Solvents that are suitable for use with polyurethane-polyurea based rheology modifying agents of the type which, in the past, have generally been formulated as solids or viscous liquids. The present solvents enable the rheology modifying agents to be prepared and formulated in a liquid or solution form more suited to prepare coating formulations that include polyurethane-polyurea based rheology modifying agents. The present solvents are N-alkyl substituted caprolactams, including N-methyl caprolactam, N-ethyl caprolactam, N-butyl caprolactam, and mixtures thereof, which are aprotic, non-toxic, have good solvency for polar groups such as those found in polyurethanes and polyureas, are thermally stable, and have high boiling points and low vapor pressure.

Solvents that are suitable for use with polyurethane-polyurea based rheology modifying agents of the type which, in the past, have generally been formulated as solids or viscous liquids. The present solvents enable the rheology modifying agents to be prepared and formulated in a liquid or solution form more suited to prepare coating formulations that include polyurethane-polyurea based rheology modifying agents. The present solvents are N-alkyl substituted caprolactams, including N-methyl caprolactam, N-ethyl caprolactam, N-butyl caprolactam, and mixtures thereof, which are aprotic, non-toxic, have good solvency for polar groups such as those found in polyurethanes and polyureas, are thermally stable, and have high boiling points and low vapor pressure.

Provided is a liquid crystal aligning agent composition comprising a hindered amine-based light stabilizer and a polyamic acid polymer derived from a diamine, a method for preparing a liquid crystal alignment film using the same, and a liquid crystal alignment film and a liquid crystal display using the same.

A heat-resistant laminate including a substrate and an adhesive layer, the adhesive layer including a (meth)acrylic adhesive polymer and a self-crosslinking (meth)acrylic copolymer having an epoxy group and an epoxy group-reactive functional group, the adhesive layer having a sea-island structure including a sea including the (meth)acrylic adhesive polymer and an island including the self-crosslinking (meth)acrylic copolymer, and the laminate having a 180 degree peeling force of 0.9 N/cm or more after bonding to a SUS board and leaving at 120° C. for 30 minutes as measured at a temperature of 60° C. and a peeling speed of 300 mm/min.

A heat-resistant laminate including a substrate and an adhesive layer, the adhesive layer including a (meth)acrylic adhesive polymer and a self-crosslinking (meth)acrylic copolymer having an epoxy group and an epoxy group-reactive functional group, the adhesive layer having a sea-island structure including a sea including the (meth)acrylic adhesive polymer and an island including the self-crosslinking (meth)acrylic copolymer, and the laminate having a 180 degree peeling force of 0.9 N/cm or more after bonding to a SUS board and leaving at 120° C. for 30 minutes as measured at a temperature of 60° C. and a peeling speed of 300 mm/min.

A method of manufacture of a coated material is provided. A polyvinyl alcohol polymer, where the polyvinyl alcohol polymer has a degree of hydrolysis of 90% or greater and a melting point in the range of 180° C. to 225° C. is melted on a cellulosic substrate and extruded to form a molten polyvinyl alcohol polymeric film which is then applied directly to the surface of the substrate to form the coated material.

A method of manufacture of a coated material is provided. A polyvinyl alcohol polymer, where the polyvinyl alcohol polymer has a degree of hydrolysis of 90% or greater and a melting point in the range of 180° C. to 225° C. is melted on a cellulosic substrate and extruded to form a molten polyvinyl alcohol polymeric film which is then applied directly to the surface of the substrate to form the coated material.

The invention describes a method for manufacture of plasticized homopolymeric polyvinyl alcohol, the method including the steps of introducing a polyvinyl alcohol polymer or a blend thereof having a degree of hydrolysis in the range of 93 wt % to 98 wt % into a mixing reactor; adding a processing agent, a plasticizer and a reactive stabilizer to form a reaction mixture; wherein the plasticizer is selected from the group consisting of sugar alcohols, diols, triols, polyols and mixtures thereof; wherein the reactive stabilizer is selected from the group consisting of sodium stearate, potassium oleate, sodium benzoate, calcium stearate, stearic acid, dimethyl propionic acid, and mixtures thereof;-reacting the reaction mixture in a reaction zone to form plasticized polymer; and-allowing the plasticized polymer to pass from the reaction zone.

The present invention relates to a low friction polymerizable composition, a prepolymer thereof, and a friction component material prepared using the same, and the low friction polymerizable composition according to the present invention includes a curing agent and a filler together with a phthalonitrile compound, and thus has an excellent low friction property as well as high heat resistance and excellent processability.

The invention relates to polyamide moulding compounds comprising the following components: a) 50 to 95% by weight of a single amorphous copolyamide constructed from monomers a1) to a6), b) 5 to 50% by weight of at least one glass filler, c) 0 to 15% by weight of at least one monomeric lactam and/or polyamide 12, d) 0 to 19% by weight of additives, the sum of components a) to d) producing 100% by weight. Furthermore, the invention relates to moulded articles made of this polyamide moulding compound.