A ductile iron composition including, by weight: about 3.1% to about 3.6% C; about 3.5% to about 4.0% Si; about 0.035% to about 0.050% Mg; about 0.001% to about 0.004% Ce; up to about 0.005% Sb; about 0.008% to about 0.016% S; up to about 0.04% P; up to about 0.3% Mn; and balance iron and incidental impurities;
The ductile iron composition includes a ratio of Sb/Ce greater than or equal to about 1.25, has a ferritic microstructure and graphite nodules, and greater than about 65% of the graphite nodules having a highly spherical geometry. A method and apparatus for forming a ductile iron composition are also disclosed.

A ductile iron composition including, by weight: about 3.1% to about 3.6% C; about 3.5% to about 4.0% Si; about 0.035% to about 0.050% Mg; about 0.001% to about 0.004% Ce; up to about 0.005% Sb; about 0.008% to about 0.016% S; up to about 0.04% P; up to about 0.3% Mn; and balance iron and incidental impurities;
The ductile iron composition includes a ratio of Sb/Ce greater than or equal to about 1.25, has a ferritic microstructure and graphite nodules, and greater than about 65% of the graphite nodules having a highly spherical geometry. A method and apparatus for forming a ductile iron composition are also disclosed.

Disclosed herein are embodiments of iron-based corrosion resistant hardfacing alloys. The alloys can be designed through the use of different compositional, thermodynamic, microstructural, and performance criteria. In some embodiments, chromium content in the alloy can be increased while avoiding the formation of different hard chromium carbides, thereby increasing the corrosion resistance of the alloy.

Disclosed herein are embodiments of iron-based corrosion resistant hardfacing alloys. The alloys can be designed through the use of different compositional, thermodynamic, microstructural, and performance criteria. In some embodiments, chromium content in the alloy can be increased while avoiding the formation of different hard chromium carbides, thereby increasing the corrosion resistance of the alloy.

Disclosed herein are embodiments of hardfacing/hardbanding materials, alloys, or powder compositions that can have low chromium content or be chromium free. In some embodiments, the alloys can contain transition metal borides and borocarbides with a particular metallic component weight percentage. The disclosed alloys can have high hardness and ASTM G65 performance, making them advantageous for hardfacing/hardbanding applications.

Disclosed herein are embodiments of hardfacing/hardbanding materials, alloys, or powder compositions that can have low chromium content or be chromium free. In some embodiments, the alloys can contain transition metal borides and borocarbides with a particular metallic component weight percentage. The disclosed alloys can have high hardness and ASTM G65 performance, making them advantageous for hardfacing/hardbanding applications.

A ferrosilicon inoculant for gray cast iron containing between 0.1 to 10% by weight strontium, less than 0.35% by weight calcium, 1.5 to 10% by weight aluminum and 0.1 to 15% zirconium, The inoculant, method for producing the inoculant, method for inoculating the melt and a gray cast iron inoculated with the inoculant are covered.

A ferrosilicon inoculant for gray cast iron containing between 0.1 to 10% by weight strontium, less than 0.35% by weight calcium, 1.5 to 10% by weight aluminum and 0.1 to 15% zirconium, The inoculant, method for producing the inoculant, method for inoculating the melt and a gray cast iron inoculated with the inoculant are covered.

A spheroidal graphite cast iron comprising: C: 3.3 to 4.0 mass %, Si: 2.1 to 2.7 mass %, Mn: 0.20 to 0.50 mass %, S: 0.005 to 0.030 mass %, Cu: 0.20 to 0.50 mass %, Mg: 0.03 to 0.06 mass % and the balance: Fe and inevitable impurities, wherein a tensile strength is 550 MPa or more, and an elongation is 12% or more.

A spheroidal graphite cast iron comprising: C: 3.3 to 4.0 mass %, Si: 2.1 to 2.7 mass %, Mn: 0.20 to 0.50 mass %, S: 0.005 to 0.030 mass %, Cu: 0.20 to 0.50 mass %, Mg: 0.03 to 0.06 mass % and the balance: Fe and inevitable impurities, wherein a tensile strength is 550 MPa or more, and an elongation is 12% or more.