The present invention aims to provide a method for forming a multilayer coating film having good coating film smoothness. A method for forming a multilayer coating film, comprising a first aqueous coating composition application step of applying a first aqueous coating composition (A) to form an uncured first aqueous coating film; a second aqueous coating composition application step of applying a second aqueous coating composition (B) onto the uncured first aqueous coating film to form an uncured second aqueous coating film; a clear coating step of applying a clear coating composition (C) onto the uncured second aqueous coating film to form an uncured clear coating film; and a curing step of heat-curing at once these coating films to form a multilayer coating film, wherein the first aqueous coating composition (A) contains a water-dispersible polyurethane resin (a1) and a viscosity modifier (a2), and the second aqueous coating composition (B) contains water and an organic solvent as diluent components besides solid matters in a state of dilution to a coating viscosity.

The present invention aims to provide a method for forming a multilayer coating film having good coating film smoothness. A method for forming a multilayer coating film, comprising a first aqueous coating composition application step of applying a first aqueous coating composition (A) to form an uncured first aqueous coating film; a second aqueous coating composition application step of applying a second aqueous coating composition (B) onto the uncured first aqueous coating film to form an uncured second aqueous coating film; a clear coating step of applying a clear coating composition (C) onto the uncured second aqueous coating film to form an uncured clear coating film; and a curing step of heat-curing at once these coating films to form a multilayer coating film, wherein the first aqueous coating composition (A) contains a water-dispersible polyurethane resin (a1) and a viscosity modifier (a2), and the second aqueous coating composition (B) contains water and an organic solvent as diluent components besides solid matters in a state of dilution to a coating viscosity.

The present invention discloses a super-flexible high electrical and thermal conductivity flexible base material and a preparation method thereof, wherein the method comprises the steps of: S1. carbonizing and blackleading a polyimide thin film, doping nano-metal to the polyimide thin film, and performing ion implantation and ion exchange; S2. performing plasma irradiation modification treatment on a surface of the material obtained after the step S1 to form a heterogeneous surface layer; and S3. forming a metal conductor layer on the heterogeneous surface layer by physical vapor deposition (PVD) or chemical vapor deposition (CVD), so as to obtain the super-flexible high-ductility high electrical and thermal conductivity flexible base material. The method can obtain the C-C-FPC, C-C-COF or C-C-FCCL flexible circuit base material with super flexibility, high ductility, high electrical conductivity, high thermal conductivity and high frequency performance.

The invention is a dust control substances-solution (DCSS). The invention discloses the substances the DCSS is made of, how they are to be mixed and how the DCSS is to be applied. The DCSS is based on treated soft wood particles and substances that form a layer oved dust covered surfaces. The layer traps water that is applied to the surface, thus, maintaining the dust in aggregates and prevents its raising to the air.

Methods and devices for modifying a building panel are disclosed. A solution is applied to a surface of the building panel. The solution consists of light alcohols. A force is applied to a portion of the building panel substantially normal to a horizontal plane of the panel. The force causes a deformation of the portion of the building panel.

In at least one example, a composition for surface activation of an aerospace vehicle consists essentially of an organic solvent present in an amount from about 95 to about 99.5 volume percent, a transition metal alkoxide present in an amount from about 0.5 to about 5 volume percent, and a water content in an amount from about 0 to about 5 volume percent. In at least one example, a method of sealing a surface of an aerospace vehicle includes applying the composition to a surface of an aerospace vehicle. The composition applied to the surface is dried to form a transition metal oxide from the transition metal alkoxide. Excess of the transition metal oxide is removed from the surface. A sealant is applied over a remaining layer of the transition metal oxide on the surface.

The invention is generally related to a method for producing, in a consistent manner, contact lenses each having an intact durable coating thereon, wherein the coating is a hydrogel coating formed by covalently attached a hydrophilic polymeric material having azetidinium groups onto a base coating of a polyanionic polymer on a contact lens at a relatively low temperature (e.g., from about 40 C. to about 60 C.). The coating temperature for forming a durable hydrogel coating on top of the base coating of a contact lens can be significantly lowered by raising, in situ, the pH (to about 9.5 or higher) of a reactive coating solution which contains the hydrophilic polymeric material having azetidinium groups.

Provided is a coating composition containing: water; a water-soluble organic solvent that has a flash pint of at least 80 C. and not more than 200 C. and dissolves a fluorine resin; a fluorine resin; hydrophilic silica particles; and hydrophobic silica particles. The hydrophilic silica particles are preferably contained in the coating composition in an amount of at least 0.001 mass % and not more than 1 mass %. The average particle diameter of the hydrophilic silica particles is preferably at least 5 nm and not more than 30 nm.

The present invention belongs to the field of super-hydrophobic surface technology, and discloses a durable hydrophilic-super-hydrophobic bipolar self-cleaning composite film and a preparation method therefor. The preparation method is as follows: adding an epoxy silane coupling agent into an organic solvent; after stirring and mixing well, adding an amine curing agent and distilled water to the mixture; stirring and adding micron-sized solid particles and hydrophobic nano silicon dioxide particles; continuing stirring to obtain a hydrophilic layer solution; adding a hydrophobic modifier and a hydrophilic nano silicon dioxide particles into the solvent to obtain a hydrophobic layer solution; coating a pretreated substrate surface with the hydrophilic layer solution, and performing heating treatment at 60 C. to 80 C. for 10-50 min; then coating the surface with the hydrophobic layer solution, and performing heating treatment at 100 C. to 140 C. for 50-90 min to obtain the durable hydrophilic-super-hydrophobic bipolar self-cleaning composite film. The preparation method of the present invention is simple, and the super-hydrophobic surface of the obtained composite film has strong mechanical durability and a good industrial application prospect.

The present disclosure relates to a primer coating material composition, obtainable by combining at least two components (A) and (B) of a coating material system, which are different from one another and present separately from one another, with component (B) being nonaqueous and including at least one polyisocyanate having more than two free isocyanate groups, at least one organic solvent, and, further, at least one Si-containing compound which contains at least one hydrolyzable radical and at least one non-hydrolyzable organic radical, for at least partial application to at least one optionally pretreated surface of a plastics substrate, to a method for producing a corresponding coating on such a substrate, and to a method for at least partially coating at least one surface of a plastics substrate with a multicoat paint system.