Provided is a method for producing a composite alloy for use in an electrode for an alkaline storage battery, including a powder preparation step of preparing a hydrogen storage alloy powder containing Ti and Cr and having a BCC structure, an etching step of applying an acid to the hydrogen storage alloy powder prepared in the powder preparation step, a Pd film forming step of coating the surface of the hydrogen storage alloy powder subjected to the etching step with Pd using a substitution plating method, and a heat treatment step of heating the hydrogen storage alloy powder having a Pd film formed, at said heating being a temperature of 500° C. or less, wherein in the Pd coating forming step, the hydrogen storage alloy powder is coated with Pd under the condition that the Pd element weight ratio of the composite alloy to be produced is 0.47% or more.

Provided is a method for producing a composite alloy for use in an electrode for an alkaline storage battery, including a powder preparation step of preparing a hydrogen storage alloy powder containing Ti and Cr and having a BCC structure, an etching step of applying an acid to the hydrogen storage alloy powder prepared in the powder preparation step, a Pd film forming step of coating the surface of the hydrogen storage alloy powder subjected to the etching step with Pd using a substitution plating method, and a heat treatment step of heating the hydrogen storage alloy powder having a Pd film formed, at said heating being a temperature of 500° C. or less, wherein in the Pd coating forming step, the hydrogen storage alloy powder is coated with Pd under the condition that the Pd element weight ratio of the composite alloy to be produced is 0.47% or more.

The present invention can provide light-colored magnetic particles having a zirconium oxide coating layer formed on a magnetic core, and having a silver coating layer formed on the zirconium oxide coating layer, and a part of the surface of the zirconium oxide coating layer is exposed to the outside, but chemical resistance is excellent, and thus the magnetic particles hardly cause a change of magnetic characteristics so as to be suitable for security elements.

A copper paste for joining contains metal particles and a dispersion medium, in which the copper paste for joining contains copper particles as the metal particles, and the copper paste for joining contains dihydroterpineol as the dispersion medium. A method for manufacturing a joined body is a method for manufacturing a joined body which includes a first member, a second member, and a joining portion that joins the first member and the second member, the method including: a first step of printing the above-described copper paste for joining to at least one joining surface of the first member and the second member to prepare a laminate having a laminate structure in which the first member, the copper paste for joining, and the second member are laminated in this order; and a second step of sintering the copper paste for joining of the laminate.

The present invention pertains to a process for preparing particles of rare earth sulfide comprising the steps of:—preparing a reaction mixture comprising at least one compound comprising at least one rare earth element (A) and at least one alkali metal sulfide (B),—submitting said reaction mixture to a mechanical stress so as to cause a chemical reaction that produces the particles of rare earth sulfide.

The present invention pertains to a process for preparing particles of rare earth sulfide comprising the steps of:—preparing a reaction mixture comprising at least one compound comprising at least one rare earth element (A) and at least one alkali metal sulfide (B),—submitting said reaction mixture to a mechanical stress so as to cause a chemical reaction that produces the particles of rare earth sulfide.

Disclosed is a conductive ink composition and a manufacturing method thereof. The composition includes about 50 to about 99 wt % copper nanoparticles and about 1 to about 50 wt % tin. Copper nanoparticles are atomized and suspended in a tin bath, wherein the copper nanoparticles are evenly dispersed within the bath through sonification. The composition is cooled, extracted, and formed into a filament for use as a conductive ink. The ink has a resistivity of about 46.2×E-9 Ω*m to about 742.5×E-9 Ω*m. Once in filament form, the tin-copper mix will be viable for material extrusion, thus allowing for a lower cost, electrically conductive traces to be used in additive manufacturing.

Embodiments of the present invention relate to methods for preparing high optical density solutions of nanoparticle, such as nanoplates, silver nanoplates or silver platelet nanoparticles, and to the solutions and substrates prepared by the methods. The process can include the addition of stabilizing agents (e.g., chemical or biological agents bound or otherwise linked to the nanoparticle surface) that stabilize the nanoparticle before, during, and/or after concentration, thereby allowing for the production of a stable, high optical density solution of silver nanoplates. The process can also include increasing the concentration of silver nanoplates within the solution, and thus increasing the solution optical density.

A method for synthesis of nanoparticles are described. The method includes dispersing metal oxide powder in a mixture of a base liquid and a surfactant to form a primary mixture, grinding the primary mixture using a grinding media by periodically adding a surfactant solution to form a slurry, extracting a predetermined amount of sample from the slurry at periodic time intervals to obtain a testing solution to assess particle size of in the slurry using a particle size analyzer; and systematically adding the surfactant solution and the grinding media to the slurry based on the assessed particle size in the testing solution until a mean particle size of the nanoparticles is achieved.

A ceramic reinforced metal composite (CRMC) comprising a composition composite as an interpenetrating network of at least two interconnected composites is described. The interpenetrating networks comprise a ceramic matrix composite (CMC) and a metal matrix composite (MMC). The composition composite is particularly useful as an electrically conductive pathway extending through the ceramic body of a hermetically sealed component, for example, a feedthrough in an active implantable medical device (AIMD).