Collagen-coated tissue-based membranes

Abstract

A collagen-coated tissue-based membrane that is smooth on both sides so as to inhibit cell and tissue adhesion. The tissue-based membrane is a serous membrane having a fibrous surface and a smooth surface and the collagen is coated on the fibrous surface. Also provided are methods for making the collagen-coated tissue-based membrane.

Claims

1. A tissue-based coated membrane, comprising a serous membrane and a type I collagen coating, wherein the serous membrane has a fibrous surface and a smooth surface, the type I collagen coating, having a thickness of 5 m to 100 m, is in contact with the fibrous surface, wherein the type I collagen coating is present as a single layer, the type I collagen-coated fibrous surface being smooth, and both the type I collagen-coated fibrous surface and the smooth surface adhere poorly to cells and tissues.

2. The tissue-based membrane of claim 1, wherein the serous membrane is pericardium, peritoneum, amnion, small intestine submucosa, pleural, or vaginal tunics.

3. The tissue-based membrane of claim 1, wherein the serous membrane is pericardium or peritoneum.

4. A biocompatible collagen-coated serous membrane prepared by the steps of: scraping a fibrous side of a serous membrane to remove adhering fibers; treating the serous membrane to remove cells, lipids, and extractable blood and non-collagenous molecules; freeze-drying the treated serous membrane; compressing the fibrous side of the serous membrane; coating type I collagen onto the fibrous side of the serous membrane, thereby rendering the fibrous side of the serous membrane smooth, wherein the type I collagen is coated onto the fibrous side of the serous membrane in a single layer; and exposing the type I collagen-coated serous membrane to a crosslinking agent to effect crosslinking, wherein the type I collagen coating has a thickness of 5 m to 100 m.

5. A biocompatible collagen-coated serous membrane prepared by the steps of: scraping a fibrous side of a serous membrane to remove adhering fibers; treating the serous membrane to remove cells, lipids, and extractable blood and non-collagenous molecules; freeze-drying the treated serous membrane; compressing the fibrous side of the serous membrane; spraying a collagen coat onto the fibrous side of the serous membrane, thereby rendering the fibrous side of the serous membrane smooth, wherein the collagen coat is sprayed onto the fibrous side of the serous membrane in a single layer; and exposing the collagen-coated serous membrane to a crosslinking agent to effect crosslinking, wherein the serous membrane is pericardium or peritoneum, the collagen coating has a thickness of 5 m to 100 m, and the collagen is type I collagen.

Description

DETAILED DESCRIPTION

(1) This invention relates to a method for preparing a tissue-based coated membrane resulting in a membrane that is smooth on both sides so as to minimize tissue adhesion.

(2) The method for producing a smooth tissue-based coated membrane includes the following six key steps. First, the fibrous, i.e., parietal, side of an isolated tissue-based membrane is scraped to remove adhering fibers. Second, the tissue-based membrane is processed with an enzyme and chemicals to remove cells, lipids, and extractable blood and non-collagenous molecules. Third, the processed tissue-based membrane is freeze dried. Fourth, the fibrous side of the tissue-based membrane is compressed. Fifth, the compressed fibrous side of the tissue-based membrane is coated with collagen. Finally the collagen coated tissue-based membrane is exposed to a crosslinking agent.

(3) Tissue-based membranes, e.g., bovine or porcine peritoneum or pericardium, provided by commercial suppliers generally contain fibers that adhere to the parietal side of the membrane, resulting from mechanical separation of the tissue-based membrane from neighboring tissues.

(4) Depending on the location of the membrane in the body and the harvesting technique, the amount of adhering fibers varies. Removal of the adhering fibers is important to minimize potential surface irregularities. Applicants disclose that rinsing the membrane with a dehydrating agent, such as a low molecular weight organic compound or an alcohol, can facilitate the removal of adhering fibers, as partial dehydration renders the fibers stiff and more easily removed by scraping or other mechanical means. For example, the membrane can be rinsed with acetone, methanol, ethanol, or isopropanol.

(5) The next step in processing the tissue-based membrane is to remove as much of the loosely associated proteins, cell debris, DNA materials, blood associated proteins, water soluble moieties, and lipids as possible using a combination of enzymes and chemicals. A series of sequential chemical treatments and treatment with an enzyme are performed to remove non-collagenous moieties from the tissue, to remove DNA molecules from cells and cell nuclei from the tissue, and to inactivate undesired potentially harmful viruses from the tissue. The chemicals and enzyme used for carrying out this step include 0.1-3% octylphenol ethoxylate (TRITON X100, 2-8 hour treatment), DNAse (2-18 hour treatment), 1 M NaOH (5-10 hour treatment), 0.5 M HCl (5-10 hour treatment), 1 M NaCl (24-48 hour treatment), isopropyl alcohol (24-72 hour treatment), and water (5-24 hour treatment).

(6) The enzyme and chemical treatments described above remove most of the non-collagenous proteins, lipids, and cell-associated moieties from the tissue. Yet, the tissue retains its native structure and associated handling and mechanical properties.

(7) The clean, treated tissue is then freeze-dried under conditions well known in the art, such as those disclosed in U.S. Pat. No. 6,391,333, the content of which is hereby incorporated by reference in its entirety. Typically, for thin membranes, freeze drying is accomplished by incubation of the membrane at 20 C. for 24-48 hours at a vacuum below 300 Torr, followed by drying at 20 C. for 8-24 hours.

(8) After the above treatments, the freeze-dried membrane is still rough on its parietal, i.e., fibrous, side. In order to make the fibrous side smooth, it is coated with collagen. The membrane is prepared for coating in two steps. First, it is softened by incubation in a humidified chamber. Exposure of the membrane to a relative humidity greater than 90% for 1 to 4 hours is normally sufficient to soften the membrane for further processing. Second, the softened membrane is then compressed by passing a roller over the fibrous side of the membrane. The roller has sufficient weight to completely flatten and smooth any surface fibers still adhering to the fibrous side of the membrane. For example, the weight of the roller can be between 2 and 8 kg.

(9) The coating of the membrane can be accomplished by spraying the surface with acid dispersed collagen fibers (e.g., dispersed in lactic acid) at a pH of 2.3-2.5, or alkaline dispersed collagen fibers (e.g., dispersed in NaOH) at a pH of 11 to 12. Any commercial sprayer (e.g., Badger Airbrush Model 150) can be used to spray the dispersed collagen fibers onto the fibrous side of the membrane. Spraying can be performed at 10-60 psi using a nozzle size of 0.1-1.0 mm. The concentration of collagen fibers in the spraying solution ranges from about 0.05% to about 0.1% (w/v) such that the collagen is sprayed in the form of a mist that coats the membrane surface uniformly despite any microscopic irregularities that may exist. A single layer or multiple layers of a collagen coating can be applied via this spraying technique. Typically, the thickness of the collagen coating is in the range of 5-50 m.

(10) Alternatively, the fibrous surface can be coated with an acid dispersed collagen using a brush. The concentration of collagen used for brush coating can be significantly higher than that used for spraying, ranging from about 0.1% to about 0.9% (w/v). The collagen coating applied using a brush is significantly thicker than that applied by spraying, ranging from about 50 m to about 100 m.

(11) Further, the membrane can be dipped into a collagen dispersion in order to coat the fibrous surface of the membrane.

(12) Irrespective of the collagen coating technique employed, the coated membrane is dried so as to more strongly integrate collagen with the membrane surface.

(13) The coated membranes can be crosslinked using a crosslinking agent that is well known in the art. Crosslinking can be conducted in a solution containing a crosslinking agent (e.g., glutaraldehyde, formaldehyde) or by exposing the coated membrane to the vapor of a crosslinking agent (e.g., formaldehyde vapor). The extent of crosslinking in solution is a function of the concentration of the crosslinking agent, the temperature of the solution, and the time of crosslinking. For example, crosslinking can be accomplished by exposing the coated membrane to a 0.5% formaldehyde solution for 5 hours at room temperature. The crosslinking condition can significantly affect the characteristics of the membrane. For example, a high concentration of the crosslinking agent and a longer crosslinking time will result in a less conformable membrane having a slow rate of in vivo resorption. Conversely, in order to prepare a more conformable membrane, a low concentration of a crosslinking agent is preferred. The same principle applies to the vapor crosslinking, where a lower vapor pressure of a crosslinking agent will produce a more conformable membrane. The crosslinked membrane can be rinsed or exposed to air in order to reduce the amount of any crosslinking agent residue to a level that is acceptable for human implantation.

(14) Without further elaboration, it is believed that the above description has adequately enabled the present invention. The following three examples are, therefore, to be construed as merely illustrative, and not limitative of the remainder of the disclosure in any way whatsoever.

Example 1: Collagen-Coated Bovine Pericardium Membrane

(15) Preparation of Purified Tendon Collagen

(16) The fat and fascia of a bovine flexor tendon were carefully removed and the tendon washed with water. The cleaned tendon was frozen and comminuted by slicing into 0.5 mm slices with a slicer. The sliced tendon was first extracted in purified water at room temperature for 24 hours. After decanting the water, a solution of 0.2 M HCl in 0.5 M Na.sub.2SO.sub.4 was added and the tendon slices were extracted at room temperature for 24 hours. The acid solution was neutralized by adding 3 M NaOH to raise the pH to approximately 7. The tendon slices were extracted in this first neutralized salt solution for 18 hours, after which the solution was removed by decanting. The acid-extracted tendon was then further extracted with 0.75 M NaOH in 1 M Na.sub.2SO.sub.4 at room temperature for 24 hours. This base solution was neutralized to a pH of approximately 7 by adding 3M HCl. The tendon slices were extracted in this second neutralized salt solution for 18 hours, after which the solution was removed by decanting. After the two just-mentioned neutralized salt extractions, the tendon slices were rinsed with purified water 4 times in order to remove any residual salts. The extracted, rinsed tendon was then defatted with 99% isopropanol for 8 hours at room temperature. The isopropanol was decanted and a second equal volume of 99% isopropanol was added to further extract the tendon slices for 18 hours at room temperature.

(17) All extraction steps described above were performed under constant agitation. Further, all extractions, with the exception of the isopropanol extractions, were performed using 5 ml of extracting solution per gram of tendon processed. The isopropanol extractions were performed using 3 ml of isopropanol per gram of tendon processed.

(18) The defatted tendon was then dried under a clean air hood. The processed tendon material, consisting primarily of purified fibrillar collagen, was stored dry at room temperature for later use.

(19) Preparation of Acid Dispersed Collagen Fibers

(20) A 0.1% (w/v) acidic collagen dispersion was prepared by swelling 1 g of purified fibrillar collagen in one liter of 0.07 M Lactic acid at 4 C. in a refrigerator overnight. The swollen fibers were then homogenized for 60 seconds using a Silverson homogenizer and filtered through a 50 mesh stainless steel filter. The acidic dispersion was then stored in the refrigerator for later use.

(21) Purification of Bovine Pericardium Membrane

(22) Fat and extraneous tissue were mechanically removed from the raw bovine pericardium tissue and washed with water. The pre-cleaned bovine pericardium was first washed in purified water at room temperature for 2 hours. The water was decanted, 0.1% TRITON X-100/DNase was added, and the pericardium was extracted for two hours at room temperature. The amount of DNase used was 4 units of activity per cm.sup.2 of membrane. The solution was decanted and the bovine pericardium was then rinsed with purified water for 2 hours. The detergent/enzyme-extracted bovine pericardium was then defatted by incubation with 99% isopropanol three times for 6, 18, and 24 hours at room temperature. The defatted bovine pericardium was then extracted in 0.5 M HCl in 0.5 M Na.sub.2SO.sub.4 for 6 hours at room temperature. This acidic solution was neutralized by adding 3 M NaOH to a pH of approximately 7. The bovine pericardium was then extracted in the neutralized salt solution for 18 hours and the solution was decanted. The acid extracted bovine pericardium was then further extracted in 1 M NaOH in 1.2 M Na.sub.2SO.sub.4 at room temperature for 6 hours. This basic solution was neutralized by adding 3 M HCl to a pH of approximately 7. The bovine pericardium was then extracted in the neutralized salt solution for 18 hours and the solution was decanted. After the salt extractions, the bovine pericardium was washed 4 times with purified water to remove the residual salts associated with the purified bovine pericardium. All extraction steps were performed under constant agitation.

(23) All extractions, with the exception of the isopropanol extractions, were performed using 3 ml of extracting solution per cm.sup.2 of bovine pericardium processed. The isopropanol extractions were performed using 2.7 ml of isopropanol per cm.sup.2 of bovine pericardium processed.

(24) The purified bovine pericardium was then freeze-dried and stored until later use.

(25) Coating of the Purified Bovine Pericardium with Acid Dispersed Collagen

(26) The freeze-dried purified bovine pericardium was humidified in a humidification tank for approximately 30-60 minutes at a relative humidity of 90-100%. The fibrous (parietal) side of the membrane was then compressed using a roller under light pressure in a single uniform direction to flatten the fibers along that direction. The roller weighed 4 kg, and the light pressure was provided solely by the weight of the roller. The membrane was placed in a clean air hood to dry for a minimum of 15 minutes. The membrane was then placed in a holding frame and, using an air-brush gun (Badger Airbrush Model 150), the membrane was sprayed with a 0.1% (w/v) acidic collagen dispersion for 30 seconds. The collagen dispersion was sprayed at 40 psi through a 0.3 mm nozzle. The sprayed membrane was then placed into a glass dish and lightly crosslinked with a 0.001% glutaraldehyde solution for 3 hours. The crosslinked membrane was then rinsed with purified water and freeze-dried again.

(27) Characterization of the Collagen-Coated Bovine Pericardium Membrane

(28) Scanning electron microscopy (SEM) was performed on collagen-coated and non-coated samples at 50 magnification using a scanning electron microscope (JEOL Ltd. Model JSM 6100 SEM). The samples were mounted on an aluminum planchet using adhesive carbon tape. Approximately 500 angstroms of pure gold was sputtered onto the samples to improve electron beam conduction and prevent sample charging.

(29) The fibrous (parietal) side of a bovine pericardial membrane has a rough appearance as visualized under SEM as a result of randomly-oriented fibers on the surface of the membrane. A smooth surface is seen under SEM after coating the parietal surface of the bovine pericardial membrane with collagen following the procedure described above. The smooth (visceral) non-coated side of the bovine pericardial membrane is similar in appearance to the coated fibrous side.

Example 2: Collagen-Coated Porcine Peritoneum Membrane

(30) Fat and extraneous tissue were mechanically removed from the porcine peritoneum and washed with water. The pre-cleaned porcine peritoneum was first washed in purified water at room temperature for 2 hours. The water was decanted and 3% TRITON X100 was added to the peritoneum and incubated for 7 hours at room temperature. The TRITON X100 solution was decanted and the peritoneum then incubated in a DNase solution for 18 hours. The amount of DNase used was 8 units of activity per cm.sup.2 of membrane. The detergent and enzyme extracted porcine peritoneum was defatted by incubating it with 99% isopropanol three times for 3, 3, 18, and 24 hours at room temperature. The defatted porcine peritoneum was extracted in 0.5 M HCl in 0.5 M Na.sub.2SO.sub.4 for 6 hours at room temperature. This acidic solution was neutralized using 3 M NaOH to a pH of approximately 7. The porcine peritoneum was further extracted in the neutralized salt solution for 18 hours and the solution was decanted. The acid extracted porcine peritoneum was then extracted in 1 M NaOH in 1.2 M Na.sub.2SO.sub.4 at room temperature for 6 hours. This basic solution was neutralized using 3 M HCl to a pH of approximately 7. The porcine peritoneum was further extracted in the neutralized salt solution for 18 hours and the solution was decanted. After the salt extractions, the porcine peritoneum was washed 4 times with purified water to remove the residual salts associated with the purified porcine peritoneum.

(31) All extractions, with the exception of the isopropanol extractions, were performed using 3 ml of extracting solution per cm.sup.2 of porcine peritoneum processed. The isopropanol extractions were performed using 2.7 ml of isopropanol per cm.sup.2 of porcine peritoneum processed.

(32) The purified porcine peritoneum was freeze-dried and stored until later use.

(33) The purified porcine peritoneum membrane was coated with acid dispersed collagen as described above for the bovine pericardium membrane.

Example 3: Coating of Bovine Pericardium with Alkaline Dispersed Collagen Fibers

(34) A 0.1% (w/v) alkaline collagen dispersion was prepared by swelling 1 g of fibrillar collagen purified as described above in one liter of 0.01 M NaOH at 4 C. in a refrigerator overnight. The swollen fibers were then homogenized for 90 seconds using a Silverson homogenizer, after which they were filtered through a 50 mesh stainless steel filter. The alkaline dispersion was then stored in the refrigerator for later use.

(35) A bovine pericardium membrane is purified as described above. Alkaline dispersed collagen fibers are coated onto the purified membrane as described above for acid dispersed collagen fibers.

Example 4: Coating of Porcine Peritoneum with Alkaline Dispersed Collagen Fibers

(36) A 0.1% (w/v) alkaline collagen dispersion was prepared by swelling 1 g of fibrillar collagen purified as described above in one liter of 0.01 M NaOH at 4 C. in a refrigerator overnight. The swollen fibers were then homogenized for 90 seconds using a Silverson homogenizer, after which they were filtered through a 50 mesh stainless steel filter. The alkaline dispersion was then stored in the refrigerator for later use.

(37) A porcine peritoneum membrane is purified as described above. Alkaline dispersed collagen fibers are coated onto the purified membrane as described above for acid dispersed collagen fibers.

OTHER EMBODIMENTS

(38) All of the features disclosed in this specification may be combined in any combination. Each feature disclosed in this specification may be replaced by an alternative feature serving the same, equivalent, or similar purpose. Thus, unless expressly stated otherwise, each feature disclosed is only an example of a generic series of equivalent or similar features. From the above description, one skilled in the art can easily ascertain the essential characteristics of the present invention, and without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions. Thus, other embodiments are also within the scope of the following claims.