A PROCESS FOR TREATING GAS STREAMS WITH HIGH CONCENTRATION OF N2O

Abstract

A process for catalytically reducing N.sub.2O concentration by more than 90% in an off-gas stream containing more than 15 vol. % N.sub.2O, comprising the steps of a) adding a reducing agent and a fresh dilution gas and/or a recirculated gas to the off-gas stream to provide a diluted off-gas stream; b) introducing the diluted off-gas into a decomposing reaction of N.sub.2O in the diluted off-gas stream by reaction with the reducing agent in presence of a catalyst containing cobalt to N.sub.2 and O.sub.2; c) withdrawing a reacted outlet gas stream from step (b) having a temperature higher than 300 C. as the diluted off-gas stream introduced into step (b) due to exothermal decomposition of the N.sub.2O; and d) transferring heat from the outlet gas stream to the off-gas stream upstream step (b) and/or step (a) by indirect heat exchange.

Claims

1. A process for catalytically reducing N.sub.2O concentration by more than 90% in an off-gas stream containing more than 15 vol. % N.sub.2O, comprising the steps of a) adding a fresh dilution gas and/or a recirculated gas to the off-gas stream to provide a diluted off-gas stream with a reduced N.sub.2O concentration; b) introducing the diluted off-gas into a decomposing reaction of N.sub.2O in the diluted off-gas stream in presence of a catalyst containing cobalt to N.sub.2 and O.sub.2; c) withdrawing a reacted outlet gas stream from step (b) having a temperature higher than 600 C. due to exothermal decomposition of the N.sub.2O; and d) transferring heat from the reacted outlet gas stream to the diluted off-gas stream up-stream step (b) and/or the fresh dilution gas by indirect heat exchange.

2. The process of claim 1, wherein the cobalt containing catalyst comprises cobalt spinel.

3. The process of claim 1, wherein the catalyst containing cobalt has a monolithic or honeycomb shape.

4. The process of claim 1, wherein the diluted off-gas stream is introduced into the decomposing reaction at an inlet temperature of between 250-400 C.

5. The process of claim 1, wherein the temperature of the reacted outlet gas stream is between 700 C. and 900 C.

6. The process of claim 1, wherein the process further comprises removal of VOC.

7. The process of claim 1, wherein the process further comprises removal of NO.sub.x prior and/or after the adding the dilution gas and/or the recirculated gas to the gas stream and/or simultaneously with the decomposition of the N.sub.2O.

Description

[0012] A method of keeping the maximum temperature down with reactions with a high exothermic reaction temperature is to dilute the process gas with for instance dilution air or recirculate treated process gas. Both will lower the actual N.sub.2O concentration and thus the exothermic reaction temperature in the decomposition reactor. However, there is a cost both in terms of operating costs for blower and investment cost for all equipment due to the increased flow. Secondly the higher the outlet gas temperature is, the more valuable it is for heat recovery.

[0013] When treating off-gas streams with a high concentrations of N.sub.2O, like off-gas from adipic acid production, the gas needs to be diluted with large amounts of dilution gas. For 30 vol. % N.sub.2O, the dilution air flow is typically more than 4 times the process gas flow.

[0014] As the dilution gas needs to be blown into the off-gas stream, large amounts of dilution air to be blown into the off-gas stream require high energy consumption and high expenses for the suitable equipment.

[0015] This invention relates to a process for reducing N.sub.2O concentration in a gas stream with higher than 15 vol. % N.sub.2O.

[0016] Thus, the present invention provides a process for catalytically reducing N.sub.2O concentration by more than 90% in an off-gas stream containing more than 15 vol. % N2O at the inlet to the catalytic treatment, comprising the steps of [0017] a) adding a dilution gas and/or a recirculated gas to the off-gas stream to provide a diluted off-gas stream; [0018] b) introducing the diluted off-gas into a decomposing reaction of N.sub.2O in the diluted off-gas stream by reaction with the reducing agent in presence of a catalyst containing cobalt to N.sub.2 and H.sub.2O; [0019] c) withdrawing a reacted outlet gas stream from step (b) having a temperature higher than 300 C. as the diluted off-gas stream introduced into step (b) due to exothermal de-composition of the N.sub.2O; and [0020] d) transferring heat from the outlet gas stream to the off-gas stream upstream step (b) and/or step (a) by indirect heat exchange.

[0021] Preferably, the cobalt containing catalyst comprises cobalt spinel.

[0022] A cobalt spinel phase catalyst is highly thermally stable and active in N.sub.2O decomposition. The catalyst is also active at relatively low temperatures at about 300 C. to 400 C., giving a large temperature window and thus less need for dilution air or recirculation flow to keep temperature down, when treating off-gases with a high concentration of N.sub.2O.

[0023] In order to reduce pressure drop in the N.sub.2O decomposition the catalyst containing cobalt has preferably a monolithic or honeycomb shape.

[0024] As an example, the adiabatic temperature increase from the exothermic decomposition of for example 30 vol % N.sub.2O would at an inlet temperature of 350 C. result in an outlet temperature of approximately 1040 C., depending naturally on the actual gas composition. Adding dilution air to keep the temperature down below 500 C., a dilution air flow of more than 400% is required, resulting in a flow more than 5 times larger than the flow to be treated.

[0025] If instead at outlet temperature of 850 C. can be accepted without damaging the catalyst, the dilution air flow can be reduced to less than 50% of the original flow. The resulting total flow is less than 30% of the flow where the maximum temperature is 500 C. This has a major impact on cost of the system.

[0026] According to the invention, the off-gas stream gas is diluted with a dilution gas (for instance ambient air or recirculated gas already treated catalytically) to an extend that results in a temperature between 600 and 900 C., preferred 700 and 900 C. and most preferred 800 and 900 C. after the catalytic decomposition of N.sub.2O.

[0027] With an inlet temperature of 400 C., decomposing 15% of N.sub.2O to N.sub.2 and O.sub.2 will give a temperature increase in an adiabatic reactor up near 750 C.depending on actual gas composition.

[0028] The N.sub.2O concentration must be reduced as much as possible to reduce the environmental impact of the emission and thus by at least 90%, but preferred more than 95% and most preferred more than 99%.

[0029] The diluted gas is passed over a catalyst comprising preferably cobalt spinel, which is thermally stable and active for N.sub.2O decomposition.

[0030] The outlet gas stream is used to feed energy into the inlet gas stream for the N.sub.2O decomposition reactor using a heat exchanger, for instance a feed/effluent heat exchanger or preheating dilution air. This can also be steam generation and then using part of this steam for heating the diluted off-gas stream or the dilution gas.

[0031] The effluent gas stream from the N.sub.2O decomposition reactor can also be used for additional heat recovery, such as steam generation. This can be either before or after the heat exchanger feeding energy into the inlet gas stream for the N.sub.2O decomposition reactor.

[0032] Most effective is using the outlet gas stream to first preheating dilution air and then steam generation as that gives the highest degree of energy recovery. Due to the increased gas flow and the required reaction temperature, the steam superheating and steam generation can typically cool the reacted outlet gas to a lower temperature than dilution air preheating and therefore results in higher energy recovery. The last portion of the energy can be used for steam generation.

[0033] Catalytic removal of VOC (volatile organic compounds) can be included in the catalytic N.sub.2O decomposition for streams containing VOC. VOC can also be removed upstream and will help increase the temperature of the gas stream to be heated to a temperature suitable for N.sub.2O decomposition.

[0034] If the off-gas stream contains NOx it is preferred to remove the NOx in an SCR stage prior and/or after the adding the dilution gas and/or the recirculated gas to the gas stream and/or simultaneously with the decomposition of the N.sub.2O. If an SCR stage is included in the process, the off-gas stream can advantageously preheated by indirect heat exchange with the recirculated outlet gas from the N.sub.2O composition.

[0035] In summary, preferred features of the invention are: [0036] 1. A process for reducing N.sub.2O concentration by more than 90% in an off-gas stream containing more than 15 vol. % N.sub.2O, comprising the steps of [0037] a) adding a reducing agent and a fresh dilution gas and/or a recirculated gas to the off-gas stream to provide a diluted off-gas stream; [0038] b) introducing the diluted off-gas into a decomposing reaction of N.sub.2O in the diluted off-gas stream by reaction with the reducing agent in presence of a catalyst containing cobalt to N.sub.2 and O.sub.2; [0039] c) withdrawing a reacted outlet gas stream from step (b) having a temperature higher than 300 C. as the diluted off-gas stream introduced into step (b) due to exothermal decomposition of the N.sub.2O; and [0040] d) transferring heat from the outlet gas stream to the off-gas stream upstream step (b) and/or step (a) by indirect heat exchange. [0041] 2. The process of feature 1, wherein the cobalt containing catalyst comprises cobalt spinel. [0042] 3. The process of feature 1 or 2, wherein the catalyst containing cobalt has a monolithic or honeycomb shape.

[0043] 4. The process of any one of features 1 to 3, wherein the diluted off-gas stream is introduced into the decomposing reaction at an inlet temperature of between 250-400 C.

[0044] 5. The process of any one of features 1 or 4, wherein the temperature of the reacted outlet gas stream is between 700 C. and 900 C. [0045] 6. The process according to any one of features 1 to 5, wherein the process further comprises removal of VOC. [0046] 7. The process according to any one of features 1 to 6, wherein the process further comprises removal of NOx prior and/or after the adding the dilution gas and/or the recirculated gas to the gas stream and/or simultaneously with the decomposition of the N.sub.2O.