Resin-soluble thermoplastic veil for composite materials

Abstract

A resin-soluble thermoplastic polymer veil toughening element for a curable composition wherein the polymer element is a non-woven veil in solid phase adapted to undergo at least partial phase transition to fluid phase on contact with a component of the curable resin matrix composition in which it is soluble at a temperature which is less than the temperature for substantial onset of gelling and/or curing of the curable composition and which temperature is less than the polymer elements melt temperature; a method for the preparation thereof, a preform support structure for a curable composition comprising the at least one thermoplastic veil element together with structural reinforcement fibers, methods for preparation thereof, a curable composition comprising the at least one thermoplastic veil element or the support structure and a curable resin matrix composition, a method for preparation and curing thereof, and a cured composite or resin body obtained thereby, and known and novel uses thereof.

Claims

1. A thermoplastic toughening element for resin infusion manufacturing of composite comprising: a layer of a plurality of resin-soluble thermoplastic fibers randomly oriented and adhered to one another into a veil consisting of the resin soluble thermoplastic fibers with an areal weight of about 5 to about 80 gsm, wherein the toughening element is interposed between and in direct contact with adjacent plies consisting of structural reinforcement fibers, wherein the resin-soluble thermoplastic fibers are in a solid phase and undergo at least partial phase transition to a fluid phase on contact with a curable resin matrix in which the thermoplastic fibers are soluble at a first temperature for substantial dissolution, which is less than a second temperature for substantial onset of curing of the curable resin matrix, and wherein the concentration of toughening element is highest in the resin matrix between the adjacent plies and decreases in concentration as the matrix approaches the plies.

2. The toughening element of claim 1 wherein the resin-soluble thermoplastic fibers comprise a first resin-soluble thermoplastic material and a second resin-soluble thermoplastic material.

3. The toughening element of claim 2 wherein the first resin-soluble thermoplastic material and the second resin-soluble thermoplastic material are the same.

4. The toughening element of claim 2 wherein the first resin-soluble thermoplastic material and the second resin-soluble thermoplastic material are different.

5. The toughening element of claim 1 wherein the resin-soluble thermoplastic is selected from the group consisting of cellulose derivatives, polyester, polyamide, polyimide, polycarbonate, polyurethane, poly(methyl methacrylate), polystyrene, polyaromatics; polyesteramide, polyamideimide, polyetherimide, polyaramide, polyarylate, polyacrylate, poly(ester) carbonate, poly(methyl methacrylate/butyl acrylate), polysulphone, polyethersulphone, polyetherethersulphone polyethersulphone-etherketone, and copolymers and combinations thereof.

6. The toughening element of claim 1 wherein the fibers solubilize in a curable resin matrix at a first temperature less than a second cure temperature of the curable resin matrix.

7. The toughening element of claim 6 wherein the solubilized fibers chain link with the curable resin matrix at the second cure temperature of the curable resin matrix.

8. The toughening element of claim 1 wherein the fibers carry modifiers.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 illustrates the concentration gradient of the toughening element of the present invention interposed between plies of structural reinforcement fibers after diffusing into the curable resin that may be controlled to provide a higher concentration of toughening material where it is most preferred, between the structural reinforcement fiber plies.

(2) FIG. 2 illustrates data supporting the improved toughness of a composite manufactured using the present resin-soluble thermoplastic veil for a resin infused composite part.

(3) FIG. 3 illustrates the use of the present invention for localized toughening.

(4) FIG. 4 illustrates the manufacturing of a composite incorporating the resin-soluble thermoplastic veil of the present invention with resin infusion technology.

(5) FIG. 5 illustrates the detailed layup of the resin-soluble thermoplastic veil of the present invention interposed between structural reinforcement fiber plies.

(6) FIG. 6 illustrates the process for stabilizing a structural reinforcement fiber ply into a stable preform using the resin-soluble thermoplastic veil of the present invention.

(7) FIG. 7 illustrates the short beam strength (SBS) mechanical properties.

(8) FIG. 8 illustrates the compression strength (CS) mechanical properties.

(9) FIG. 9 illustrates the compression after impact (CAI) mechanical properties.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

(10) By the term resin infusion is meant the method of introducing or injecting a curable resin matrix into a reinforcement fiber substrate, structural fabric or preform for composite part manufacture.

(11) By the term resin-soluble thermoplastic polymer element, thermoplastic fiber, or polymer fiber is meant any flexible polymer element which is both chemically and physically adapted to at least partially dissolve in a curable resin matrix making up the curable composition, at a first temperature, that is less than the melt temperature of the resin-soluble thermoplastic polymer, wherein the resin-soluble thermoplastic polymer is at least partially dispersed into the curable resin matrix as a common phase by dissolution whereby it loses, at least partially, its physical element form to the curable composition, and whereby the resin-soluble thermoplastic reacts with the curable resin matrix at a second, chain linking, temperature to cross-link with the curable resin matrix. These thermoplastic fibers may be adapted to a non-woven veil or mat.

(12) By the term method of manufacturing is meant a means for forming a non-woven veil by the arrangement of chopped or continuous fibers into a sheet, web, veil, mat or the like. The fibers can be chopped fibers, staple fibers packed in bales or continuous filaments extruded from molten polymer granules or pellets.

(13) By the term flow temperature is meant the temperature at which the resin-soluble thermoplastic polymer and curable resin matrix attain a suitably fluid state to enable a degree of polymer chain mobility. Preferably the flow temperature corresponds to a solution temperature at which the resin-soluble thermoplastic polymer dissolves and which temperature is less than a chain linking temperature.

(14) By the term chain linking temperature is meant a temperature at which a resin-soluble thermoplastic polymer chain linking reaction may be initiated. Preferably the chain linking temperature is higher than the resin-soluble thermoplastic polymer dissolution temperature. Preferably the chain linking temperature corresponds to the gelling or coalescence temperature of the curable matrix resin.

(15) By the term reinforcing fibers is meant structural or stabilizing fibers that are insoluble fibers as known in the art which stiffen composites, such as organic or inorganic polymer, carbon, glass, quartz, aramid, PBO, polyethylene, inorganic oxide, carbide, ceramic, boron or metal and the like fibers. Poly{2,6-diimidazol[4,5-b: 4s-e]pyridinylene-1,4(2,5-dihydroxy)phenylene} (PIPD commercially available from Akzo Nobel Central Research, The Netherlands), graphite and basalt.

(16) By the term preform is meant to be any number of physical presentations such as in the form of a support structure or preform as known in the art.

(17) By the term epoxy resin matrix is meant the curable resin matrix for resin infusion systems that is introduced by injection, infusion or the like into a preform to manufacture a composite part.

(18) The present invention is a resin-soluble thermoplastic element for a curable composition adapted to be interposed between layers of reinforcement fibers wherein the resin-soluble thermoplastic element is in a solid phase and adapted to undergo at least partial phase transition to a fluid phase on contact with a component of the curable composition in which it is soluble, at a temperature which is less than the temperature for substantial onset of gelling and/or coalescence of the curable composition and which temperature is less than the inherent melting temperature of the resin-soluble thermoplastic element.

(19) The resin-soluble thermoplastic element for a curable composition is preferably in the form of a veil. The resin-soluble thermoplastic veil shall have a preferred areal weight of about 2 to about 150 grams per square meter (gsm), and most preferably between about 5 and about 50 gsm. The resin soluble thermoplastic veil shall have a preferred real weight range of .+.20% on nominal and most preferably of .+.10% on nominal real weight.

(20) The permeability of the resin-soluble thermoplastic veil of the present invention provides more uniform flow and delivery of curable resin matrix throughout a preform than traditional thermoplastic films which are not porous.

(21) The resin-soluble polymer may be present in the form of an interleaf film.

(22) The veil of the present invention is preferably comprised of a random mat of continuous or chopped polymer fibers that have a diameter of about 0.1 to about 100 microns and preferably between about 1.0 and about 50 microns.

(23) The resin-soluble thermoplastic polymer of the present invention is selected from the group consisting of rubber, elastomeric polymers, thermoplastic polymers and combinations thereof. Preferably, the polymer is a thermoplastic polymer and more preferably it is an amorphous thermoplastic polymer or a crystalline polymer having a relatively low melting point, but generally in excess of about 300 F.

(24) More particularly, the resin-soluble thermoplastic polymer according to the present invention can be any type of resin-soluble fibrous thermoplastic toughening material such as cellulose derivatives, polyester, polyamide, polimide, polycarbonate, polyurethane, poly(methyl methacrylate), polystyrene, polyaromatics; polyesteramide, polyamideimide, polyetherimide, polyaramide, polyarylate, polyacrylate, poly(ester) carbonate, poly(methyl methacrylate/butyl acrylate), polysulphone, polyethersulphone, polyetherethersulphone polyethersulphone-etherketone, and copolymers and combinations thereof. Preferably the thermoplastic toughening material is a polyethersulphone or polyetherethersulphone polyethersulphone-etherketone.

(25) More preferably, the resin-soluble thermoplastic polymer comprises a polymer preferably having a number molecular weight from about 1000 to about 60,000, more preferably in the range of from about 2,000 to about 20,000.

(26) Examples of suitable thermoplastic polymers include, but are not limited to members of the group consisting of cellulose derivatives, polyester, polyamide, polyimide, polycarbonate, polyurethane, poly(methyl methacrylate), polystyrene, polyaromatics; polyesteramide, polyamideimide, polyetherimide, polyaramide, polyarylate, polyacrylat, poly(ester) carbonate, poly(methyl methacrylate/butyl acrylate), polysulphone, polyethersulphone, polyetherethersulphone polyethersulphone-etherketone, and copolymers and combinations thereof.

(27) A particularly preferred polyaromatic thermoplastic polymer for use as the fiber in the present invention preform is a polyaromatic sulphone comprised of ether-linked repeating units or thioether-linked repeating units, the units being selected from the group consisting of
-(PhAPh).sub.n-
and
-(Ph).sub.a-
wherein A=CO or SO.sub.2, Ph is phenylene, n=1 to 2 and can be fractional, a=1 to 4 and can be fractional, with the proviso that when a exceeds 1, the phenylenes are linked linearly through a single chemical bond or a divalent group other than CO or SO.sub.2 or are fused together directly or via a cyclic moiety selected from the group consisting of an acid alkyl group, a (hetero) aromatic, a cyclic ketone, a cyclic amide, an imide, a cyclic imine and combinations thereof. Preferably, the polyaromatic sulphone comprises polyethersulphone (PES) and more preferably, a combination of polyethersulphone-etherketone and of polyether ether sulphone linked repeating units (PES:PEES), in which the phenylene group is meta- or para-; wherein the phenylenes are linked linearly through a single chemical bond or a divalent group other than sulphone, or are fused together. The preferred relative proportions of the repeating units of the polyarylsulphone in the PEES:PES may be expressed in terms of the weight percent SO.sub.2 content defined as 100 times (weight of SO.sub.2)/(weight of average repeat unit). The preferred SO.sub.2 content is at least about 35, more preferably at least about 30 and most preferably at least about 22%. When a=1 this corresponds to PES/PEES ratio of at least 20:80, preferably in the range 25:75 to 75:25 and most preferably 35:65 to 65:35.

(28) Alternatively, when the thermoplastic polymer for use as the fiber is polyurethane, it is more preferably a thermoplastic polyurethane rubber and when the fiber is a polyacrylate, the polyacrylate is at least 85 wt % acrylonitrile. When the thermoplastic polymer is a polyamide, it is preferably a nylon material and more preferably an amorphous nylon.

(29) The polymer may be characterized by a range of Molecular Weight (MW) which may typically be defined either by number average molecular weight (Mn), peak MW and other means, usually determined by NMR and GPC. Preferably the polymer is selected in the range up to 70,000 for example 9000-60,000 for toughening, and in this case the Mn of the polyaromatic is suitably in the range 2000 to 25000, preferably 2000 to 20000, more preferably 5000 or 7000 to 18000, most preferably 5000 or 7000 to 15000.

(30) The polyaromatic is preferably of relatively low molecular weight. It also preferably contains in-chain, pendant or chain-terminating chemical groups which are capable of self-assembling to form higher molecular weight complexes through non covalent bonds with similar or different chemical groupings in the polymer. These maybe, for example, hydrogen bonds, London forces, charge transfer complexes, ionic links or other physical bonds. Preferably the non-covalent bonds are hydrogen bonds or London forces which will dissociate in solution to regenerate the relatively low molecular weight precursor polyaromatic. The polyaromatic preferably contains pendant or chain-terminating groups that will chemically react with groups in the thermosetting resin composition to form covalent bonds. Such groups may be obtained by a reaction of monomers or by subsequent conversion of product polymer prior to or subsequently to isolation. Preferably groups are of formula:
-A-Y
where A is a divalent hydrocarbon group, preferably aromatic, and Y is a group reactive with epoxide groups or with curing agent or with like groups on other polymer molecules.

(31) Examples of Y are groups providing active hydrogen especially OH, NH.sub.2, NHR or SH, where R is a hydrocarbon group containing up to eight (8) carbon atoms, or providing other cross-linking reactivity especially epoxy, (meth)acrylate, cyanate, isocyanate, acetylene or ethylene, as in vinyl allyl or maleimide, anhydride, oxazaline and monomers containing saturation. Preferred end groups include amine and hydroxyl.

(32) A particular advantage is that the polymer element may have low molecular weight, but be adapted to react on curing to provide the higher molecular weight required for effective toughening or the like. Specifically the polymer may comprise chains of at least one aromatic polymer or a mixture thereof together with at least one chain linking component wherein the at least one aromatic polymer comprises polymer chains in a first range of 2000 to 11000 Mn, especially 3000 to 9000 Mn and characterized by a polymer flow temperature, and wherein one of the at least one polyaromatic and the at least one chain linking component comprises at least one reactive end group and the other comprises, at least two linking sites reactive end groups Y and chain linking sites, Z are selected OH, NH.sub.2, NHR or SH wherein R is a hydrocarbon group containing up to eight (8) carbon atoms, epoxy, (meth)acrylate, (iso)cyanate, isocyanate ester, acetylene or ethylene as in vinyl or allyl, maleimide, anhydride, acid, oxazoline and monomers containing unsaturation characterized in that a plurality of the end groups are adapted to react with the linking sites at chain linking temperature in excess of the polymer flow temperature to form linked polymer chains in a second range of 9000 to 60000 Mn, especially 11000 to 25000 Mn, which is in excess of the first range, substantially thermoplastic in nature.

(33) The fiber characteristics include, but are not limited to yarns or monofilaments of spun strands, extruded strands, cast strands, continuous fibers, random fibers, staple fibers, discontinuous fibers, chopped fibers, whiskers, filaments, ribbons, tapes, hollow fibers, veils, fleeces, and combinations thereof.

(34) The fiber may be both a yarn made up of multiple monofilaments or single and multiple monofilaments. Preferably the fiber (or yarn) comprises fibers each having a diameter less than or equal to about 100 micron. Preferably a fiber or filament has a diameter d, or is a film or ribbon having thickness t wherein d or t are in the range up to 100 micron, preferably from about 1.0 to about 80.0 micron, more preferably between about 10 and about 50 micron.

(35) The thermoplastic veil should be provided in dimensions of about 1 inch to about 200 inches wide and preferably between about 20 inches and about 70 inches.

(36) The fiber cross section can be a variety of different shapes to allow control of the wetting of the polymer fiber such as star, square, cauliflower or kidney bean shape as well as standard oval, circular and flat ribbons. Additionally, the fiber may be hollow or contain different materials in different concentric layers: for example, an inner core and an external shell. Preferably, the fibers are cylindrical in shape with a circular cross section for optimal surface area for dissolution.

(37) The thermoplastic veil preferably comprises chopped fibers with an average length of about 10 microns to about 100 inches and preferably about 1 inch to about 20 inches.

(38) The thermoplastic veil should at least partially maintain its solid phase while resin is infused into the system so as to not dissolve into the resin and increase the resin viscosity during infusion. Dissolution during resin infusion would impede the resin flow through the reinforcement fibers. More preferably the veil should not significantly or appreciably dissolve during resin infusion temperatures between 20 C. and about 90 C. or preferable resin infusion temperatures of between about 30 C. and about 65 C.

(39) The thermoplastic veil should begin appreciable dissolution into the curable resin matrix above 90 C. with substantially complete dissolution occurring between about 90 C. to 175 C. with the preferred dissolution temperature being between about 120 C. and 140 C. and most preferably about 130 C.

(40) The melting temperature of the resin-soluble thermoplastic element of the present invention is from about 175 C. to about 400.C or greater and preferably between about 250 C. and 400 C. The particular melting temperature of the resin-soluble thermoplastic element is dependent upon the molecular weight of the particular thermoplastic employed.

(41) The thermoplastic veil does not substantially react with the curable resin matrix system at the dissolution temperature.

(42) The thermoplastic veil may further comprise a combination of more than one resin-soluble thermoplastic polymer in first or second amounts.

(43) The methods of manufacturing the thermoplastic veil of the present invention include drylaying; airlaying; meltblowing/spunlaying/spunbonding; and wetlaying. Preferably the resin-soluble thermoplastic veil of the present invention is manufactured through meltblowing.

(44) In the meltblowing manufacturing process, the resin-soluble thermoplastic polymer in powder form is melted at between about 250 C. and 400 C., preferably about 325 C. and extruded through a plurality of spinnerets. The orifice size of the spinneret is between about 0.1 microns to about 100 microns and preferably between about 1.0 microns and about 50 microns. Air in the temperature range of 350 C. to 500 C. is blown onto the fibers extruded onto a conveyor from the spinnerets to randomize the fibers into a veil.

(45) The meltblowing process can use polymer powder or granules which are melted into a molten polymer that is extruded through the spinnerets. The continuous filaments are deposited onto a conveyer and cooled to form a uniform non-woven veil. Some remaining heat content of the soft filaments can cause the filaments to at least partially adhere to one another, but this cannot be regarded as the principal method of bonding the filaments to one another. This process has the advantage of giving the resulting non-woven veil a greater tensile strength and resistance to tearing or fraying during manufacture of the veil and during manufacture of a composite.

(46) Co-extrusion of second thermoplastic polymer component is possible, usually to provide additional toughening properties, fire retardancy properties, bonding capabilities and the like.

(47) The drylaying process is an alternate means of manufacturing the resin-soluble thermoplastic veil of the present invention and starts with the opening of bales of thermoplastic polymer fibers which are blended and conveyed to the next stage by air transport. The fibers are then combed into a veil by a carding machine, which is a rotating drum or series of drums covered in fine wires or teeth. The precise configuration of cards will depend on the fabric weight and fiber orientation required. The veil can be parallel-laid, where most of the fibers are laid in the machine direction, or they can be random-laid. Typical parallel-laid carded veils result in good tensile strength, low elongation and low tear strength in the machine direction and the reverse in cross direction. Relative speeds and veil composition can be varied to produce a wide range of properties.

(48) The airlaying process is another method of drylaying. In airlaying, the fibers, which can be very short, are fed into an air stream and from there to a moving belt or perforated drum, where they can form a randomly oriented veil. Compared with carded veils, airlaid veils have a lower density, a greater softness and an absence of laminar structure. Airlaid veils offer great versatility in terms of the fiber blends that can be used.

(49) In the wetlaying process, dilute slurry of water and fibers is deposited on a moving wire screen and drained to form a veil. The veil is further dewatered, consolidated, by pressing between rollers and dried. Wetlaid veil-forming allows a wide range of fiber orientations ranging from near random to near parallel. The strength of the random oriented veil is similar in all directions in the plane of the fabric.

(50) A further method of manufacturing a non-woven resin-soluble thermoplastic fabric veil comprises the steps of heat blow extruding of the resin-soluble thermoplastic into a thread; chopping the thread into a plurality of thermoplastic pieces of lengths from about 10 microns to about 100 inches and preferably about 1 inch to about 20 inches; scattering the pieces onto a heated mandrel and cooling the veil.

(51) Preferably polymers in the form of fibers or film are obtained by continuous extrusion of resin melt onto reels and film forming or spinning as known in the art of synthetic textiles manufacture by mechanical stretching with heating, more preferably by providing the polymer melt, drawing off in elemental shape, subjecting to a heating and mechanical stretching regime which may orient polymer chains and render the element elastomeric and predisposed to dissolution, and cooling, preferably by pulling in air for a desired distance, e.g. 50 to 500 mm. Preferably polymer melt is drawn off through a die head or the like providing a desired number of apertures or slots, using a pump with controlled pump rate for a desired linear density (tex) of polymer for example up to 180 tex.

(52) The thermoplastic polymers may be prepared from micronized or unmicronized polymer, pellets, particles or other extrudate and the like. Preferably fibers are prepared as multifilaments of up to 20 same or different polymer filaments, which are drawn off from the molten polymer, cooled and optionally twisted as desired, and then subjected to heating and stretching. The multifilament is more resistant to breaking; there is a tradeoff between higher strength and lower flexibility in selection of filaments and twists/metre.

(53) In a further aspect of the present invention there is provided a process for the preparation of a curable composition as known in the art comprising contacting a resin-soluble thermoplastic veil with a curable resin matrix for example by interleaving, impregnating, injecting or infusing, mixing and the like.

(54) The composition may then be laid up with other component parts such as reinforcing fibers to provide the curable composition, or other composite parts such as metal or polymer or other bodies or structures prior to curing in known manner.

(55) Another aspect of the present invention is for use as interleaves for introducing thermoplastics into the interlaminar region of conventional prepregs. The resin-soluble thermoplastic veils can also be utilized in dry preforms where the open weave structure optimally allows for the injection/infusion of the thermosetting curable resin matrix to occur throughout the preform. This is unlike the inclusion of continuous films which act as obstructions to the resin flow which in turn can lead to porosity and poor mechanical and environmental performance.

(56) Another aspect of the present invention is for stabilization of performs and perform precursors. The present invention provides for the use of a resin-soluble thermoplastic veil to combine, bond, stabilize, debulk and preform structural fibers, fabrics, textiles and preforms by using a combination of time, temperature and pressure.

(57) For the purposes of the present invention, the terms combine, bond, stabilize, debulk and preform are used to mean 1) the stabilization of fibers or single sheet, layer or ply or multiple sheets, layers or plies of structural fabric so that it can be moved, cut, transported, resin infused, or handled in a typical manner without fraying, unravelling, pulling apart, bending, wrinkling or otherwise distorting the integrity of the structural fabric, 2) the stabilization and binding together of multiple layers of reinforcing or structural fabrics for cutting, molding or shaping, by placing in a mold or otherwise so that the resulting preform will not be distorted by being moved, transported or manipulated in any way and so that the fibers that make up the structural fabrics remain intact during resin infusion, and 3) fixing a preform in a desired shape.

(58) The stabilized preform according to the present invention comprises a veil according to the present invention comprising all of its characteristics and features, that has been subjected to a stabilizing temperature that is preferably suitable to soften the stabilizing fiber and is most preferably of from about 100 C. to about 250 C. for a time period from about 5 seconds to about 100 minutes or more.

(59) The stabilized preform according to the present invention can typically comprise more than one layer of structural fabric. The layers or plies of structural fabric can be stacked, cut and shaped prior to having been subjected to a stabilizing temperature.

(60) In the present process the heat can be applied in any manner and from any source, preferred examples including, but not being limited to heat sources selected from infrared, microwave, convection, induction, ultrasonic, radiant and combinations thereof. The heat should preferably be applied in an amount that is sufficient to soften the stabilizing fiber. More preferably the heat is applied at a temperature of from about 125 C. to about 185 C. for a time period of from about 1 min to about 100 min. The step of applying heat can be performed under a vacuum of from about 500 mbar to about 999 mbar or under pressure applied by using a press, nip rollers and the like.

(61) Optionally, in the present process more than one layer of structural fabric can be provided. The process can then further comprise the steps of stacking and cutting the layers or plies of structural fabric after the step of integrating the stabilizing fiber into the structural fabric and before the step of applying heat. The present process can optionally further comprise the step of shaping the layers of structural fabric after the layers have been stacked and cut and before the step of applying heat.

(62) In the present process, the step of integrating the resin-soluble veil into the structural fabric can be carried out by using any known method for integrating or incorporating a veil into a structural fabric, preferred examples of which include a method selected from punching, overwinding, intermeshing, aligning, hot compacting and combinations thereof.

(63) The present invention also comprises a process for debulking a preform precursor comprised of reinforcing fibers for composite material manufacture. The process comprises the same steps utilized for stabilization in order to reduce the thickness of the stack. The step of applying heat is preferably performed under a vacuum of from about 500 mbar to about 999 mbar or under pressure applied by using a press, nip rollers and the like.

(64) The process can further comprise the step of shaping the stack of structural fabric after the step of cutting and before the step of applying heat.

(65) The resin-soluble thermoplastic fibers of the present invention and any reinforcing fibers are incorporated with the curable resin matrix at any suitable stage in the process.

(66) The resin-soluble thermoplastic veil of the present invention can also carry modifiers such as additional toughening agents, additives, curing agents, metal flakes, fire retardants, nanoparticles, etc, that cannot be included in a standard resin matrix or adhesive.

(67) Localized toughening of a composite is also uniquely possible through the present invention by providing a means for separately laying up additional layers of thermoplastic toughening fabric in the areas requiring additional toughening.

(68) The resin-soluble thermoplastic veil is preferably capable of being combined with structural reinforcement fibers by being drawn from a laminating type machine without damaging the product.

(69) The resin-soluble thermoplastic veil of the present invention is characterized as being compatible and complementary to a curable resin matrix system. In this regard the resin matrix may further comprise a compatible or complementary thermoplastic toughening material that is the same or different than the resin-soluble thermoplastic in the veil. The thermoplastic incorporated in the resin may be soluble or insoluble.

(70) The resin-soluble thermoplastic polymer of the present invention is characterized as being soluble within the curable resin matrix. The polymer should have the ability to at least partially and preferably completely dissolve, (as opposed to melt) in the curable resin matrix, most preferably a curable resin matrix for infusing into a preform comprising reinforcement fibers and the present invention to manufacture the composite. The dissolution characteristic thus allows for more controlled distribution into the resin matrix than meltable thermoplastics.

(71) Additionally, as manufacturing with the thermoplastic polymer does not require a high temperature to dissolve and diffuse the thermoplastic polymer into the resin matrix, high processing temperatures are not required and out of autoclave manufacturing is possible.

(72) Dissolution should preferably occur at a dissolution temperature below that of the cure temperature for the resin and below the melt temperature of the polymer.

(73) The polymer element is preferably adapted to dissolve during the preliminary stages of the process, after resin infusion, during temperature ramping to the temperature for onset of gelling coalescence and/or curing.

(74) The polymer element is substantially independently undetectable in the properties of the cured composition. It is a particular advantage that the polymer element is soluble and may be physically traceless as a separate phase in the cured composition.

(75) The polymer element preferably chain links with the curable resin matrix and contributes to the properties of the resulting cured composite.

(76) In a preferred embodiment of the present invention, the fluid phase of the polymer element undergoes excellent dispersion by solvating effect in the curable component. This is particularly important to the properties of the resulting cured composite product. Raman spectroscopy at co-ordinates throughout the cured composite product shows complete dispersion, with identical scans at each coordinate.

(77) Thus, through control of the cure cycle, the extent of dispersion of the thermoplastic polymer in the curable resin matrix may be controlled to allow for full dispersion or local concentration of the polymer.

(78) Phase separation in the case of a fiber as a polymer element is characterized by complete dissolution. Phase transition e.g. solution of polymer element may be determined or monitored with use of any suitable techniques, for example TEM, SEM, neutron scattering and the like and such techniques may be employed by those skilled in the art to determine suitable polymer element characteristics and curable resin matrix characteristics and processing conditions for commercial production of cured compositions.

(79) The polymer is preferably adapted to undergo phase transition, i.e., to at least partially dissolve in the resin matrix at a temperature Ts in a range at least part of which is less than the cure temperature of the resin matrix Tc. The polymer element may be configured in manner to improve or hinder thermal conductivity and speed or slow transfer of heat into the element to endure rapid or delayed solution thereof.

(80) The polymer element may undergo complete or partial phase transition, e.g. may completely dissolve, or may partially dissolve whereby a portion thereof is dispersed into the matrix and a portion retains its elemental form, either by ensuring that precuring time and temperature are insufficient for complete dissolution or preferably by providing the polymer as a blend or co-polymer with one or more further insoluble polymers, for example in the form of a random or block co-polymer or other blend or derivative with organic or inorganic substrates. By this means the polymer element may be combined with one or more further polymers or other soluble or insoluble organic or inorganic substrates in the cured composition.

(81) The desired level resulting cured composite toughness is obtained by control of the morphology and phase sizes in the thermoset/thermoplastic blend through the chemistries of the thermoplastic polymer and the thermosetting resin precursors, as well as the other parameters of any desired morphology.

(82) Composites formed through the use of the instant resin-soluble thermoplastic veil in a resin infusion process exhibit equivalent toughness to standard prepreg systems formed with equivalent amounts of thermoplastic polymer toughening material.

(83) The percentage of thermoplastic polymer dissolved into the resin matrix between the structural reinforcement fibers provides surprising benefits over toughening material woven into the structural reinforcement fibers or pre-dissolved into the curable resin matrix. This is because while the total amount of thermoplastic toughening material in the system may be the same as a standard prepreg system, the concentration throughout the finished composite may be controlled, and in particular between plies. In the present invention, the dispersion of the thermoplastic polymer may be controlled such that the concentration of thermoplastic toughening material may be highest between the structural reinforcement fiber plies, decreasing in concentration as you approach a structural reinforcement fiber ply, being nominal within the fiber ply.

(84) FIG. 1 illustrates a possible polymer toughening material concentration gradient. This toughening material concentration gradient can provide for the increased toughening between fiber plies, rather than within the structural reinforcement fiber ply.

(85) FIG. 2 shows comparison data for toughness tests among a system with the polymer toughening material interleafed between layers of reinforcement fibers and without. This illustrates the improved toughening capability of the present invention.

(86) Localized toughening is also available through the use of the present invention in the instance where fasteners, openings or other forms of penetrations through the finished composite are required. A weakness in the composite in the form of cracking due to stresses around the penetration is created. It is known in the art that that this weakness is most prominent between the first and second ply, known as first-ply failure. The present invention can provide localized toughening in these failure prone regions, and in particular between the first and second ply through the addition of more layers of non-woven toughening material. This additional toughening material reduces cracking and weakness due to the penetrations.

(87) The concentration profile of dissolved toughening material as discussed above is only increased where additional toughener is added.

(88) FIG. 3 illustrates this localized toughening.

(89) It is further intuitive that this form of localized toughening may be incorporated anywhere with the composite and indeed may be incorporated throughout the composite at a local stress site.

(90) The present invention is further adaptable to chain linking during the cure cycle to further toughen the resulting cured composite. Chain linking components are preferably selected from the formula
B(Z).sub.n
wherein B is an oligomer or polymer backbone or is an aliphatic, alicyclic or aromatic hydrocarbon having from 1 to 10 carbon atoms and optionally including heteroatoms N, S, O and the like and optionally substituted, or is C, O, S, N or a transition metal nucleus or is a single bond, n is a whole number integer selected from 2 to 10000 preferably 2 to 8 or 5 to 500 or 500 to 10000.

(91) Accordingly it will be apparent that self-reaction between methacrylate ended polymer and chain linking component or between maleimide ended polymer and chain linking component or between oxazoline ended polymer and chain linking component, for example, is possible and within the scope of the present invention.

(92) In a preferred embodiment, the reactive end group is hydroxy and corresponds to a linking site functionality which is epoxy, whereby reaction thereof produces a hydroxy ether linkage in polymers of increased number average molecular weight having either hydroxy or epoxy end groups as desired. Alternatively, the reactive end group is NH.sub.2 and the linking site functionality is anhydride, whereby reaction thereof produces an imide linkage in polymers of increased number average molecular weight having NH.sub.2 or anhydride end groups. Alternatively the reactive end group is NH.sub.2 and the linking site functionality is maleimide. Mixtures of the above may be employed to produce a mixed architecture including a plurality of reactive end group-linking site combinations.

(93) Preferred linking components include multifunctional epoxy resins, amines and in particular triazines, and anhydrides. Suitable epoxy resins and amines are selected from resins hereinafter defined for matrix resins, and are preferably selected from MY0510, Epikote 828 [O(CH.sub.2CH)CH.sub.2OPh].sub.2C(CH.sub.3).sub.2 and the Cymel class of epoxies including Cymel 0510, benzophenone tetra carboxylic acid dianhydride (BTDA) [O(CO).sub.2Ph].sub.2CO, and maleic anhydride.

(94) Preferably polymer elements comprising two or more polymers comprise a blend or copolymer of amorphous polymers or of amorphous and semi crystalline polymer. This is of particular advantage in enabling the preparation of multiblock compositions having lowered processing temperatures whilst nevertheless retaining excellent product properties such as solvent resistance.

(95) The present invention is particularly beneficial to preforms for resin infusion technology. In a further aspect of the invention there is provided a resin-soluble thermoplastic veil for interposing between structural fiber layers for a curable composition comprising at least one resin-soluble polymer element together with structural elements, preferably reinforcing fibers, wherein the at least one resin-soluble polymer element is present in solid phase and adapted to undergo at least partial phase transition to fluid phase on contact with a resin matrix component of a curable composition in which the element is soluble, at a temperature which is less than the temperature for substantial onset of gelling and/or curing of the curable component.

(96) The structural reinforcement fibers can be of any type of textile structure known in the art for manufacturing composite materials made from reinforcing structural fabrics adaptable to infused liquid resins. Examples of suitable fabric types or configurations include, but are not limited to: all woven fabrics, examples of which include, but are not limited to polar weaves, spiral weaves and uniweaves; all multiaxial fabrics, examples of which include, but are not limited to multi warp knitted fabrics, non-crimp fabrics (NCF) and multidirectional fabrics; knitted fabrics braided fabrics; tailored fiber placement fabrics such as for example only fiber placement and embroidered fabrics, all non-woven fabrics, examples of which include but are not limited to mat fabric, felts, veils and chopped strands mats and fabrics that are comprised of combinations thereof.

(97) The fibers that make up the reinforcing structural fabric can be any type of fiber known in the art of composites, examples of which include, but are not limited to spun strands, extruded strands, cast strands, continuous fibers, random fibers, discontinuous fibers, chopped fibers, whiskers, filaments, ribbons, tapes, hollow fibers and combinations thereof. Suitable materials from which the fibers can be made include, but are not limited to those selected from the group consisting of carbon, aramid, quartz, boron, glass, polyethylene, polybenzazole, poly(p-phenylene-2,6-benzobisoxazole) polybenzothiazole alumina, zirconia, silicon carbide, Poly{2,6-diimidazol[4,5-b: 4s-e]pyridinylene-1,4(2,5-dihydroxy)phenylene} (PIPD, commercially available from Akzo Nobel Central Research, The Netherlands), graphite and basalt and combinations thereof.

(98) The structural reinforcement fiber layers used in conjunction with the present invention may be prepared in continuous manner for example as a roll of fabric which may be tailored by stitching and weaving in desired manner.

(99) Structural reinforcement fibers as hereinbefore defined can be short or chopped typically of mean fiber length not more than 2 cm, for example about 6 mm. Alternatively, and preferably, the fibers are continuous and may, for example, be unidirectionally-disposed fibers or a woven fabric, i.e. the composite material of structural reinforcement fibers and resin matrix forms a prepreg. Combinations of both short and/or chopped fibers and continuous fibers may be utilized. The fibers may be sized or unsized.

(100) Structural reinforcement fibers are typically at a concentration of 5 to 35; preferably at least 20% by weight of the prepreg. For structural applications, it is preferred to use continuous fiber for example glass or carbon, especially at 30 to 70, more especially 50 to 70% by volume.

(101) The structural reinforcement fiber can be organic, especially of stiff polymers such as poly paraphenylene terephthalamide, or inorganic. Among inorganic fibers glass fibers such as E or S can be used, or alumina, zirconia, silicon carbide, other compound ceramics or metals. A very suitable reinforcing fiber is carbon, especially as graphite. Graphite fibers which have been found to be especially useful in the invention are those supplied by Cytec Carbon Fibers under the trade designations T650-35, T650-42, T40/800 and T300; those supplied by Toray under the trade designations T300, T700, T800-HB, and T1000; and those supplied by Hexcel under the trade designations AS4, AU4, AS7, IM 8 and IM 7, and HTA; and those supplied by Tobo-Tenax under the trade designations HTA, HTS and IMS fibers.

(102) Organic or carbon fiber is preferably unsized or is sized with a material that is compatible with the curable composition according to the invention, in the sense of being soluble in the liquid curable composition without adverse reaction or of bonding both to the structural reinforcement fiber and to the thermoset/thermoplastic curable composition. In particular, carbon or graphite fibers that are unsized or are sized with epoxy resin precursor are preferred. Inorganic fiber preferably is sized with a material that bonds both to the structural reinforcement fiber and to the curable composition.

(103) The curable resin matrix composition may be any suitable resin known for use in the art that is preferably a liquid or a paste at ambient temperatures and is preferably selected in conjunction with the selection of material for use as the resin-soluble thermoplastic polymer so as to completely dissolve the resin-soluble thermoplastic polymer when elevated to a temperature that is less than or equal to the curing temperature for the resin, but below the melt temperature of the resin-soluble thermoplastic polymer. Thermosetting resins are particularly preferred.

(104) Preferably, the curable resin matrix composition is an epoxy resin and can be selected from any known epoxy resin suitable to be infused into a structural reinforcement fabric for composite manufacture.

(105) The curable resin matrix composition is preferably selected from the group consisting of an epoxy resin, an addition-polymerization resin, especially a bis-maleimide resin, a formaldehyde condensate resin, especially a formaldehyde-phenol resin, a cyanate resin, an isocyanate resin, a phenolic resin, polyester resins, vinylester resins and mixtures of two or more thereof, and is preferably an epoxy resin derived from the mono or poly-glycidyl derivative of one or more of the group of compounds consisting of aromatic diamines, aromatic monoprimary amines, aminophenols, polyhydric phenols, polyhydric alcohols, polycarboxylic acids, cyanate ester resin, benzimidazole, polystyryl pyridine, polyimide or phenolic resin and the like, or mixtures thereof. Examples of addition-polymerization resin are acrylics, vinyls, bis-maleimides, and unsaturated polyesters. Examples of formaldehyde condensate resins are urea, melamine and phenols.

(106) More preferably the curable resin matrix composition comprises at least one epoxy, cyanate ester or phenolic resin precursor, which is liquid at ambient temperature for example as disclosed in EP-A-0311349, EP-A-0365168, EP-A-91310167.1 or in PCT/GB95/01303. Preferably the thermoset is an epoxy or cyanate ester resin or a mixture thereof.

(107) An epoxy resin may be selected from N,N,NN-tetraglycidyl diamino diphenylmethane (e.g., MY 9663, MY 720 or MY 721 sold by Ciba-Geigy) viscosity 10-20 Pa s at 50 C. (MY 721 is a lower viscosity version of MY 720 and is designed for higher use temperatures); N,N,N,N-tetraglycidyl-bis(4-aminophenyl)-1,4-diiso-propylbenzene (e.g., Epon 1071 sold by Shell Chemical Co.) viscosity 18-22 Poise at 110 C.; N,N,N,N-tetraglycidyl-bis(4-amino-3,5-dimethylphenyl)-1-,4-diisopropylb-enzene, (e.g., Epon 1072 sold by Shell Chemical Co.) viscosity 30-40 Poise at 110 C.; triglycidyl ethers of p-aminophenol (e.g. MY 0510 sold by Ciba-Geigy), viscosity 0.55-0.85 Pa s at 25 C.; preferably of viscosity 8-20 Pa at 25 C.; preferably this constitutes at least 25% of the epoxy components used; diglycidyl ethers of bisphenol A based materials such as 2,2-bis(4,4-dihydroxy phenyl) propane (e.g., DE R 661 sold by Dow, or Epikote 828 sold by Shell), and Novolak resins preferably of viscosity 8-20 Pa s at 25.degree. C.; glycidyl ethers of phenol Novolak resins (e.g., DEN 431 or DEN 438 sold by Dow), varieties in the low viscosity class of which are preferred in making compositions according to the invention; diglycidyl 1,2-phthalate, e.g., GLY CEL A-100; diglycidyl derivative of dihydroxy diphenyl methane (Bisphenol F) (e.g., PY 306 sold by Ciba Geigy) which is in the low viscosity class. Other epoxy resin precursors include cycloaliphatics such as 3,4-epoxycyclohexyl-3,-4-epoxycyclohexane carboxylate (e.g., CY 179 sold by Ciba Geigy) and those in the Bakelite range of Union Carbide Corporation.

(108) A cyanate ester resin may be selected from one or more compounds of the general formula NCOAr(Y.sub.xAr.sub.m).sub.qOCN and oligomers and/or polycyanate esters and combinations thereof wherein Ar is a single or fused aromatic or substituted aromatics and combinations thereof and therebetween nucleus linked in the ortho, meta and/or para position and x=0 up to 2 and m and q=0 to 5 independently. The Y is a linking unit selected from the group consisting of oxygen, carbonyl, sulphur, sulphur oxides, chemical bond, aromatic linked in ortho, meta and/or para positions and/or CR.sub.2 wherein R.sub.1 and R.sub.2 are hydrogen, halogenated alkanes, such as the fluorinated alkanes and/or substituted aromatics and/or hydrocarbon units wherein said hydrocarbon units are singularly or multiply linked and consist of up to 20 carbon atoms for each R.sub.1 and/or R.sub.2 and P(R.sub.3R.sub.4R.sub.4R.sub.5) wherein R.sub.3 is allyl, aryl alkoxy or hydroxy, R.sub.4 may be equal to R.sub.4 and a singly linked oxygen or chemical bond and R.sub.5 is doubly linked oxygen or chemical bond or Si(R.sub.3R.sub.4R.sub.4R.sub.6) wherein R.sub.3 and R.sub.4, R.sub.4 are defined as in P(R.sub.3R.sub.4R.sub.4R.sub.5) above and R.sub.5 is defined similar to R.sub.3 above. Commercially available cyanate esters include cyanate esters of phenol/formaldehyde derived Novolaks or dicyclopentadiene derivatives thereof, an example of which is XU71787 sold by the Dow Chemical Company, and low viscosity cyanate esters such as L10 (Lonza, Ciba-Geigy, Bisphenol derived).

(109) A phenolic resin may be selected from any aldehyde condensate resins derived from aldehydes such as methanal, ethanal, benzaldehyde or furfuraldehyde and phenols such as phenol, cresols, dihydric phenols, chlorphenols and C.sub.1-9 alkyl phenols, such as phenol, 3- and 4-cresol(1-methyl, 3- and 4-hydroxy benzene), catechol(2-hydroxy phenol), resorcinol(1,3-dihydroxy benzene) and quinol(1,4-dihydroxy benzene). Preferably phenolic resins comprise cresol and novolak phenols.

(110) Suitable bismaleimide resins are heat-curable resins containing the maleimido group as the reactive functionality. The term bismaleimide as used herein includes mono-, bis-, tris-, tetrakis-, and higher functional maleimides and their mixtures as well, unless otherwise noted. Bismaleimide resins with an average functionality of about two are preferred. Bismaleimide resins as thus defined are prepared by the reaction of maleic anhydride or a substituted maleic anhydride such as methylmaleic anhydride, with an aromatic or aliphatic di- or polyamine. Examples of the synthesis may be found, for example in U.S. Pat. Nos. 3,018,290, 3,018,292, 3,627,780, 3,770,691 and 3,839,358. The closely related nadicimide resins, prepared analogously from a di- or polyamine but wherein the maleic anhydride is substituted by a Diels-Alder reaction product of maleic anhydride or a substituted maleic anhydride with a diene such as cyclopentadiene, are also useful. As used herein and in the claims, the term bismaleimide shall include the nadicimide resins.

(111) Preferred di- or polyamine precursors include aliphatic and aromatic diamines. The aliphatic diamines may be straight chain, branched, or cyclic, and may contain heteroatoms. Many examples of such aliphatic diamines may be found in the above cited references. Especially preferred aliphatic diamines are hexanediamine, octanediamine, decanediamine, dodecanediamine, and trimethylhexanediamine.

(112) The aromatic diamines may be mononuclear or polynuclear, and may contain fused ring systems as well. Preferred aromatic diamines are the phenylenediamines; the toluenediamines; the various methylenedianilines, particularly 4,4-methylenedianiline; the naphthalenediamines; the various amino-terminated polyarylene oligomers corresponding to or analogues to the formula H.sub.2NAr[XAr].sub.nNH.sub.2, wherein each Ar may individually be a mono- or polynuclear arylene radical, each X may individually be O, S, CO.sub.2, SO.sub.2, OCO, C.sub.1-C.sub.10 lower alkyl, C.sub.1-C.sub.10 halogenated alkyl, C.sub.2-C.sub.10 lower alkyleneoxy, aryleneoxy, polyoxyalkylene or polyoxyarylene, and wherein n is an integer of from about 1 to 10; and primary aminoalkyl terminated di- and polysiloxanes.

(113) Particularly useful are bismaleimide eutectic resin mixtures containing several bismaleimides. Such mixtures generally have melting points which are considerably lower than the individual bismaleimides. Examples of such mixtures may be found in U.S. Pat. Nos. 4,413,107 and 4,377,657. Several such eutectic mixtures are commercially available.

(114) Preferably the resin-soluble polymer element and dissolving matrix are selected as a solution pair providing not only dissolution at desired time and temperature, but also good matrix injection, dispersion, morphology such as phase separation and traceless dispersion if desired, and the like. Suitable solution pairs include a low viscosity curable resin matrix composition for good injection and rapid dissolution, and compatibility with the resin-soluble polymer element. Alternatively or additionally less compatible resins may be used if it is desired to introduce phase separation for enhanced mechanical properties. Combinations of different viscosity resins may be used each contributing several of the above properties where these are not provided by a single resin.

(115) A curing agent may also be introduced in combination with the present invention such as any known thermoset curing agent, for example epoxy curing agents, as disclosed in EP-A-0 311 349, EP-A 91310167.1, EP-A-0 365 168 or in PCT/GB95/01303, which are incorporated herein by reference, such as an amino compound having a molecular weight up to 500 per amino group, for example an aromatic amine or a guanidine derivative. Particular examples are 3,3- and 4-,4-diaminodiphenylsulphone, (available as DDS from commercial sources), methylenedianiline,bis(4-amino-3,5-dimethylphenyl)-1,4-diisopropylbenzene (available as EPON 1062 from Shell Chemical Co); bis(4-aminophenyl)-1,4-diisopropylbenzene (available as EPON 1061 from Shell Chemical Co); 4-chlorophenyl-N,N-dimethyl-urea, eg Monuron; 3,4-dichlorophenyl-N,N-dimethyl-urea, eg Diuron and dicyanodiamide (available as Amicure CG 1200 from Pacific Anchor Chemical). Other standard epoxy curing agents such as aliphatic diamines, amides, carboxylic acid anhydrides, carboxylic acids and phenols can be used if desired. If a novolak phenolic resin is used as the main thermoset component a formaldehyde generator such as hexamethylenetetraamine (HMT) is typically used as a curing agent.

(116) A catalyst may be introduced into a preferred embodiment of the present invention. In this case, the curing catalyst employed preferably comprises a Lewis acid having amine functionality, instead of in addition to conventional catalysts.

(117) Preferably the catalyst is of the formula:
LX.sub.nR
where LX.sub.n is a Lewis acid and R is an amine. Preferably L is selected from Groups IIb, IIIb, VIII of the Periodic Table of the Elements and X is a halogen.

(118) Preferred catalysts include BF.sub.3, BCl.sub.3, AlF.sub.3, FeF.sub.3, ZnF.sub.2 as Lewis acid component and primary or secondary aliphatic or aromatic amine such as monoethyl amine (mea), dimethylamine (dma), benzylamine (bea) or piperidine.

(119) A composite may be manufactured using the present invention, preferably through resin infusion obtained by a method known in the art wherein a support structure comprising structural reinforcement fibers (dry) and the at least one resin-soluble thermoplastic veil element is placed into a bag, mold or tool to provide a preform and a curable resin matrix composition is injected/infused directly into the combined structural reinforcement fibers and veil.

(120) The preform is preferably formed, injected/infused and cured by processing techniques such as Resin Transfer Molding (RTM), Liquid Resin Infusion (LRI), Resin Infusion Flexible Tooling (RIFT), Vacuum Assisted Resin Transfer Molding (VARTM), Resin Film Infusion (RFI) and the like as hereinbefore referred.

(121) Suitably, the process includes a preliminary stage of infusion of curable resin matrix composition at reduced pressure, followed by a degassing stage drawing off air for reducing voidage. Traditionally the degassing is carried out under elevated pressure.

(122) The resin-soluble thermoplastic veil element remains in solid form during the initial stages of resin infusion and degassing, at ambient or reduced pressure, whereafter the polymer fibers dissolve and disperse without trace allowing the fluid phase components to compact, without external applied pressure, prior to onset of gelling coalescence and curing. If external pressure is applied, the performance is simply enhanced, however it is a particular advantage that this configuration allows for curing large panels without the need for an autoclave or the like.

(123) Suitably resin-soluble thermoplastic fibers are present in an amount of 2 to 50 wt %, preferably 2 to 40 wt %, more preferably 4 to 16 wt % in this embodiment.

(124) Additionally the configuration has advantages during resin infusion, whereby channels remain open and clear to assist in rapid and uniform resin infusion throughout the panel.

(125) Suitably, the process of the invention comprises subjecting to elevated temperature in the range up to 300 C., for example, 60 C. to 200 C., more preferably 75 C. to 150 C. for a period of up to 45 minutes, preferably 0.5 to 35 minutes to effect phase transition. Temperatures in the range 100 C-150 C. are particularly suitable for phase transition of readily soluble polymer elements for example of low MW, present in readily soluble concentration in an effective curable component solvent, and in the range 150 C. to 300 C. for less readily soluble polymer elements. Suitable elevated temperature is selected in a desired range to effect phase transition in a desired time, for example a given flexible polymer element may be subjected to elevated temperature in the range 135 C. to 170 C. for 2-10 minutes, 125 to 135 C. for 5-30 minutes or 105 C. to 125 C. for 10-40 minutes.

(126) Phase transition may be at ambient or elevated pressure corresponding to the desired injection, degassing and curing conditions.

(127) The process includes subjecting to further elevated temperature after phase transition to cause onset of gelling or curing. Gelling may be at temperatures in the range corresponding to pre-cure in known manner. Gelling is preferably followed by further elevated temperature cure, or the gelled composition may be cooled for later curing, for example if gel or cure is in an autoclave, or mold, the composition may be removed from the autoclave or mold and cure continued at ambient pressure in regular oven.

(128) Gelling or curing is suitably carried out by known means at elevated temperature and pressure for a suitable period, including temperature ramping and hold as desired. A suitable gelling or cure cycle corresponds to that for a conventional composition comprising the same component types and amounts and reference is made to the description and example illustrating calculation of amount of flexible polymer element present in the composition.

(129) Preferably cure is at temperature in the range 150 C. to 400 C. for 1-4 hours, for example. Additionally the process may include post curing at suitable conditions to enhance properties such as Tg and the like.

(130) Gelling or curing may be with use of catalysts as hereinbefore defined, whereby temperature increase causes activation, and cooling below activation temperature halts curing.

(131) The process may be monitored in real time but preferably a suitable reaction time and temperature is predetermined for a given composition, for example by preparing samples and analyzing solution and dispersion after completion of gelling or cure, for example by use of Raman spectroscopy or the like.

(132) The invention is now illustrated in non-limiting manner with reference to the following Examples.

EXAMPLES

Example 1

Veil Manufacturing

(133) 54 tex fibers made from a PES polymer are chopped to an average fiber length of 8 mm using a rotary blade chopper. The chopped fibers are then dispersed by hand on a release film and pressed between a press hot platens at 180 C. for 1 hour with a 15 bar piston pressure. The platens are then cooled down to 60.degree. C. and the resulting product is extracted. The product has a dimension of 15.times.15 and an AW of 60 gsm. The veil is stable and handleable for processing purposes during manufacture.

Example 2

Veil Dissolution

(134) A sample of veil made in the previous example (AW=60 gsm) weighing 10 grams is combined with 30 g of Cycom 977 20 resin by dipping the veil into the resin. The veil/resin combination is then placed in an oven at 130 C. for 1 hour. The resulting product is then observed under a microscope. The microscopic observation shows a homogeneous solution without visible traces of undissolved fibers or high concentration of thermoplastic.

Example 3

Composite Manufacturing

(135) Layers of a HTA-6K-370 GSM 5HS carbon fabric were interleafed with non-woven fabrics to manufacture RTM panels with a Vf=55% and a target thermoplastic content of 25% wt in the resin (54 gsm in the fabric). FIG. 4 illustrates this resin infusion process while FIG. 5 illustrates the veil and reinforcement fiber orientation.

(136) The results show that the insertion of the non-woven veil provides compression after impact (CAI) testing numbers equivalent to traditional toughened prepreg systems using the non-woven resin-soluble veil. The key mechanical properties were tested and the results are illustrated in FIG. 7-9.

Example 4

Stabilization of a Preform

(137) A resin-soluble thermoplastic PES polymer veil was adhered to a carbon reinforcement fabric by contacting the PES polymer veil to the carbon reinforcement fiber to form a stabilized preform for resin infusion.

(138) A layer of PES polymer veil and a layer of carbon reinforcement fabric were fed between pressure rollers and a heat plate. FIG. 6 illustrates this process for stabilization of the preform using the thermoplastic polymer veil of the present invention. The line speed of the process was about 1.7 ft/min, the heat rollers were at a temperature, T.sub.1, of about 163.degree. C.; and the chill roller was at a temperature, T.sub.2, of about 21.degree. C. All of the rollers had an applied pressure, P.sub.1, P.sub.2, and P.sub.3, respectively, of 100 psi.

(139) This process provided in-plane stabilization of the preform carbon fiber/thermoplastic polymer veil and allowed for subsequent heat bonding, stabilization, and preforming of dry fabric stacks prior to composite manufacturing using resin infusion techniques.