Method for transferring a thin layer with supply of heat energy to a fragile zone via an inductive layer

Abstract

A method of transferring a thin layer from a first substrate to a second substrate with different coefficients of thermal expansion, including: providing at least one intermediate layer which temperature is increased by induction when an electromagnetic field is applied to it, more than a temperature increase in the first and second substrates; making contact between the first substrate and the second substrate, with the at least one intermediate layer interposed between them; fracturing the first substrate at a weakened zone making use of supply of thermal energy at the weakened zone made by applying an electromagnetic field to a heterostructure formed by making contact between the first substrate and the second substrate, the application generating local induction heating in the intermediate layer that induces a temperature gradient with a local value at the weakened zone activating the fracture mechanism.

Claims

1. A method of transferring a thin layer from a first substrate with a first coefficient of thermal expansion to a second substrate with a second coefficient of thermal expansion different from the first coefficient of thermal expansion, the first substrate comprising a weakened zone delimiting the thin layer and a solid part of the first substrate, the method comprising: bringing the first substrate into contact with the second substrate; fracturing the first substrate at the weakened zone by making use of supply of thermal energy at the weakened zone; providing at least one intermediate layer to a surface of at least one of the first and second substrates before the contact is made with the at least one intermediate layer interposed between the first substrate and the second substrate, a temperature of the at least one intermediate layer being increased by induction when an electromagnetic field is applied to it; applying an electromagnetic field to a heterostructure formed by the contact made between the first substrate and the second substrate, the applying generating a localized induction heating at the at least one intermediate layer, said localized induction heating inducing a thermal diffusion towards the weakened zone that provides said supply of thermal energy at the weakened zone, wherein, the temperature increase of the at least one intermediate layer is greater than a temperature increase in the first and second substrates respectively, and during the application of the electromagnetic field, no additional heat energy is applied to the heterostructure.

2. The method according to claim 1, wherein the at least one intermediate layer is made from a material that has a dissipated power density at least 100 times higher than a dissipated power density of the material of the first and the second substrates, respectively, when the materials in the intermediate layer and in the first and the second substrates are subjected to an electromagnetic field.

3. The method according to claim 1, wherein said supply of thermal energy at the weakened zone by application of the electromagnetic field to the heterostructure leads to fracture of the first substrate at the weakened zone.

4. The method according to claim 1, wherein said supply of thermal energy at the weakened zone by application of the electromagnetic field to the heterostructure leads to weakening of the first substrate at the weakened zone, and the method further comprises an additional supply of mechanical and/or thermal energy to cause fracture of the first substrate at the weakened zone.

5. The method according to claim 1, further comprising forming the weakened zone by implantation of species in a thickness of the first substrate.

6. The method according to claim 1, wherein during the supply of thermal energy, at least one of the first and second substrates is disposed on a temperature controlled chuck.

7. The method according to claim 1, wherein the contact is made by direct bonding of the first substrate and the second substrate.

8. The method according to claim 7, wherein the at least one intermediate layer is provided on the surface of the first and the second substrates, and the first substrate is bonded to the second substrate through the intermediate layer acting as a bonding layer.

9. The method according to claim 1, further comprising, before bringing the first substrate into contact with the second substrate, forming a thermal insulation layer on at least either the first substrate or the second substrate such that, after contact is made, the thermal insulation layer is interposed between the intermediate layer and the second substrate.

10. The method according to claim 1, wherein the intermediate layer is a metal layer.

11. The method according to claim 1, wherein the intermediate layer is a copper layer.

12. The method according to claim 1, wherein the first substrate is made from LiNbO3 and the second substrate is made from Si.

13. The method according to claim 1, wherein the electromagnetic field applied to the heterostructure to make the supply of thermal energy to the weakened zone is a pulsed electromagnetic field.

14. The method according to claim 5, wherein the first substrate is a lithium niobate substrate and the implanted species is helium.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) Other aspects, purposes, advantages and characteristics of the invention will become clear after reading the following detailed description of preferred embodiments, given as non-limitative examples, with reference to the appended drawings on which:

(2) FIGS. 1a-1c diagrammatically show the steps of a possible embodiment of the method according to the invention;

(3) FIG. 2 shows thermal diffusion in an example heterostructure of the method according to the invention;

(4) FIGS. 3a and 3b are diagrams illustrating the temperature increase at different points of an example heterostructure of the method according to the invention.

DETAILED PRESENTATION OF PARTICULAR EMBODIMENTS

(5) With reference to FIGS. 1a-1c, the invention relates to a method of transferring a thin layer 3 from a first substrate B with a first coefficient of thermal expansion to a second substrate A with a second coefficient of thermal expansion different from the first coefficient of thermal expansion, typically by at least 10% or 20% at ambient temperature.

(6) For example, the invention relates to the transfer of a thin layer from a substrate made from lithium niobate onto a silicon substrate. At ambient temperature (20 C.), the coefficient of thermal expansion of silicon is 310.sup.6C.sup.1 while the coefficient of thermal expansion of lithium niobate is of the order of 5 to 7 times higher than that of silicon, depending on which axis is considered.

(7) The method according to one possible embodiment of the invention comprises a first step in which at least one intermediate layer is supplied on the surface of at least either the first or the second substrates. With reference to FIG. 1a, the intermediate layer 1 is formed for example on the first substrate B.

(8) The intermediate layer 1 may be a layer deposited on either or both of the substrates A, B, for example by Physical Vapour Deposition (PVD). The thickness of the intermediate layer 1 is typically less than 10 m.

(9) The intermediate layer 1 is a layer sensitive to electromagnetic actions, typically a metal layer, for example a copper layer. The temperature of the intermediate layer is thus increased by induction when a magnetic field is applied to it, more than the temperature increase in the first and the second substrates respectively.

(10) The intermediate layer 1 may for example be made from a material with a dissipated power density (expressed in W/m.sup.3) at least 100 times, and preferably at least 1000 times higher than the dissipated power density in the material of the first and the second substrates respectively, when said materials in the intermediate layer and the first and second substrates are subjected to the same electromagnetic field, particularly at the same working frequency.

(11) Refer to the table in FIG. 4 in patent application US 2003/0164371 A1 to see examples of power densities dissipated for different types of materials. In particular, as purely illustrative examples, the power density of silicon or germanium (with an n-type doping level of the order of 10.sup.15/cm.sup.3) is of the order of 10 000 times lower than that for aluminium or copper. These materials are thus perfectly suitable for implementation of the invention.

(12) As shown in FIG. 1b, the method comprises a second step in which the first substrate B and the second substrate A are brought into contact with the at least one intermediate layer 1 interposed between them. Contact may particularly lead to direct bonding of the substrates, in other words bonding that does not require the addition of a bonding layer (such as glue, etc.) and that may or may not include an input of thermal energy.

(13) A heterostructure is obtained after making this contact, in the sense that the two substrates A, B have different physico-thermal properties, particularly a difference in the coefficient of thermal expansion.

(14) In one possible embodiment shown in FIGS. 1a-1c, the method includes a step in which a thermal insulation layer 2 is formed on at least either the first substrate B or the second substrate A before contact is made between substrates A, B, such that after contact is made (see FIG. 1b) the thermal insulation layer 2 is interposed between the intermediate layer 1 and the first substrate A.

(15) As can be seen in FIG. 1a, the intermediate layer and the thermal insulation layer may both be formed on the first substrate B. A thermal insulation layer may then also be formed on the second substrate A. As a variant, the thermal insulation layer and the intermediate layer may be formed on the second substrate A. Or also, the intermediate layer may be formed on the first substrate while the thermal insulation layer is formed on the second substrate.

(16) The thermal insulation layer may for example be a silicon dioxide SiO.sub.2 layer.

(17) The method also comprises a step, before contact, made to form a weakened zone Z within the thickness of the first substrate B. The weakened zone delimits a thin surface layer 3 and a solid part 4 in the first substrate B. As shown in FIG. 1a, the weakened zone Z may be formed by implantation of species I in the first substrate B. The weakened zone Z is located at a distance equal to between 30 nm and 2 m from the intermediate layer.

(18) After contact is made, the method comprises the addition of energy at the weakened zone to fracture the first substrate B at the weakened zone, and consequently transfer the thin layer 3 from the first substrate B to the second substrate A as shown in FIG. 1c.

(19) The composite substrate (thin layer on intermediate layer on substrate A) obtained after transfer can be used in radiofrequency applications in which the intermediate metal layer acts as a buried metal electrode, or also in power applications with a buried metal electrode.

(20) Unlike conventional methods in which this input of energy is made fully or partly by a heat treatment applied to the entire heterostructure obtained by making contact, the invention discloses creation of an indirect local temperature rise in the heterostructure in order to provide the implanted species with the energy necessary to generate a gas phase and thus increase the pressure in microdefects resulting from implantation without affecting the entire heterostructure.

(21) Thus, within the framework of the invention, such an input of thermal energy is provided by application of a magnetic field to the heterostructure formed by making contact between the first substrate and the second substrate, said application generating induction heating located at the intermediate layer that induces thermal diffusion towards the weakened zone, thus providing said input of thermal energy at the weakened zone.

(22) The electromagnetic field is typically applied by means of a current loop surrounding the heterostructure, for example a copper loop through which an electric current passes to produce the electromagnetic field that will induce local induction heating in the intermediate layer. The current loop may particularly be in the form of an open torus, the heterostucture being located within the opening of the torus.

(23) The intermediate layer thus acts as a local heat source, the maximum temperature increase being observed in this layer. A temperature gradient is then created in the heterostructure for which the local value at the implanted zone will activate the fracture mechanism. This temperature gradient can allocate all or some of the heat budget necessary for the fracture phenomenon to the weakened zone while limiting the temperature increase in the remaining part of the heterostructure. Thermal expansion of substrates A, B is thus limited, which limits strain and prevents breakage of the heterostructure.

(24) In one embodiment, this supply of thermal energy at the weakened zone by application of an electromagnetic field to the heterostructure leads to fracture of the first substrate at the weakened zone. In another embodiment, this input of thermal energy leads to weakening of the first substrate at the weakened zone, and additional mechanical and/or thermal energy is added to lead to fracture of the first substrate at the weakened zone. This additional energy input is preferably made after thermal energy has been supplied by induction.

(25) It should be noted that when the intermediate layer is used as a bonding layer during the step in which contact is made (an intermediate layer being previously formed for this purpose on each of the first and second substrates), application of the magnetic field can strengthen bonding, not only due to the thermal effect related to heating of the intermediate layer, but also by circulation of induced electric currents that contribute to closing the bonding interface by electro-migration.

(26) The presence of a thermal insulation layer 2 is advantageous in that this layer 2 favors thermal diffusion on only one side of the intermediate layer 1, the thermal gradient generated by the induction phenomenon then being in the form of an asymmetric Gaussian profile. FIG. 2, that shows simulation results under stationary conditions, provides four examples of this type of asymmetric diffusion depending on the degree of heating generated in the intermediate layer by different applications of magnetic field. In this FIG. 2, the 0 position separates an Si substrate (at the left) from a 1 m thick SiO2 thermal insulation layer followed by an intermediate copper layer and then a second substrate B made from lithium niobate (at the right), the abscissa axis showing the deviation at this 0 position expressed in micrometers.

(27) In one embodiment, during said supply of thermal energy by induction, at least either the first or the second substrate is arranged on a temperature controlled chuck, particularly to cool the back face of the first and/or second substrates and thus limit the increase in temperature within the first and/or second substrates.

(28) In one embodiment, the magnetic field applied to the heterostructure to make the said input of thermal energy to the weakened layer is a pulsed electromagnetic field. This increases the temperature differential between the vicinity of the weakened zone and the remainder of the heterostructure, particularly when the substrates do not have the same thermal time constant, as is the case for example for silicon and lithium niobate substrates.

(29) FIGS. 3a and 3b are diagrams showing the increase in temperature at different points of an example heterostructure formed by the assembly of a first 250 m thick 50 mm diameter substrate B made from lithium niobate LiNbO3 with a second 250 m thick 50 mm diameter substrate A made from silicon Si through a 10 m thick intermediate copper layer 1 and a 10 m thick SiO.sub.2 thermal insulation layer 2.

(30) The magnetic field is applied in the ambient environment, using a water cooled copper loop, with a radius of 5 mm, with a power of the order of 7 kW, a current of 34 A and a frequency of 500 kHz.

(31) FIG. 3b shows the temperature increase as a function of the duration of the electromagnetic excitation at different points of the heterostructure in FIG. 3a, namely in the first substrate B at T1=10 m from the intermediate layer 1 and at T2=150 m from the intermediate layer, and in the second substrate A at T3=150 m from the intermediate layer 1. It should be observed particularly that after about 100 seconds of electromagnetic excitation, the temperature at T2 and T3 does not exceed 27 C. while the temperature at T1 reaches 60 C. The temperature difference between the two substrates is thus low, while a relatively high temperature increase is observed close to the intermediate layer.

(32) A substrate made from lithium niobate implanted with helium at a dose of 10.sup.17/cm.sup.2 is conventionally fractured by a global heat treatment at 70 C. for a few hours. The weakened zone is typically located at 1 m from the intermediate layer, the high temperature increase close to the intermediate layer achieved in the framework of the invention thus being used to cause the fracture, remembering that the kinetics of the fracture phenomenon respects an Arrhenius law in which the activation energy for lithium niobate is estimated at 1.3 eV (fracture about 1000 times faster every 70 C.).