The present invention provides A magnesium oxide whisker in-situ formed MA spinel-reinforced magnesium oxide-based ceramic foam filter and a method for preparing the same. The method comprising: 1) preparing a ceramic slurry having a solid content of 60%-70% by dosing 15%-25% by mass of a nanometer alumina sol, 0.8%-1.5% by mass of a rheological agent, and the balance magnesium oxide ceramic powder comprising magnesium oxide whiskers, and then adding deionized water and ball milling to mix until uniform, and then vacuum degassing the mixture; 2) soaking a polyurethane foam template into the ceramic slurry, squeezing by a roller press the polyurethane foam template to remove redundant slurry therein to make a biscuit, and drying the biscuit by heating it to 80° C.-1200° C.; 3) putting the dried biscuit into a sintering furnace, elevating the temperature to 1400° C.-1600° C. and performing a high temperature sintering, cooling to the room temperature with the furnace to obtain the magnesium oxide-based ceramic foam filter.

To provide a sintered body with improved impact resistance due to impact absorption through plastic deformation before brittle fracture for an impact exceeding the fracture resistance of the sintered body, and/or a method for producing the sintered body.

A sintered body including: zirconia containing a stabilizer; and a region in which an impact mark is formed when an impact force is applied.

A sputtering target comprising a top coat including a composition of lithium cobalt oxide LiyCozOx. x is smaller than or equal to y+z, and the lithium cobalt oxide has an X-Ray diffraction pattern with a peak P2 at 44°±0.2° 2-theta. The X-Ray diffraction pattern is measured with an X-Ray diffractometer with CuKα1 radiation.

A multilayer coil component includes a multilayer body in which a plurality of insulating layers are stacked in a stacking direction and a coil inside, and outer electrodes on surfaces of the multilayer body and electrically connected to the coil. The insulating layers have a magnetic phase having spinel structure containing at least Fe, Ni, Zn, and Cu and a non-magnetic phase containing at least Si. When grain sizes D50 and D90 of crystal grains constituting the magnetic phase are respectively defined as equivalent-area circle diameters of 50% and 90% on a cumulative sum basis in a cumulative distribution of equivalent-area circle diameters of the crystal grains, the grain size D50 is from 50 nm to 750 nm, and the grain size D90 is from 200 nm to 1500 nm.

A method includes molding a raw material powder containing a ceramic powder and a thermoplastic resin having a glass transition temperature higher than room temperature into a shape by isostatic pressing and in which a raw material powder slurry is prepared by adding the ceramic powder and the thermoplastic resin to a solvent so that the thermoplastic resin is 2% by weight or more and 40% by weight or less with respect to a total weight of the ceramic powder and the thermoplastic resin, a cast-molded body is to formed by wet-casting the raw material powder slurry into a shape, dried, and subjected to first-stage isostatic press molding at a temperature lower than the glass transition temperature of the thermoplastic resin, then this first-stage press-molded body is heated to the glass transition temperature of the thermoplastic resin or above, and warm isostatic press (WIP) molding is performed.

A composition and a solid material is especially suitable for the manufacture of an antenna adapted to operate in the very high frequency and ultra high frequency or V/UHF band. The composition has the formula Ni.sub.aZn.sub.bCu.sub.cCo.sub.dFe.sub.2-δO.sub.4, in which 2(a+b+c+d)+3(2−δ)=8, 0.05<b<0.5, e.g. 0.1<b<0.5, e.g. 0.1<b<0.4, e.g. 0.15<b<0.35, 0.10<c<0.25, preferably 0.15<c<0.25, alternatively c is 0.20, 0.04<d<0.25, preferably 0.06<d<0.25, and more preferably 0.07<d<0.25, and δ<0.05.

A method for manufacturing a sintered body, the method including heating a mixture that contains a plurality of particles of a metal oxide having a spinel-type structure, and a metal acetylacetonate under pressure at a temperature of from a melting point or higher of the metal acetylacetonate to 600° C. or lower, to form a sintered body that contains the metal oxide having the spinel-type structure.

The present disclosure relates to a negative temperature coefficient product comprising an electrically conductive percolation network of printable NTC material as particles in a cross-linked dielectric polymer matrix and to a method of manufacturing thereof. The particles comprising a spinel phase, preferably a C-spinel phase, having a general formula M.sub.3O.sub.4 comprising at least a first metal M.sup.I that is manganese and second metal M.sup.II that is nickel. In addition the particles include a nickel oxide phase. The printable NTC material can be dispersed in a printable NTC ink comprising a dispersant, from which the NTC product, e.g. a thermistor, can be formed, e.g., after drying of the dispersant. During processing the ink is kept at a temperature below 300° C. Optionally, the spinel phase comprises a further metal M.sup.III. The weight fraction of nickel oxide with respect to the overall mass of the printable NTC material is preferably in a range between one and twenty weight percent.

A method for forming a transparent ceramic, in accordance with one embodiment, includes forming a green body by material jetting an ink, and processing the green body to form the ceramic to transparency. A product, in accordance with one embodiment, includes an ink for forming a transparent ceramic. The ink is physically characterized as having a density, surface tension, and viscosity configured to enable material jetting of the ink in contained, sequential droplets having a volume in the range of about 1 picoliter to about 1 nanoliter when jetted from a nozzle having an inner diameter in the range of about 10 microns to about 300 microns. A product, in accordance with another embodiment, includes a transparent ceramic, at least a portion of the transparent ceramic having layers of less than 50 microns per layer with physical characteristics of formation by material jetting.

The present invention relates to a ferrite particle containing a crystal phase component containing a perovskite crystal represented by a compositional formula: RZrO.sub.3 (provided that R represents an alkaline earth metal element), having a surface roughness Rz of 0.8 .Math.m or more and 3.5 .Math.m or less, and having a standard deviation Rzσ of the surface roughness Rz falling in a range represented by the following formula 0.15 × Rz ≤ Rzσ ≤ 0.60 × Rz. The ferrite particle can be used as an electrophotographic developer carrier core material. In addition, an electrophotographic developer carrier and an electrophotographic developer can be obtained.