SELECTIVE PRODUCTION OF N-PARAFFIN HYDROCRACKING PRODUCTS FROM HEAVIER N-PARAFFINS

Abstract

A process for selectively making hydrocracked n-paraffins from hydrocarbon compositions comprising heavy n-paraffins is disclosed. The process generally comprises the use of a hydrocracking catalyst comprising an unsulfided low acidity noble metal containing zeolite. The invention is useful for making lighter n-paraffin products for various applications, generally including upgrading hydrocarbon feedstocks to produce fuels, solvents, lubricants, chemicals and other hydrocarbonaceous compositions, and more particularly, as feedstocks for ethylene and linear alkyl benzene production and as jet and diesel fuel blend components.

Claims

1. A process for selectively producing hydrocracked n-paraffins from heavy n-paraffins comprising contacting a hydrocarbon feed comprising heavy n-paraffins with a hydrocracking catalyst comprising an unsulfided low acidity noble-metal containing zeolite under hydrocracking conditions to produce a hydrocarbon product comprising hydrocracked n-paraffins.

2. The process of claim 1, wherein the zeolite is an aluminosilicate.

3. The process of claim 1, wherein the zeolite is an aluminosilicate having a low alumina content and/or a high silica-to-alumina ratio.

4. The process of claim 2, wherein the zeolite silica-to-alumina ratio is of a sufficient value or range to selectively produce n-paraffin cracking products, preferably n-paraffin products over isoparaffin products.

5. The process of claim 2, wherein the zeolite silica-to-alumina ratio is at least about 70, or 80, or 90, or 100, or 110, or 120.

6. The process of claim 1, wherein the zeolite is an aluminosilicate that does not contain boron or is not a borosilicate or aluminoborosilicate, or is other than a borosilicate or aluminoborosilicate.

7. The process of claim 1, wherein the zeolite is an aluminosilicate zeolite hydrocracking catalyst selected from USY, Beta, ZSM-4, ZSM-12, ZSM-18, ZSM-20, Y, L or a combination thereof.

8. The process of claim 7, wherein the zeolite is selected from USY and ZSM-12, or a combination thereof.

9. The process of claim 1, wherein the heavy n-paraffins comprise C.sub.12+ n-paraffins, or are predominantly C.sub.12+ n-paraffins, or wherein the C.sub.12+ content is greater than about 50 wt %, or 60, or 70, or 80, or 90, or 95, or 98, or is about 100%.

10. The process of claim 1, wherein the noble metal comprises platinum.

11. The process of claim 1, wherein the hydrocracking conditions comprise a temperature of about 270° C. to about 330° C., a pressure in the range of about 200 psig to about 2000 psig and a space velocity in the range of about 0.4 to about 2.0 LHSV hr.sup.−1.

12. The process of claim 1, wherein the fractional yield of hydrocracked n-paraffin product is at least about 10 mol % greater than a corresponding fractional yield obtained using a hydrocracking catalyst that differs only in having a zeolite silica-to-alumina ratio that is no greater than about 60.

13. The process of claim 12, wherein the fractional yield of hydrocracked n-paraffin product is at least about 20, or 30, or 40, or 50, or 60, or 70, or 80, or 90, or 100 mol % greater.

14. Use of an unsulfided low acidity noble-metal containing zeolite for selectively producing hydrocracked n-paraffins from heavy n-paraffins in accordance with the process of claim 1.

15. Use of an unsulfided low acidity noble-metal containing zeolite according to claim 14, wherein the zeolite is an aluminosilicate zeolite hydrocracking catalyst selected from USY, Beta, ZSM-4, ZSM-12, ZSM-18, ZSM-20, Y, L or a combination thereof.

16. Use of an unsulfided low acidity noble-metal containing zeolite according to claim 14, wherein the zeolite is an aluminosilicate zeolite hydrocracking catalyst selected from USY and ZSM-12, or a combination thereof.

17. A hydrocracked n-paraffin composition produced in accordance with the process of claim 1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] The scope of the invention is not limited by any representative figures accompanying this disclosure and is to be understood to be defined by the claims of the application.

[0009] FIGS. 1a, 1b, 1c, 1d, and 1e show selectivity profiles of paraffin cracking products using a Pt/USY, SAR=60 hydrocracking catalyst, as described in the examples.

[0010] FIGS. 2a, 2b, 2c, 2d, and 2e show selectivity profiles of paraffin cracking products using a Pt/USY, SAR=108 hydrocracking catalyst, as described in the examples.

[0011] FIGS. 3a, 3b, and 3c show a comparison of selectivities to normal and branched paraffin cracking products between Pt/USY, SAR=60 and Pt/USY, SAR=108 for C.sub.6, C.sub.8, and C.sub.10 products, as described in the examples.

DETAILED DESCRIPTION

[0012] Although illustrative embodiments of one or more aspects are provided herein, the disclosed processes, and compositions formed therefrom, may be implemented using any number of techniques. The disclosure is not limited to the illustrative or specific embodiments, drawings, and techniques illustrated herein, including any exemplary designs and embodiments illustrated and described herein, and may be modified within the scope of the appended claims along with their full scope of equivalents.

[0013] Unless otherwise indicated, the following terms, terminology, and definitions are applicable to this disclosure. If a term is used in this disclosure but is not specifically defined herein, the definition from the IUPAC Compendium of Chemical Terminology, 2nd ed (1997), may be applied, provided that definition does not conflict with any other disclosure or definition applied herein, or render indefinite or non-enabled any claim to which that definition is applied. To the extent that any definition or usage provided by any document incorporated herein by reference conflicts with the definition or usage provided herein, the definition or usage provided herein is to be understood to apply.

[0014] “Periodic Table” refers to the version of IUPAC Periodic Table of the Elements dated Jun. 22, 2007, and the numbering scheme for the Periodic Table Groups is as described in Chemical and Engineering News, 63(5), 27 (1985).

[0015] “Hydrocarbonaceous”, “hydrocarbon” and similar terms refer to a compound containing only carbon and hydrogen atoms. Other identifiers may be used to indicate the presence of particular groups, if any, in the hydrocarbon (e.g., halogenated hydrocarbon indicates the presence of one or more halogen atoms replacing an equivalent number of hydrogen atoms in the hydrocarbon).

[0016] “Hydroprocessing” or “hydroconversion” refers to a process in which a carbonaceous feedstock is brought into contact with hydrogen and a catalyst, at a higher temperature and pressure, for the purpose of removing undesirable impurities and/or converting the feedstock to a desired product. Such processes include, but not limited to, methanation, water gas shift reactions, hydrogenation, hydrotreating, hydrodesulphurization, hydrodenitrogenation, hydrodemetallation, hydrodearomatization, hydroisomerization, hydrodewaxing and hydrocracking including selective hydrocracking. Depending on the type of hydroprocessing and the reaction conditions, the products of hydroprocessing can show improved physical properties such as improved viscosities, viscosity indices, saturates content, low temperature properties, volatilities and depolarization.

[0017] “Hydrocracking” refers to a process in which hydrogenation and dehydrogenation accompanies the cracking/fragmentation of hydrocarbons, e.g., converting heavier hydrocarbons into lighter hydrocarbons, or converting aromatics and/or cycloparaffins into non-cyclic paraffins.

[0018] The terms “binder” or “support”, particularly as used in the term “catalyst support”, refers to conventional materials that are typically a solid with a high surface area, to which catalyst materials are affixed. Support materials may be inert or participate in the catalytic reactions, and may be porous or non-porous. Typical catalyst supports include various kinds of carbon, alumina, silica, and silica-alumina, e.g., amorphous silica aluminates, zeolites, alumina-boria, silica-alumina-magnesia, silica-alumina-titania and materials obtained by adding other zeolites and other complex oxides thereto.

[0019] “Molecular sieve” refers to a material having uniform pores of molecular dimensions within a framework structure, such that only certain molecules, depending on the type of molecular sieve, have access to the pore structure of the molecular sieve, while other molecules are excluded, e.g., due to molecular size and/or reactivity. Zeolites, crystalline aluminophosphates and crystalline silicoaluminophosphates are representative examples of molecular sieves.

[0020] “Middle distillates” include jet fuel, diesel fuel, and kerosene, typically with cut points as shown below:

TABLE-US-00001 Typical Cut Points, ° F. (° C.) for Products North American Market Light Naphtha C5-180 (C5-82)  Heavy Naphtha 180-300 (82-149)  Jet  300-380 (149-−193) Kerosene 380-530 (193-277) Diesel 530-700 (277-371)

[0021] SiO.sub.2/Al.sub.2O.sub.3 ratio (SAR) is determined by inductively coupled plasma (ICP) elemental analysis. A SAR of infinity means there is no aluminum in the zeolite, i.e., the mole ratio of silica to alumina is infinity.

[0022] In this disclosure, while compositions and methods or processes are often described in terms of “comprising” various components or steps, the compositions and methods may also “consist essentially of” or “consist of” the various components or steps, unless stated otherwise.

[0023] The terms “a,” “an,” and “the” are intended to include plural alternatives, e.g., at least one. For instance, the disclosure of “a transition metal” or “an alkali metal” is meant to encompass one, or mixtures or combinations of more than one, transition metal or alkali metal, unless otherwise specified.

[0024] All numerical values within the detailed description and the claims herein are modified by “about” or “approximately” the indicated value, and take into account experimental error and variations that would be expected by a person having ordinary skill in the art.

[0025] The inventive process selectively produces hydrocracked n-paraffins from heavy n-paraffins by contacting a hydrocarbon feed comprising heavy n-paraffins with a hydrocracking catalyst that is selective for producing such n-paraffins. In general, the hydrocracking catalyst comprises an unsulfided low acidity noble-metal containing zeolite, while the under hydrocracking conditions are suitable to produce a hydrocarbon product comprising hydrocracked n-paraffins.

[0026] The zeolite may typically be an aluminosilicate with low acidity, including low alumina content and/or a high silica-to-alumina ratio. While not specifically limited to a particular lower value or range, the zeolite silica-to-alumina ratio is of a sufficient value or range to selectively produce n-paraffin cracking products, preferably n-paraffin products over isoparaffin products. More specific useful ranges include low acidity zeolites having silica-to-alumina ratios of at least about 70, or 80, or 90, or 100, or 110, or 120. The zeolite may an aluminosilicate that does not contain boron or is not a borosilicate or aluminoborosilicate, or is other than a borosilicate or aluminoborosilicate. Specific examples of suitable zeolites may include hydrocracking catalysts selected from USY, Beta, ZSM-4, ZSM-12, ZSM-18, ZSM-20, Y, L or a combination thereof. Useful zeolites noted herein are well-described in the patent literature, e.g., U.S. Pat. Nos. 5,284,985 and 5,364,997.

[0027] The process of may be used to produce hydrocracked n-paraffin compositions from heavier n-paraffins, e.g., where the heavy n-paraffins comprise C.sub.12+ n-paraffins, or are predominantly C.sub.12+ n-paraffins, or wherein the C.sub.12+ content is greater than about 50 wt %, or 60, or 70, or 80, or 90, or 95, or 98, or is about 100%. Suitable feeds comprising heavier n-paraffins are not necessarily limited, and may include waxy feedstocks, such as high molecular weight Fischer-Tropsch waxes, hydrocracker recycle streams, gas oils, and paraffinic resids. Feeds with up to about 30 wt. % and higher of normal and slightly branched paraffins having 2 or less alkyl substituents may also be used.

[0028] The noble metal may generally include any noble metal such as platinum and palladium, along with other Group VIIIA metals such as iridium and rhodium. Preferably, the noble metal comprises platinum, or is platinum.

[0029] The noble metal may be incorporated into the catalyst by any suitable method such as impregnation or exchange onto the zeolite. The noble metal may be incorporated in the form of a cationic, anionic or neutral complex such as Pt(NH.sub.3).sub.4.sup.2+ and cationic complexes of this type will be found convenient for exchanging metals onto the zeolite. The amount of noble metal is suitably from about 0.01 to about 10 percent by weight, normally from about 0.1 to about 2.0 percent by weight. In a preferred method of synthesizing Pt/boron-containing zeolite Beta the platinum compound is tetraamineplatinum hydroxide. The noble metal is preferably introduced into the catalyst composition with a pH neutral solution.

[0030] A high level of noble metal dispersion is generally preferred. For example, platinum dispersion is measured by the hydrogen chemisorption technique and is expressed in terms of H/Pt ratio. The higher the H/Pt ratio, the higher the platinum dispersion. Preferably the resulting zeolite should have an H/Pt ratio greater than about 0.8.

[0031] Binder materials may also be used with the zeolite, such as silica, silica alumina, silica-boria, silica-magnesia, silica-zirconia, silica-thoria, silica-berylia, silica-titania as well as ternary compositions such as silica-alumina-boria, silica alumina-thoria, silica-alumina-zirconia, silica-alumina magnesia or silica-magnesia-zirconia. When used, the ratio of binder to zeolite will typically vary from about 9:1 to about 1:9, more commonly from about 3:1 to about 1:3 (by weight).

[0032] The process is conducted under suitable hydrocracking conditions for the particular catalyst used; such conditions typically comprise a temperature of about 270° C. to about 330° C., a pressure in the range of about 200 psig to about 2000 psig and a space velocity in the range of about 0.4 to about 2.0 LHSV hr.sup.−1.

[0033] The process is typically conducted with a low sulfur feed having less than about 500 ppm sulfur and less than about 50 ppm nitrogen. It is preferable that the feed to the process have less than about 50 ppm sulfur. Feeds having less than about 500 ppm sulfur without preliminary hydrotreatment prior to contacting with the unsulfided catalyst composition of the present invention are preferred.

[0034] A hydrotreating step using a conventional hydrotreating catalyst may also be carried out to remove nitrogen and sulfur and to saturate aromatics to naphthenes without substantial boiling range conversion. Suitable hydrotreating catalysts generally comprise a metal hydrogenation component, usually a Group VIA or VIIIA metal. Hydrotreating will usually improve catalyst performance and permit lower temperatures, higher space velocities, lower pressures or combinations of these conditions to be employed.

[0035] The process of the invention provides a number of advantages, as supported by the examples that follow, including improved fractional yield of hydrocracked n-paraffin product relative to isoparaffins produced, as compared with hydrocracking catalysts that do not utilize a low acidity zeolite. For example, when hydrocracking performance for n-paraffin production is compared with a similar zeolite that differs from the low acidity zeolite only in the silica-to-alumina ratio (SAR), significant improvements in product n-paraffin content may be realized. While not necessarily limited thereto, such fractional yield improvements may be, e.g., at least about 10 mol % greater than a corresponding fractional yield obtained using a hydrocracking catalyst that differs only in having a zeolite silica-to-alumina ratio that is no greater than about 60. In some embodiments, such fractional yield improvements may be even greater, e.g., at least about 20, or 30, or 40, or 50, or 60, or 70, or 80, or 90, or 100 mol % greater than a corresponding fractional yield obtained using a hydrocracking catalyst that differs only in having a zeolite silica-to-alumina ratio that is no greater than about 60.

EXAMPLES

Example 1: Preparation of Pt/USY Zeolite with a Silica-to-Alumina Ratio (SAR)=60

[0036] The USY zeolite used, CBV-760, was obtained from Zeolyst. The platinum addition was carried out as follows:

[0037] 1 gram of CBV-760 (FAU zeolite from Zeolyst) was added to a vial along with 5 g of 0.148M NH.sub.4OH solution and 6 mL of DI water. A platinum-containing solution was prepared by dissolving 350 mg of Pt(NH.sub.3).sub.4(NO.sub.3).sub.2 in 5 g of 0.148M NH.sub.4OH solution and 32 ml of H.sub.2O. One mL of the latter platinum solution was added to the vial containing CVB-760, 0.148 M NH.sub.4OH solution, and water.

[0038] The solution was left to stand for 2-3 d at room temperature and subsequently filtered. The platinum-containing zeolite powder was dried at 90° C. in an oven for 2-4 hr and then placed as a fine powder in a thin glass dish and calcined to 300° C. in air flowing at 20-40 ft.sup.3/min. A stepped heating program was used: a) heat at 1° C./min to 120° C., b) hold for 2 hr, c) heat at 1° C./min to 300° C., d) hold for 3 hr, e) turn off heat and allow cooling to room temperature.

[0039] The catalyst was pressed into a pellet, which was crushed to give solids with a 20-40-mesh size upon sieving.

[0040] The properties of the lower SAR Pt/USY catalyst are provided below: [0041] Pt content, wt %: 0.43 [0042] Pt dispersion, strong, %: 52.20 [0043] Pt dispersion, total, %: 128.20 [0044] Al content, wt %: 1.22 [0045] Si content, wt %: 44.5 [0046] SiO.sub.2/Al.sub.2O.sub.3 molar ratio (SAR): 58.5

Example 2: Selectivity Profiles Using Pt/USY (SAR=60), Preparation Described in Example 1

[0047] 0.7 g of the catalyst whose preparation is described in Example 1 was diluted with inert alundum and charged to a reactor comprised of a 0.25″-OD tube of 0.035″ wall thickness placed in a furnace.

[0048] The catalyst was dried by flowing 50 cm.sup.3/min of N.sub.2 over the catalyst bed at 250° F. for at least 2 hr. The catalyst was reduced by heating to 600° F. in H.sub.2 flowing at 50 cm.sup.3/min at atmospheric pressure and keeping it at that temperature for at least 1 hr. The reactor was cooled to the 518° F. temperature and pressurized to 1200 psig with hydrogen; the reactant n-hexadecane was then pumped through the reactor.

[0049] Yield periods were carried out after allowing steady state to be approached at a particular set of conditions (temperature, pressure, weight hourly space velocity [WHSV]). The conversion was varied by changing WHSV.

[0050] The yield of iso- and normal C.sub.4-C.sub.13 paraffin products, as functions of conversion at 1200 psig and 518° F., are shown FIGS. 1a to 1e.

[0051] As shown in FIGS. 1a to 1e, conversions below 60% iso and normal cracking products are formed in similar yields. At higher conversion, the yields of isoparaffin cracking products predominate. Yields at 50% n-hexadecane conversion are given in Table A; the yield ratios of normal- to iso-paraffin cracking products by carbon number are generally below 1. Such a catalyst would not be suitable for selectively producing light n-paraffins.

TABLE-US-00002 TABLE A Fractional Molar Yields at 50% n-Hexadecane conversion with Pt/USY, SAR = 60 (1200 psig, 518° F.) Molar Yield Carbon n-paraffin i-paraffin Number (×10.sup.3) (×10.sup.3) Ratio n/i 4 2.98 1.92 1.56 5 3.13 3.17 0.99 6 3.22 3.52 0.91 7 3.24 4.16 0.78 8 2.99 4.34 0.69 9 2.67 4.28 0.62 10 2.29 4.06 0.56 11 1.77 3.86 0.46 12 1.47 3.02 0.49 13 0.788 1.06 0.74

[0052] In general, with the catalyst of this example, yields of iso- and n-paraffin cracking products are similar at conversions below 60%, but isoparaffin yields predominate at higher conversions.

Example 3: Preparation of Pt/USY Zeolite with SAR=108

[0053] 3 g of a high-silica FAU zeolite (Tosoh product 385 HUA, SAR=100 nominal) are placed into a vial with 18 cc of water and 15 g of 0.148M NH.sub.4OH. Then 3 g of a platinum tetraamine dinitrate solution [prepared by dissolving 0.286 g of platinum tetramine dinitrate (Aesar, 49 wt % Pt) in 24.5 g of water and 4.1 g of a 0.148 M NH.sub.4OH solution] are added and the reaction mixture is left at room temperature for 3 days.

[0054] The solids then are collected by filtration and washed with 50 cc of water in 3 portions. Upon drying in vacuo, the solids are transferred to an oven and dried for 2 hr at 90° C. The solids are then spread thinly on a Pyrex dish and calcined according to the program described in Example 1.

[0055] The catalyst was pressed into a pellet, which was crushed to give solids with a 20-40-mesh size upon sieving.

[0056] The properties of the high SAR Pt/USY catalyst are provided below: [0057] Pt content, wt %: 0.472 [0058] Pt dispersion, strong, %: 70.2 [0059] Pt dispersion, total, %: 117.4 [0060] Al content, wt %: 0.739 [0061] Si content, wt %: 41.6 [0062] SiO.sub.2/Al.sub.2O.sub.3 molar ratio (SAR): 108

Example 4: Selectivity Profiles Using Pt/USY (SAR=108), Preparation Described in Example 3

[0063] 0.7 g of the catalyst whose preparation is described in Example 3 is diluted with inert alundum and charged to a reactor comprised of a 0.25″ OD tube of 0.035″ wall thickness placed in a furnace. The catalyst is dried and reduced as indicated in Example 1. Experiments are performed at 1200 psig with conversion varied by changing WHSV, but because this catalyst's lower activity, a higher temperature (626 vs. 518° F.) was needed to obtain a conversion range similar to that shown for Example 2.

[0064] The yield of iso- and normal C4-C13 paraffin products, as functions of conversion at 1200 psig and 626° F., are shown FIGS. 2a to 2e.

[0065] As shown in FIGS. 2a to 2e, n-paraffins are produced in significantly greater yields than corresponding isoparaffins at all conversions, in marked contrast to selectivities obtained with Pt/USY, SAR=60, illustrating the selective formation of n-paraffin cracking products. Yields at 50% n-hexadecane conversion are given in Table B; for a given carbon number, the n:i ratio is greater than 1. The advantages of Pt/USY, SAR=108 for selectively producing n-paraffins are thus indicated.

TABLE-US-00003 TABLE B Fractional Molar Yields at 51% n-Hexadecane conversion with Pt/USY, SAR = 105 (1200 psig, 626° F.) Molar Yield Carbon n-paraffin i-paraffin Number (×10.sup.2) (×10.sup.3) Ratio n/i 4 3.66 4.31 8.49 5 3.74 5.06 7.39 6 3.65 5.67 6.44 7 3.52 6.72 5.24 8 3.33 7.29 4.58 9 3.04 8.03 3.78 10 2.78 9.26 3.00 11 2.46 10.2 2.41 12 2.06 9.88 2.09 13 1.53 7.77 1.97

[0066] In general, with the catalyst of this example, i.e., a catalyst comprising Pt on a low-acidity (i.e., high SAR) USY zeolite, n-paraffin cracking products predominate, and the selective production of the latter is important to note.

[0067] The selectivities to normal and branched cracking products can also be compared between the two catalysts by plotting the respective isomer yields of normal and branched cracking products from each catalyst on the same graph for a given carbon number. Representative results, shown in FIGS. 3a to 3c for C.sub.6, C.sub.8, and C.sub.10 species, indicate the yields of normal paraffin cracking products are much greater with Pt/USY, SAR=108 at a given conversion (indicating greater selectivity) but that the yields and selectivities of branched paraffin cracking products are similar for the two catalysts.

Example 5: Preparation of Pt/SiO.SUB.2 .Catalyst

[0068] To 1.22 g of Cabosil M5 fumed silica (impurities<5 ppm) are added 1.22 g of a platinum tetraamine dinitrate solution; the latter solution is prepared by adding 0.286 grams of platinum tetramine dinitrate (Aesar; 49 wt % Pt) to in 24.5 grams of water and 4.1 grams of a 0.148 M NH.sub.4OH solution. An additional 4.2 grams of water was added but in increments with gentle mixing, to achieve incipient wetness.

[0069] The catalyst was prepared on a thin Pyrex plate so that it could then be directly dried and calcined as has been described for the other 2 catalysts (see Examples 1 and 3).

[0070] The properties of the Pt/SiO.sub.2 catalyst are provided below: [0071] Pt content, wt %: 0.480 [0072] Pt dispersion, strong, %: 37.2 [0073] Pt dispersion, total, %: 62.3

Example 6: n-Hexadecane Reactivity in the Presence of the Catalyst Prepared in Example 5

[0074] 0.7 g of the catalyst whose preparation is described in Example 5 was diluted with inert alundum and charged to a reactor comprised of a 0.25″-OD tube of 0.035″ wall thickness placed in a furnace. The catalyst is dried and reduced as indicated in Example 3.

[0075] Experiments were carried out at 1200 psig, WHSV=0.97, and two temperatures: 518 and 536° F. In all cases, n-hexadecane conversion was below 2%, indicating that Pt/SiO.sub.2 catalyst is less active than the catalyst described in Examples 3 and 4.

[0076] In a subsequent experiment, tetralin is fed to the reactor at 1200 psig, 518° F., and WHSV=10 (i.e., much milder conditions than those used for the experiments with n-hexadecane), complete hydrogenation of give cis- and trans-decalin occurs, indicating the high hydrogenation activity of the Pt/SiO.sub.2 catalyst.

[0077] From this example, it is seen that Pt/SiO.sub.2 has very low activity for n-hexadecane conversion at conditions comparable to those used in Example 2 and 4. Therefore, selective n-paraffin cracking products formation requires platinum loaded on a low-acidity (high SAR) zeolite. Despite its high hydrogenation activity, the Pt/SiO.sub.2 does not catalyze selective n-paraffin production, indicating that a catalyst comprising platinum loaded on a low-acidity zeolite is needed to catalyze the selective production of n-paraffin cracking products.

Example 7: Preparation of Pt/ZSM-12 Catalyst

[0078] A 2-gram sample of ZE0217, a ZSM-12 structure available from Zeolyst, was calcined to remove the organic template, and then loaded into a vial with 12 grams of water and 20 grams of 0.148 M NH4OH solution. Platinum tetraamine dinitrate solution (2 grams) was added to the vial. The platinum tetraamine dinitrate solution was prepared from dissolving 0.286 grams of platinum tetraamine dinitrate (Aesar; 49 wt % Pt), in 24.5 grams of water and 4.1 grams of a 0.148 M NH4OH solution to provide buffering. 1 gram of this solution provided a catalyst with 0.5 wt % loading if all the Pt ends up on the zeolite.

[0079] The contents were let to sit at room temperature for 2 days. Then the solids were collected by filtration and washed with 50 cc of water in 3 portions. Upon drying in vacuo, the solids were then transferred to an oven at 90° C. and dried for 2 hours. Then the solids were spread thinly on a Pyrex dish and calcined according to the following program: in positive flow of air at 1° C./minute, raise the temperature to 120° C.; then hold for 2 hours at this temperature; and then again at the same rate, raise the temperature to 300° C. and hold for 3 hours.

[0080] The properties of the Pt/ZSM-12 catalyst are provided below: [0081] Pt content, wt %: 0.447 [0082] Pt dispersion, strong, %: 29.5 [0083] Pt dispersion, total, %: 70.0 [0084] Al content, wt %: 0.701 [0085] Si content, wt %: 44.8 [0086] SiO.sub.2/Al.sub.2O.sub.3 molar ratio (SAR): 115

Example 8: n-Hexadecane Reactivity in the Presence of the Catalyst Prepared in Example 7

[0087] 0.7 g of the catalyst whose preparation is described in Example 7 was diluted with inert alundum and charged to a reactor comprised of a 0.25″ OD tube of 0.035″ wall thickness placed in a furnace. The catalyst was dried and reduced as indicated in Example 3.

[0088] Experiments were carried out at 1200 psig, WHSV=1.0, and at a temperature of 518° F. Conversion of n-hexadecane was 76%, which is significantly greater than the foregoing Pt/SiO.sub.2 and Pt/USY catalysts. Pt/ZSM-12 catalyst is therefore much more active than the Pt/SiO.sub.2 and Pt/USY catalysts and selective for n-paraffin cracking products.

[0089] From this example, it is seen that Pt/ZSM-12 has high activity for n-hexadecane conversion at conditions comparable to those used in Example 2 and 4. Selective n-paraffin cracking products formation is therefore seen to require platinum loaded on a low-acidity (high SAR) zeolite. As noted, despite its high hydrogenation activity, the Pt/SiO.sub.2 catalyst does not catalyze selective n-paraffin production, indicating that a catalyst comprising platinum loaded on a low-acidity zeolite, such as a Pt/ZSM-12 catalyst, is needed to catalyze the selective production of n-paraffin cracking products.

[0090] For the avoidance of doubt, the present application is directed to the subject-matter described in the following numbered paragraphs:

1. A process for selectively producing hydrocracked n-paraffins from heavy n-paraffins comprising contacting a hydrocarbon feed comprising heavy n-paraffins with a hydrocracking catalyst comprising an unsulfided low acidity noble-metal containing zeolite under hydrocracking conditions to produce a hydrocarbon product comprising hydrocracked n-paraffins.
2. The process of paragraph 1, wherein the zeolite is an aluminosilicate.
3. The process of paragraph 1, wherein the zeolite is an aluminosilicate having a low alumina content and/or a high silica-to-alumina ratio.
4. The process in accordance with paragraphs 2 or 3, wherein the zeolite silica-to-alumina ratio is of a sufficient value or range to selectively produce n-paraffin cracking products, preferably n-paraffin products over isoparaffin products.
5. The process in accordance with paragraphs 2 or 3, wherein the zeolite silica-to-alumina ratio is at least about 70, or 80, or 90, or 100, or 110, or 120.
6. The process in accordance with paragraphs 1 to 5, wherein the zeolite is an aluminosilicate that does not contain boron or is not a borosilicate or aluminoborosilicate, or is other than a borosilicate or aluminoborosilicate.
7. The process in accordance with paragraphs 1 to 6, wherein the zeolite is an aluminosilicate zeolite hydrocracking catalyst selected from USY, Beta, ZSM-4, ZSM-12, ZSM-18, ZSM-20, Y, L or a combination thereof.
8. The process in accordance with paragraph 7, wherein the zeolite is selected from USY and ZSM-12, or a combination thereof.
9. The process in accordance with paragraphs 1 to 8, wherein the heavy n-paraffins comprise C.sub.12+ n-paraffins, or are predominantly C.sub.12+ n-paraffins, or wherein the C.sub.12+ content is greater than about 50 wt %, or 60, or 70, or 80, or 90, or 95, or 98, or is about 100%.
10. The process in accordance with paragraphs 1 to 9, wherein the noble metal comprises platinum.
11. The process in accordance with paragraphs 1 to 10, wherein the hydrocracking conditions comprise a temperature of about 270° C. to about 330° C., a pressure in the range of about 200 psig to about 2000 psig and a space velocity in the range of about 0.4 to about 2.0 LHSV hr.sup.−1.
12. The process in accordance with paragraphs 1 to 11, wherein the fractional yield of hydrocracked n-paraffin product is at least about 10 mol % greater than a corresponding fractional yield obtained using a hydrocracking catalyst that differs only in having a zeolite silica-to-alumina ratio that is no greater than about 60.
13. The process in accordance with paragraph 12, wherein the fractional yield of hydrocracked n-paraffin product is at least about 20, or 30, or 40, or 50, or 60, or 70, or 80, or 90, or 100 mol % greater.
14. Use of an unsulfided low acidity noble-metal containing zeolite for selectively producing hydrocracked n-paraffins from heavy n-paraffins in accordance with the process of paragraphs 1 to 13.
15. Use of an unsulfided low acidity noble-metal containing zeolite in accordance with paragraph 14, wherein the zeolite is an aluminosilicate zeolite hydrocracking catalyst selected from USY, Beta, ZSM-4, ZSM-12, ZSM-18, ZSM-20, Y, L or a combination thereof.
16. Use of an unsulfided low acidity noble-metal containing zeolite in accordance with paragraph 14, wherein the zeolite is an aluminosilicate zeolite hydrocracking catalyst selected from USY and ZSM-12, or a combination thereof.
17. A hydrocracked n-paraffin composition produced in accordance with the process of paragraphs 1 to 13.

[0091] Additional details concerning the scope of the invention and disclosure may be determined from the appended claims.

[0092] The foregoing description of one or more embodiments of the invention is primarily for illustrative purposes, it being recognized that variations might be used which would still incorporate the essence of the invention. Reference should be made to the following claims in determining the scope of the invention.

[0093] For the purposes of U.S. patent practice, and in other patent offices where permitted, all patents and publications cited in the foregoing description of the invention and any other part of the application are incorporated herein by reference to the extent that any information contained therein is consistent with and/or supplements the foregoing disclosure.