A glass sheet is a single glass sheet having a first surface and a second surface facing the first surface. The glass sheet has a curvature part curved in a first direction and a second direction orthogonal to the first direction. A radius of curvature in the first direction of the curvature part is 8,500 mm or less. At least a part of the first surface has been chemically strengthened in the curvature part. In the first direction within the chemically strengthened region in the curvature part, an Na amount in the first surface is smaller than the Na amount in the second surface.

A method of manufacturing a glass container in preparation for direct digital printing includes forming a glass container having a glass wall and applying a primer coating to the glass container. The primer coating is applied by directing an atomized spray of an aqueous primer composition onto the glass container over an adherent base layer, such as a hot-end coating, which deposits the primer coating, followed by heating the primer coating with a heat source such as a flame. Upon being heated, the clarity of the primer coating is increased. As a result, a decorative marking may be printed onto the glass container without having to pretreat the glass container in a way that involves pyrolytically depositing a layer of silicon dioxide onto the glass container prior to printing.

In one or more embodiments disclosed herein, an electronic device may include a display device operable to project an image, a front cover substrate positioned over the display device and including a transparent material, and a protective coating disposed on at least a portion of the non-display area of the front cover substrate. The front cover substrate may include a display area over the display device and a non-display area around at least the perimeter of the front cover substrate. The protective coating may include an inorganic material. The protective coating may not be positioned over the display area.

An anti-fog glass includes a glass body configured as a single layer or a multilayer stack; an active anti-fog layer disposed on the glass body and heating up when being provided with power; and a passive anti-fog layer disposed on the glass body and inhibiting fog from forming on the passive anti-fog layer. The passive anti-fog layer is a super hydrophobic coating and/or hydrophilic coating. Both the active anti-fog layer and the passive anti-fog layer are simultaneously disposed on the glass body to inhibit fog from forming. In this way, in a region of the glass body not covered by the active anti-fog layer, the anti-fog function is achieved by the passive anti-fog layer to a certain degree; in addition, in a region where the passive anti-fog layer itself cannot provide a desired anti-fog level, the active anti-fog layer together with the passive anti-fog layer provide a better anti-fog effect.

The invention relates to a glass substrate for chemical strengthening where a surface is coated by magnetron sputtering with a temporary thin film that reduces the extent of ion exchange upon chemical strengthening and where the temporary thin film can be removed after the chemical strengthening by treatment with an etchant solution. Other embodiments relate to a method for making a chemically strengthened glass substrate with controlled curvature comprising: providing a substrate with opposed surfaces that are durable to a given etchant solution, forming a temporary thin film upon at least part of a surface of the glass substrate, chemically strengthening the glass substrate bearing the temporary thin film, and removing the temporary thin film after said chemical strengthening with said etchant solution. The thickness of the temporary thin film is chosen such that a controlled curvature is obtained upon chemical strengthening.

A light transmissive substrate having a coating is disclosed. The coating is formed of an adhesion promoter that includes a metal, a metal oxide, or a metal nitride. A laminate including a coated substrate is also disclosed. A method of coating a substrate is further disclosed.

A low-E coating supported by a glass substrate, the coating from the glass substrate outwardly including at least the following layers: a dielectric layer of or including silicon nitride; a high index layer having a refractive index of at least 2.1; another dielectric layer of or including silicon nitride; a layer comprising zinc oxide; an infrared (IR) reflecting layer, wherein the coating includes only one IR reflecting layer; and an overcoat including (i) a layer comprising tin oxide and (ii) a layer comprising silicon nitride located over and contacting the layer comprising tin oxide. An IG unit including the coating may have a visible transmission of at least 70%.

The presently claimed invention relates to a low-e coating (20) applied onto a glass (10), in order to provide neutrality at first sight from inside and outside of automotive and architectural glasses.

The present invention is directed to a method for preparing a coated optical article including providing a non-conductive substrate; forming a conductive coating layer over the substrate; electrodepositing a first electrodepositable coating composition over the conductive coating layer to form a first electrodeposited inorganic coating layer; and electrodepositing a second electrodepositable coating composition over the first electrodeposited coating layer to form a second electrodeposited inorganic coating layer thereover, thereby forming a multi-layer antireflective inorganic coating over the conductive coating layer. Each of the first electrodepositable coating composition and the second electrodepositable coating composition is different one from the other, and each includes a sol prepared from a composition of a metal oxide precursor and protic acid such that each coating composition is hydrolyzed. Coated optical articles are also provided.

A nanoparticle coater includes a housing; a nanoparticle discharge slot; a first combustion slot; and a second combustion slot.