Articles including ITO inclusive coatings and/or methods of making the same

Abstract

Certain example embodiments of this invention relate to articles including anticondensation coatings that are exposed to an external environment, and/or methods of making the same. In certain example embodiments, the anticondensation coatings may be survivable in an outside environment. The coatings also may have a sufficiently low sheet resistance and hemispherical emissivity such that the glass surface is more likely to retain heat from the interior area, thereby reducing (and sometimes completely eliminating) the presence condensation thereon. The articles of certain example embodiments may be, for example, skylights, vehicle windows or windshields, IG units, VIG units, refrigerator/freezer doors, and/or the like.

Claims

1. A laminated coated article, for use in a window, comprising: a coating supported by a first glass substrate, a second glass substrate, wherein the first and second glass substrates are laminated, wherein: the coating comprises the following thin-film layers moving away from the first glass substrate: a dielectric layer comprising silicon nitride; a transparent conductive layer comprising indium tin oxide (ITO), a layer comprising silicon oxynitride located over and directly contacting the transparent conductive layer comprising indium tin oxide (ITO), a protective layer comprising oxygen and aluminum, the protective layer comprising oxygen and aluminum being located over the silicon-inclusive contact layer; wherein the protective layer comprising oxygen and aluminum is the outermost layer of the coating and is to be exposed to an environment adjacent the window; wherein the coating is disposed on a surface of the first glass substrate so that the first glass substrate is located between the coating and the second glass substrate, and wherein the coating is not located between the first and second glass substrates, and wherein the coating has a hemispherical emissivity of less than 0.23 and a sheet resistance of less than 30 ohms/square.

2. The coated article of claim 1, wherein the coated article has a visible transmission of at least 70%.

3. The coated article of claim 1, wherein the transparent conductive layer comprising indium tin oxide (ITO) is located over and directly contacting the dielectric layer comprising silicon nitride.

4. The coated article of claim 3, wherein the coating further comprises another dielectric layer located between the glass substrate and the dielectric layer comprising silicon nitride.

5. The coated article of claim 1, wherein the transparent conductive layer consists essentially of ITO.

6. The coated article of claim 1, wherein the coated article is provided in a vehicle windshield.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) These and other features and advantages may be better and more completely understood by reference to the following detailed description of exemplary illustrative embodiments in conjunction with the drawings, of which:

(2) FIG. 1 is a coated article including an anticondensation coating in accordance with an example embodiment;

(3) FIG. 2 is an insulating glass unit including an anticondensation coating disposed on an outermost surface exposed to the exterior atmosphere in accordance with an example embodiment;

(4) FIG. 3 is an insulating glass unit including an anticondensation coating disposed on an innermost surface exposed to the interior environment in accordance with an example embodiment;

(5) FIG. 4 is an insulating glass unit including anticondensation coatings disposed on outermost and innermost surfaces of the insulating glass unit in accordance with an example embodiment; and

(6) FIG. 5 is a graph illustrating the performance of an example embodiment, a current anticondensation product, and a bare glass substrate as the temperature, humidity, and dew point change over an 18 hour time period.

DETAILED DESCRIPTION OF EXAMPLE EMBODIMENTS OF THE INVENTION

(7) Certain example embodiments of this invention relate to thin-film anticondensation coatings that are exposed to the environment. Such coatings have a low hemispherical emissivity in certain example embodiments, which helps the glass surface retain heat provided from the interior side. For instance, in skylight and/or other building window example applications, the glass surface retains more heat from the interior of the building. In vehicle example applications, the windshield retains more heat from the interior of the vehicle. This helps reduce (and sometimes even prevent) the initial formation of condensation. As alluded to above, such anticondensation coatings may be provided on a surface (or multiple surfaces) exposed to the environment in certain example instances. As such, the anticondensation coatings of certain example embodiments may be robust so as to be able to survive such conditions.

(8) FIG. 1 is a coated article including an anticondensation coating in accordance with an example embodiment. The FIG. 1 example embodiment includes a glass substrate 1 supporting a multilayer thin-film anticondensation coating 3. The anticondensation coating 3 has a low hemispherical emissivity. In certain example embodiments, the hemispherical emissivity is less than 0.25, more preferably less than 0.23, still more preferably less than 0.2, and sometimes even less than 1.0-1.5. This is achieved by providing a thin transparent conductive oxide layer (TCO) 5 such that a suitably low sheet resistance is achieved. In the FIG. 1 example, the TCO 5 is indium tin oxide (ITO). A sheet resistance of the 10-30 ohms/square generally will be sufficient to achieve the desired hemispherical emissivity values. Certain example embodiments described herein provide a sheet resistance of 13-27 ohms/square, with the example provided below providing a sheet resistance of 17 ohms/square. In certain example instances, it is possible to select a TCO 5 such that the sheet resistance drops to as low as about 5 ohms/square, although this low value is not need in all embodiments of this invention.

(9) The TCO 5 is protected from the environment by a layer or zirconium oxide 7. A silicon-inclusive barrier layer 11 may be provided between the TCO 5 and the substrate 1 also to help protect the TCO 5, e.g., from sodium migration. In the FIG. 1 example, the silicon-inclusive barrier layer 11 is silicon nitride, and the silicon nitride barrier layer 11 is provided adjacent to a layer of titanium oxide 13. The silicon nitride barrier layer 11 and the layer of titanium oxide 13 in the FIG. 1 example help with the optics of the overall article. It will be appreciated that a low/high/low layer stack system also may be used to improve the optics of the end product in certain example instances. In certain example embodiments, the silicon nitride barrier layer 11 may be oxided, e.g., so that it is a layer of silicon oxynitride. In certain example embodiments, a barrier layer comprising silicon nitride (e.g., Si.sub.3N.sub.4 or other suitable stoichiometry) may replace the silicon-inclusive barrier layer 11 and the titanium oxide layer 13 in the FIG. 1 example.

(10) Additional silicon-inclusive layers 9a and 9b may sandwich the TCO 5. As shown in the FIG. 1 example, the upper silicon-inclusive layer 9a is a layer of silicon nitride, whereas the lower silicon-inclusive layer 9b is a layer of silicon oxynitride. It will be appreciated that any suitable combination of silicon with oxygen and/or nitrogen may be used in different embodiments of this invention.

(11) The following table provides example physical thicknesses and thickness ranges for the FIG. 1 example embodiment:

(12) TABLE-US-00001 Example Thickness Range (nm) Example Thickness (nm) ZrOx 2-15 7 SiNx 10-50 30 ITO 75-175 130 SiOxNy 10-50 35 TiOx 2-10 3.5 SiNx 10-20 13

(13) As indicated above, other TCOs may be used in place of, or in addition to, ITO. For instance, certain example embodiments may incorporate an ITO/Ag/ITO sandwich. Certain example embodiments, may incorporate zinc oxide, aluminum-doped zinc oxide (AZO), p-type aluminum oxide, doped or un-doped Ag, FTO, and/or the like. When Ag is incorporated into the layer stack system as a TCO, layers comprising Ni and/or Cr may be provided directly adjacent (contacting) the Ag. In certain example embodiments, each layer in the layer stack system may be sputter-deposited. In certain example embodiments, one or more layers may be deposited using a different technique. For instance, when FTO is incorporated as the TCO 5, it may be pyrolytically deposited (e.g., using combustion vapor deposition or CVD).

(14) In certain example embodiments, layer of diamond-like carbon (DLC) may be provided directly over and contacting the zirconium oxide. This may help to create a more survivable, hydrophilic-like coating in certain example instances. Hydrophilic coatings generally involve a contact angle of less than or equal to 10 degrees. Sputter-deposited zirconium oxide tends to have a contact angle of less than about 20 degrees. However, forming DLC on top of the DLC on top of the zirconium oxide helps with its wettability and creates a harder layer. When tempered, for example, a zirconium oxide/DLC layer stack reaches a contact angle of less than or equal to about 15 degrees. Thus, a survivable, hydrophilic-like coating may be achieved. It is noted that this layer may be created by providing a layer of zirconium nitride followed by a layer of DLC which, upon tempering, will produce a layer of zirconium oxide followed by a layer of DLC. See, for example, Applicant Ser. No. 12/320,664, which describes a heat treatable coated article including DLC and/or zirconium in its coating. The entire contents of this application are hereby incorporated herein by reference.

(15) In addition or in the alternative, in certain example embodiments, a thin hydrophilic and/or photocatalytic coating may be provided over the zirconium oxide. Such a layer may comprise anatase TiO.sub.2, BiO, BiZr, BiSn, SnO, and/or any other suitable material. Such a layer also may help with wettability and/or provide self-cleaning properties to the article.

(16) In certain example embodiments, the zirconium oxide protective layer 7 may be replaced with aluminum oxide and/or aluminum oxide.

(17) Although not shown in the FIG. 1 example, a silver-based low-E coating may be provided on the glass substrate opposite the anticondensation coating 3. For example, the silver-based low-E coating may be any one of the low-E coatings described in application Ser. Nos. 12/385,234; 12/385,802; 12/461,792; 12/591,611; and Ser. No. 12/654,594, the entire contents of which are hereby incorporated herein by reference. Of course, other low-E coatings commercially available from the assignee of the instant invention and/or other low-E coatings also may be used in connection with different embodiments of this invention. When the coated article is tempered, it may be run through a tempering furnace face down. In other words, when the coated article is tempered, the anticondensation coating may face the rollers.

(18) In certain example embodiments, the visible transmission may be high when an anticondensation coating is applied. For example, in certain example embodiments, the visible transmission preferably will be at least about 50%, more preferably at least about 60%, still more preferably at least about 65%. In certain example embodiments, the visible transmission may be 70%, 80%, or even higher.

(19) The coated article shown in FIG. 1 may be incorporated into a insulating glass (IG) unit. For example, FIG. 2 is an insulating glass unit including an anticondensation coating disposed on an outermost surface exposed to the exterior atmosphere in accordance with an example embodiment. The IG unit in the FIG. 2 example includes first and second substantially parallel spaced apart glass substrates 1 and 21. These substrates define a space or gap 22 therebetween. The first and second substrates 1 and 21 are sealed using an edge seal 23, and a plurality of pillars 25 help maintain the distance between the first and second substrates 1 and 21. The first substrate 1 supports the anticondensation coating 3. As will be appreciated from the FIG. 2 example embodiment, the anticondensation coating 3 is exposed to the exterior environment. This is a departure from common practices, where low-E coatings generally are protected from the external environment. The FIG. 2 arrangement becomes possible because of the durability of the anticondensation coating 3.

(20) Although not shown in FIG. 2, similar to as described above, a low-E coating (e.g., a silver-based low-E coating) may be provided on an interior surface of one of the first and second substrates 1 and 21. In other words, although not shown in FIG. 2, a low-E coating may be provided on surface 2 or surface 3 of the IG unit shown in FIG. 2.

(21) When the FIG. 2 example embodiment is provided in connection with a skylight application, for example, the outer substrate 1 may be tempered and the inner substrate 21 may be laminated, e.g., for safety purposes. This may be true of other IG unit products, as well, depending on the desired application. In addition, it will be appreciated that the IG unit structure shown in the FIG. 2 example may be used in connection with generally vertical and generally horizontal applications. In other words, the IG unit structure shown in the FIG. 2 example may be used in refrigerator/freezer doors that are either generally upright or generally horizontal.

(22) In certain example embodiments, the space or gap 22 between the first and second substrates 1 and 21 may be evacuated and/or filed with an inert gas (such as argon, for example), and the edge seal 23 may provide an hermetic seal, e.g., in forming a vacuum insulated glass (VIG) unit.

(23) FIG. 2 shows an IG unit having two glass substrates. However, the example anticondensation coatings described herein may be used in connection with products that contain first, second, and third substantially parallel and spaced apart glass substrates (also sometimes referred to as triple-glaze products). The anticondensation coating may be disposed on surface 1 (the outermost surface exposed to the environment), and low-E coatings may be disposed on one or more interior surfaces (surfaces other than surface 1 and surface 6). For example, the anticondensation coating may be disposed on surface 1, and low-E coatings may be disposed on surfaces 2 and 5, 3 and 5, etc., in different embodiments of this invention. Such triple-glaze products may be IG units containing three lites or substrates, trip VIG units containing three lites or substrates, etc., in different embodiments of this invention.

(24) As indicated above, certain example embodiments may be used in connection with vehicle windshields, windows, mirrors, and/or the like. The hemispherical emissivity of the exterior glass surfaces of a vehicle typically is greater than about 0.84. However, by reducing the hemispherical emissivity to the above-identified (and/or other) ranges, the glass surface may retain more heat provided by the interior of the vehicle. This, in turn, may result in reduced or eliminated condensation buildup on the lite surface when a moving vehicle goes from colder to warmer climate (e.g., in hilly areas), reduced or eliminated condensation and/or frost buildup on the lite when parked and left over night, etc. The anticondensation coating in vehicle applications may be provided on the side of the glass that is exterior to the vehicle cabin.

(25) The zirconium oxide topcoat is advantageous for vehicle window applications, as it has a comparatively low coefficient of friction. More particularly, this lower coefficient of friction facilitates the upward and downward movement of windows.

(26) Certain example embodiments may be used in connection with any suitable vehicle including, for example, automobiles; trucks; trains; boats, ships and other vessels; airplanes; tractors and other work equipment; etc. In vehicle mirror applications, the optics of the coating may be tune such that a double reflection does not occur.

(27) The inventors of the instant application have also realized that the anticondensation coating of certain example embodiments may be used to help meet the so-called 0.30/0.30 standard. Briefly, the 0.30/0.30 standard refers to a U-value of less than or equal to 0.30 and a solar heat gain coefficient (SHGC) of less than or equal to 0.30. Current legislation in the U.S. would give a tax credit for investing in windows, skylights, doors, etc., that meet these criteria.

(28) FIG. 3 is an insulating glass unit including an anticondensation coating disposed on an innermost surface exposed to the interior environment in accordance with an example embodiment. The FIG. 3 example embodiment is similar to the FIG. 2 example embodiment, except that the FIG. 3 example embodiment has the anticondensation coating 3 located on surface 4, which is the exterior surface of the inner glass substrate 1 that is exposed to the building interior rather than the outside environment.

(29) In certain example embodiments, the inner substrate 1 may be annealed (rather than tempered). The anticondensation coating may remain the same or substantially the same as between the FIG. 2 and FIG. 3 example embodiments, although the modifications described above in connection with FIGS. 1 and 2 also may be made in connection with an embodiment like FIG. 3. One change that might be made is increasing the thickness of the ITO to achieve the desired U-value performance. In such cases where the ITO is thickened, the thicknesses of the other layers may also be adjusted so that the desired optical properties are achieved. Additional layers also may be added to achieve the desired optical properties. The other structural elements remain the same as between FIGS. 2 and 3, and similar modifications may be made thereto.

(30) When the anticondensation coating 3 is disposed on surface 4 as shown in FIG. 3, the U-value has been determined to be 0.29. When an additional low-E coating is provided on surface 2 of the IG unit, the U-value has been found to drop to 0.23. Certain example embodiments also may provide a SHGC less than or equal to 0.30, thereby helping meet the 0.301.30 standard.

(31) In products with low U-values (e.g., IG or VIG units with the anticondensation coating on surface 4, two- and three-lite VIG units, etc.), condensation can become a problem, e.g., as the glass is not heated because of the low-emissivity coatings. One solution to this challenge is presented in FIG. 4, which is an insulating glass unit including anticondensation coatings disposed on outermost and innermost surfaces of the insulating glass unit in accordance with an example embodiment. In the FIG. 4 example, first and second substrates 1a and 1b are provided. First and second anticondensation coatings 3a and 3b are provided on surfaces 1 and 4, respectively. In certain example embodiments, additional low-E coatings also may be provided on one or both of the inner surfaces (surfaces 2 and/or 3). In this way, it is possible to provide a product that exhibits U-value reduction and anticondensation behaviors.

(32) FIG. 5 is a graph illustrating the performance of an example embodiment, a current anti condensation product, and a bare glass substrate as the temperature, humidity, and dew point change over an 18 hour time period. The images in FIG. 5 each have a crisscross pattern printed thereon to help demonstrate the presence or absence of condensation. As can be seen from FIG. 5, there is virtually no condensation formed on those samples that were produced in accordance with an example embodiment. By contrast, the comparative example, which includes pyrolytically deposited FTO, shows some condensation being formed in the first observed period, with the level of condensation greatly increasing through the second and third observed periods, and abating slightly by the fourth observed period. Indeed, the crisscross pattern is significantly blurry at the second observed period and barely visible during the third. The uncoated glass sample shows significant condensation during all observed periods. The crisscross pattern in the second and third observed periods cannot be seen. The FIG. 5 example thus demonstrates that the example embodiments described herein provide superior performance when compared to the current comparative example and uncoated glass.

(33) Peripheral and edge seals herein do not mean that the seals are located at the absolute periphery or edge of the unit, but instead mean that the seal is at least partially located at or near (e.g., within about two inches) an edge of at least one substrate of the unit. Likewise, edge as used herein is not limited to the absolute edge of a glass substrate but also may include an area at or near (e.g., within about two inches) of an absolute edge of the substrate(s).

(34) As used herein, the terms on, supported by, and the like should not be interpreted to mean that two elements are directly adjacent to one another unless explicitly stated. In other words, a first layer may be said to be on or supported by a second layer, even if there are one or more layers therebetween.

(35) While the invention has been described in connection with what is presently considered to be the most practical and preferred embodiment, it is to be understood that the invention is not to be limited to the disclosed embodiment, but on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims.