An abrasive grain is disclosed and may include a body. The body may define a length (l), a height (h), and a width (w). In a particular aspect, the length is greater than or equal to the height and the height is greater than or equal to the width. Further, in a particular aspect, the body may include a primary aspect ratio defined by the ratio of length:height of at least about 2:1. The body may also include an upright orientation probability of at least about 50%.

A tableted catalyst support, characterized by an alpha-alumina content of at least 85 wt.-%, a pore volume of at least 0.40 mL/g, as determined by mercury porosimetry, and a BET surface area of 0.5 to 5.0 m.sup.2/g. The tableted catalyst support is an alpha-alumina catalyst support obtained with high geometrical precision and displaying a high overall pore volume, thus allowing for impregnation with a high amount of silver, while exhibiting a surface area sufficiently large so as to provide optimal dispersion of catalytically active species, in particular metal species. The invention further provides a process for producing a tableted alpha-alumina catalyst support, which comprises i) forming a free-flowing feed mixture comprising, based on inorganic solids content, at least 50 wt.-% of a transition alumina; ii) tableting the free-flowing feed mixture to obtain a compacted body; and iii) heat treating the compacted body at a temperature of at least 1100° C., preferably at least 1300° C., more preferably at least 1400° C., in particular at least 1450° C., to obtain the tableted alpha-alumina catalyst support. The invention moreover relates to a compacted body obtained by tableting a free-flowing feed mixture which comprises, based on inorganic solids content, at least 50 wt.-% of a transition alumina having a loose bulk density of at most 600 g/L, a pore volume of at least 0.6 mL/g, as determined, and a median pore diameter of at least 15 nm. The invention moreover relates to a shaped catalyst body for producing ethylene oxide by gas-phase oxidation of ethylene, comprising at least 15 wt.-% of silver, relative to the total weight of the catalyst, deposited on the tableted alpha-alumina catalyst support. The invention moreover relates to a process for producing ethylene oxide by gas-phase oxidation of ethylene, comprising reacting ethylene and oxygen in the presence of the shaped catalyst body.

A method for preparing high purity alumina (HPA) is provided. The method includes subjecting an aluminum feedstock to acid leaching, thereby yielding an aluminum bearing leachate; subjecting the aluminum bearing leachate to solvent extraction, thereby yielding an organic phase which is loaded with aluminum; stripping the aluminum from the loaded organic phase with a stripping solution containing an acid, thereby yielding an aluminum bearing extract; crystallizing an aluminum salt from the aluminum bearing extract; dissolving the aluminum salt in an ammoniacal solution, thereby generating a boehmite precursor compound and an ammonium salt; calcining the boehmite precursor compound to yield HPA; subjecting the ammonium salt to electro-dialysis, thereby yielding ammonia and the acid; and performing at least one step of (a) utilizing the ammonia in preparing the ammoniacal solution used in a subsequent iteration of the method, or (b) utilizing the acid in preparing the stripping solution used in a subsequent iteration of the method.

Provided is an inorganic filler powder (3) having a structure in which at least a portion of the surface of inorganic particles (1) having a particle size of 1 μm or more is covered with inorganic microparticles (2) having a particle size of 10 nm or more and less than 0.1 μm, in which the coverage ratio of the surface of the inorganic particles (1) by the inorganic microparticles (2) is 30% or greater.

Provided is an inorganic filler powder (3) having a structure in which at least a portion of the surface of inorganic particles (1) having a particle size of 1 μm or more is covered with inorganic microparticles (2) having a particle size of 10 nm or more and less than 0.1 μm, in which the coverage ratio of the surface of the inorganic particles (1) by the inorganic microparticles (2) is 30% or greater.

A pseudo-boehmite has a dry basis content of 55-85 wt % and contains a phosphoric acid ester group. The sodium oxide content is not greater than 0.5 wt %, and the phosphorus content (in terms of phosphorus pentoxide) is 1.2-5.7 wt %, relative to 100 wt % of the total weight of the pseudo-boehmite. The pseudo-boehmite has a low sodium content.

There is provided a process for purifying aluminum ions comprising: reacting an aluminum-containing material with an acid so as to obtain a composition comprising aluminum ions; precipitating said aluminum ions in the form of AlCl.sub.3; optionally converting AlCl.sub.3 into Al(OH).sub.3; and heating said AlCl.sub.3 or said Al(OH).sub.3 under conditions effective for converting AlCl.sub.3 or Al(OH).sub.3 into Al.sub.2O.sub.3 and optionally recovering gaseous HCl so-produced. Aluminum ions so purified are thus useful for preparing various types of alumina.

An abrasive grain is disclosed and may include a body. The body may define a length (l), a height (h), and a width (w). In a particular aspect, the length is greater than or equal to the height and the height is greater than or equal to the width. Further, in a particular aspect, the body may include a primary aspect ratio defined by the ratio of length:height of at least about 2:1. The body may also include an upright orientation probability of at least about 50%.

A process of forming a sintered article includes heating a green portion of a tape of polycrystalline ceramic and/or minerals in organic binder at a binder removal zone to a temperature sufficient to pyrolyze the binder; horizontally conveying the portion of tape with organic binder removed from the binder removal zone to a sintering zone; and sintering polycrystalline ceramic and/or minerals of the portion of tape at the sintering zone, wherein the tape simultaneously extends through the removal and sintering zones.

A method for preparing high purity alumina (HPA) is provided. The method includes subjecting an aluminum feedstock to acid leaching, thereby yielding an aluminum bearing leachate; subjecting the aluminum bearing leachate to solvent extraction, thereby yielding an organic phase which is loaded with aluminum; stripping the aluminum from the loaded organic phase with a stripping solution containing an acid, thereby yielding an aluminum bearing extract; crystallizing an aluminum salt from the aluminum bearing extract; dissolving the aluminum salt in an ammoniacal solution, thereby generating a boehmite precursor compound and an ammonium salt; calcining the boehmite precursor compound to yield HPA; subjecting the ammonium salt to electro-dialysis, thereby yielding ammonia and the acid; and performing at least one step of (a) utilizing the ammonia in preparing the ammoniacal solution used in a subsequent iteration of the method, or (b) utilizing the acid in preparing the stripping solution used in a subsequent iteration of the method.