A nonwoven article includes a plurality of electrospun polycrystalline, aluminosilicate ceramic filaments that form a cohesive nonwoven mat. Each of the aluminosilicate ceramic filaments in the mat have an average diameter of about 200 nm to about 1000 nm as determined with electron microscopy, and the aluminosilicate ceramic filaments have an average crystalline mullite content of about 15 wt % to about 80 wt %.

A method includes: providing a mold having a plurality of mold cavities, wherein each mold cavity is bounded by a plurality of faces joined along common edges; filling at least some of the mold cavities with a sol-gel composition that includes a release agent dispersed therein; at least partially drying the sol-gel composition thereby forming shaped ceramic precursor particles; calcining at least a portion of the shaped ceramic precursor particles to provide calcined shaped ceramic precursor particles; and sintering at least a portion of the calcined shaped ceramic precursor particles to provide ceramic shaped abrasive particles. A sol-gel composition, shaped ceramic precursor particles, and ceramic shaped abrasive particles associated with practice of the method are also disclosed.

A method includes: providing a mold having a plurality of mold cavities, wherein each mold cavity is bounded by a plurality of faces joined along common edges; filling at least some of the mold cavities with a sol-gel composition that includes a release agent dispersed therein; at least partially drying the sol-gel composition thereby forming shaped ceramic precursor particles; calcining at least a portion of the shaped ceramic precursor particles to provide calcined shaped ceramic precursor particles; and sintering at least a portion of the calcined shaped ceramic precursor particles to provide ceramic shaped abrasive particles. A sol-gel composition, shaped ceramic precursor particles, and ceramic shaped abrasive particles associated with practice of the method are also disclosed.

The present invention describes various methods for manufacturing gel composite sheets using segmented fiber or foam reinforcements and gel precursors. Additionally, rigid panels manufactured from the resulting gel composites are also described. The gel composites are relatively flexible enough to be wound and when unwound, can be stretched flat and made into rigid panels using adhesives.

The present invention describes various methods for manufacturing gel composite sheets using segmented fiber or foam reinforcements and gel precursors. Additionally, rigid panels manufactured from the resulting gel composites are also described. The gel composites are relatively flexible enough to be wound and when unwound, can be stretched flat and made into rigid panels using adhesives.

Disclosed here is a method for producing a graphene macro-assembly (GMA)-fullerene composite, comprising providing a mixture of graphene oxide and water, adding a hydroxylated fullerene to the mixture, and forming a gel of the hydroxylated fullerene and the mixture. Also described are a GMA-fullerene composite produced, an electrode comprising the GMA-fullerene composite, and a supercapacitor comprising the electrode.

Disclosed here is a method for producing a graphene macro-assembly (GMA)-fullerene composite, comprising providing a mixture of graphene oxide and water, adding a hydroxylated fullerene to the mixture, and forming a gel of the hydroxylated fullerene and the mixture. Also described are a GMA-fullerene composite produced, an electrode comprising the GMA-fullerene composite, and a supercapacitor comprising the electrode.

A nonwoven article includes a plurality of polycrystalline, aluminosilicate ceramic filaments entangled to form a cohesive nonwoven mat. Each of the aluminosilicate ceramic filaments in the mat has an average diameter of less than about 2 microns (μm), and the aluminosilicate ceramic filaments include an average of about 15 wt % to about 80 wt % crystalline mullite.

A nonwoven article includes a plurality of polycrystalline, aluminosilicate ceramic filaments entangled to form a cohesive nonwoven mat. Each of the aluminosilicate ceramic filaments in the mat has an average diameter of less than about 2 microns (μm), and the aluminosilicate ceramic filaments include an average of about 15 wt % to about 80 wt % crystalline mullite.

A method of preparation of a ceramic slurry for use in 3D printing includes steps of: (A) providing a plasticizer and a disperser and mixing the plasticizer and the disperser evenly; (B) mixing the mixture obtained in step (A) with an adhesive, wherein the adhesive is polyvinyl alcohol; and (C) adding a Yttria-stabilized zirconia powder to the mixture obtained in step (B) to produce, by sufficient blending and deaerating, the ceramic slurry for use in 3D printing. A method of preparation of a ceramic product includes steps of: (A) preparing a ceramic slurry with the method; (B) performing 3D printing with the ceramic slurry to form a primary green body; (C) placing the primary green body in a freezer to undergo a refrigeration process, thereby causing crystallization of polyvinyl alcohol; and (D) thawing the frozen primary green body to form a plastic green body with gel structure.