The disclosure relates to tiles or slabs comprising a fired ceramic material which has a chemical composition with a particular combination of oxides; to a method for the manufacture of said tiles or slabs; and to the use thereof for construction or decoration applications.

Sintered product having a relative density of greater than 90%, with, to more than 80% of the volume thereof, a stack of flat ceramic platelets, the assembly of the platelets having a mean thickness of less than 3 μm, having a width of greater than 50 mm, and including more than 20% of alumina, as a percentage on the basis of the weight of the product. The width of the product is the largest dimension measured in the plane in which the length of the product is measured, along a direction perpendicular to the direction of the length. The length of the product is the largest dimension thereof in a plane parallel to the general plane in which the platelets extend.

A manganese-zinc ferrite with a high magnetic permeability at negative temperature and low loss at high temperature consists of Fe.sub.2O.sub.3, MnO and ZnO, and additives consisting of CaCO.sub.3, ZrO.sub.2, Co.sub.2O.sub.3 and SnO.sub.2 are also added. A method for preparing the manganese-zinc ferrite is further provided. According to the method, by reasonably adjusting a ratio of Mn to Zn to Fe and appropriately increasing the content of Co in the additives, a manganese-zinc ferrite material with both a high magnetic permeability and low loss at about −20° C. and low loss at 120-140° C. is obtained. The manganese-zinc ferrite material has two loss valleys at about −20° C. and about 100° C. in a temperature range of −30° C. to 140° C., which expands the application range of the manganese-zinc ferrite material.

Coated zirconia fine particle containing a zirconia fine particle and a coating layer coating the surface of the fine particle. The coating layer includes one or more metal elements selected from Mg, Ca, Al and rare-earth elements, and the coated zirconia fine particle has an average particle size of 3 to 100 nm and a specific surface area of 20 to 500 m.sup.2/g.

In an embodiment a ceramic material includes ZnO as main constituent, Y as a first additive, second additives including at least one compound containing a metal element, wherein the metal element is selected from the group consisting of Bi, Cr, Co, Mn, Ni and Sb, Si.sup.4+ as a first dopant and second dopants having at least one compound containing a metal cation from Al.sup.3+, B.sup.3+, or Ba.sup.2+, wherein a corresponds to a molar proportion of Bi calculated as Bi.sub.2O.sub.3, b corresponds to a molar proportion of Y calculated as Y.sub.2O.sub.3, c corresponds to a molar proportion of Al calculated as Al.sub.2O.sub.3, d corresponds to a molar proportion of Ba calculated as BaO, e corresponds to a molar proportion of B calculated as B.sub.2O.sub.3, f corresponds to a molar proportion of Si calculated as SiO.sub.2, g corresponds to a molar proportion of Ni calculated as NiO, h corresponds to a molar proportion of Co calculated as Co.sub.3O.sub.4, i corresponds to a molar proportion of Cr calculated as Cr.sub.2O.sub.3, j corresponds to a molar proportion of Sb calculated as Sb.sub.2O.sub.3, and k corresponds to a molar proportion of Mn calculated as Mn.sub.3O.sub.4.

Batch compositions containing pre-reacted inorganic spheroidal particles, small amount of fine inorganic particles (“fines”), and an extremely large amount of liquid vehicle. The batch compositions contain pre-reacted inorganic particles having a particle size distribution with 20 μm≤D50≤100 μm, D90≤100 μm, and D5≥10 μm; less than 20 wt % of fine inorganic particles (fines) whose particle distribution(s) have a median diameter of less than 5 μm; and a liquid vehicle in a weight percent (LV %≥28%) by super-addition to all inorganic particles in the batch composition. Fast extruding batch compositions having extremely high Tau Y/Beta ratios are provided. Green bodies, such as green honeycomb bodies and methods of manufacturing green honeycomb bodies are provided, as are other aspects.

The invention relates to a ceramic material, comprising lead zirconate titanate, which additionally contains K and optionally Cu. The ceramic material can be used in an electroceramic component, for example a piezoelectric actuator. The invention also relates to methods for producing the ceramic material and the electronic component.

Provided is a powder material for forming a three-dimensional object, the powder material containing granulated particles containing: a resin; and inorganic particles of which primary particles have a volume average particle diameter of 1 micrometer or less, wherein the granulated particles have a volume average particle diameter of 10 micrometers or greater but 70 micrometers or less and a BET specific surface area of 6 m.sup.2/g or greater but 8 m.sup.2/g or less.

Ceramic-bonded diamond composite particle includes a plurality of diamond grains and silicon carbide reaction bonded to the diamond grains having a composition of 60-90 wt. % diamond, 10-40 wt. % silicon carbide, ≦2 wt. % silicon. Particles are formed by processes that forms granules in a pre-consolidation process, forms a densified compact including ceramic-bonded diamond composite material in a consolidation process or forms ceramic-bonded diamond composite material directly, and a post-consolidation process in which the densified compact or ceramic-bonded diamond composite material is mechanically broken to form a plurality of the particles. Inert or active material can be incorporated into the densified compact or coated on granules to reduce the number and extent of diamond to silicon carbide bonding occurring in the consolidation process and make the ceramic-bonded diamond composite material more friable and easily breakable into composite particles.

A method of producing a dielectric material by preparing a slurry by mixing a dielectric powder, water, one of an organic-acid metal salt and an inorganic metal salt, and an organic silicon compound, causing the slurry to come into contact with an anion exchange resin to remove an anion derived from the one of the organic-acid metal salt and the inorganic metal salt from the slurry, and drying the slurry to obtain the dielectric material.