METHOD OF MANUFACTURING SEMICONDUCTOR DEVICES AND CORRESPONDING DEVICE

Abstract

In one embodiment, a method of manufacturing semiconductor devices including metallizations (e.g. a Re-Distribution Layer—RDL metallizations) includes providing a capping stack onto the metallizations. The stack includes a pair of nickel layers having therebetween a layer of ductile material such as palladium or gold.

Claims

1. A method, comprising: manufacturing a semiconductor device including a metallization, the manufacturing including: providing a capping stack onto said metallization, wherein said capping stack includes a pair of nickel layers and a layer of ductile material positioned between the nickel layers.

2. The method of claim 1, wherein said ductile material is selected out of palladium and gold.

3. The method of claim 1, including providing said metallization as a copper metallization.

4. The method of claim 1, wherein providing said capping stack includes providing an outer layer of ductile material on an opposite side of the capping stack with respect to the metallization.

5. The method of claim 4, wherein providing the outer layer includes providing a palladium layer and an outermost layer including gold.

6. The method of claim 1, including providing a barrier layer underlying said metallization.

7. The method of claim 6, wherein: providing said barrier layer includes providing a titanium tungsten layer.

8. The method of claim 6, wherein providing the capping stack includes providing the capping stack adjoining said barrier layer to provide full coverage of said metallization.

9. The method of claim 1, wherein providing the capping stack includes providing said stack onto said metallization by e-less deposition.

10. A semiconductor device, comprising: a metallization, and a capping stack provided onto said metallization, wherein said stack includes a pair of nickel layers and a layer of ductile material between the nickel layers.

11. The semiconductor device of claim 10, wherein: said ductile material is selected out of palladium and gold.

12. The semiconductor device of claim 10, wherein: the stack includes an outer layer of ductile material on an opposite side of the capping layer with respect to the metallization.

13. The semiconductor device of claim 10, further comprising a barrier layer underlying said metallization.

14. The semiconductor device of claim 13, wherein said barrier layer includes a titanium tungsten layer.

15. The semiconductor device of claim 13, wherein the stack contacts the metallization and the barrier layer.

16. A semiconductor device, comprising: a metal layer; a first nickel layer in contact with the metal layer; a first layer of ductile material on the first nickel layer; and a second nickel layer on the layer of ductile material, the layer of ductile material being between the first and second nickel layers.

17. The semiconductor device of claim 16, wherein said ductile material is selected out of palladium and gold.

18. The semiconductor device of claim 16, further comprising a second layer of ductile material on the second nickel layer, the first and second nickel layers and the first layer of ductile material being between the second layer of ductile material and the metallization.

19. The semiconductor device of claim 16, further comprising a barrier layer underlying said metallization, wherein the stack contacts the metallization and the barrier layer.

20. The semiconductor device of claim 19, wherein said barrier layer includes a titanium tungsten layer.

Description

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

[0023] One or more embodiments will now be described, purely by way of example, with reference to the annexed figures, in which:

[0024] FIG. 1 is a top view of a stack arrangement which may incorporate one or more embodiments,

[0025] FIG. 2 is a reproduction of a SEM-microscope cross-section across a conventional (single) stack arrangement, and

[0026] FIG. 3 is a reproduction of a SEM microscope cross-section across a (double) stack arrangement according to embodiments.

[0027] It will be appreciated that for the sake of clarity of representation certain features of the figures (e.g., layer thicknesses) may not be drawn to scale.

DETAILED DESCRIPTION

[0028] In the ensuing description, one or more specific details are illustrated, aimed at providing an in-depth understanding of examples of embodiments in the present description. The embodiments may be obtained without one or more of the specific details, or with other methods, components, materials, etc. In other cases, known structures, materials, or operations are not illustrated or described in detail so that certain aspects of embodiments will not be obscured.

[0029] Reference to “an embodiment” or “one embodiment” in the framework of the present description is intended to indicate that a particular configuration, structure, or characteristic described in relation to the embodiment is comprised in at least one embodiment. Hence, phrases such as “in an embodiment” or “in one embodiment” that may be present in one or more points of the present description do not necessarily refer to one and the same embodiment. Moreover, particular conformations, structures, or characteristics may be combined in any adequate way in one or more embodiments.

[0030] The references used herein are provided merely for convenience and hence do not define the extent of protection or the scope of the embodiments.

[0031] U.S. Pat. No. 6,815,789, which is incorporated herein by reference in its entirety, discloses a semiconductor electronic device comprising a die of semiconductor material and a support, the die of semiconductor material including an integrated electronic circuit and a plurality of contact pads associated with the electronic circuit and connected electrically to the support by wire leads. Each contact pad comprises a lower layer of aluminum, copper, or alloys thereof, and an upper layer comprising at least one film of a metal and/or metallic alloy selected from a group comprising nickel, palladium, and alloys thereof, and being deposited by an electroless chemical process.

[0032] While not referring to RDL technology and, more to the point, not disclosing multiple layers of the type contemplated in one or more embodiments the disclosure of U.S. Pat. No. 6,815,789 provides some background information on such processes.

[0033] FIG. 1 is a top view of a portion of a semiconductor device S produced, e.g., by BCD-RDL technology including a stack arrangement which may incorporate one or more embodiments.

[0034] The semiconductor device S (e.g., an integrated circuit—IC) may be produced an RDL process including (in a manner known per se) a sequence of steps leading to the formation of RDL metallizations 10, e.g., Cu with an underlying barrier layer 12, e.g., titanium tungsten (TiW) or other barrier materials such as TiN/Ti/TiN and tantalum/tantalum nitride (Ta/TaN), as shown in FIG. 2.

[0035] A combined (stacked) outer surface coating or “capping” may then be provided on the outer surface of the metallization 10, the coating or capping having a thickness of, e.g., approximately 2 micron (2×10.sup.−6 m).

[0036] In a conventional arrangement as exemplified in FIG. 2, such a stacked capping (that is, a multi-layer) may include a Ni—Pd layer with, e.g., Ni at 14, Pd at 16. In other conventional arrangements, the stacked capping may include Ni—Pd—Au or Ni—Au multiple layers.

[0037] While successfully adopted in production, such a Ni/Pd layer may exhibit a certain amount of stress, e.g., if exposed to temperatures in the range of, e.g., 300°-400° C.

[0038] Specifically, it was observed that such a “single” Ni—Pd stack 14, 16 can induce too high a stress on a passivation layer during a thermal cycle.

[0039] One or more embodiments as exemplified in FIG. 3 may reduce the local stress due to, e.g., the Ni layer by resorting to “multiple” stacked arrangement, including, starting from the (e.g., Cu) metallization 10: [0040] a first Ni layer 141, [0041] a first (thin) Pd layer 161, [0042] a second Ni layer 142, [0043] a second Pd layer 162.

[0044] In one or more embodiments, a (thin, e.g., 0.1-0.5 micron 0.1-0.5×10.sup.−6 m) layer 161 of a ductile material, e.g., Pd may be provided between two Ni layers 141, 142.

[0045] In one or more embodiments, the presence of the layer 161 (Pd, or possibly, other ductile materials such as, e.g., Au) may lead to the Ni stress being “de-coupled” into two separate contributes, lower in magnitude due to the ductility of the layer 161.

[0046] Even without wishing to be bound to any specific theory in that respect, the ductility of an, e.g., Pd interlayer may be held to absorb the mechanical stress during a thermal cycle.

[0047] Also, one or more embodiments may benefit from Ni deposition on, e.g., Pd being practicable without any Ni surface chemical pre-treatment.

[0048] Additionally, no differences may be observed on wafers (dice) by optical inspection, see, e.g., the exemplary enlarged view of FIG. 1.

[0049] In one or more embodiments by resorting to an alternate deposition of, e.g., Ni/Pd/Ni/Pd (see, e.g., 141, 161, 142, 162) on, e.g., copper could reduce the stress effect due to the ductility of Pd interlayer that can absorb the mechanical stress during the thermal cycle.

[0050] One or more embodiments may facilitate meeting with request specifications for power packages used, e.g., in the automotive field.

[0051] As indicated, one or more embodiments may include stacked depositions other than Ni (layer 141)-Pd (layer 161)-Ni (layer 142)-Pd (layer 162).

[0052] Such alternative depositions may include, e.g., [0053] using another ductile material (e.g., Au) for the layer 161, and/or [0054] an outer layer (e.g., Au as schematically indicated in chain line as 18 in FIG. 3) at the outer surface of the stack.

[0055] Depositions such as: [0056] (Cu) Ni—Pd—Ni—Pd—Au [0057] (Cu) Ni—Au—Ni—Pd [0058] (Cu) Ni—Au—Ni—Pd—Au
are thus exemplary of such alternative deposition options.

[0059] The following may be exemplary thickness values for layers in a stack according to one or more embodiments: [0060] layer 141: 0.1-0.5 micron (0.1-0.5×10.sup.−6 m) [0061] layer 161: 0.1-0.5 micron (0.1-0.5×10.sup.−6 m [0062] layer 142: 0.5-1.5 micron (0.5-1.5)×10.sup.−6 m [0063] layer 162: 0.2-0.5 micron (0.2-0.5×10.sup.−6 m

[0064] One or more embodiments may thus provide a method of manufacturing semiconductor devices including at least one metallization (e.g., 10), the method including: [0065] providing (e.g., by e-less deposition) a capping stack (e.g., 141, 161, 142, 162) onto said metallization, wherein said stack includes at least one nickel layer, [0066] including in said stack a pair of nickel layers (e.g., 141, 142) having sandwiched therebetween a layer of ductile material (e.g., 161).

[0067] In one or more embodiments, said ductile material may be selected out of palladium (Pd) and gold (Au).

[0068] One or more embodiments may include providing said metallization as a copper metallization, optionally as a Re-Distribution Layer—RDL metallization.

[0069] One or more embodiments may include providing in said stack, opposed said metallization, at least one outer layer (e.g., 162, 18) of ductile material.

[0070] One or more embodiments may include providing in said stack, opposed said metallization, a first outer layer (e.g., 162) including palladium and an outermost layer (e.g., 18) including gold.

[0071] One or more embodiments may include providing a barrier layer (e.g., 12) underlying said at least one metallization.

[0072] In one or more embodiments, said barrier layer underlying said at least one metallization may include TiW.

[0073] One or more embodiments may include providing the capping stack adjoining said barrier layer (see, e.g., FIG. 3, bottom right) to provide full coverage of said at least one metallization.

[0074] One or more embodiments may provide a semiconductor device including: [0075] at least one metallization (e.g., 10), and [0076] a capping stack (e.g., 141, 161, 142, 162; 18) provided onto said metallization, wherein said stack includes a pair of nickel layers having a layer of ductile material therebetween.

[0077] In one or more embodiments: [0078] said ductile material (161) may be selected out of palladium and gold, and/or [0079] the stack may include, opposed said metallization, at least one outer layer of ductile material.

[0080] Without prejudice to the underlying principles, the details and embodiments may vary, even significantly, with respect to what has been disclosed merely by way of example, without departing from the extent of protection.

[0081] The various embodiments described above can be combined to provide further embodiments. These and other changes can be made to the embodiments in light of the above-detailed description. In general, in the following claims, the terms used should not be construed to limit the claims to the specific embodiments disclosed in the specification and the claims, but should be construed to include all possible embodiments along with the full scope of equivalents to which such claims are entitled. Accordingly, the claims are not limited by the disclosure.