Embodiments relate to polycrystalline diamond compacts (“PDCs”), methods of fabricating PDCs, and applications for such PDCs. In an embodiment, a method includes providing an at least partially leached polycrystalline diamond (“PCD”) body. A residual amount of acid may remain in and/or on the at least partially leached PCD body. The method further includes removing and/or neutralizing at least some of the residual amount of acid from the at least partially leached PCD body and/or a substrate to which the at least partially leached PCD body is attached.

Embodiments relate to polycrystalline diamond compacts (“PDCs”), methods of fabricating PDCs, and applications for such PDCs. In an embodiment, a method includes providing an at least partially leached polycrystalline diamond (“PCD”) body. A residual amount of acid may remain in and/or on the at least partially leached PCD body. The method further includes removing and/or neutralizing at least some of the residual amount of acid from the at least partially leached PCD body and/or a substrate to which the at least partially leached PCD body is attached.

An abrasive article includes a body having a bond material extending throughout the body and abrasive particles contained in the bond material. The bond material can include aluminum oxide (Al.sub.2O.sub.3) and lithium oxide (Li.sub.2O). In an embodiment, the bond material can include a ratio (Al.sub.2O.sub.3/Li.sub.2O) of a content of aluminum oxide (Al.sub.2O.sub.3) relative to a content of lithium oxide (Li.sub.2O), based on weight percent, of greater than 11.5 and at most 20. In another embodiment, the abrasive article can have a versatility factor of greater than 1.90.

A free standing PCD body comprises a PCD material formed of combination of intergrown diamond grains forming a diamond network and an interpenetrating metallic network, the PCD body not being attached to a second body or substrate formed of a different material. The diamond network is formed of diamond grains having a plurality of grain sizes, and comprises a grain size distribution having an average diamond grain size, wherein the largest component of the diamond grain size distribution is no greater than three times the average diamond grain size. The PCD material forming the free standing PCD body is homogeneous, such that the PCD body is spatially constant and invariant with respect to diamond network to metallic network volume ratio. The homogeneity is measured at a scale greater than ten times the average grain size and spans the dimension of the PCD body. The PCD material is also macroscopically residual stress free at said scale.

A free standing PCD body comprises a PCD material formed of combination of intergrown diamond grains forming a diamond network and an interpenetrating metallic network, the PCD body not being attached to a second body or substrate formed of a different material. The diamond network is formed of diamond grains having a plurality of grain sizes, and comprises a grain size distribution having an average diamond grain size, wherein the largest component of the diamond grain size distribution is no greater than three times the average diamond grain size. The PCD material forming the free standing PCD body is homogeneous, such that the PCD body is spatially constant and invariant with respect to diamond network to metallic network volume ratio. The homogeneity is measured at a scale greater than ten times the average grain size and spans the dimension of the PCD body. The PCD material is also macroscopically residual stress free at said scale.

Embodiments relate to polycrystalline diamond compacts (“PDCs”) including a polycrystalline diamond (“PCD”) table in which a metal-solvent catalyst is alloyed with at least one alloying element to improve thermal stability of the PCD table. In an embodiment, a PDC includes a substrate and a PCD table bonded to the substrate. The PCD table includes diamond grains defining interstitial regions. The PCD table includes an alloy comprising at least one Group VIII metal and at least one metallic alloying element that lowers a temperature at which melting of the at least one Group VIII metal begins. The alloy includes one or more solid solution phases comprising the at least one Group VIII metal and the at least one metallic alloying element and one or more intermediate compounds comprising the at least one Group VIII metal and the at least one metallic alloying element.

Embodiments relate to polycrystalline diamond compacts (“PDCs”) including a polycrystalline diamond (“PCD”) table in which a metal-solvent catalyst is alloyed with at least one alloying element to improve thermal stability of the PCD table. In an embodiment, a PDC includes a substrate and a PCD table bonded to the substrate. The PCD table includes diamond grains defining interstitial regions. The PCD table includes an alloy comprising at least one Group VIII metal and at least one metallic alloying element that lowers a temperature at which melting of the at least one Group VIII metal begins. The alloy includes one or more solid solution phases comprising the at least one Group VIII metal and the at least one metallic alloying element and one or more intermediate compounds comprising the at least one Group VIII metal and the at least one metallic alloying element.

Polycrystalline diamond compacts, polycrystalline diamond blanks, polycrystalline diamond cutters, and tools incorporating same for cutting, milling, grinding, drilling and other abrasive operations, particularly in metal cutting applications, include a diamond table having a gradient in iron content that increases as distance into the volume of the diamond table increases. The iron gradient increases resistance to wear, such as in interrupted milling tests. The disclosure further relates to methods of manufacturing polycrystalline diamond compacts having a gradient in iron concentration in the diamond table, blanks and cutters including polycrystalline diamond compacts, cutting tools incorporating such compacts, blanks and cutters, and methods of cutting, milling, grinding and drilling, particularly metal machining, using such compacts, blanks, cutters, cutting tools and drill bits.

Polycrystalline diamond compacts, polycrystalline diamond blanks, polycrystalline diamond cutters, and tools incorporating same for cutting, milling, grinding, drilling and other abrasive operations, particularly in metal cutting applications, include a diamond table having a gradient in iron content that increases as distance into the volume of the diamond table increases. The iron gradient increases resistance to wear, such as in interrupted milling tests. The disclosure further relates to methods of manufacturing polycrystalline diamond compacts having a gradient in iron concentration in the diamond table, blanks and cutters including polycrystalline diamond compacts, cutting tools incorporating such compacts, blanks and cutters, and methods of cutting, milling, grinding and drilling, particularly metal machining, using such compacts, blanks, cutters, cutting tools and drill bits.

An abrasive article can include an abrasive component including a body. The body can include a bond matrix and abrasive particles contained in the bond matrix. In an embodiment, the body can include an interconnected phase extending through at least a portion of the bond matrix. The body can include a discontinuous phase including a plurality of discrete members. At least one of the discrete member can include a macroscopic pore. In another embodiment, the body can include a porosity of at least 15 vol % for a total volume of the body.