A ceramic electronic component includes a body, including a dielectric layer and an internal electrode. The dielectric layer includes a plurality of dielectric grains, and at least one of the plurality of dielectric grains has a core-dual shell structure having a core and a dual shell. The dual shell includes a first shell, surrounding at least a portion of the core, and a second shell, surrounding at least a portion of the first shell. The dual shell includes different types of rare earth elements R1 and R2, and R2.sub.S1/R1.sub.S1 is 0.01 or less and R2.sub.S2/R1.sub.S1 is 0.5 to 3.0, where R1.sub.S1 and R1.sub.S2 denote concentrations of R1 included in the first shell and the second shell, respectively, and R2.sub.S1 and R2.sub.S2 denote concentrations of R2 included in the first shell and the second shell, respectively.

A method for enhanced depth penetration of energy into a formation may include mechanically stimulating proppant in proppant-containing fractures in the formation at a first frequency to induce mechanical stress in the proppant and directing electromagnetic radiation at a second frequency into the proppant-containing fractures of the formation while mechanically stimulating the proppant, wherein the first frequency and the second frequency are the same or different and wherein the proppant includes silica.

Ceramic-bonded diamond composite particle includes a plurality of diamond grains and silicon carbide reaction bonded to the diamond grains having a composition of 60-90 wt. % diamond, 10-40 wt. % silicon carbide, ≦2 wt. % silicon. Particles are formed by processes that forms granules in a pre-consolidation process, forms a densified compact including ceramic-bonded diamond composite material in a consolidation process or forms ceramic-bonded diamond composite material directly, and a post-consolidation process in which the densified compact or ceramic-bonded diamond composite material is mechanically broken to form a plurality of the particles. Inert or active material can be incorporated into the densified compact or coated on granules to reduce the number and extent of diamond to silicon carbide bonding occurring in the consolidation process and make the ceramic-bonded diamond composite material more friable and easily breakable into composite particles.

A sintered body includes a crystal grain containing silicon nitride, and a grain boundary phase. If dielectric losses of the sintered body are measured while applying an alternating voltage to the sintered body and continuously changing a frequency of the alternating voltage from 50 Hz to 1 MHz, an average value ε.sub.A of dielectric losses of the sintered body in a frequency band from 800 kHz to 1 MHz and an average value ε.sub.B of dielectric losses of the sintered body in a frequency band from 100 Hz to 200 Hz satisfy an expression |ε.sub.A−ε.sub.B|≤0.1.

An energy storage element and method of fabrication thereof are disclosed. An energy storage element includes a set of electrodes where one or more electrodes have extended conductive paths through nano-channel electric interconnections with ceramic particles in one or more dielectric layers. The electrode's electric field is extended into the dielectric material providing increased capacitance. The set of electrodes can include a pair of electrode layers respectively attached directly to opposing sides of one dielectric layer. The set of electrodes, which can also be referred to as multi-layer electrodes, can include a plurality of electrode layers interleaved between, and directly attached to, a plurality of stacked dielectric layers.

The present invention relates to a SiC composite and a method for manufacturing the same. More particularly, the present invention relates to a slurry composition for ceramic matrix composites which can not only reduce the number of precursor impregnation pyrolysis (PIP) cycles but also be useful in the PIP process to increase hardness, thermal stability, and relative density.

An abrasive particle can include a coating overlying at least a portion of a core. In an embodiment, the coating can include a first portion overlying at least a portion of the core and a second portion overlying at least a portion of the core, wherein the first portion can include a ceramic material and the second portion can include a silane or a silane reaction product. In a particular embodiment, the first portion can consist essentially of silica. In another particular embodiment, the first portion can include a surface roughness of not greater than 5 nm and a crystalline content of not greater than 60%.

A method for forming a refractory material is described comprising the steps of placing a core material 12 into a granulator device 16, operating the granulator device 16 to form the core material into granules 16, adding a coating material 18 to the granulator device 16, operating the granulator device 16 to result in the formation of a layer 20 of the coating material 18 encapsulating the granules 16, and then heating the coated granules 22. Materials manufactured using the method are also described.

A method of manufacturing ceramic matrix composites includes producing chemical vapor deposition functionalized ceramic particles before injecting the functionalized ceramic particles into the CMC fabric. The functionalized ceramic particles are mixed with a binder solution and then dispensed into voids present between adjacent tows of the CMC fabric. Injecting the particles in the center of the voids reduces the size and volume fraction of the voids/defects, improving the homogeneity of surface texture, homogeneity of microstructure, and part model shape conformity.

The present invention provides an antimicrobial ceramic tile and manufacturing method thereof. A manufacturing method of an antimicrobial ceramic tile comprises: grinding soils into slurries; drying the slurries into powders by hot air; pressing the powders into a green body through a molding machine; dotting or spraying or showering a glaze slurry on the surface of the green body to form an engobe; dotting the glaze slurry on the engobe to form a ground glaze; mixing a surface glaze and an antimicrobial material into an antimicrobial glaze in a weight ratio of 100:5˜10; grinding water and the antimicrobial glaze into the antimicrobial glaze in a weight ratio of 5˜6:4˜5; and dotting antimicrobial glaze on the ground glaze; finally, rapidly firing the ceramic tile and the antimicrobial glaze into an antimicrobial ceramic tile.