Provided are a synthetic wood and a preparation method thereof. More particularly, provided are a synthetic wood having excellent flexural property and impact strength by including a polyester resin having excellent compatibility with wood flour, and a preparation method thereof.

A composite wood product in accordance with a particular embodiment of the present technology includes a composite substrate and a sealant disposed within a surface portion of the substrate. The substrate includes wood and a binder. The sealant includes photoresponsive molecules present within the surface portion of the substrate at an average concentration greater than 1000 parts per million. In response to a 120-day exposure at 7 inches separation distance to a UV lamp with a UVA (315-400 nm) output of 13.6 W and a UVB (280-315 nm) output of 3.0 W, a CIELab b* value of the substrate decreases by a first amount, a CIELab b* value of the sealant increases by a second amount, and a CIELab b* value of the overall wood product decreases by an amount less than the first amount, increases by an amount less than the second amount, or is unchanged.

An additive formulation for lignocellulosic composites comprising a) a first aqueous emulsion comprising i) a component selected from the group consisting of petroleum wax, a triglyceride, and combinations thereof; and ii) a first anionic emulsifier; and b) a second aqueous emulsion comprising: i) a reaction product of I) a derivative of a polyol selected from the group consisting of saccharides, sugar alcohols, sugar acids, gluconic acids, and gluconic acid lactones; and II) a polyisocyanate; and ii) an emulsifier selected from the group consisting of a second anionic emulsifier, a non-ionic emulsifier, and mixtures thereof, is disclosed.

The invention relates to a method for treating a wood board. According to the invention, a composition containing a hydrophobic agent is provided onto the surface of the wood board and coating agent is provided over it to form a coating layer.

Disclosed is a method for the continuous impregnation of wood elements, such as wood chips. The method comprises the subsequent steps of subjecting the wood elements to vacuum, to contact with acetylation fluid, and to impregnation pressure. Preferably, the process is conducted in a plant having conveyors, such as transportation screws, in suitable positions between the zones in which the subsequent process steps are conducted. The impregnation method is used in connection with the acetylation of the wood elements, and preferably is followed by a continuous acetylation process conducted in an acetylation reaction zone downstream of the zone where the impregnation is conducted.

The disclosure relates to a method for the production of wood fiberboards such as MDF boards.

Fire impregnation substance is produced by polymerization of non-toxic components in such a way that pentaerythritol (5% to 90% of the mass) and ammonium polyphosphate (5% to 90% of the mass) are added to the water (30% to 96% of the mass) with temperature from 5 C. to 98 C. and the solution is mixed until it is pure. The mutual ratio of the components of pentaerythritol and ammonium polyphosphate can range from 1:18 to 18:1 During the production of the cellulose product or fibrous wood products such as chipboards or particle boards the wood chips or sawmill shavings are dipped in the impregnation substance before connecting and pressing, or the impregnation substance is added to adhesive or binder, respectively, which coats the chips or shavings before pressing into desired product. The cores of microintumescence inside the material, mainly on surfaces of the original chips, shavings or fibers subsequently produce gradually activate layers preventing the permeation of the fire's effects.

The present disclosure relates, according to some embodiments, to methods and systems for impregnating wood with a polymer solution and products thereof. In some embodiments, the present disclosure relates to a method of processing a wood piece to generate a wood product, the method comprising: (a) placing the wood piece into a reactor having a chamber pressure of a vacuum environment; (b) exposing the wood piece to a polymer solution; (c) performing an iterative process where each cycle of the iterative process comprises a pressurizing period during which the chamber pressure is increased to an increased chamber pressure and a stabilizing period during which the chamber pressure is monitored to measure a chamber pressure decrease, if any; (d) when the decrease of chamber pressure during the stabilizing period is less than or equal to the certain threshold change, normalizing the reactor chamber to a normalized pressure; and (e) setting the wood piece to generate the wood product. The present disclosure further relates to a wood product generated by a method of processing a wood piece.

The invention relates to a process for treating a lignocellulosic material, preferably wood, comprising the following steps: (1) soaking of the material with organic fluid in order to dissolve at least 40% and at most 85%, in weight %, of the lignin of the material; (2) washing with organic fluid so as to discharge the dissolved lignin; (3) filling with a filling compound; and (4) finishing, so as to obtain a composite formed of a three-dimensional network of transformed filling compound incorporated into a cellulose and lignin network. The invention also relates to a composite structure able to be obtained in this way, and to any part comprising at least one such structure.

A treated cellulosic material comprising a cellulosic material having a porous structure defining a plurality of pores, at least a portion of the pores containing a treating agent comprising a polymer comprising a sulfopolyester polymer. The present disclosure further describes a method for preparing a treated cellulosic material comprising (a) providing a cellulosic material; and (b) a first treatment protocol comprising impregnating the cellulosic material with an aqueous dispersion comprising a polymer, the polymer comprising a sulfopolyester polymer.