The present invention relates to a thermoplastic resin composition and a molded article manufactured thereofrom. In accordance with the present invention, a thermoplastic resin composition providing higher chemical resistance with respect to a blowing agent while providing the same impact strength, gloss, and vacuum moldability as existing resin compositions when used to produce an inner case of a refrigerator, and a molded article manufactured from the same are provided.

The present disclosure relates to thermoplastic collagen elastomer compositions comprising collagen, at least one reactive thermoplastic elastomer, and at least one softener, as well as composite materials made from these compositions. Methods of making and using the thermoplastic collagen elastomer composite materials to produce engineered leather are also disclosed.

The present invention relates to a resin composition for forming an optical film, an optical film, and a polarizing plate, in which the resin composition for forming an optical film improves adhesion between an antiglare layer and a light-transmitting substrate film and enables the antiglare layer and the optical film to exhibit excellent optical properties such as appropriate haze, low gloss value, and excellent antiglare properties. The composition for forming an optical film is a resin composition for forming an optical film for forming an infiltration layer and an antiglare layer having surface irregularities on a light-transmitting substrate film, and comprises: a binder-forming compound including a polyfunctional (meth)acrylate-based compound having three or more functionalities, and a permeable compound having a hydrophilic functional group and a photo-curable functional group; two or more light-transmitting fine particles having a sub-micron (sub-μm) scale; and a permeable solvent capable of dissolving at least a part of the light-transmitting substrate film, wherein the binder-forming compound and the permeable solvent have a weight ratio of 1:0.04 or more.

A thermoplastic resin composition and a molded article including the same are disclosed in which the thermoplastic resin composition includes 100 parts by weight of a base resin including an acrylate-aromatic vinyl compound-vinyl cyanide compound graft copolymer; and 0.5 to 10 parts by weight of a matting agent having a refractive index of 1.46 to 1.53, and a molded article including the thermoplastic resin composition, wherein the thermoplastic resin composition satisfies Equations 1 and 2 below:

G≤20,  [Equation 1] wherein G denotes the gloss of a sheet having a size of 0.15 T as measured at 60° using a gloss meter,

Hz<Tt,  [Equation 2] wherein Hz and Tt denote the haze (%) and total light transmittance (%) of a sheet having a size of 0.15 T, respectively.

A transparent static-dissipative polycarbonate (PC) resin composition includes the following components: 70-95 parts by weight of PC resin, 5-30 parts by weight of antistatic agent masterbatch and 0.5-1.5 parts by weight of a transesterification inhibitor. The antistatic agent masterbatch includes the following components by mass percentage: 40-60% of an antistatic agent, 0.5-1.6% of a transesterification accelerator, 1-3% of an assistant cross-linkinger, and the balance of PC resin. A method for preparing the transparent static-dissipative PC resin composition includes the following steps: (I) preparing the components of the transparent static-dissipative PC resin composition according to the formulation, and mixing the components evenly to obtain a premix; and (II) adding the premix into a twin-screw extruder, melting, extruding, cooling and pelletizing, to obtain a target product.

A water- and oil-proofing composition which can provide an article with high utility oil resistance is provided. A water- and oil-proofing composition comprising a fluorinated polymer comprising units based on the following monomer (a) and units based on the following monomer (b), a fatty acid ester of polyglycerin and an aqueous medium: Monomer (a): a compound represented by CH.sub.2═CH—R.sup.f (wherein R.sup.f is a C.sub.1-8 perfluoroalkyl group). Monomer (b): a monomer copolymerizable with the monomer (a).

The present invention relates to a plastic film. More particularly, the present invention relates to a plastic film which exhibits high hardness, self-healing property and excellent processability. The plastic film of the present invention exhibits high hardness, self-healing property, scratch resistance, high transparency, durability, light resistance, light transmittance or the like, and thus can be applied to various fields.

A biodegradable composite comprising a polymeric matrix including but not limited to poly lactide (PLA), poly (butylene succinate) 20 (PBS), poly(butylene succinate adipate) (PBSA), including bio-based PBSA (BioPBSA), poly(butylene adipate-co-terephthalate) (PBAT), polycaprolactone (PCL), polyhydroxyalkanoate (PHA(s)), poly(3-hydroxy)butyrate (PHB), poly(3-hydroxy-butyrate-hydroxyvalerate) (PHBV), copolyester of the monomers 1.4-butanediol, adipic acid and terephthalic acid (Ecoflex™) and polypropylene carbonate (PPC), and biocarbon, a.k.a. biochar or pyrolyzed biomass as a sustainable filler. The biodegradable composite achieves high oxygen barrier with balanced water barrier. Also, a method of manufacturing the biodegradable composite and articles of manufacturing comprising the biodegradable composite. The articles of manufacturing have application in limiting gas permeation into a package and extending shelf life of a material.

The present invention relates to a weather-resistant thermoplastic resin, a thermoplastic resin composition containing the same, and a method of preparing the thermoplastic resin composition. More particular, the present invention relates to a thermoplastic resin including a) a hard core having a refractive index of 1.530 to 1.590; b) a crosslinked rubber layer that surrounds the hard core, has an average thickness of 30 to 80 nm, and is prepared by polymerizing an alkyl (meth)acrylate compound and a crosslinking agent; and c) a non-crosslinked hard shell that surrounds the crosslinked rubber layer and is prepared by polymerizing an aromatic vinyl compound and a vinyl cyanide compound, a thermoplastic resin composition including the thermoplastic resin, and a method of preparing the thermoplastic resin composition. In accordance to the present disclosure, a weather-resistant thermoplastic resin having superior rigidity and impact resistance, particularly excellent surface gloss and coloring properties, a thermoplastic resin composition containing the same, and a method of preparing the thermoplastic resin composition may be provided.

The present invention relates to an acrylic processing aid, a method for preparing the same, and a polyvinyl chloride resin composition comprising the same. More specifically, the present invention relates to an acrylic processing aid having a core-shell structure comprising the core and shell comprise a polymer prepared by copolymerizing a methyl methacrylate monomer and an alkyl acrylate monomer having 1 to 18 carbon atoms, and wherein the core comprises the polymer having a weight-average molecular weight ranging from 10,000,000 to 18,000,000 g/mol, a method for preparing the same, and a polyvinyl chloride resin composition comprising the same.