COMPOSITION FOR RADIATION SHIELDING AND METHOD FOR PREPARING SAME

Abstract

Embodiments of the invention provide a composition for shielding radiation, including 100 parts by weight of a first resin including one or more selected from the group consisting of a polyurethane resin, a polysiloxane resin, a silicone resin; a fluorine resin, an acrylic resin, and an alkyd resin; 5 to 30 parts by weight of a second resin including one or more selected from the group consisting of polyvinyl alcohol (PVA), medium-density polyethylene (MDP E), high-density polyethylene (HDPE), and low-density polyethylene (LDPE); 5 to 30 parts by weight of a polyether ether ketone (PEEK) resin powder; 5 to 80 parts by weight of a metal powder; 1 to 70 parts by weight of a metal oxide powder; 1 to 50 parts by weight of paraffin; 5 to 15 parts by weight of a boron compound; and 10 to 50 parts by weight of a carbon powder. Accordingly, a fiber complex, protective clothing, and the like including the composition for shielding radiation of the present invention includes a PEEK resin without use of lead, and thus, may shield even neutron rays as well as radiation, such as alpha rays, beta rays, proton rays, gamma rays, and X-rays.

Claims

1. A composition for shielding radiation,comprising: 100 parts by weight of a first resin comprising one or more selected from the group consisting of a polyurethane resin, a polysiloxane resin, a silicone resin, a fluorine resin, an acrylic resin, and an alkyd resin; 5 to 30 parts by weight of a second resin comprising one or more selected from the group consisting of polyvinyl alcohol (PVA), medium-density polyethylene (MDPE), high-density polyethylene (HDPE), and low-density polyethylene (LDPE); 5 to 30 parts by weight of a polyether ether ketone (PEEK) resin powder; 5 to 80 parts by weight of a metal powder; 1 to 70 parts by weight of a metal oxide powder; 1 to 50 parts by weight of paraffin; 5 to 15 parts by weight of a boron compound; and 10 to 50 parts by weight of a carbon powder.

2. The composition according to claim 1, wherein the composition for shielding radiation further comprises 1 to 80 parts by weight of an inorganic additive based on 100 parts by weight of the first resin.

3. The composition according to claim 1, wherein the first resin is a polyurethane resin.

4. The composition according to claim 1, wherein the metal powder comprises one or more selected from the group consisting of aluminum, titanium, zirconium, scandium, yttrium, cobalt, tantalum, molybdenum, and tungsten.

5. The composition according to claim 1, wherein the metal oxide powder comprises one or more selected from the group consisting of palladium oxide, iridium oxide, ruthenium oxide, osmium oxide, rhodium oxide, platinum oxide, iron oxide, nickel oxide, cobalt oxide, indium oxide, aluminum oxide, potassium oxide, titanium oxide, tungsten oxide, and magnesium oxide.

6. The composition according to claim 2, wherein the inorganic additive comprises one or more selected from the group consisting of calcium hydroxide, calcium carbonate, magnesium hydroxide, magnesium carbonate, barium chloride, and barium sulfate.

7. The composition according to claim 1, wherein the boron compound comprises one or more selected from the group consisting of boric acid colemanite, zinc borate, boron carbide, boron nitride, and boron oxide.

8. The composition according to claim 1, wherein the carbon powder comprises one or more selected from the group consisting of fullerene, carbon nanofiber, and a carbon nanotube.

9. The composition according to claim 1, wherein the composition for shielding radiation further comprises 10 to 100 parts by weight of a hardener based on 100 parts by weight of the first resin.

10. A sheet for shielding radiation, comprising the composition for shielding radiation according to claim 1.

11. A textile complex for shielding radiation, comprising: a textile; and the sheet for shielding radiation according to claim 9 formed on the textile.

12. The textile complex according to claim 11, wherein the textile comprises any one of woven fabrics, knitted fabrics, and non-woven fabrics.

13. The textile complex according to claim 11, wherein the textile comprises any one selected from among polyester fiber, nylon fiber, and aramid fiber.

14. The textile complex according to claim. 11, wherein the textile complex for shielding radiation further comprises an adhesive layer between the textile and the sheet for shielding radiation,

15. The textile complex according to claim 11, wherein the textile complex for shielding radiation is used in one or more of a bag, protective equipment, and protective clothing for shielding radiation.

16. A textile complex for shielding radiation, comprising a laminate manufactured by sequentially laminating a first textile; a first adhesive layer disposed on the first textile; a sheet for shielding radiation disposed on the first adhesive layer; a second adhesive layer disposed on the sheet for shielding radiation; and a second textile disposed on the second adhesive layer.

17. A method of manufacturing a textile complex for shielding radiation, the method comprising: a step of coating an interior of a side dam, which comprises a release paper on a bottom surface thereof, with the composition for shielding radiation prepared according to claim 1 (step 1); a step of preparing a sheet for shielding radiation by drying the composition coated according to step 1 (step 2); and a step of manufacturing a textile complex for shielding radiation by attaching a textile to the sheet for shielding radiation (step 3).

Description

BRIEF DESCRIPTION OF DRAWINGS:

[0037] These and other features, aspects, and advantages of the invention are better understood with regard to the following Detailed Description, appended Claims, and accompanying Figure. It is to be noted, however, that the Figure illustrates only various embodiments of the invention and are therefore not to be considered limiting of the invention's scope as it may include other effective embodiments as well.

[0038] FIG. 1 illustrates a sectional view of a textile complex for shielding radiation according to an embodiment of the invention.

[0039] FIG. 2 illustrates a sectional view of another textile complex for shielding radiation according to an embodiment of the invention.

[0040] FIG. 3 schematically illustrates a coating system employing a side dam manner used to manufacture a sheet for shielding radiation according to an embodiment of the invention.

[0041] FIG. 4 schematically illustrates a side view of a sheet for shielding radiation which is manufactured through a coating system employing a side dam manner and side dams according to an embodiment of the invention. Here, a member number 10 indicates side dams, a member number 20 indicates a first release film, a member number 30 indicates a sheet for shielding radiation, and a member number 40 indicates a second release film.

[0042] FIG. 5 schematically illustrates the structures of side dams according to an embodiment of the invention. Here, a member number 10 indicates side dams and a member number 20 indicates a first release film.

DETAILED DESCRIPTION:

[0043] Advantages and features of embodiments of the invention and methods of accomplishing the same will be apparent by referring to embodiments described below in detail in connection with the accompanying drawings. However, embodiments of the invention is not limited to the embodiments disclosed below and may be implemented in various different forms. The embodiments are provided only for completing the disclosure of the invention and for fully representing the scope of the embodiments of the invention to those skilled in the art.

[0044] For simplicity and clarity of illustration, the drawing figure illustrates the general manner of construction, and descriptions and details of well-known features and techniques may be omitted to avoid unnecessarily obscuring the discussion of the described embodiments of the invention. Additionally, elements in the drawing figure is not necessarily drawn to scale. For example, the dimensions of some of the elements in the figure may be exaggerated relative to other elements to help improve understanding of embodiments of the invention. Like reference numerals refer to like elements throughout the specification.

[0045] Embodiments of the invention will be described below, but the invention is not limited to the embodiments described below, and it should be understood that the scope of the invention includes various embodiments in which the embodiments described below are modified, improved, or changed as appropriate, based on the ordinary knowledge of those skilled in the art, within the scope not deviating from the spirit of the embodiments of the invention.

[0046] Embodiments of the invention provide a composition for shielding radiation.

[0047] According to at least one embodiment, the composition for shielding radiation includes 100 parts by weight of a first resin including one or more selected from the group consisting of a polyurethane resin, a polysiloxane resin, a silicone resin, a fluorine resin, an acrylic resin, and an alkyd resin; 5 to 30 parts by weight of a second resin including one or more selected from the group consisting of polyvinyl alcohol (PVA), medium-density polyethylene (MDPE), high-density polyethylene (HDPE), and low-density polyethylene (LDPE); 5 to 30 parts by weight of a PEEK resin powder; 5 to 80 parts by weight of a metal powder; 1 to 70 parts by weight of a metal oxide powder; 1 to 50 parts by weight of paraffin; 5 to 15 parts by weight of a boron compound; and 10 to 50 parts by weight of a carbon powder.

[0048] According to at least one embodiment, the specific gravity of the medium-density polyethylene may be 0.926 to 0.940, the specific gravity of the high-density polyethylene may be 0.941 or more, and the specific gravity of the low-density polyethylene may be 0.925 or less.

[0049] Preferably, the composition for shielding radiation may further include 1 to 80 parts by weight of an inorganic additive based on 100 parts by weight of the first resin.

[0050] According to at least one embodiment, the first resin is preferably a polyurethane resin. The polyurethane resin has superior bonding strength to a fiber material, superior durability, and excellent flexibility, and thus is suitable as a material for radiation-shielding. In addition, since the polyurethane resin has a high hydrogen density, it may effectively reduce high-speed neutron rays. In addition, the polyurethane resin has advantages such as superior bonding strength to a fiber material, high durability, and superior flexibility.

[0051] According to at least one embodiment, the second resin may enhance neutron ray shielding.

[0052] When the content of the second resin is less than 5 parts by weight based on 100 parts by weight of the first resin, neutron ray shielding effect may be decreased. When the content of the second resin is 30 parts by weight or more based on 100 parts by weight of the first resin, bonding strength to fiber may be decreased or, when being manufactured into a sheet, strength is decreased and thus it may be difficult to apply the same to a material for radiation-shielding.

[0053] As the metal powder, aluminum, titanium, zirconium, scandium, yttrium, cobalt, tantalum, molybdenum, tungsten, or the like may be used. However, embodiments of the invention are not limited thereto and a metal having a relatively large electron density may be used.

[0054] As the metal oxide powder, palladium oxide, iridium oxide, ruthenium oxide, osmium oxide, rhodium oxide, platinum oxide, iron oxide, nickel oxide, cobalt oxide, indium oxide, aluminum oxide, potassium oxide, titanium oxide, tungsten oxide, magnesium oxide, or the like may be used.

[0055] A complex of the metal powder and the metal oxide powder may be used, but the embodiments of the invention are not limited thereto.

[0056] According to at least one embodiment, the metal powder and the metal oxide powder respectively have a particle diameter of 0.01 to 100 m.

[0057] As the inorganic additive, calcium hydroxide, calcium carbonate, magnesium hydroxide, magnesium carbonate, barium chloride, barium sulfate, or the like may be used. Such an inorganic additive is harmless to the human body and provides superior radiation-shielding effect. Accordingly, as the inorganic additive, a material having a high density is preferably used.

[0058] According to at least one embodiment, the inorganic additive preferably has a particle diameter of 0.01 to 100 m.

[0059] According to at least one embodiment, the paraffin, a main component of which is a straight-chain paraffin hydrocarbon (CH.sub.3(CH.sub.2).sub.nCH.sub.3), has abundant carbon atoms therein and the boron compound has a micro-absorption cross section and a high and wide energy distribution. Accordingly, the paraffin and the boron compound are suitable for shielding of neutron rays. In shielding neutron rays, a material containing a large amount of light atoms, such as hydrogen, oxygen, carbon, etc. having a mass similar to neutrons, is preferred.

[0060] As the boron compound, boric acid (H.sub.3BO.sub.3), colemanite (Ca.sub.2O.sub.14B.sub.6H.sub.10), zinc borate (Zn.sub.2O.sub.14, 5H.sub.7B.sub.6, Zn.sub.4O.sub.8B.sub.2H.sub.2, and Zn.sub.2O.sub.11B.sub.6), boron carbide (B.sub.4C), boron nitride (BN) and boron oxide (B.sub.2O.sub.3), or the like may be used. More preferably, a composite material of zinc borate and boron carbide may be used.

[0061] As the carbon powder, fullerene, carbon nanofiber, a carbon nanotube, or the like may be used.

[0062] According to at least one embodiment, the particle diameter of the carbon powder is preferably 5 to 200 nm.

[0063] According to at least one embodiment, the composition for shielding radiation may further include 10 to 100 parts by weight of a hardener based on 100 parts by weight of the first resin.

[0064] In this case, the composition for shielding radiation is a two-component composition. When the first resin includes one or more of thermosetting resins, i.e., a polyurethane resin, a polysiloxane resin, a fluorine resin, and an alkyd resin, the hardener is preferably included.

[0065] As needed, a catalyst for facilitating hardening of the composition for shielding radiation may be additionally included.

[0066] A sheet for shielding radiation according to various embodiments of the invention includes the aforementioned composition for shielding radiation.

[0067] FIGS. 1 and 2 schematically illustrate a sectional view of a textile complex for shielding radiation according to embodiments of the invention. Hereinafter, the textile complex for shielding radiation according to various embodiments of the invention is described in detail with reference to FIGS. 1 and 2.

[0068] The textile complex for shielding radiation according to at least one embodiment may include a textile and the sheet for shielding radiation formed on the textile.

[0069] According to at least one embodiment, the textile may include woven fabrics, knitted fabrics, non-woven fabrics, etc.

[0070] In detail, an adhesive layer may be further included between the textile and the sheet for shielding radiation as illustrated in FIG. 1.

[0071] In particular, the textile complex for shielding radiation may be a laminate formed by sequentially laminating a textile; an adhesive layer disposed on the textile; and the sheet for shielding radiation disposed on the adhesive layer.

[0072] As needed, the textile complex for shielding radiation may be a laminate formed by sequentially laminating a first textile; a first adhesive layer disposed on the first textile; the sheet for shielding radiation disposed on the first adhesive layer; a second adhesive layer disposed on the sheet for shielding radiation; and a second textile disposed on the second adhesive layer, as illustrated in FIG. 2.

[0073] The textile may include polyester fiber, nylon fiber, aramid fiber, and the like, but the various embodiments of the invention are not limited thereto.

[0074] When the two-component composition including a hardener is used as described in the description of the composition for shielding radiation of the present invention, a separate adhesive layer provided for adhesion between the textile and the sheet for shielding radiation may be omitted. In particular, in a state in which the sheet for shielding radiation is semi-dried, the textile is bonded to the sheet and, by applying heat, is completely dried and bonded to the sheet, thereby being attached to the sheet.

[0075] The textile complex for shielding radiation may be applied to all textiles requiring radiation-shielding abilities, such as bags, protective equipment, and protective clothing for shielding radiation.

[0076] Hereinafter, a method of preparing the composition for shielding radiation according to various embodiments of the invention are described.

[0077] First, a first preliminary composition that includes 100 parts by weight of a first resin including one or more selected from the group consisting of a polyurethane resin, a polysiloxane resin, a silicone resin, a fluorine resin, an acrylic resin, and an alkyd resin; 5 to 30 parts by weight of a second resin including one or more selected from the group consisting of PVA, MDPE, HDPE, and LDPE; and 5 to 30 parts by weight of a PEEK resin powder is prepared (step a).

[0078] In addition, when one or more of isopropyl alcohol (IPA), methyl ethyl ketone (MEK), toluene, dimethyl formamide (DMF), and xylene is additionally included, dispersion and viscosity of the composition may be controlled. Accordingly, a process of forming a coating layer using a composition for shielding radiation and control of the thickness of the coating layer using the composition may be facilitated.

[0079] Subsequently, 5 to 80 parts by weight of a metal powder; 1 to 70 parts by weight of a metal oxide powder; 1 to 50 parts by weight of paraffin; 5 to 15 parts by weight of a boron compound; and 10 to 50 parts by weight of a carbon powder are added to the first preliminary composition, thereby preparing a composition for shielding radiation (step b).

[0080] In step b, 1 to 80 parts by weight of an inorganic additive may be additionally included based on 100 parts by weight of the first resin.

[0081] Here, the paraffin, the boron compound, and the carbon powder are preferably added and mixed after mixing the metal powder and the metal oxide powder with the first preliminary composition and then performing preliminary mixing.

[0082] Such preliminary mixing is performed to finally increase radiation-shielding effects of a coating layer consisting of the composition for shielding radiation of the present invention by allowing uniform dispersion.

[0083] Types of the inorganic additive, boron compound, and carbon powder are the same as those described above, and thus, detailed description thereof is omitted.

[0084] FIG. 3 schematically illustrates a coating system employing a side dam manner used to manufacture a sheet for shielding radiation according to an embodiment of the invention, and FIG. 4 schematically illustrates a side view of a sheet for shielding radiation which is manufactured through a coating system employing a side dam manner and side dams according to an embodiment of the invention. In addition, FIG. 5 is a sectional view schematically illustrating the structure of the side dam.

[0085] Referring to FIGS. 3 to 5, the sheet for shielding radiation is described in detail.

[0086] Hereinafter, a method of manufacturing a sheet for shielding radiation according to an embodiment of the invention is described.

[0087] First, an interior of a side dam apparatus 10 including a first release film 20 on a bottom surface thereof is coated with a composition for shielding radiation 30 prepared according to the preparation method to a predetermined thickness (step 1).

[0088] Coating with the composition for shielding radiation 30 is performed by means of a cylinder coater and thus a coating layer is formed to a predetermined thickness. A resultant coating layer preferably has a thickness of 20 m to 4000 m, but the thickness thereof may be properly controlled as needed.

[0089] According to at least one embodiment, the thickness of a formed composition coating layer may be controlled depending upon the height (H) of the side dam apparatus 10. In addition, the height (H) of the side dam apparatus 10 may be controlled by wrapping the bottom surface of the side dam apparatus 10 with the first release film 20 and thus controlling the height of the bottom surface. In other words, when the height of the bottom surface increases by wrapping the first release film 20 several times, the height (H) of the side dam apparatus 10 is relatively decreased, whereby a thin sheet for shielding radiation may be manufactured. On the other hand, when the number of times of wrapping with the first release film 20 is low or the bottom surface is merely formed without wrapping, the height of the bottom surface is lowered and the height (H) of the side dam apparatus 10 relatively increases, whereby a relatively thick sheet for shielding radiation may be manufactured.

[0090] Next, the composition 30 coated in step 1 is dried, thereby manufacturing a sheet for shielding radiation 30 (step 2).

[0091] According to at least one embodiment, the drying is preferably performed at 110 to 140 C. for 30 to 60 seconds, but the scope of the present invention is not limited. The drying temperature and time may be properly controlled depending upon the thickness or ingredients of the composition 30.

[0092] According to at least one embodiment, the second release film 40 may be attached onto the sheet for shielding radiation 30 and thus may protect the same.

[0093] Hereinafter, a method of manufacturing the textile complex for shielding radiation according to an embodiment of the invention is described.

[0094] First, a sheet for shielding radiation is manufactured according to the aforementioned method (steps 1 and 2).

[0095] Subsequently, a textile is attached to the sheet for shielding radiation, thereby manufacturing a textile complex for shielding radiation (step 3).

[0096] Before step 3, a step of forming an adhesive layer on one surface of the sheet for shielding radiation or the textile may be additionally included. In addition, after step 3, a step of drying and hardening the adhesive layer may be additionally included.

[0097] According to at least one embodiment, the adhesive layer may be formed to a uniform thickness by means of a comma knife, but a method of forming a uniform thickness is not limited thereto.

[0098] When the textile complex for shielding radiation manufactured according to the method is used to manufacture protective equipment, bags, and the like for shielding radiation, the textile complex for shielding radiation may be used in multiple layers used to increase shielding effect depending upon radiation intensity. As needed, an inner textile may be additionally included at a surface which a content emitting radiation contacts.

EXAMPLES

[0099] Hereinafter, the configuration of the present invention is particularly described through the following examples, but the scope of the present invention is not limited thereto.

Example 1

[0100] 5 parts by weight of MDPE, as a polyethylene-based powder, 10 parts by weight of HDPE, and 5 parts by weight of a LDPE resin (manufactured by KUMHO PETROCHEMICAL) were mixed Based on 100 parts by weight of a polyurethane resin (manufactured by DONGSUNG CORPORATION, grade D-ACE 760).

[0101] Subsequently, 15 parts by weight of a PEEK, manufactured by VICTREX, grade 90p, a structural formula:

##STR00001##

was mixed with the polyurethane resin 100 parts by weight, and then 20 parts by weight of MEK, 10 parts by weight of toluene, and 20 parts by weight of DMF were additionally added based on 100 parts by weight of the polyurethane resin. As a result, a first preliminary composition was prepared.

[0102] Preliminary mixing was performed by adding 4 parts by weigh of a molybdenum powder (manufactured by AOMETAL CO., LTD.), as a metal powder, 3 parts by weight of a tantalum powder (manufactured by AOMETAL CO., LTD.), 35 parts by weight of tungsten oxide (WO.sub.3) powder (manufactured by AOMETAL CO., LTD.), as a metal oxide powder, and 5 parts by weight of barium sulfate (BaSO.sub.4), as an inorganic additive (manufactured by SOLVAY) to the first preliminary composition.

[0103] Subsequently, 13 parts by weight of paraffin, 8 parts by weight of boron carbide (B.sub.4C), and 25 parts by weight of carbon nanofiber (manufactured by Columbia Chemical, grade CD7097U) were added and mixed based on 100 parts by weight of a polyurethane resin, thereby preparing a solution including a composition for shielding radiation.

[0104] The solution including the composition for shielding radiation was coated to a thickness of 150 m on a release film (or release paper) by means of a dam coater, thereby manufacturing a film for shielding radiation shield. Subsequently, drying and hardening were performed at 130 C. for 50 seconds. Subsequently, an adhesive was prepared by 100 parts by weight of a polyurethane adhesive resin (a two-component type, D-ACE 5038B manufactured by DONGSUNG CHEMICAL CO., LTD.), 10 parts by weight of a hardener (D-ACE575 manufactured by DONGSUNG CHEMICAL CO., LTD.), 20 parts by weight of DMF, and 20 parts by weight of MEK. A resultant adhesive was coated to a thickness of 50 m on a surface layer of the film for shielding radiation by means of a comma knife. Woven fabric including polyester fiber was laminated on the adhesive and drying and hardening were performed at 130 C. for 50 seconds. As a result, a textile complex for shielding radiation was manufactured.

Example 2

[0105] 10 parts by weight of MDPE, as a polyethylene-based powder, 5 parts by weight of HDPE, and 5 parts by weight of a LDPE resin (manufactured by KUMHO PETROCHEMICAL) were mixed Based on 100 parts by weight of a polyurethane resin.

[0106] Subsequently, 30 parts by weight of a polyether ether ketone resin, which was the same as that used in Example 1, was mixed with the polyurethane resin 100 parts by weight, and then 20 parts by weight of MEK, 10 parts by weight of toluene, and 20 parts by weight of DMF were additionally added based on 100 parts by weight of the polyurethane resin. As a result, a first preliminary composition was prepared.

[0107] Preliminary mixing was performed by adding 10 parts by weigh of a molybdenum powder, as a metal powder, 10 parts by weight of a tantalum powder, 20 parts by weight of tungsten oxide (W0.sub.3) powder, as a metal oxide powder, and 5 parts by weight of barium sulfate (BaSO.sub.4), as an inorganic additive, to the first preliminary composition.

[0108] Subsequently, 25 parts by weight of paraffin, 5 parts by weight of boron carbide (B.sub.4C), and 15 parts by weight of carbon nanofiber, which is the same as that used in Example 1, were added and mixed based on 100 parts by weight of a polyurethane resin, thereby preparing a solution including a composition for shielding radiation.

[0109] A textile complex for shielding radiation was manufactured in the same manner as in Example 1, except that the solution including the composition for shielding radiation was coated to a thickness of 350 m, instead of 150 m, on a release film by means of a dam coater and an adhesive was coated to a thickness of 20 m, instead of 50 m.

Example 3

[0110] 100 parts by weight of a hardener (SVS-12,000-B manufactured by ShinEtsu), 10 parts by weight of a medium-density polyethylene powder, 5 parts by weight of a low-density polyethylene powder, and 5 parts by weight of a high-density polyethylene powder were mixed based on 100 parts by weight of a silicone resin (SVS-12,000-A manufactured by ShinEtsu).

[0111] Subsequently, 5 parts by weight of polyether ether ketone, which is the same as that of Example 1, was mixed therewith based on 100 parts by weight of the silicone resin, and 20 parts by weight of MEK and 30 parts by weight of toluene were additionally added based on 100 parts by weight of the silicone resin. As a result, a first preliminary composition was prepared.

[0112] Preliminary mixing was performed by adding 4 parts by weight of a molybdenum powder and 10 parts by weight of a tantalum powder, as metal powders, 60 parts by weight of tungsten oxide (WO.sub.3) powder, as a metal oxide powder, and 10 parts by weight of barium sulfate (BaSO.sub.4), as an inorganic additive, to the first preliminary composition.

[0113] Subsequently, 5 parts by weight of paraffin, 8 parts by weight of boron carbide (B.sub.4C), and 10 parts by weight of carbon nanofiber which is the same as that of Example 1 were added and mixed based on 100 parts by weight of the silicone resin, as a main material. As a result, a solution including a composition for shielding radiation was prepared.

[0114] The solution including the composition for shielding radiation was coated to a thickness of 100 m on a release film (or release paper) by means of a dam coater, thereby manufacturing a film for shielding radiation. Subsequently, drying was performed at 110 C. for 40 seconds such that a surface of the film was become a semi-dry state, and, in this state, woven fabric including polyester fiber was immediately laminated, followed by drying and hardening at 130 C. for 50 seconds. As a result, a textile complex for shielding radiation was manufactured.

Example 4

[0115] 10 parts by weight of a medium-density polyethylene powder 5 parts by weight of, a low-density polyethylene powder, and 5 parts by weight of a high-density polyethylene powder were mixed based on 100 parts by weight of an acrylic resin (manufactured by Hyup-Jin Chem. Industrial Co., Ltd.).

[0116] Subsequently, 20 parts by weight of polyether ether ketone, which is the same as that of Example 1, was mixed therewith based on 100 parts by weight of the acrylic resin, and 10 parts by weight of MEK and 15 parts by weight of toluene were additionally added based on 100 parts by weight of the acrylic resin, as a main material. As a result, a first preliminary composition was prepared.

[0117] Preliminary mixing was performed by adding 10 parts by weight of a molybdenum powder and 5 parts by weight of a tantalum powder, as metal powders, 40 parts by weight of tungsten oxide (WO.sub.3) powder, as a metal oxide powder, and 20 parts by weight of barium sulfate (BaSO.sub.4), as an inorganic additive, to the first preliminary composition.

[0118] Subsequently, 15 parts by weight of paraffin, 12 parts by weight of boron carbide (B.sub.4C), and 7 parts by weight of carbon nanofiber which is the same as that of Example 1 were added and mixed based on 100 parts by weight of the acrylic resin. As a result, a solution including a composition for shielding radiation was prepared.

[0119] The solution including the composition for shielding radiation was coated to a thickness of 80 m on a release film (or release paper) by means of a dam coater, thereby manufacturing a film for shielding radiation. Subsequently, an adhesive was prepared by mixing 100 parts by weight of a polyurethane adhesive resin, 10 parts by weight of a hardener, 20 parts by weight of DMF, and 20 parts by weight of MEK. A resultant adhesive was coated to a thickness of 300 m by means of a comma knife. Woven fabric including polyester fiber was laminated on the adhesive and drying and hardening were performed at 130 C. for 50 seconds. As a result, a textile complex for shielding radiation was manufactured.

Comparative Example 1

[0120] A textile complex for shielding radiation was manufactured under the same conditions as Example 1, except that a polyurethane resin was used alone instead of the first preliminary composition.

Comparative Example 2

[0121] A textile complex for shielding radiation was manufactured by the same method and under the same conditions as Example 1, except that paraffin and carbon nanofiber were not used.

Comparative Example 3

[0122] A textile complex for shielding radiation was manufactured by the same method and under the same conditions as Example 1, except that 35 parts by weight of tungsten oxide, as a metal component, was used alone instead of 4 parts by weight of a molybdenum powder and 3 parts by weight of a tantalum powder, as metal powders, 35 parts by weight of tungsten oxide (WO.sub.3) powder, as a metal oxide powder, and 5 parts by weight of barium sulfate (BaSO.sub.4), as an inorganic additive.

Experimental Examples

Experimental Example 1

Evaluation of Radiation-Shielding Performance

[0123] The textile complex for shielding radiation manufactured according to each of Examples 1 to 4 and Comparative Examples 1 to 3 was subjected to a radiation-shielding experiment in a linear accelerator laboratory.

[0124] In particular, the textile complex for shielding radiation manufactured according to each of Examples 1 to 4, and Comparative Examples 1 to 3 was cut to a size of 5050 cm, and then a radiation-shielding rate was measured 10 times while varying a measurement position according to radioactive sources and average energy values in summarized Tables 1 and 2 below. Subsequently, average values and change rates were measured and summarized in Tables 1 and 2 below.

[0125] The change rate is calculated by Equation 1 below.

Change rate (%)=Measured maximum radiation-shielding rateMeasured minimum radiation-shielding rate [Equation 1]

TABLE-US-00001 TABLE 1 Shielding rate (%) Radiation Radioactive Average Comparative Comparative Comparative type Source energy Example 1 Example 2 Example 3 Example 4 Example 1 Example 2 Example 3 Alpha Po-210 5,300 KeV 100 100 100 100 100 100 100 rays Beta Sr-90 69 KeV 92 98 92 95 75 71 74 rays Ti-204 72.4 KeV 98 95 90 92 88 74 77 Gamma Am- 60 KeV 94 98 92 90 82 78 75 rays 241 Co-57 122 KeV 88 92 88 85 76 72 66 Cs-137 661.7 KeV 78 83 85 81 64 67 48 X- Braking 40 kV 100 100 100 100 96 95 86 rays radiation 60 kV 98 98 96 95 93 90 80 80 kV 98 96 92 93 90 84 76 100 kV 96 93 91 92 87 77 73 120 kV 92 92 90 90 78 65 63

TABLE-US-00002 TABLE 2 Change rate (%) Radiation Radioactive Average Comparative Comparative Comparative type Source energy Example 1 Example 2 Example 3 Example 4 Example 1 Example 2 Example 3 Alpha Po-210 5,300 KeV 0 0 0 0 0 0 0 rays Beta Sr-90 69 KeV 2 2 3 3 25 27 23 rays Ti-204 72.4 KeV 4 4 6 5 19 20 22 Gamma Am-241 60 KeV 3 2 3 4 17 21 24 rays Co-57 122 KeV 5 4 6 7 23 24 26 Cs-137 661.7 KeV 7 6 8 10 28 28 31 X- Braking 40 kV 0 0 0 0 20 19 22 rays radiation 60 kV 2 2 3 5 22 22 24 80 kV 4 2 5 3 23 25 28 100 kV 7 6 9 8 26 29 31 120 kV 7 8 9 10 30 32 34

[0126] As shown in Tables 1 and 2, the fibers for shielding radiation according to Comparative Examples 1 to 3 exhibit low shielding rates against radiation, except for alpha rays, and high change rates, compared to the textile complexes for shielding radiation according to Examples 1 to 4.

[0127] Therefore, it can be confirmed that the textile complexes for shielding radiation according to Examples 1 to 4 of the present invention have excellent shielding effect against radiation such as beta rays, gamma rays, and X-rays.

Experimental Example 2

Evaluation of Neutron Ray Shielding Performance

[0128] The textile complex for shielding radiation manufactured according to each of Examples 1 to 4, and Comparative Examples 1 to 3 was subjected to neutron ray shielding performance evaluation. Results are summarized in Table 3 below.

[0129] An exit of neutron ray beams was manufactured in a predetermined size, and the intensity of neutron rays was calculated as a thermal neutron ray absorption cross section coefficient using a ratio of the number of incident neutron rays to the number of neutron rays passing through the textile complex for shielding radiation, after disposing a detector for measuring to be a predetermined distance (5 cm) away from the exit.

[0130] The neutron ray absorption cross section coefficient was calculated according to Equation 2 below.

I/I0=L or =[log(I0/I)][Equation 2]

[0131] (IO: incident beam, I: Transmission beam, L: scattering cross section coefficient, and : absorption cross section coefficient)

TABLE-US-00003 TABLE 3 Comparative Comparative Comparative Example 1 Example 2 Example 3 Example 4 Example 1 Example 2 Example 3 Thermal 4.545 4.402 4.505 4.565 5.454 5.090 4.773 neutron ray absorption cross section coefficient (cm.sup.1)

[0132] As shown in Table 3, it can be confirmed that, in Comparative Example 1 in a polyethylene based resin (second resin component) was not used, neutron ray shielding effect reduces by about 20%. In addition, it can be confirmed that, in Comparative Example 2 in which a single material was used as a material for shielding neutron rays, i.e., a boron compound was merely used and paraffin and carbon nanofiber were not used, radiation-shielding effect decreases by about 10%. Therefore, it can be confirmed that the textile complexes for shielding radiation of Examples 1 to 4, in which a polyethylene based resin was included and paraffin, a boron compound, and carbon nanofiber were used as materials for shielding neutron rays, exhibit superior shielding effect even against neutron rays.

[0133] Embodiments of the invention provide non-obvious advantages over the conventional art. For example, there is provided a sheet for shielding radiation and a textile complex for shielding radiation, which includes a composition for shielding radiation according to various embodiments of the invention, and protective clothing including the same include a PEEK resin without use of lead, and thus, may shield even neutron rays as well as radiation, such as alpha rays, beta rays, proton rays, gamma rays, and X-rays.

[0134] Terms used herein are provided to explain embodiments, not limiting the invention. Throughout this specification, the singular form includes the plural form unless the context clearly indicates otherwise. When terms comprises and/or comprising used herein do not preclude existence and addition of another component, step, operation and/or device, in addition to the above-mentioned component, step, operation and/or device.

[0135] Embodiments of the invention may suitably comprise, consist or consist essentially of the elements disclosed and may be practiced in the absence of an element not disclosed. According to at least one embodiment, it can be recognized by those skilled in the art that certain steps can be combined into a single step.

[0136] The terms and words used in the specification and claims should not be interpreted as being limited to typical meanings or dictionary definitions, but should be interpreted as having meanings and concepts relevant to the technical scope of the invention based on the rule according to which an inventor can appropriately define the concept of the term to describe the best method he or she knows for carrying out the invention.

[0137] The singular forms a, an, and the include plural referents, unless the context clearly dictates otherwise.

[0138] As used herein and in the appended claims, the words comprise, has, and include and all grammatical variations thereof are each intended to have an open, non-limiting meaning that does not exclude additional elements or steps.

[0139] Occurrences of the phrase according to an embodiment herein do not necessarily all refer to the same embodiment.

[0140] Therefore, the embodiments disclosed herein are not intended to limit the present invention but to describe the embodiments of the invention, and the embodiments will not limit the spirit and scope of the embodiments of the invention. The scope of the embodiments of the invention should be interpreted from the appended claims, and all techniques within the range of equivalency should be interpreted as being included in the scope of the embodiments of the invention.