DIRECT RECYCLING OF LITHIUM-ION BATTERY SCRAPS FOR MANUFACTURING A NEW ANODE

Abstract

An improved method of recycling lithium-ion battery anode scraps is provided. The method involves isolating an anode scrap including a graphite anode film adhered to a current collector foil with a polyvinylidene fluoride binder. The anode scrap is combined with deionized water to form a first mixture. The graphite anode film is delaminated from the current collector foil to form a second mixture comprising a free collector foil and a free graphite anode film. The free graphite anode film is filtered and dried from the second mixture to recover the free graphite anode film. The free graphite anode film is combined with a solvent comprising N-methyl-2-pyrrolidone (NMP) to form an anode formation slurry. The slurry is coated onto a copper current collector to produce a new anode.

Claims

1. A method of recycling lithium-ion battery anodes, said method comprising: isolating an anode scrap, the anode scrap comprising a graphite anode film adhered to a current collector foil with a polyvinylidene fluoride (PVDF) binder; combining deionized water with the anode scrap to form a first mixture; delaminating the graphite anode film from the current collector foil to form a second mixture comprising a free collector foil and a free graphite anode film; filtering and drying the free graphite anode film from the second mixture to recover the free graphite anode film; combining the free graphite anode film with a solvent comprising N-methyl-2-pyrrolidone (NMP) to form an anode formation slurry; and wherein combining the deionized water with the anode scrap occurs before delaminating the graphite anode film from the current collector foil.

2. The method of claim 1 wherein the current collector foil comprises copper.

3. The method of claim 1 further comprising the step of using the anode formation slurry in the manufacture of a new anode.

4. The method of claim 1 further comprising the step of shredding the anode scrap into a collection of smaller anode fragments before the step of combining deionized water with the anode fragment to form a first mixture.

5. The method of claim 1 further comprising the step of modulating a temperature of the first mixture.

6. The method of claim 1 further comprising milling the free graphite anode film and free collector foil.

7. The method of claim 1 further comprising sieving the free graphite anode film and free collector foil.

8. The method of claim 1 wherein the first mixture consists of deionized water and the anode scrap.

9. The method of claim 1 wherein the method is performed at a temperature of from 15 to 100 degrees Celsius.

10. The method of claim 1 wherein the method is performed at room temperature.

11. The step of delaminating the graphite anode film from the current collector foil of claim 1, wherein the step occurs in under 30 minutes.

12. The step of delaminating the graphite anode film from the current collector foil of claim 1, wherein the step occurs in under 10 minutes.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] FIG. 1 is a flow chart illustrating a method for the recycling of lithium-ion battery anode scraps.

[0009] FIG. 2 is a graphical depiction of the method for the recycling of lithium-ion battery anode scraps.

DETAILED DESCRIPTION OF THE CURRENT EMBODIMENT

[0010] As discussed herein, the current embodiment generally relates to a method of recycling lithium-ion battery anodes. The method generally includes the contacting of an anode fragment with deionized water to recycle anode scraps, typically those rejected during the course of lithium-ion battery manufacturing. Each operation is discussed below.

[0011] The method of recycling lithium-ion battery anodes includes a step of isolating an anode fragment. In specific embodiments, the step of isolating an anode scrap is a first step of the method that precedes all other steps. Lithium-ion batteries are generally produced via a lithium-ion battery manufacturing process. In the course of the lithium-ion battery manufacturing process, anode scraps are typically generated from various coatings, trimmings, and other material rejections. Once generated, the anode scraps are collected. In some embodiments, the anode scraps are cleaned and/or isolated from waste produced by the lithium-ion battery manufacturing process.

[0012] Generally, the anode scrap comprises an anode film adhered to a current collector with a binder. In some applications, the anode film comprises silicon or carbon. In other applications, the anode film is a graphite anode film. Typically, the current collector is a current collector foil. Generally, the current collector comprises a metal such as silver, copper, aluminum, zinc, nickel, cobalt, tin, or combinations thereof. In specific embodiments, the current collector comprises copper. Typically, the anode film is adhered to a current collector with a binder. In some applications the binder includes a Styrene-Butadiene Rubber (SBR) binder. In other applications, the binder includes a polyvinylidene fluoride (PVDF) binder.

[0013] In some embodiments, the method of recycling lithium-ion battery anodes further includes the step of shredding the anode scrap into a collection of smaller anode fragments. The step of shredding the anode fragments occurs before the step of combining deionized water with the anode fragment to form a first mixture. In some embodiments, the anode scrap is shredded into smaller anode fragments of about 1 cm.sup.2. An industrial shredder for shredding lithium-ion battery anodes can include the Model 600E dual rotor shear shredder from SSI Shredding Systems of Wilsonville, Oreg.

[0014] The method of recycling lithium-ion battery anodes generally comprises a step of combining deionized water with the anode fragments to form a first mixture. Generally, the anode fragments are submerged in deionized water. In particular embodiments, the step of combining deionized water with the anode fragments occurs after the step of isolating the anode fragments. In some such embodiments, the step of combining deionized water with the anode fragments is the second step. Typically, the first mixture consists of deionized water and the anode fragments such that there are no other solvents except deionized water. In certain embodiments, the method of recycling further comprises modulating a temperature of the first mixture. In certain embodiments, the method is performed at 15 to 100 degrees Celsius. In specific embodiments, the method is performed at room temperature.

[0015] The method of recycling lithium-ion battery anodes comprises the step of delaminating the graphite anode film from the current collector foil to form a second mixture comprising a free current collector foil and a free graphite anode film. In the second mixture the free current collector foil and free graphite anode film are configured such that they are not adhered or affixed to each other. In some embodiments, the current collector foil is mechanically peeled from the graphite anode film. In alternative embodiments, the graphite anode film and the current collector foil delaminate in the deionized water without mechanical stimulation. In certain embodiments, the first mixture is agitated such that the graphite anode and current collector foil delaminate in the deionized water. Generally, the step of delaminating the graphite anode film from the current collector foil occurs after combining the anode fragment with deionized water. In some such embodiments, the step of delaminating the graphite anode from the current collector is the third step. In some embodiments, the step of delaminating the graphite anode film from the current collector foil occurs in under 30 minutes, alternatively under 10 minutes. The step of combining the deionized water with the anode fragment occurs before delaminating the graphite anode film from the current collector foil.

[0016] The method generally comprises the step of filtering and drying the free graphite anode film from the second mixture to recover the free graphite anode film. The filtering of the free graphite anode film from the second mixture typically uses a filter. The drying of the second mixture can include an industrial dryer and/or heater to evaporate the deionized water of the second mixture. In particular embodiments, the second mixture is dried through evaporation without the aid of any drying and/or heating equipment. In particular embodiments, the second mixture is dried before it is filtered. Typically, however, the second mixture is filtered before it is dried. In some embodiments, the step of filtering and drying the free graphite anode film from the second mixture occurs after the step of delaminating the graphite anode film from the current collector foil. In some such embodiments, the step of filtering and drying the free graphite anode film is the fourth step.

[0017] In some embodiments, the method further comprises the step of milling the free graphite anode film and free current collector foil. Generally, the step of milling the free graphite anode film and the free current collector foil is performed after the second mixture is filtered and dried. The objective of the milling step is to further reduce the size of the free graphite anode film, typically in preparation for a step of sieving the free graphite anode film and the free current collector foil. In certain embodiments, the method further comprises the step of sieving the free graphite anode film and the free current collector foil. Generally, the step of sieving the free graphite anode film from the free current collector foil substantially separates the free graphite anode film and the free collector foil such that the free graphite anode film and the free collector foil are not contacting one another. Typically, the step of sieving the free graphite anode film and the free current collector foil occurs after the step of milling the free graphite anode film and free current collector foil. Additionally, the step of sieving the free graphite anode film and the free current collector foil generally occurs after the step of filtering and drying the free graphite anode film from the second mixture. In some embodiments, the free current collector foil is discarded. In alternative embodiments, the free current collector foil is recycled. In some such embodiments, the recycled free current collector foil is used in the manufacture of new anodes.

[0018] The method comprises the step of combining the free graphite anode film with a solvent to form an anode formation slurry. Typically, the solvent comprises N-methyl-2-pyrrolidone (NMP). Generally, the step of combining the free graphite anode film with a solvent occurs after the step of filtering and drying the free graphite anode film from the second mixture. In some such embodiments, step of combining the free graphite anode film with a solvent is the fifth step.

[0019] In some embodiments, the method comprises the step of using the anode formation slurry in the manufacture of a new anode. Typically, the anode slurry is formed in a shear mixer after adding the solvent N-methyl-2-pyrrolidone (NMP) to the graphite anode films. The slurry is coated onto the current collector through a slot-die coater to produce a new anode. In some such embodiments, the PVDF binder is the same that adhered the graphite anode film to the current collector foil, wherein the graphite anode film was used to form the anode slurry. In some embodiments, the new current collector foil is made from a recycled current collector foil.

[0020] The above description is that of current embodiments of the invention. Various alterations and changes can be made without departing from the spirit and broader aspects of the invention as defined in the appended claims, which are to be interpreted in accordance with the principles of patent law including the doctrine of equivalents. This disclosure is presented for illustrative purposes and should not be interpreted as an exhaustive description of all embodiments of the invention or to limit the scope of the claims to the specific elements illustrated or described in connection with these embodiments. For example, and without limitation, any individual element(s) of the described invention may be replaced by alternative elements that provide substantially similar functionality or otherwise provide adequate operation. This includes, for example, presently known alternative elements, such as those that might be currently known to one skilled in the art, and alternative elements that may be developed in the future, such as those that one skilled in the art might, upon development, recognize as an alternative. Further, the disclosed embodiments include a plurality of features that are described in concert and that might cooperatively provide a collection of benefits. The present invention is not limited to only those embodiments that include all of these features or that provide all of the stated benefits, except to the extent otherwise expressly set forth in the issued claims. Any reference to claim elements in the singular, for example, using the articles “a,” “an,” “the” or “said,” is not to be construed as limiting the element to the singular.