Ceramic-bonded diamond composite particle includes a plurality of diamond grains and silicon carbide reaction bonded to the diamond grains having a composition of 60-90 wt. % diamond, 10-40 wt. % silicon carbide, ≦2 wt. % silicon. Particles are formed by processes that forms granules in a pre-consolidation process, forms a densified compact including ceramic-bonded diamond composite material in a consolidation process or forms ceramic-bonded diamond composite material directly, and a post-consolidation process in which the densified compact or ceramic-bonded diamond composite material is mechanically broken to form a plurality of the particles. Inert or active material can be incorporated into the densified compact or coated on granules to reduce the number and extent of diamond to silicon carbide bonding occurring in the consolidation process and make the ceramic-bonded diamond composite material more friable and easily breakable into composite particles.

A tableted catalyst support, characterized by an alpha-alumina content of at least 85 wt.-%, a pore volume of at least 0.40 mL/g, as determined by mercury porosimetry, and a BET surface area of 0.5 to 5.0 m.sup.2/g. The tableted catalyst support is an alpha-alumina catalyst support obtained with high geometrical precision and displaying a high overall pore volume, thus allowing for impregnation with a high amount of silver, while exhibiting a surface area sufficiently large so as to provide optimal dispersion of catalytically active species, in particular metal species. The invention further provides a process for producing a tableted alpha-alumina catalyst support, which comprises i) forming a free-flowing feed mixture comprising, based on inorganic solids content, at least 50 wt.-% of a transition alumina; ii) tableting the free-flowing feed mixture to obtain a compacted body; and iii) heat treating the compacted body at a temperature of at least 1100° C., preferably at least 1300° C., more preferably at least 1400° C., in particular at least 1450° C., to obtain the tableted alpha-alumina catalyst support. The invention moreover relates to a compacted body obtained by tableting a free-flowing feed mixture which comprises, based on inorganic solids content, at least 50 wt.-% of a transition alumina having a loose bulk density of at most 600 g/L, a pore volume of at least 0.6 mL/g, as determined, and a median pore diameter of at least 15 nm. The invention moreover relates to a shaped catalyst body for producing ethylene oxide by gas-phase oxidation of ethylene, comprising at least 15 wt.-% of silver, relative to the total weight of the catalyst, deposited on the tableted alpha-alumina catalyst support. The invention moreover relates to a process for producing ethylene oxide by gas-phase oxidation of ethylene, comprising reacting ethylene and oxygen in the presence of the shaped catalyst body.

A sacrificial ceramic CO.sub.2 sequestration architectural product comprising a sintered/heat-treated mixture that comprises: one or more reactive solid phases, wherein each reactive solid phase comprises one or more weathering materials capable of enhanced mineralization, and one or more particle-bridging phases that bridge the one or more reactive solid phases, and an open porosity that is in a range from about 15 vol% to about 30 vol%.

Disclosed herein is a sintered ceramic body comprising from 90% to 99.9% by volume of polycrystalline yttrium aluminum garnet (YAG) as measured using XRD and image processing methods and a volumetric porosity of from 0.1 to 4% as calculated from density measurements performed in accordance with ASTM B962-17. The sintered ceramic body may have a total purity of 99.99% and greater and a grain size of from 0.3 to 8 μm. A method of making the sintered ceramic body is also disclosed.

Antiballistic armour plate includes a ceramic body including a hard material, provided, on its inner face, with a back energy-dissipating coating. The ceramic body is monolithic. The constituent material of the ceramic body includes grains of ceramic material having a Vickers hardness that is higher than 15 GPa, and a matrix binding the grains, the matrix including a silicon nitride phase and/or a silicon oxynitride phase, the matrix representing between 5 and 40% by weight of the constituent material of the ceramic body. The maximum equivalent diameter of the grains of ceramic material is smaller than or equal to 800 micrometres. The constituent material of the ceramic body has an open porosity that is higher than 5% and lower than 14%. The metallic silicon content in the material, expressed per mm of thickness of the body, is lower than 0.5% by weight.

The invention concerns the area of ceramics an relates to a method for separating impurities from silicon carbide, said method being applicable to SiC powders from grinding sludges, and to temperature-treated and purified silicon carbide powder. The aim of the invention is to provide a method with which different impurities are substantially completely removed using a simple and economical process. This is achieved by a method in which pulverulent SiC waste products that have a mass percent of SiC of at least 50% and an average grain size d.sub.50 ranging from 0.5 to 1000 μm and have been subjected to a temperature treatment and cooled are mechanically treated and physically separated. The physically separated SiC powder is then divided into two fractions, one of which has a mass of impurities that is greater than the mass of impurities in the other fraction at least by a factor of 2.

Aspects of the present disclosure relate to a piezoelectric device having at least one piezoelectric element, which has a support plane oriented to a force introduction element, wherein in the event of a thermal loading of the piezoelectric device in the support plane, expansion differences between the piezoelectric element and the force introduction element occur. To compensate for shear loadings, at least one transition element is arranged between the piezoelectric element and the force introduction element, the E-module of which is smaller than the E-module of the piezoelectric element in the support plane.

(Problem) In conventional method for producing artificial graphite, in order to obtain a product having excellent crystallinity, it was necessary to mold a filler and a binder and then repeat impregnation, carbonization and graphitization, and since carbonization and graphitization proceeded by a solid phase reaction, a period of time of as long as 2 to 3 months was required for the production and cost was high and further, a large size structure in the shape of column and cylinder could not be produced. In addition, nanocarbon materials such as carbon nanotube, carbon nanofiber and carbon nanohorn could not be produced. (Means to solve) A properly pre-baked filler is sealed in a graphite vessel and is subsequently subjected to hot isostatic pressing (HIP) treatment, thereby allowing gases such as hydrocarbon and hydrogen to be generated from the filler and precipitating vapor-phase-grown graphite around and inside the filler using the generated gases as a source material, and thereby, an integrated structure of carbide of the filler and the vapor-phase-grown graphite is produced. In addition, nanocarbon materials are produced selectively and efficiently by adding a catalyst or adjusting the HIP treating temperature.

The invention relates to a refractory product, a batch for producing the product, a method for producing the product, and a use of the refractory product.

The invention relates to a method for manufacturing a colored blank, which contains zirconium dioxide and is intended for the manufacture of a dental restoration, whereby raw materials in powder form, at least some of which contain one coloring substance each, are mixed with, zirconium dioxide as the main ingredient, the resulting mixture is pressed and subsequently subjected to at least one thermal treatment. To generate the desired fluorescence, it is intended that in the raw materials in powder form one uses as coloring substances at least terbium, erbium, cobalt, as well as one substance that generates a fluorescence effect in the dental restoration, however not iron, aside from naturally occurring impurities.