An aluminum-based plated steel sheet according to an aspect of the present invention includes: a base material; an aluminum-based plating layer located above the base material; and an intermetallic compound layer that is located between the base material and the aluminum-based plating layer and contains an intermetallic compound of Al and Fe, in which the base material has a chemical component within a predetermined range, the aluminum-based plating layer contains, on average, 80 mass % or more and 97 mass % or less of Al, 3 mass % or more and 15 mass % or less of Si, 0 mass % or more and 5 mass % or less of Zn, 0 mass % or more and 5 mass % or less of Fe, 0 mass % or more and 3 mass % or less in total of one or more selected from the group consisting of Mg and Ca, and impurities so that a total amount thereof is 100 mass %, an average value of a thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less, a maximum value of the thickness of the intermetallic compound layer is 10 μm or more and 25 μm or less, and a standard deviation of the thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less.

The present disclosure relates to a method of manufacturing an aluminum alloy with excellent mechanical properties by controlling a heat treatment step and a cooling step in a process of manufacturing the aluminum alloy. In detail, there is provided a method of manufacturing an aluminum alloy, including: a heating step of heating an aluminum alloy made of an aluminum alloy composite up to 500 to 560° C.; a solution treatment step of maintaining the heated aluminum alloy for 5 to 7 hours; a cooling step of cooling the solution-treated aluminum alloy for 15 seconds to 1 minute; and an aging step of age-hardening the cooled aluminum alloy for 2.5 to 4 hours at 140 to 180° C.

According to the method of manufacturing an aluminum alloy of the present disclosure and an aluminum alloy manufactured by the method, elongation is secured by reducing the solution treatment time and strength is increased by remaining heat by relatively increasing the drop speed of a pallet between a solution treatment furnace and a cooling container, the distance between the furnace and the container, and the cooling time, thereby being able to provide an aluminum alloy having excellent mechanical properties.

Fe-Al-based plated hot-stamped member exhibiting excellent formed part corrosion resistance and post-coating corrosion resistance and manufacturing method. The hot-stamping member includes Fe-Al-based plated layer on one or both surfaces of a base material, the base material has a predetermined steel component, Fe-Al-based plated layer has a thickness of 10 μm or more and 60 μm or less, formed by A, B, C and D layers sequentially from a surface toward the base material, and each of the four layers is a Fe-Al-based intermetallic compound containing Al, Fe, Si, Mn and Cr for predetermined contents with the balance made up of impurities, the D layer further contains Kirkendall voids each of which cross-sectional area is 3 μm.sup.2-30 μm.sup.2 for 10 pieces/6000 μm.sup.2 or more and 40 pieces/6000 μm.sup.2 or less.

Fe-Al-based plated hot-stamped member exhibiting excellent formed part corrosion resistance and post-coating corrosion resistance and manufacturing method. The hot-stamping member includes Fe-Al-based plated layer on one or both surfaces of a base material, the base material has a predetermined steel component, Fe-Al-based plated layer has a thickness of 10 μm or more and 60 μm or less, formed by A, B, C and D layers sequentially from a surface toward the base material, and each of the four layers is a Fe-Al-based intermetallic compound containing Al, Fe, Si, Mn and Cr for predetermined contents with the balance made up of impurities, the D layer further contains Kirkendall voids each of which cross-sectional area is 3 μm.sup.2-30 μm.sup.2 for 10 pieces/6000 μm.sup.2 or more and 40 pieces/6000 μm.sup.2 or less.

Provided is a highly corrosion-resistant plated steel sheet having plating adhesion and resistance to liquid metal embrittlement. A highly corrosion-resistant plated steel sheet comprises a base steel sheet and a plated layer, which sequentially comprises an Fe—Al alloy layer and an MgZn.sub.2 layer from an interface with the base steel sheet.

Provided is a highly corrosion-resistant plated steel sheet having plating adhesion and resistance to liquid metal embrittlement. A highly corrosion-resistant plated steel sheet comprises a base steel sheet and a plated layer, which sequentially comprises an Fe—Al alloy layer and an MgZn.sub.2 layer from an interface with the base steel sheet.

The invention relates to a process for laser welding monolithic semi-finished products made of aluminium alloy without filler wire, known to a person skilled in the art under the name “Remote Laser Welding” comprising the following steps:—supplying at least two semi-finished products made of aluminium alloy, at least one of which is a laminated plate with the composition (% by weight): Si: 2.5-14; Fe: 0.05-0.8; Cu: 0.25-1.0; Mg: 0.05-0.8; Mn: ≤0.70; Cr: ≤0.35; Ti: 0.02-0.30; Sr up to 500 ppm; Na up to 200 ppm; Sb up to 0.15%, unavoidable impurities <0.05 each and <0.15 in total, remainder aluminium,—laser welding the semi-finished products made of aluminium alloy without filler wire, which process is known to a person skilled in the art under the name “Remote Laser Welding”. The invention also includes a structural, body-in-white, skin or opening component of a motor vehicle obtained by a process according to the invention.

The present invention is applicable to the technical field of material processing and provides an aluminum alloy and a preparation method thereof. The preparation method of the aluminum alloy includes: weighing raw material components according to a preset weight ratio; melting the weighed raw materials, sequentially performing refinement, standing, slag removal, degassing and filtering, and then performing horizontal casting to obtain an aluminum alloy ingot; homogenizing the ingot; heating the ingot to 440-500° C., and placing the ingot in an extruder with an extrusion ratio of 30-100 for extrusion treatment; annealing the extruded blank; heating the annealed blank to 440-480° C. for deformation treatment, and controlling the deformation amount in the thickness direction to be 12%-28%; carrying out solution treatment on the deformed blank; and subjecting the blank after the solution treatment to artificial aging treatment.

The present invention relates to plates with a thickness of between 8 and 50 mm and made from aluminum alloy with a composition, as % by weight, Si: 0.7-1.3; Mg: 0.6-1.2; Mn: 0.65-1.0; Fe: 0.05-0.35; at least one element selected from Cr: 0.1-0.3 and Zr: 0.06-0.15; Ti<0.15; Cu<0.4; Zn<0.1; other elements <0.05 each and <0.15 in total, the remainder aluminum, and the method for manufacturing same. The plates according to the invention are particularly useful as precision plates, in particular for producing elements of machines, for example assembly or inspection equipment. The plates according to the invention have improved dimensional stability in particular during the machining steps, while having sufficient static mechanical properties, and excellent suitability for anodizing.

The present invention relates to plates with a thickness of between 8 and 50 mm and made from aluminum alloy with a composition, as % by weight, Si: 0.7-1.3; Mg: 0.6-1.2; Mn: 0.65-1.0; Fe: 0.05-0.35; at least one element selected from Cr: 0.1-0.3 and Zr: 0.06-0.15; Ti<0.15; Cu<0.4; Zn<0.1; other elements <0.05 each and <0.15 in total, the remainder aluminum, and the method for manufacturing same. The plates according to the invention are particularly useful as precision plates, in particular for producing elements of machines, for example assembly or inspection equipment. The plates according to the invention have improved dimensional stability in particular during the machining steps, while having sufficient static mechanical properties, and excellent suitability for anodizing.