A concrete and asphalt repair coating formulation includes a cement component and an aggregate component. The cement component includes a calcium sulfoaluminate cement and a Portland cement. The aggregate component includes coarse aggregates between 125-500 microns in diameter and fine aggregates between 5-62.5 microns in diameter.

Described herein are compositions and methods relating to functionalized sands or soils.

Described herein are compositions and methods relating to functionalized sands or soils.

An erosion resistant composition includes a granular material and a wax including oil in which a weight percent of the oil in the wax is between 0.01-15%. The granular material includes a sand and has a first resistance to flow prior to being coated with the wax. The wax at least partially coats a portion of the granular material to form the erosion resistant composition which has a second resistance to flow after coating that is greater than the first resistance to flow prior to coating. The erosion resistant composition may be used, for example, in golf course bunkers or other landscaping applications. Related methods of making the erosion resistant composition are also described in which the granular material is dried, the wax is heated, and the granular material is blended with the melted wax.

An erosion resistant composition includes a granular material and a wax including oil in which a weight percent of the oil in the wax is between 0.01-15%. The granular material includes a sand and has a first resistance to flow prior to being coated with the wax. The wax at least partially coats a portion of the granular material to form the erosion resistant composition which has a second resistance to flow after coating that is greater than the first resistance to flow prior to coating. The erosion resistant composition may be used, for example, in golf course bunkers or other landscaping applications. Related methods of making the erosion resistant composition are also described in which the granular material is dried, the wax is heated, and the granular material is blended with the melted wax.

A waterproofing membrane including a reinforcing material coated with a blend formulation, the blend formulation including glass spheres having a particle size between 0.25-0.50 mm and a particle density between 0.5-0.8 g/cm.sup.3.

A waterproofing membrane including a reinforcing material coated with a blend formulation, the blend formulation including glass spheres having a particle size between 0.25-0.50 mm and a particle density between 0.5-0.8 g/cm.sup.3.

An erosion resistant composition includes a granular material and a wax including oil in which a weight percent of the oil in the wax is between 0.01-15%. The granular material includes a sand and has a first resistance to flow prior to being coated with the wax. The wax at least partially coats a portion of the granular material to form the erosion resistant composition which has a second resistance to flow after coating that is greater than the first resistance to flow prior to coating. The erosion resistant composition may be used, for example, in golf course bunkers or other landscaping applications. Related methods of making the erosion resistant composition are also described in which the granular material is dried, the wax is heated, and the granular material is blended with the melted wax.

An erosion resistant composition includes a granular material and a wax including oil in which a weight percent of the oil in the wax is between 0.01-15%. The granular material includes a sand and has a first resistance to flow prior to being coated with the wax. The wax at least partially coats a portion of the granular material to form the erosion resistant composition which has a second resistance to flow after coating that is greater than the first resistance to flow prior to coating. The erosion resistant composition may be used, for example, in golf course bunkers or other landscaping applications. Related methods of making the erosion resistant composition are also described in which the granular material is dried, the wax is heated, and the granular material is blended with the melted wax.

Bitumen which is solid at ambient temperature, in the form of granules including a core made of a first bituminous material and a coating layer made of a second bituminous material, in which: the first bituminous material includes at least one bitumen base and the second bituminous material includes: at least one bitumen base and at least one chemical additive chosen from: an organic compound, a viscosifying compound, a paraffin, a polyphosphoric acid and mixtures thereof; or at least one pitch having a ring-and-ball softening point (RBSP) greater than or equal to 80° C., it being understood that the RBSP is measured according to the EN 1427 standard; or a mixture of these materials.