A dental gypsum slurry includes water and a dental gypsum powder containing hemihydrate gypsum and a polycarboxylic acid salt-based water-reducing agent, wherein a powder-water ratio of the water to the dental gypsum powder is 0.24 to 0.50, and when the water and the dental gypsum powder being mixed are poured up to a height of 50 mm in a cylindrical mold having an inner diameter of 35 mm, which is vertically placed on a flat surface, and then, the cylindrical mold is pulled upward at 10 mm/s at 30 seconds after start of mixing so that a mixture spreads planarly, the diameter of the mixture is 141.4 mm or more.

A dental gypsum slurry includes water and a dental gypsum powder containing hemihydrate gypsum and a polycarboxylic acid salt-based water-reducing agent, wherein a powder-water ratio of the water to the dental gypsum powder is 0.24 to 0.50, and when the water and the dental gypsum powder being mixed are poured up to a height of 50 mm in a cylindrical mold having an inner diameter of 35 mm, which is vertically placed on a flat surface, and then, the cylindrical mold is pulled upward at 10 mm/s at 30 seconds after start of mixing so that a mixture spreads planarly, the diameter of the mixture is 141.4 mm or more.

It is an object of the present invention to provide fine fibrous cellulose capable of enhancing transparency and suppressing coloring, when the fine fibrous cellulose are processed into a dispersed solution or a sheet. The present invention relates to fine fibrous cellulose, in which the amount of substituents introduced is less than 0.5 mmol/g and the fiber width is 1 to 10 nm. Moreover, the present invention relates to a dispersed solution and a sheet, each of which comprises fine fibrous cellulose. Furthermore, the present invention relates to a method for producing fine fibrous cellulose, comprising: (A) removing at least a part of substituents from fine fibrous cellulose with a fiber width of 1000 nm or less having the substituents, and (B) performing a uniform dispersion treatment on the resulting fine fibrous cellulose after completion of the (A).

Disclosed are endodontic filling materials and methods. A method for filling a dental root canal may include providing a hydrosetting filling material and inserting the hydrosetting filling material into the dental root canal, the material setting in the root canal to form a biocompatible filling. The hydrosetting filling material comprises a hydrogel former and a filler. The hydrogel former is at least one of a reactive organic hydrogel formers, an inorganic hydrogel formers, and a non-reactive organic hydrogel formers, and the filler is at least one of a self-hardening and a non-hardening filler. Plural filling material precursor compositions that collectively contain hydrogel formers and fillers may be provided.

An embodiment according to the present invention provides a dental gypsum powder including a hemihydrate gypsum and a water-reducing agent, wherein the mass ratio of the water-reducing agent to the hemihydrate gypsum is 0.1 to 1%, the content of particles having a particle diameter of 10 μm or less is 15 to 35 volume %, the content of particles having a particle diameter of 20 μm or less is 40 to 55 volume %, and the content of particles having a particle diameter of 30 μm or less is 55 to 75 volume %.

An embodiment according to the present invention provides a dental gypsum powder including a hemihydrate gypsum and a water-reducing agent, wherein the mass ratio of the water-reducing agent to the hemihydrate gypsum is 0.1 to 1%, the content of particles having a particle diameter of 10 μm or less is 15 to 35 volume %, the content of particles having a particle diameter of 20 μm or less is 40 to 55 volume %, and the content of particles having a particle diameter of 30 μm or less is 55 to 75 volume %.

The present invention provides a dental hydraulic temporary sealing material composition on which a protection of tooth substance, such as tooth substance strengthening and control of secondary dental caries, can be expected by sustained-releasing various ions including a fluoride ion, while having a high initial setting ability. More specifically, the present invention provides a dental hydraulic temporary sealing material composition comprising 65.0% to 85.0% by mass of component (1): a hydraulic inorganic powder; 10.0% to 25.0% by mass of component (2): an organic solvent; 3.0% to 15.0% by mass of component (3): a resin; and 0.01% to 10.0% by mass of component (4): an ion sustained-release glass.

The present invention provides a dental hydraulic temporary sealing material composition on which a protection of tooth substance, such as tooth substance strengthening and control of secondary dental caries, can be expected by sustained-releasing various ions including a fluoride ion, while having a high initial setting ability. More specifically, the present invention provides a dental hydraulic temporary sealing material composition comprising 65.0% to 85.0% by mass of component (1): a hydraulic inorganic powder; 10.0% to 25.0% by mass of component (2): an organic solvent; 3.0% to 15.0% by mass of component (3): a resin; and 0.01% to 10.0% by mass of component (4): an ion sustained-release glass.

A dental gypsum slurry includes water and a dental gypsum powder containing hemihydrate gypsum and a polycarboxylic acid salt-based water-reducing agent, wherein a powder-water ratio of the water to the dental gypsum powder is 0.24 to 0.50, and when the water and the dental gypsum powder being mixed are poured up to a height of 50 mm in a cylindrical mold having an inner diameter of 35 mm, which is vertically placed on a flat surface, and then, the cylindrical mold is pulled upward at 10 mm/s at 30 seconds after start of mixing so that a mixture spreads planarly, the diameter of the mixture is 141.4 mm or more.

An embodiment according to the present invention provides a dental gypsum powder including a hemihydrate gypsum and a water-reducing agent, wherein the mass ratio of the water-reducing agent to the hemihydrate gypsum is 0.1 to 1%, the content of particles having a particle diameter of 10 m or less is 15 to 35 volume %, the content of particles having a particle diameter of 20 m or less is 40 to 55 volume %, and the content of particles having a particle diameter of 30 m or less is 55 to 75 volume %.