The present invention relates to processes for the preparation of mesoporous zeolites by post-synthetic technologies, the properties of resulting materials, and the use of the resulting materials as catalysts in the refining and petrochemical industry.

The present invention relates to processes for the preparation of mesoporous zeolites by post-synthetic technologies, the properties of resulting materials, and the use of the resulting materials as catalysts in the refining and petrochemical industry.

A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Jr and Pt.

A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Jr and Pt.

The invention relates to a method for preparing a hierarchical porous zeolite membrane and an application thereof, comprising the following steps: a mesoporous structure-directing agent is added to limit the growth of zeolite crystals, and self-assembled in the crystallization process to generate a mesoporous structure. Based on a seed crystal induced secondary nucleation mechanism, this method can realize one-step hydrothermal synthesis of hierarchical porous zeolite membrane with the advantages of mild and controllable synthesis conditions, simple process, good repeatability, reduced energy consumption and cost savings. The hierarchical porous zeolite membrane prepared by the method has good cut-off performance, and the cut-off molecular weight is adjustable between 200 to 500,000 Da.

The invention relates to a method for preparing a hierarchical porous zeolite membrane and an application thereof, comprising the following steps: a mesoporous structure-directing agent is added to limit the growth of zeolite crystals, and self-assembled in the crystallization process to generate a mesoporous structure. Based on a seed crystal induced secondary nucleation mechanism, this method can realize one-step hydrothermal synthesis of hierarchical porous zeolite membrane with the advantages of mild and controllable synthesis conditions, simple process, good repeatability, reduced energy consumption and cost savings. The hierarchical porous zeolite membrane prepared by the method has good cut-off performance, and the cut-off molecular weight is adjustable between 200 to 500,000 Da.

Methods are provided for using a molecular sieve catalyst for dewaxing formed using a synthesis mixture comprising a morphology modifier. The catalyst may be used, for example, for production of a lubricant base stock. For example, ZSM-48 crystals formed using the morphology modifier (and/or formulated catalysts made using such crystals) can have an increased activity and/or can provide an improved yield during catalytic dewaxing of lubricant base stocks.

A zeolite membrane complex comprises: a support; and a zeolite membrane formed on the support. The membrane is of SAT-type zeolite, and in an X-ray diffraction pattern obtained by X-ray irradiation to the zeolite membrane, a peak intensity around 2θ=13.9° is 1.5 times or more a peak intensity around 2θ=8.5°.

A phosphorus-containing molecular sieve has a phosphorus content of about 0.3-5 wt %, a pore volume of about 0.2-0.95 ml/g, and a ratio of B acid content to L acid content of about 2-10. The molecular sieve has a specific combination of characteristics, including a high ratio of B acid content to L acid content, thereby exhibiting higher hydrocracking activity and ring-opening selectivity when used in the preparation of a hydrocracking catalyst.

A phosphorus-containing molecular sieve has a phosphorus content of about 0.3-5 wt %, a pore volume of about 0.2-0.95 ml/g, and a ratio of B acid content to L acid content of about 2-10. The molecular sieve has a specific combination of characteristics, including a high ratio of B acid content to L acid content, thereby exhibiting higher hydrocracking activity and ring-opening selectivity when used in the preparation of a hydrocracking catalyst.