM252 131.8 120.9 93.0 76.95% example 3

    [0084] From Tables 1-2 above, it can be seen that by adding B and P elements to the cathode active material for sodium-ion batteries, and controlling the ratio of all elements, the present disclosure can achieve the formation of a perfect layered single-crystal structure of the cathode active material, with large single-crystal particles and dense growth, the cathode active material has a significantly increased tap density, low pH, stable surface properties, and minimal side reactions with electrolytes, and when used in sodium-ion batteries, it can significantly improve the cycling performance at high temperatures while ensuring high grain capacity.

    [0085] The embodiments described above are only for illustrating the technical concepts and features of the present disclosure, and are intended to make those skilled in the art being able to understand the present disclosure and thereby implement it, and should not be concluded to limit the protective scope of this disclosure. Any equivalent variations or modifications according to the spirit of the present disclosure should be covered by the protective scope of the present disclosure.