Process for the preparation of isomers of xylene

Abstract

The present disclosure relates to a process for the preparation of isomers of xylene. The process includes method step of contacting an activated alkylation catalyst composite with toluene and methanol in the presence of an inert gas, at a temperature of 300 to 500 C. to obtain isomers of xylene. The alkylation catalyst composite used in accordance with the present disclosure comprises a molecular sieve loaded with at least one metal ion. The metal loaded on the molecular sieve is at least one alkali earth metal selected from the group consisting of barium, strontium, magnesium and calcium.

Claims

1. A process for the preparation of isomers of xylene, said process comprising the following steps: i. obtaining an alkylation catalyst composite consisting of X-zeolite loaded with at least one metal ion, wherein said metal is selected from the group consisting of barium, strontium, and calcium; ii. activating the alkylation catalyst composite at a temperature of 450 to 650 C. for a time period of 30 minutes to 2 hours in a reactor to obtain an activated alkylation catalyst composite, wherein the temperature for activating the alkylation catalyst composite is attained by heating the reactor at a rate of 4 to 10 C. per minute; and iii. contacting the activated alkylation catalyst composite with toluene and methanol in the presence of an inert gas, at a temperature of 300 to 500 C. to obtain a reaction mixture comprising isomers of xylene, wherein a mass of ortho-xylene in said reaction mixture is greater than individual mass of para-xylene and meta-xylene.

2. The process as claimed in claim 1, wherein a weight ratio of toluene to methanol ranges between 1:1 and 4:1.

3. The process as claimed in claim 1, wherein a flow rate of toluene is maintained at a weight hourly space velocity of 1 per hour to 5 per hour of the activated alkylation catalyst composite.

4. The process as claimed in claim 1, wherein the inert gas is at least one selected from the group consisting of nitrogen, argon and helium.

5. The process as claimed in claim 1, wherein a flow rate of the inert gas ranges between 5 and 15 ml per minute.

Description

BRIEF DESCRIPTION OF THE ACCOMPANYING DRAWING

(1) FIG. 1: illustrates the XRD for the alkylation catalyst composite of the present disclosure, in which A represents XRD for the CaX zeolite catalyst composite, B represents XRD for the MgX zeolite catalyst composite, C represents XRD for the SrX zeolite catalyst composite and D represents XRD for the BaX zeolite catalyst composite.

(2) FIG. 2: illustrates the XRD for the Sr ion exchanged X zeolite catalyst composite of the present disclosure, in which:

(3) A represents XRD for the SrX zeolite catalyst composite obtained after refluxing Na X-zeolite with strontium nitrate;

(4) B represents XRD for the SrX zeolite catalyst composite obtained after repeating the method step of refluxing Na X-zeolite with strontium nitrate two times; and

(5) C represents XRD for the SrX zeolite catalyst composite obtained after repeating the method step of refluxing Na X-zeolite with strontium nitrate three times.

(6) FIG. 3: illustrates amount of toluene alkylated using MgX zeolite catalyst composite, CaX zeolite catalyst composite, SrX zeolite catalyst composite and BaX zeolite catalyst composite of the present disclosure. In which A represents percent conversion of toluene, B represents percent alkylation of toluene to m-xylene, C represents percent alkylation of toluene to p-xylene and C represents percent alkylation of toluene to o-xylene.

SUMMARY

(7) In accordance with one aspect of the present disclosure there is provided a process for the preparation of isomers of xylene; said process comprising the following steps: i. obtaining an alkylation catalyst composite comprising a molecular sieve loaded with at least one metal ion; ii. activating the alkylation catalyst composite at a temperature of 450 to 650 C. for a time period of 30 min to 2 hrs. in a reactor to obtain an activated alkylation catalyst composite; wherein the temperature for activating the alkylation catalyst composite is attained by heating the reactor at a rate of 4 to 10 C. per minute; and iii. contacting the activated alkylation catalyst composite with toluene and methanol in the presence of an inert gas, at a temperature of 300 to 500 C. to obtain a reaction mixture comprising isomers of xylene; wherein the mass of the ortho-xylene in said reaction mixture is greater than the individual mass of para-xylene and meta-xylene.

(8) Typically, the molecular sieve is at least one zeolite selected from the group consisting of X-zeolite, Y-zeolite, beta-zeolite, ZSM-5 zeolite mordenite, ZSM-48, ZSM-22, ZSM-23, ZSM-57 and MCM-22.

(9) Typically, the molecular sieve is at least one silico aluminophosphate (SAPO) selected from the group consisting of SAPO-5, SAPO-11, SAPO-17, SAPO-18, SAPO-44, SAPO-34 and SAPO-48.

(10) Typically, the metal is at least one selected from the group consisting of group I elements, group II elements, group III elements, lanthanides and transition metals.

(11) Typically, the metal is at least one selected from the group consisting of barium, strontium, magnesium and calcium.

(12) Typically, the ratio of toluene to methanol ranges between 1:1 and 4:1.

(13) Typically, the flow rate of toluene is maintained at a weight hourly space velocity of 1 to 5 per hr. of the activated alkylation catalyst composite.

(14) Typically, the inert gas is at least one selected from the group consisting of nitrogen, argon and helium.

(15) Typically, the flow rate of the inert gas ranges between 5 and 15 per min.

DETAILED DESCRIPTION

(16) Alkylation of toluene using the acidic alkylation catalyst predominantly produces meta and para isomers of xylene, while the basic alkylation catalyst produces ethyl benzene and styrene. Therefore, with the view of increasing the yield of ortho-xylene, the inventors of the present disclosure have conducted several experiments and trials using number of alkylation catalysts. The inventors surprisingly found that the basic alkylation catalyst composite comprising molecular sieve loaded with at least one metal ion can selectively be used for the preparation of the isomers of xylene typically, ortho-xylene. Accordingly, the inventors of the present disclosure have developed a novel process for alkylation of toluene using the basic alkylation catalyst composite.

(17) In accordance with one aspect of the present disclosure there is provided a process for the preparation of isomers of xylene.

(18) In the initial step, the alkylation catalyst composite comprising a molecular sieve loaded with at least one metal ion is activated at a temperature of 450 to 650 C. for a time period of 30 min to 2 hrs. in a reactor to obtain an activated alkylation catalyst composite. The temperature for activating the alkylation catalyst composite is attained by heating the reactor at a rate of 4 to 10 C. per minute.

(19) In accordance with one embodiment of the present disclosure the molecular sieve may be zeolite selected from the group consisting of X-zeolite, Y-zeolite, beta-zeolite, ZSM-5 zeolite mordenite, ZSM-48, ZSM-22, ZSM-23, ZSM-57, MCM-22 and mixtures thereof.

(20) In accordance with another embodiment of the present disclosure the molecular sieve may be silico aluminophosphate (SAPO) selected from the group consisting of SAPO-5, SAPO-11, SAPO-17, SAPO-18, SAPO-44, SAPO-34, SAPO-48 and combinations thereof.

(21) Typically, the metal loaded on molecular sieve is at least one selected from the group consisting of group I elements, group II elements, group III elements, lanthanides and transition metals. Typically, the metal loaded on molecular sieve is at least one selected from the group consisting of barium, strontium, magnesium and calcium.

(22) In the next step, the activated alkylation catalyst composite is contacted with toluene and methanol at a temperature of 300 to 500 C. to obtain a reaction mixture comprising isomers of xylene as ortho-xylene, meta-xylene and para-xylene.

(23) The mass of ortho-xylene present in the reaction mixture is greater the individual mass of para-xylene and meta-xylene.

(24) The ratio of toluene to methanol is maintained in the range of 1:1 to 4:1 and the flow rate of toluene is maintained at a weight hourly space velocity of 1 to 5 per hr. of the activated catalyst. The method step of contacting the activated alkylation catalyst composite with toluene and methanol is carried out in the presence of inert gas selected from the group consisting of nitrogen, argon, helium and combinations thereof. The flow rate of inert gas is maintained in the range of 5 to 15 ml/min.

(25) The present disclosure is further described in light of the following examples which are set forth for illustration purpose only and not to be construed for limiting the scope of the disclosure.

Example 1: Preparation of BaX Zeolite Using NaX Zeolites

(26) Step 1: Preparation of NaX Zeolite:

(27) 5 gm of zeolite was treated with 20 liter of 0.5 M aqueous solution of sodium nitrate (NaNO.sub.3) under reflux for 8 hrs, followed by filtration, washing with water until the filtrate became free from sodium ions, drying at 120 C. for 8 h and calcination at 550 C. for 4 h in air. The ratio of aqueous solution of sodium nitrate to zeolite was maintained as 10:1. The procedure was repeated twice to obtain NaX zeolites.

(28) Step IIPreparation of an Alkylation Catalyst Composite (BaX Zeolite Catalyst Composite) Using NaX Zeolite:

(29) The NaX zeolite was treated with 0.5 M of barium acetate solution using the method described in step I to obtain a BaX zeolite. In this process the sodium nitrate is replaced with barium acetate.

(30) Step IIIPreparation of Isomers of Xylene Using BaX Zeolite Catalyst Composite:

(31) 2 g of BaX zeolites catalyst composite of 0.8 to 1.7 mm mesh size was taken in a quartz micro reactor. Temperature in the reactor was ramped with 8 C./min to 500 C. Catalyst was activated in presence of air for a time period of 1 hr. Then the temperature of the activated catalyst was brought down to 420 C. Feed of Toluene and methanol (4:1) with a weight hourly space velocity (WHSV) (toluene)=2.5 h.sup.1 was fed into pre-heater with a syringe pump and nitrogen was fed with calibrated Rota meter with the flow of 10 ml/min. Products were cooled in condenser maintained at 2 C. and products are collected in gas liquid separator maintained at 5 C. Products were analyzed through gas chromatograph equipped with FID using a carbowax (polar) column of 60 m0.25 um0.25 mm.

(32) TABLE-US-00001 TABLE 1 1 hr. 2 hrs. 3 hrs. 4 hrs. Product distribution (wt %) Benzene 0.01 0.007 0.04 0.005 Toluene 98.60 98.67 98.78 98.93 Ethyl benzene 0.03 0.024 0.024 0.023 p-xylene 0.26 0.26 0.23 0.21 m-xylene 0.25 0.23 0.20 0.19 o-xylene 0.78 0.77 0.68 0.60 Styrene 0.01 0.01 0.01 0.005 Trimethyl benzene 0.02 0.02 0.02 0.02 Others 0.03 0.02 0.01 0.01 Performance (wt %) Toluene conversion 1.4 1.3 1.2 1.1 Styrene selectivity 0.8 0.8 1 0.4 Ethyl benzene selectivity 2 2.1 2 2 Mixed xylene selectivity 92.3 95.4 92.3 90.9

Example 2: Preparation of an Alkylation Catalyst Composite (CaX Zeolite Catalyst Composite) Using NaX Zeolite

(33) The NaX zeolite was treated with 0.5 M of calcium nitrate (CaNO.sub.3) solution using the step-I of Example 1 to obtain a CaX zeolite. In this process sodium nitrate is replaced with calcium nitrate.

(34) Preparation of Isomers of Xylene Using CaX Zeolite Catalyst Composite:

(35) The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process BaX zeolites catalyst composite is replaced with CaX zeolite catalyst composite

(36) TABLE-US-00002 TABLE 2 1 hr. 2 hrs. 3 hrs. 4 hrs. Product distribution (wt %) Benzene 0.26 0.36 0.44 0.51 Toluene 89.43 87.59 86.94 87.99 Ethyl benzene 0.033 0.062 0.08 0.08 p-xylene 2.55 3.35 3.66 3.49 m-xylene 2.28 2.70 2.93 2.83 o-xylene 3.98 3.43 3.06 2.65 Styrene 0.08 0.13 0.14 0.12 Trimethyl benzene 0.87 1.26 1.30 1.08 Others 0.51 1.11 1.46 1.23 Performance (wt %) Toluene conversion 10.57 12.42 13.07 12.02 Styrene selectivity 0.7 1.0 1.0 1.0 Ethyl benzene selectivity 0.3 0.5 0.6 0.7 Mixed xylene selectivity 83.1 76.24 73.75 74.65

Example 3: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(37) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(38) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(39) The isomers of xylene were prepared by employing the procedure described in the Example 1. Feed of toluene and methanol (2:1) with a weight hourly space velocity (WHSV) of 2.5 h.sup.1 was fed into pre-heater and the nitrogen was fed at a flow rate of 10 ml per min. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite wherein the amount of catalyst was 2 g. The results so obtained are shown herein table 3 below.

(40) TABLE-US-00003 TABLE 3 1 hr. 2 hr 3 hr 4 hr Product distribution (wt %) Benzene 0.06 0.039 0.0238 0.04 Toluene 83.46 85.28 85.42 86.30 Ethyl benzene 0.02 0.03 0.04 0.04 p-Xylene 2.95 2.65 2.70 2.69 m-Xylene 2.34 2.11 2.12 2.09 o-Xylene 6.028 5.05 4.74 4.44 Trimethyl benzene 1.82 1.55 1.53 1.44 Others 3.30 3.26 3.40 3.0 Performance (wt %) Toluene conversion 16.54 14.72 14.58 13.75 Mixed xylene selectivity 68.43 66.64 65.57 67.05 p-Xylene selectivity 26.06 27.01 28.24 29.18 m-Xylene selectivity 20.68 21.51 22.18 22.67 o-Xylene selectivity 53.26 51.48 49.58 48.16

Example 4: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(41) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(42) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(43) The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite.

(44) TABLE-US-00004 TABLE 4 1 hr. 2 hrs. 3 hrs. 4 hrs. Product distribution (wt %) Benzene 0.058 0.054 0.094 0.10 Toluene 88.70 89.17 87.97 88.77 Ethyl benzene 0.022 0.03 0.037 0.05 p-xylene 2.48 2.21 2.48 2.43 m-xylene 2.10 1.86 2.03 1.93 o-xylene 5.46 4.62 4.33 3.87 Styrene 0.06 0.10 0.10 0.14 Trimethyl benzene 1.1 1.04 1.23 1.12 Others 0.97 0.91 1.72 1.60 Performance (wt %) Toluene conversion 11.3 10.83 12.04 11.23 Styrene selectivity 0.5 0.1 0.8 1.2 Ethyl benzene selectivity 0.1 0.2 0.3 0.4 Mixed xylene selectivity 88.8 80 73.3 73.1

Example 5: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(45) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(46) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(47) The isomers of xylene were prepared by employing the procedure described in the Example 1. Feed of toluene and methanol (6:1) with a weight hourly space velocity (WHSV) of 2.5 h.sup.1 was fed into pre-heater and the nitrogen was fed at a flow rate of 10 ml per min. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite wherein the amount of catalyst was 2 g. The results so obtained are shown herein table 5 below.

(48) TABLE-US-00005 TABLE 5 1 hr 2 hr 3 hr 4 hr Product distribution (wt %) Benzene 0.019 0.014 0.013 0.012 Toluene 94.19 95.36 95.77 95.97 Ethyl benzene 0.01 0.01 0.01 0.01 p-Xylene 1.089 0.87 0.82 0.76 m-Xylene 0.91 0.74 0.70 0.65 o-Xylene 2.75 2.22 2.06 1.90 Trimethyl benzene 0.38 0.26 0.24 0.22 Others 0.63 0.50 0.37 0.45 Performance (wt %) Toluene conversion 5.80 4.64 4.23 4.00 Mixed xylene selectivity 81.88 82.54 84.63 82.75 p-Xylene selectivity 22.93 22.72 22.91 22.96 m-Xylene selectivity 19.16 19.32 19.55 19.64 o-Xylene selectivity 57.91 57.96 57.54 57.40

Example 6: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(49) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(50) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(51) The isomers of xylene were prepared by employing the procedure described in the Example 1. Feed of toluene and methanol (8:1) with a weight hourly space velocity (WHSV) of 2.5 h.sup.1 was fed into pre-heater and the nitrogen was fed at a flow rate of 10 ml per min. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite wherein the amount of catalyst was 2 g. The results so obtained are shown herein table 6 below.

(52) TABLE-US-00006 TABLE 6 1 hr 2 hr 3 hr 4 hr Product distribution (wt %) Benzene 0.03 0.02 0.01 0.01 Toluene 96.29 96.82 96.48 96.52 Ethyl benzene 0.01 0.01 0.01 0.01 p-Xylene 0.70 0.60 0.66 0.68 m-Xylene 0.63 0.54 0.58 0.52 o-Xylene 1.77 1.50 1.60 1.62 Trimethyl benzene 0.23 0.19 0.22 0.20 Others 0.31 0.30 0.41 0.40 Performance (wt %) Toluene conversion 3.71 3.18 3.52 3.48 Mixed xylene selectivity 83.56 83.02 80.68 81.03 p-Xylene selectivity 22.58 22.73 23.24 24.11 m-Xylene selectivity 20.32 20.45 20.42 18.44 o-Xylene selectivity 57.10 56.82 56.34 57.45

Example 7: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(53) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(54) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(55) The isomers of xylene were prepared by employing the procedure described in the Example 1. Feed of toluene and methanol (4:1) with a weight hourly space velocity (WHSV) of 1.0 h.sup.1 was fed into pre-heater and the nitrogen was fed at a flow rate of 10 ml per min. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite wherein the amount of catalyst was 2 g. The results so obtained are shown herein table 7 below.

(56) TABLE-US-00007 TABLE 7 1 hr 2 hr 3 hr 4 hr Product distribution (wt %) Benzene 0.21 0.08 0.11 0.09 Toluene 85.07 87.47 86.01 87.23 Ethyl benzene 0.02 0.02 0.02 0.02 p-Xylene 2.88 2.29 2.65 2.40 m-Xylene 2.86 2.00 2.34 2.07 o-Xylene 5.69 4.55 5.23 4.47 Trimethyl benzene 1.56 1.4 1.54 1.42 Others 1.66 2.17 2.06 2.26 Performance (wt %) Toluene conversion 14.93 12.53 14.0 12.77 Mixed xylene selectivity 76.56 70.55 73.00 70.01 p-Xylene selectivity 25.20 25.90 25.93 26.85 m-Xylene selectivity 25.02 22.62 22.90 23.15 o-Xylene selectivity 49.78 51.47 51.17 50.0

(57) The catalytic activity of SrX zeolite catalyst composite was compared with the catalytic activity of MgX zeolite catalyst composite, CaX zeolite catalyst composite and BaX zeolite. (shown in FIG. 3 and Table 8)

(58) TABLE-US-00008 TABLE 8 Percent alkylation of toluene using the alkylation catalyst comprising Sr metal ion loaded zeolites. Performance (wt %) Sr-X Sr-Y Sr-ZSM-5 Sr-Beta Toluene conversion 10.8 17.3 16 41.4 Mixed xylene selectivity 80.0 71.5 74.8 65.4 p-xylene selectivity 25.4 31.1 36.7 24.0 m-xylene selectivity 21.3 40.6 50.4 52.9 o-xylene selectivity 53.2 28.3 15.4 23
Characterization
XRD Analysis: 1. The phase purity and crystalline properties of zeolite catalysts composite (CaX zeolite catalyst composite, MgX zeolite catalyst composite, SrX zeolite catalyst composite and BaX zeolite catalyst composite) were determined by the X-ray diffractometer instrument with Cu K Source (=1.542 . The zeolite catalysts were analyzed in the 2 range of 5 to 70 with scanning rate of 0.02 degrees per second at temperature of 25 C. XRD pattern for zeolite catalysts shown in FIG. 1. 2. The phase purity and crystalline properties of Sr ion exchanged X zeolite was determined by the X-ray diffractometer instrument with Cu K Source (=1.542 A). The zeolite catalyst was analyzed in the 2 range of 10 to 70 with scanning rate of 0.02 degrees per second at temperature of 25 C. XRD pattern for Sr X zeolite shown in FIG. 2.
Atomic Absorption Spectrometry (AAS):

(59) The percent sodium (Na) exchanged with the metal ions selected from the group consisting of magnesium (Mg), calcium (Ca), strontium (Sr) and barium (Ba) was determined by Atomic Absorption Spectrometry.

(60) TABLE-US-00009 TABLE 9 S. No Catalyst Ion exchange (wt %) 1. Na-X zeolite 0.0 2 Mg-X zeolite 68.7 3. Ca-X zeolite 92.8 4. Sr-X zeolite 96.1 5. Ba-X zeolite 93.8

Comparative Example 1

(61) The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process BaX zeolite catalyst composite is replaced with commercially available NaX zeolite catalyst.

(62) TABLE-US-00010 TABLE 10 1 hr. 2 hrs. 3 hrs. 4 hrs. Product distribution (wt %) Benzene 0.023 0.010 0.008 0.008 Toluene 94.94 96.75 96.81 97.05 Ethyl benzene 0.067 0.077 0.08 0.09 p-xylene 0.715 0.61 0.65 0.60 m-xylene 0.63 0.51 0.53 0.50 o-xylene 1.69 1.49 1.57 1.46 Styrene 0.05 0.09 0.059 0.05 Trimethyl benzene 0.125 0.07 0.099 0.09 C.sub.9-C.sub.10 aromatics 1.74 0.39 0.20 0.16 Performance (wt %) Toluene conversion 5.0 3.25 3.2 3.0 Styrene selectivity 1.0 2.86 1.8 1.5 Ethyl benzene selectivity 1.34 2.3 2.6 2.9 Mixed xylene selectivity 60.76 79.38 85 85

Comparative Example 2

(63) The isomers of xylene were prepared by employing the procedure described in the Example 1. In this process BaX zeolite catalyst composite is replaced with commercially available H-Beta and H-ZSM-5. The amount of the xylene produced by the SrX zeolite composite was then compared with amount of the xylene produced using H-Beta and HZSM-5

(64) TABLE-US-00011 TABLE 11 Sr-X zeolite catalyst composite of the present disclosure H-BETA H-ZSM-5 Product distribution (wt %) Benzene 0.054 9.03 7.30 Toluene 89.17 68.66 60.24 Ethyl benzene 0.03 0.28 0.35 p-xylene 2.21 5.08 6.05 m-xylene 1.85 9.95 13.45 o-xylene 4.61 3.93 5.98 Others 0.91 3.03 6.6 Conversion and selectivity (wt %) Benzene 0.054 9.03 7.30 Toluene conversion 10.83 31.34 39.76 Mixed xylene selectivity 80 60.54 63.9 p-xylene selectivity 25.4 26.4 23.5 m-xylene selectivity 21.3 52.7 52.89 o-xylene selectivity 52.9 20.8 23.5

Example 8: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(65) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(66) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(67) The isomers of xylene were prepared by employing the procedure described in the Example 1. Feed of toluene and methanol (4:1) with a weight hourly space velocity (WHSV) of 4.0 h.sup.1 was fed into pre-heater and the nitrogen was fed at a flow rate of 10 ml per min. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite wherein the amount of catalyst was 2 g. The results so obtained are shown herein table 12 below.

(68) TABLE-US-00012 TABLE 12 1 hr 2 hr 3 hr 4 hr Product distribution (wt %) Benzene 0.021 0.01 0.011 0.01 Toluene 94.72 96.01 96.21 96.09 Ethyl benzene 0.01 0.01 0.01 0.01 p-Xylene 1.11 0.76 0.72 0.73 m-Xylene 0.90 0.68 0.65 0.67 o-Xylene 2.62 2.03 1.86 1.89 Trimethyl benzene 0.26 0.14 0.19 0.21 Others 0.34 0.35 0.33 0.38 Performance (wt %) Toluene conversion 5.28 4.0 3.79 3.9 Mixed xylene selectivity 87.69 86.75 85.22 84.36 p-Xylene selectivity 23.97 21.90 22.29 22.19 m-Xylene selectivity 19.44 19.60 20.12 20.36 o-Xylene selectivity 56.59 58.50 57.59 57.45

Example 9: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(69) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(70) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(71) The isomers of xylene were prepared by employing the procedure described in the Example 1. Feed of toluene and methanol (4:1) with a weight hourly space velocity (WHSV) of 5.5 h.sup.1 was fed into pre-heater and the nitrogen was fed at a flow rate of 10 ml per min. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite wherein the amount of catalyst was 2 g. The results so obtained are shown herein table 13 below.

(72) TABLE-US-00013 TABLE 13 1 hr 2 hr 3 hr 4 hr Product distribution (wt %) Benzene 0.030 0.009 0.009 0.009 Toluene 97.45 97.99 97.95 98.03 Ethyl benzene 0.01 0.01 0.01 0.01 p-Xylene 0.50 0.40 0.43 0.41 m-Xylene 0.44 0.35 0.37 0.36 o-Xylene 1.164 0.94 1.00 0.96 Trimethyl benzene 0.13 0.09 0.09 0.09 Others 0.27 0.20 0.12 0.11 Performance (wt %) Toluene conversion 2.55 2.01 2.05 1.97 Mixed xylene selectivity 82.51 84.08 87.80 87.82 p-Xylene selectivity 23.76 23.67 23.89 23.70 m-Xylene selectivity 20.91 20.71 20.56 20.81 o-Xylene selectivity 55.32 55.62 55.56 55.49

Example 10: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(73) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(74) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(75) The isomers of xylene were prepared by employing the procedure described in the Example 1. Feed of toluene and methanol (4:1) with a weight hourly space velocity (WHSV) of 1.0 h.sup.1 was fed into pre-heater and the nitrogen was fed at a flow rate of 10 ml per min. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite wherein the amount of catalyst was 2 g. The feed was contacted with the catalyst at a temperature of 380 C. The results so obtained are shown herein table 14 below.

(76) TABLE-US-00014 TABLE 14 1 hr 2 hr 3 hr 4 hr Product distribution (wt %) Benzene 0.01 0.017 0.016 0.017 Toluene 96.39 97.08 97.17 97.27 Ethyl benzene 0.01 0.003 0.003 0.004 p-Xylene 0.70 0.55 0.523 0.50 m-Xylene 0.60 0.49 0.47 0.45 o-Xylene 1.90 1.51 1.42 1.34 Trimethyl benzene 0.16 0.13 0.13 0.13 Others 0.21 0.20 0.25 0.27 Performance (wt %) Toluene conversion 3.61 2.92 2.83 2.73 Mixed xylene selectivity 88.64 87.33 85.27 83.88 p-Xylene selectivity 21.88 21.57 21.67 21.83 m-Xylene selectivity 18.75 19.22 19.48 19.65 o-Xylene selectivity 59.38 59.22 58.85 58.52

Example 11: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(77) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(78) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(79) The isomers of xylene were prepared by employing the procedure described in the Example 1. Feed of toluene and methanol (4:1) with a weight hourly space velocity (WHSV) of 1.0 h.sup.1 was fed into pre-heater and the nitrogen was fed at a flow rate of 10 ml per min. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite wherein the amount of catalyst was 2 g. The feed was contacted with the catalyst at a temperature of 460 C. The results so obtained are shown herein table 15 below.

(80) TABLE-US-00015 TABLE 15 1 hr 2 hr 3 hr 4 hr Product distribution (wt %) Benzene 0.09 0.09 0.22 0.31 Toluene 87.89 89.01 89.78 91.99 Ethyl benzene 0.03 0.05 0.07 0.08 p-Xylene 2.17 2.14 2.30 2.00 m-Xylene 1.97 1.89 2.00 1.76 o-Xylene 5.04 4.14 3.42 2.62 Trimethyl benzene 1.0 0.92 0.84 0.56 Others 1.7 1.73 1.34 0.65 Performance (wt %) Toluene conversion 12.11 11.0 10.22 8.01 Mixed xylene selectivity 75.81 74.27 75.54 79.65 p-Xylene selectivity 23.64 26.19 29.79 31.35 m-Xylene selectivity 21.46 23.13 25.91 27.59 o-Xylene selectivity 54.90 50.67 44.30 41.07

Example 12: Preparation of the Alkylation Catalyst Composite (SrX Zeolite Catalyst Composite) Using NaX Zeolites

(81) The NaX zeolite was treated with 0.5 M of Strontium nitrate (Sr(NO.sub.3).sub.2) solution using Step-I of Example 1 to obtain a SrX zeolite. In this process sodium nitrate is replaced with Strontium nitrate.

(82) Preparation of Isomers of Xylene Using SrX Zeolite Catalyst Composite:

(83) The isomers of xylene were prepared by employing the procedure described in the Example 1. Feed of toluene and methanol (4:1) with a weight hourly space velocity (WHSV) of 1.0 h.sup.1 was fed into pre-heater and the nitrogen was fed at a flow rate of 10 ml per min. In this process BaX zeolite catalyst composite is replaced with SrX zeolites catalyst composite wherein the amount of catalyst was 2 g. The feed was contacted with the catalyst at a temperature of 500 C. The results so obtained are shown herein table 16 below.

(84) TABLE-US-00016 TABLE 16 1 hr 2 hr 3 hr 4 hr Product distribution (wt %) Benzene 0.42 0.62 0.78 0.66 Toluene 88.62 89.85 91.46 92.31 Ethyl benzene 0.085 0.11 0.10 0.098 p-Xylene 2.71 2.55 2.18 1.99 m-Xylene 2.50 2.36 2.12 1.87 o-Xylene 3.65 2.84 2.25 2.12 Trimethyl benzene 0.94 0.72 0.51 0.43 Others 1.05 0.92 0.56 0.48 Performance (wt %) Toluene conversion 11.32 10.15 8.54 7.7 Mixed xylene selectivity 78.27 76.35 76.70 77.66 p-Xylene selectivity 30.59 32.90 33.28 33.28 m-Xylene selectivity 28.22 30.45 32.37 31.27 o-Xylene selectivity 41.20 36.65 34.35 35.45

(85) The embodiments herein and the various features and advantageous details thereof are explained with reference to the non-limiting embodiments in the description. Descriptions of well-known components and processing techniques are omitted so as to not unnecessarily obscure the embodiments herein. The examples used herein are intended merely to facilitate an understanding of ways in which the embodiments herein may be practiced and to further enable those of skill in the art to practice the embodiments herein. Accordingly, the examples should not be construed as limiting the scope of the embodiments herein.

(86) The foregoing description of the specific embodiments will so fully reveal the general nature of the embodiments herein that others can, by applying current knowledge, readily modify and/or adapt for various applications such specific embodiments without departing from the generic concept, and, therefore, such adaptations and modifications should and are intended to be comprehended within the meaning and range of equivalents of the disclosed embodiments. It is to be understood that the phraseology or terminology employed herein is for the purpose of description and not of limitation. Therefore, while the embodiments herein have been described in terms of preferred embodiments, those skilled in the art will recognize that the embodiments herein can be practiced with modification within the spirit and scope of the embodiments as described herein.

(87) Throughout this specification the word comprise, or variations such as comprises or comprising, will be understood to imply the inclusion of a stated element, integer or step, or group of elements, integers or steps, but not the exclusion of any other element, integer or step, or group of elements, integers or steps.

(88) The use of the expression at least or at least one suggests the use of one or more elements or ingredients or quantities, as the use may be in the embodiment of the invention to achieve one or more of the desired objects or results.

(89) The numerical values given for various physical parameters, dimensions and quantities are only approximate values and it is envisaged that the values higher than the numerical value assigned to the physical parameters, dimensions and quantities fall within the scope of the invention and the claims unless there is a statement in the specification to the contrary.

(90) While certain embodiments of the inventions have been described, these embodiments have been presented by way of example only, and are not intended to limit the scope of the inventions. Variations or modifications in the process or compound or formulation or combination of this invention, within the scope of the invention, may occur to those skilled in the art upon reviewing the disclosure herein. Such variations or modifications are well within the spirit of this invention. The accompanying claims and their equivalents are intended to cover such forms or modifications as would fall within the scope and spirit of the invention.