This disclosure relates to a high cBN content polycrystalline cubic boron nitride, PCBN, material. The binder matrix material comprises 19 to 50 wt. % chromium, or a compound thereof.

This disclosure relates to a high cBN content polycrystalline cubic boron nitride, PCBN, material. The binder matrix material comprises 19 to 50 wt. % chromium, or a compound thereof.

The invention concerns the field of hardmetal materials and relates to hardmetals such as those which can, for example, be used as cutting material for tools. The object of the present invention is to specify hardmetals which include a novel concept for the structural composition of the hardmetals. The object is attained with hardmetals which are at least made up of hard phases in particle form and metal binder arranged therebetween, wherein a high-entropy hard phase (HEH) is composed of at least four metals (Me) of the 4th and/or 5th and/or 6th subgroup of the PTE in the form of a solid solution of carbides, nitrides, carbonitrides, oxycarbides, and/or oxycarbonitrides of the metals, wherein the respective amounts of the metals in the HEH are essentially equal.

Disclosed are an R-T-B-based permanent magnet material, a preparation method therefor and the use thereof. The R-T-B-based permanent magnet material comprises R, B, M, Fe, Co, X and inevitable impurities, wherein: (1) R is a rare earth element, and the R includes at least Nd and RH, M being one or more of Ti, Zr and Nb, and X including Cu, “Al and/or Ga”; and (2) in percentage by weight, R: 30.5-32.0 wt%, B: 0.95-0.99 wt%, M: 0.3-0.6 wt%, X: 0.8-1.8 wt%, and Cu: 0.35-0.50 wt%, and the balance is Fe, Co and inevitable impurities. According to the present invention, under the condition of 0.3-0.6 wt% of a high melting point metal, a permanent magnet material with an excellent magnet performance and a good squareness is obtained.

Disclosed are an R-T-B-based permanent magnet material, a preparation method therefor and the use thereof. The R-T-B-based permanent magnet material comprises R, B, M, Fe, Co, X and inevitable impurities, wherein: (1) R is a rare earth element, and the R includes at least Nd and RH, M being one or more of Ti, Zr and Nb, and X including Cu, “Al and/or Ga”; and (2) in percentage by weight, R: 30.5-32.0 wt%, B: 0.95-0.99 wt%, M: 0.3-0.6 wt%, X: 0.8-1.8 wt%, and Cu: 0.35-0.50 wt%, and the balance is Fe, Co and inevitable impurities. According to the present invention, under the condition of 0.3-0.6 wt% of a high melting point metal, a permanent magnet material with an excellent magnet performance and a good squareness is obtained.

Provided is a method of producing a target material with reduced particle generation during sputtering, which is a method of producing a sputtering target material whose material is an alloy M, including a sintering step of sintering a mixed powder obtained by mixing a first powder and a second powder. A material of the first powder is an alloy M1 in which the proportion of a B content is from 40 at. % to 60 at. %. A material of the second powder is an alloy M2 in which the proportion of a B content is from 20 at. % to 35 at. %. The proportion of a B content in the mixed powder is from 33 at. % to 50 at. %. A metallographic structure including a (CoFe).sub.2B phase and a (CoFe)B phase is formed in the sintering step. A boundary length per unit area Y (1/μm), which is obtained by measuring a boundary length between the (CoFe).sub.2B phase and the (CoFe)B phase using a scanning electron microscope, and a proportion X (at. %) of a B content of the alloy M satisfy the expression

Y<−0.0015×(X−42.5).sup.2+0.15.

Provided is a method of producing a target material with reduced particle generation during sputtering, which is a method of producing a sputtering target material whose material is an alloy M, including a sintering step of sintering a mixed powder obtained by mixing a first powder and a second powder. A material of the first powder is an alloy M1 in which the proportion of a B content is from 40 at. % to 60 at. %. A material of the second powder is an alloy M2 in which the proportion of a B content is from 20 at. % to 35 at. %. The proportion of a B content in the mixed powder is from 33 at. % to 50 at. %. A metallographic structure including a (CoFe).sub.2B phase and a (CoFe)B phase is formed in the sintering step. A boundary length per unit area Y (1/μm), which is obtained by measuring a boundary length between the (CoFe).sub.2B phase and the (CoFe)B phase using a scanning electron microscope, and a proportion X (at. %) of a B content of the alloy M satisfy the expression

Y<−0.0015×(X−42.5).sup.2+0.15.

The present disclosure discloses a preparation method of a powder metallurgy (PM) superalloy with high strength and plasticity. Under the multi-field coupling action of a thermal field and a force field, the PM superalloy is obtained in a high-temperature graphite mold by using the method of conducting heat preservation and oscillating-pressure sintering in two steps. Under the action of a circulating pressure, rearrangement of powders and discharge of pores are promoted, and therefore, the PM superalloy is sintered and formed. The present disclosure further discloses a PM superalloy prepared by using the method above. The PM superalloy has the characteristics of low grade of prior particle boundary defects, uniform grain refinement and high density. The sintered PM superalloy obtained in the present disclosure has a yield strength of 955 MPa, a tensile strength of 1,437 MPa and an elongation of 31.9%, and has high strength and plasticity.

The present disclosure discloses a preparation method of a powder metallurgy (PM) superalloy with high strength and plasticity. Under the multi-field coupling action of a thermal field and a force field, the PM superalloy is obtained in a high-temperature graphite mold by using the method of conducting heat preservation and oscillating-pressure sintering in two steps. Under the action of a circulating pressure, rearrangement of powders and discharge of pores are promoted, and therefore, the PM superalloy is sintered and formed. The present disclosure further discloses a PM superalloy prepared by using the method above. The PM superalloy has the characteristics of low grade of prior particle boundary defects, uniform grain refinement and high density. The sintered PM superalloy obtained in the present disclosure has a yield strength of 955 MPa, a tensile strength of 1,437 MPa and an elongation of 31.9%, and has high strength and plasticity.

Disclosed are an outer ring for an oil pump having an increased number and size of open pores in a surface of a molded article and a method for manufacturing the outer ring.