Multi-layer chemical and biological protection fabric for mobile shelters

Abstract

A lightweight, low bulk, mobile CB shelter fabric includes a high tensile strength woven scrim laminated between two thin CB-impenetrable polymer films. Laminate adhesives can include isocyanate adhesion promotors. Coatings can provide camouflage, increased light opacity, increased CB protection, sun, fire, and weather resistance. Lamination heat and pressure can cause the films to conform and bond through the scrim, while a pre-applied coating does not flow and remains uniform in thickness. The resulting fabric weight can be approximately 50% of conventional CB fabrics. The films can be hard-drawn polymers. A coating of hammer milled kaolin clay can provide increased light opacity. The films can be 1 micron thick, and can be nylon, aliphatic nylon, urethane, or poly-ether. The scrim can be a 1500 denier Vectran (liquid crystal polymer) with a 4.5 ends-per-inch warp and a 3.5 ends-per-inch fill. The scrim yarns can be flattened bundles of untwisted fiber.

Claims

1. A multi-layer fabric suitable for constructing mobile shelters that provide protection against chemical and biological agents, the fabric comprising: a woven scrim; an outer polymer film layer attached by a first adhesive to an outer surface of the woven scrim; and an inner polymer film layer attached by a second adhesive to an inner surface of the woven scrim; both of the outer polymer film layer and the inner polymer film layer being made from hard drawn polymers, the assembled scrim and polymer film layers of said multi-layer fabric having a weight of less than 15 ounces per square yard and being substantially impenetrable to chemical and biological (CB) agents when included in a mobile shelter that has been packed in a minimized volume during transport thereof.

2. The fabric of claim 1, wherein at least one of the films has a roughness of less than 10 microns.

3. The fabric of claim 1, wherein at least one coating is applied to at least one surface of one of the films.

4. The fabric of claim 3, wherein the coating includes a hammer milled kaolin clay.

5. The fabric of claim 3, wherein the coating provides a camouflaged exterior appearance to the fabric.

6. The fabric of claim 3, wherein the coating provides at least one of increased light opacity, increased infra-red opacity, increased CB penetration protection, flame retardance, and increased resistance to damage from sunlight.

7. The fabric of claim 3, wherein the coating includes an aliphatic urethane.

8. The fabric of claim 3, wherein the coating is formed by reacting two components directly on the film.

9. The fabric of claim 3, wherein the coating is uniform in thickness.

10. The fabric of claim 1, wherein the outer and inner polymer films conform to the weave of the scrim, and the outer and inner film layers are bonded to each other through openings in the scrim weave.

11. The fabric of claim 1, wherein at least one of the first adhesive and the second adhesive includes an isocyanate adhesion promoter.

12. The fabric of claim 1, wherein at least one of the films is a 1 mil film made from at least one of nylon, polyimide, and polyester.

13. The fabric of claim 1, wherein at least one of the films is flame retardant.

14. The fabric of claim 1, wherein the outer film is an aliphatic nylon.

15. The fabric of claim 1, wherein the inner film is coated with a poly-ether urethane.

16. The fabric of claim 1, wherein the scrim is a liquid crystal polymer scrim.

17. The fabric of claim 1, wherein the scrim is a 1500 denier liquid crystal polymer scrim.

18. The fabric of claim 13, wherein the scrim has 4.5 and 3.5 ends per inch in the warp and fill directions respectively.

19. The fabric of claim 1, wherein the scrim includes flattened, non-twisted yarns.

20. The fabric of claim 1, wherein the assembled scrim and polymer film layers of said multi-layer fabric having a weight of not more than 12 ounces per square yard.

21. A method for fabricating a multi-layer fabric suitable for constructing mobile shelters that provide protection against chemical and biological agents, the method comprising: applying a first adhesive to an outer surface of a woven scrim; applying an outer polymer film to the outer surface of the woven scrim; applying a second adhesive to an inner surface of the woven scrim; applying an inner polymer film to the inner surface of the woven scrim; and applying at least one of pressure and heat to the assembled scrim and films so as to cure and set the adhesives, wherein both of the outer polymer film layer and the inner polymer film layer are made from hard drawn polymers, the assembled scrim and polymer film layers of said multi-layer fabric having a weight of less than 15 ounces per square yard and being substantially impenetrable to chemical and biological (CB) agents when included in a mobile shelter that has been packed in a minimized volume during transport thereof.

22. The method of claim 21, further comprising applying a coating to at least one surface of at least one of the films.

23. The method of claim 22, wherein the coating includes a hammer milled kaolin clay.

24. The method of claim 22, wherein: the coating is applied with a uniform thickness to the film before the film is laminated onto the scrim; sufficient heat and pressure are applied during the lamination to cause the films to conform to the weave of the scrim and to bond to each other through openings in the scrim weave; and the applied heat and pressure are insufficient to cause the coating to flow, so that the coating remains uniform in thickness after the lamination.

25. The method of claim 22, wherein the coating is formed by reacting two components on the surface of the film.

26. The method of claim 22, wherein at least one of the adhesives is applied using an isocyanate adhesion promoter.

27. The method of claim 21, further comprising: preparing yarns made of untwisted bundles of fiber; spreading the untwisted bundles into flattened shapes; and weaving the flattened yarns to form the woven scrim.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1A is a perspective view of a partially disassembled multi-layer fabric in an embodiment of the present invention;

(2) FIG. 1B is a close-up exploded perspective view of a conformal laminate embodiment of the present invention;

(3) FIG. 2A is a block diagram that illustrates the layer structure of an embodiment of the present invention;

(4) FIG. 2B is a block diagram similar to FIG. 2A, except that an opacity additive has been disbursed in the adhesive layers; and

(5) FIG. 3 is a perspective view that compares a scrim yarn formed from a rounded bundle of non-twisted fibers with a scrim yarn formed from a flattened bundle of non-twisted fibers.

DETAILED DESCRIPTION

(6) The present invention is a lightweight, low bulk, multi-layer fabric that can be used to construct mobile shelters for protecting occupants against chemical and biological (CB) agents as well as environmental factors such as rain, wind, and sun exposure. The fabric of the present invention provides chemical and biological protection that is equivalent to or better than current designs, while the bulk and weight of the present invention are typically about half of the bulk and weight of the currently used materials. For example, typical CB protection materials currently weigh about 20 oz/yd.sup.2, while embodiments of the present invention weigh only about 12 oz/yd.sup.2 or less.

(7) The excess weight and bulk of the currently used fabrics arises mainly from excess coating material that must fill in the gaps between yarns in the woven fabric before a protective coating can be formed over the entire surface. Of course, this problem could be avoided by using a non-woven fabric such as a polymer sheet. However, a polymer sheet cannot provide the required tensile strength, unless it is made so thick that it is no longer sufficiently flexible.

(8) With reference to FIG. 1A, the present invention resolves this dilemma by providing a multi-layer solution 100. The outer 102 and inner 104 layers are thin polymer films that have a high resistance to CB agents and provide smooth surfaces for the application of coatings as required. A woven scrim 106 is sandwiched between the two film layers 102, 104 so as to provide the required tensile strength. Accordingly, this multi-layer approach combines the CB barrier and smooth surface advantages of a polymer film with the tensile strength advantage of a woven fabric.

(9) In certain embodiments, either or both of the film layers 102, 104 is a hard drawn polymer film, whereby the hard-drawn feature increases the crystallinity of the polymer, and thereby increases the polymer density and reduces its permeability to CB agents.

(10) In embodiments, the use of high bulk strength adhesives overcomes the shear failure often seen in laminated systems between a hard fabric and film. In some embodiments, the use of Isocynate adhesion promoters in combination with the crosslinking of the adhesives reduces adhesive failure.

(11) With reference to FIG. 1B, in various embodiments the films 102, 104 are applied to the scrim 106 with sufficient heat and pressure to create a conformal laminate in which the films 102, 104 penetrate into the window regions 108 in the weave of the scrim 106, causing the thermoplastic urethane on the inside faces of the films 102, 104 to flow together to form one adhesive layer encapsulating the scrim 106 between them, thereby strengthening the attachment of the films 102, 104 to the laminate 100. As a result, the films 102, 104 in these embodiments are no longer strictly flat. Note that FIG. 1B is a close-up exploded view of the laminate 100 of FIG. 1A.

(12) While the polymer film layers themselves provide significant protection against CB agents, it can be desirable to apply coatings to the outer and/or to the inner surfaces of the multilayer fabric assembly 100 for camouflage, increased light opacity, increased CB protection, sun and weather resistance, flame resistance, and other requirements as needed. Due to the smooth, impenetrable nature of the films, any such applied coatings remain entirely on the surfaces, thereby minimizing their added bulk and weight. In various embodiments, the films have a roughness of less than 10 microns.

(13) In some embodiments at least one coating is applied to a film before lamination of the films onto the scrim. In embodiments such as FIG. 1B, the applied heating and pressure are controlled so that the bonding of the inside faces of the films 102, 104 through the scrim weave 106 is maximized without causing the coating to flow. As a result, the thickness of the coating on the film remains uniform even though the underlying film 102, 104 is no longer completely flat. Substantially complete coverage of the laminate 100 by the coating is thereby maintained without requiring additional coating material to fill the windows 108 in the scrim weave 106. If the face coating were allowed to flow during lamination, then excess coating material would tend to flow into the depressions 108 where the films 102, 104 penetrate into the scrim windows 108, and additional coating mass would be required to fill any holes created, thereby increasing the overall system mass.

(14) In some of these embodiments, the coatings are made with reduced viscosity in solvent formulations, while in other embodiments they are made as reactive formulations.

(15) In various embodiments, a two-part urethane (herein referred to as 2K urethane) is applied as a coating to one of the film surfaces. 2K urethane coatings are created by reacting the two components used to form urethanes, polyols and isocyanates, directly on the film. Forming the urethane directly on the film enhances adhesion of the coating to the film. Adjustments to the 2K urethane recipes can be made to control the amount of crosslinking in the polymer, which can alter the film's hardness, and can adjust its thermo-plasticity. Controlling the thermo-plasticity of the film coatings allows for the thermal lamination of the material without causing the coating to flow.

(16) FIG. 2A is a block diagram that illustrates an assembly of layers and coatings in an embodiment of the invention. The embodiment includes an outer weathering film section 200 in which a barrier film 202 includes an outer camouflage coating 204 and an inner opacity layer 206. In embodiments, the opacity layer 206 is a coating that contains hammer-milled kaolin clay to further reduce permeation by CB agents while increasing the light opacity of the assembled material.

(17) The weathering film section 200 is joined by an adhesive layer 208 to a central thin ply scrim 210, which in this embodiment is a 1500 denier Vectran (liquid crystal polymer) scrim having 4.5 and 3.5 ends per inch in the warp and fill directions respectively.

(18) A back-coated film section 212 includes a second barrier film 214 with a white back-coating 216 on its exterior surface for cosmetic purposes, and a second opacity layer 218 on its other surface. The back-coated film section 212 is joined by the adhesive layer 220 to the inner side of the scrim 210. The weight of each layer is indicated in the figure, providing a total weight of 11.2 oz/yd.sup.2.

(19) FIG. 2B is a block diagram of an embodiment that is similar to FIG. 2A, except that the separate opacity layers 206, 218 have been omitted, and instead an opacity-enhancing additive such as hammer milled kaolin clay has been disbursed into the adhesive layers 222, 224.

(20) In some embodiments, at least one of the films 202, 214 is a 1 mil nylon film. In other embodiments, at least one of the films 202, 214 is coated with a urethane, which provides good flame retardance and color. In the embodiments of FIGS. 2A and 2B, the outer film 202 is an aliphatic nylon for superior weathering, while the inner film 214 is a poly-ether for improved strength and reduced cost.

(21) With reference to FIG. 3, in various embodiments the yarn bundles of the scrim are untwisted bundles of fibers 300 that are initially round, but are spread into flattened shapes 302 so as to reduce the thickness of the scrim and increase its surface area or cover factor, thereby providing more surface area for adhesion of the film layers and reducing any tendency of the films to be depressed into gaps between the scrim yarns. FIG. 3 shows a first bundle of fibers 300 as it appears before spreading, and a second bundle of fibers 302 as it appears after spreading.

(22) The foregoing description of the embodiments of the invention has been presented for the purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed. Many modifications and variations are possible in light of this disclosure. It is intended that the scope of the invention be limited not by this detailed description, but rather by the claims appended hereto.