Olive oil-tuned broadband conjugated polymer laser medium

Abstract

The olive oil-tuned broadband conjugated polymer laser medium includes the conjugated polymer known as poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)) or Poly(FV-co-MEHPV) at a 90:10 mole ratio. The emission wavelength of the olive oil tuned broadband conjugated polymer laser can be reversibly tuned between 500 nm and 680 nm.

Claims

1. A method of producing an olive oil-tuned broadband conjugated polymer laser medium, comprising the steps of: providing poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)); providing a compound of olive oil as a dye material; and dissolving the poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)) in the compound of olive oil under heat and continuous stirring to obtain a homogenous solution, wherein the homogenous solution is excited under a pulsed laser source having a ?.sub.ex=355 nm, wherein the compound of olive oil is CH.sub.3(CH.sub.2).sub.nCOOH where n is a number between 12 and 22.

2. The method of producing an olive oil-tuned broadband conjugated polymer laser medium of claim 1, wherein said homogenous solution of poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)) and the compound of olive oil as a dye material is prepared by dissolving the poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)) of the compound of olive oil with the aid of heat and continuous stirring.

3. The method of producing an olive oil-tuned broadband conjugated polymer laser medium of claim 2, wherein a solubility of the poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)) increases with increasing temperature.

4. The method of producing an olive oil-tuned broadband conjugated polymer laser medium as recited in claim 1, wherein a third harmonic of 355 nm of an Nd: YAG laser is used as an excitation source.

5. The method of producing an olive oil-tuned broadband conjugated polymer laser medium according to claim 4, wherein a UV laser was focused by a quartz cylindrical lens of a focal length of 5 cm.

6. The method of producing an olive oil-tuned broadband conjugated polymer laser medium as recited in claim 1, wherein absorption spectrum of the conjugated polymer in the compound of olive oil occurs at five bands of 421, 450, 535, 610, and 670 nm, respectively.

7. An olive oil-tuned broadband conjugated polymer laser medium, comprising a mixture of: poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)); and a compound of olive oil as a dye material, wherein the poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)) is dissolved in the compound of olive oil under heat and continuous stirring to obtain a homogenous solution, wherein the homogenous solution is excited under a pulsed laser source having a ?.sub.ex=355 nm, and wherein the poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)) and the compound of olive oil solution is prepared by dissolving the poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)) in the compound of olive oil with the aid of heat and continuous stirring, wherein the compound of olive oil is CH.sub.3 (CH.sub.2).sub.nCOOH where n is a number between 12 and 22.

8. The method of producing an olive oil-tuned broadband conjugated polymer laser medium as recited in claim 1, wherein tunability depends on the concentration of the poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)).

9. The method of producing an olive oil-tuned broadband conjugated polymer laser medium as recited in claim 1, wherein a fluorescence spectrum of the conjugated polymer showed four bands at 505, 535, 577, and 680 nm, respectively.

10. The method of producing an olive oil-tuned broadband conjugated polymer laser medium as recited in claim 1, wherein the pulsed laser source is capable of working in both a pulsed and continuous wave modes.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is the structural formula for Poly(FV-co-MEHPV) polymer.

(2) FIG. 2 is a schematic diagram of an exemplary experimental setup for testing the olive oil-tuned broadband conjugated polymer laser medium.

(3) FIG. 3 is an absorption spectrum of the conjugated polymer of FIG. 1 in olive oil.

(4) FIG. 4 is a fluorescence spectrum of the conjugated polymer of FIG. 1 in olive oil.

(5) FIG. 5 is a laser spectrum of the conjugated polymer of FIG. 1 in olive oil at a temperature of 420 K.

(6) FIG. 6 is a laser spectrum of the conjugated polymer of FIG. 1 in olive oil at a temperature of 350 K.

(7) FIG. 7 is a laser spectrum of the conjugated polymer of FIG. 1 in olive oil at a temperature of 300 K.

(8) Similar reference characters denote corresponding features consistently throughout the attached drawings.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

(9) The olive oil-tuned broadband conjugated polymer laser medium includes olive oil and poly ((9,9-dihexyl-9H-fluorene-2,7-vinylene)-co-(1-methoxy-4-(2-ethylhexyloxy)-2,5-phenylenevinylene)), also referred to herein as Poly(FV-co-MEHPV), at a 90:10 mole ratio. The structural formula for Poly(FV-co-MEHPV) is shown in FIG. 1. The emission wavelength of the olive oil-tuned broadband conjugated polymer laser medium or conjugated polymer in olive oil can be reversibly tuned in the range of 500 nm to 700 nm, for example, 500 nm to 680 nm. The tuning range can be changed by changing the temperature of the medium.

(10) The olive oil-tuned broadband conjugated polymer laser medium demonstrates amplified spontaneous emission (ASE) at suitable concentration, temperature, and pump energy values. Under the pumping technique of Nd:YAG laser, for example, the olive oil-tuned broadband conjugated polymer laser medium produces ASE. The ASE wavelength can be tuned between 500 nm and 700 nm by changing the temperature of the laser medium within a temperature range of 300 K to 420 K (FIGS. 5-7).

(11) An embodiment of the present teachings is directed to a high-power and temperature-tunable laser based on the olive oil-tuned broadband conjugated polymer laser medium. The wavelength of the laser can be controlled in the 500 nm to 700 nm range by varying the temperature of the laser medium. The temperature can be varied within a temperature range of 300 K to 420 K.

(12) A method of producing the olive-oil tuned broadband conjugated polymer laser medium can include dissolving poly (FV-co-MEHPV) in olive oil over heat while stirring to produce a solution of poly (FV-co-MEHPV) in olive oil or the olive oil-tuned broadband conjugated polymer lasing medium.

(13) The poly (FV-co-MEHPV) in olive oil can produce a broadband laser ranging from 500 nm to 700 nm, for example from 500 nm to 680 nm. The olive oil-tuned broadband conjugated polymer laser medium is capable of working in pulsed and continuous wave (CW) mode. The olive oil-tuned broadband conjugated polymer laser medium is an environmentally friendly material that can be utilized in laser technology instead of toxic and/or carcinogenic solvents typically used as lasing media.

(14) The present disclosure may be better understood in view of the following examples, which are illustrative only and are not intended to limit the present teachings.

Example 1

(15) Preparation and Testing of (FV-Co-MEHPV)

(16) The olive oil-tuned broadband conjugate polymer laser medium was prepared by dissolving poly (FV-co-MEHPV) in olive oil over heat while stirring. The poly (FV-co-MEHPV) was purchased from AMERICAN DYE SOURCE Inc. The absorption and fluorescence spectra of the resulting solution including the conjugated polymer in olive oil were determined.

(17) FIG. 3 shows the absorption spectrum of the conjugated polymer in olive oil. As shown, there are five bands, at 421, 450, 535, 610, and 670 nm. FIG. 4 shows fluorescence spectrum of the conjugated polymer in olive oil. The fluorescence spectrum showed four bands, at 505, 535, 577, and 680 nm.

Example 2

(18) Experimental Use of the Olive Oil Tuned Broadband Conjugated Polymer Laser

(19) A schematic diagram of the experimental setup of the olive oil-tuned broadband conjugated polymer laser medium is shown in FIG. 2. The third harmonic (355 nm) of an Nd:YAG laser, with a pulse width of 9 ns, was used as the excitation source. The UV laser was focused by a quartz cylindrical lens of a focal length of 5 cm, which was used to do transverse excitation of the FV-co-MEHPV dissolved in olive oil, taken in a four-side polished quartz cell, which was kept canted to avoid feedback. At certain values of pump power, temperature, and concentration of FV-co-MEHPV, an amplified spontaneous emission (ASE) beam was emitted as a cone of light. This was collected by a 1-mm entrance slit of an ICCD camera to obtain the spectral features of ASE. The results revealed that the poly (FV-co-MEHPV) in olive oil could produce a broadband laser ranging from 500 nm to 680 nm.

(20) FIG. 5 shows laser spectra of the conjugated polymer in olive oil at a temperature of 420 K. FIG. 6 shows laser spectra of the conjugated polymer in olive oil at a temperature of 350 K. FIG. 7 shows laser spectra of the conjugated polymer in olive oil at a temperature of 300 K.

(21) It is to be understood that the olive oil-tuned broadband conjugated polymer laser medium is not limited to the specific embodiments described above but encompasses any and all embodiments within the scope of the generic language of the following claims enabled by the embodiments described herein, or otherwise shown in the drawings or described above in terms sufficient to enable one of ordinary skill in the art to make and use the claimed subject matter.