Coated zirconia fine particle containing a zirconia fine particle and a coating layer coating the surface of the fine particle. The coating layer includes one or more metal elements selected from Mg, Ca, Al and rare-earth elements, and the coated zirconia fine particle has an average particle size of 3 to 100 nm and a specific surface area of 20 to 500 m.sup.2/g.

A method for forming a refractory material is described comprising the steps of placing a core material 12 into a granulator device 16, operating the granulator device 16 to form the core material into granules 16, adding a coating material 18 to the granulator device 16, operating the granulator device 16 to result in the formation of a layer 20 of the coating material 18 encapsulating the granules 16, and then heating the coated granules 22. Materials manufactured using the method are also described.

A ceramic electronic component includes: a body including dielectric layers and internal electrodes; and external electrodes disposed on the body and connected to the internal electrodes, wherein the dielectric layer includes a plurality of first secondary phases, the first secondary phase is a secondary phase including Ni, Mg, Al, Si, and O, and at least one of the plurality of first secondary phases has a ratio of a major axis length to a minor axis length of 4 or more.

A dielectric ceramic composition contains dielectric particles containing a main component represented by a composition formula (Ba.sub.1-x-ySr.sub.xCa.sub.y).sub.m(Ti.sub.1-zZr.sub.z)O.sub.3 and grain boundaries present between the dielectric particles. The values of m, x, y, and z in the composition formula are all molar ratios. In the composition formula, 0.9≤m≤1.4, 0≤x<1.0, 0<y≤1.0, 0.9≤(x+y)≤1.0, and 0.9≤z≤1.0 are satisfied. The dielectric particles contain specific structural particles having a predetermined intragranular structure, and each of the specific structural particles intragranularly includes a first region and a second region having different Ca concentrations from each other. C2/C1 is less than 0.8 in which C1 is an average value of the Ca concentration in the first region and C2 is an average value of the Ca concentration in the second region.

There are provided a composite perovskite powder, a preparation method thereof, and a paste composition for an internal electrode having the same, the composite perovskite powder capable of preventing ions from being eluted from an aqueous system at the time of synthesis while being ultra-atomized, such that when the composite perovskite powder is used as an inhibitor powder for an internal electrode, sintering properties of the internal electrode may be deteriorated, and sintering properties of a dielectric material may be increased; accordingly, connectivity of the internal electrode may be improved, and permittivity and reliability of a multilayer ceramic capacitor (MLCC) may be increased.

A particulate material having a body including a dopant contained in the body, the dopant is non-homogenously distributed throughout the body and the body has a maximum normalized dopant content difference of at least 35%.

There is provided a ferrite sintered magnet having a high residual magnetic flux density. A ferrite sintered magnet 2 includes a plurality of main phase particles 5 including ferrite having a hexagonal structure, the number of core-shell structured particles 5A having a core 7 and a shell 9 covering the core 7, among the main phase particles 5, is smaller than the number of the main phase particles 5 other than the core-shell structured particles 5A.

A dielectric ceramic composition contains dielectric particles containing a main component represented by a composition formula (Ba.sub.1-x-ySr.sub.xCa.sub.y).sub.m(Ti.sub.1-zZr.sub.z)O.sub.3 and grain boundaries present between the dielectric particles. The values of m, x, y, and z in the composition formula are all molar ratios. In the composition formula, 0.9≤m≤1.4, 0≤x<1.0, 0<y≤1.0, 0.9≤(x+y)≤1.0, and 0.9≤z≤1.0 are satisfied. The dielectric particles contain specific structural particles having a predetermined intragranular structure, and each of the specific structural particles intragranularly includes a first region and a second region having different Ca concentrations from each other. C2/C1 is less than 0.8 in which C1 is an average value of the Ca concentration in the first region and C2 is an average value of the Ca concentration in the second region.

A method for manufacturing an environmental barrier comprising the steps of coating a rare earth silicate powder with a precursor of a densification agent in order to form a rare earth silicate powder coated with the precursor of the densification agent, thermally spraying the coated powder onto a substrate in order to obtain an at least partially amorphous environmental barrier on the substrate and thermally treating the environmental barrier in order to crystallize and densify the environmental barrier.

A thermoelectric conversion material made of a sintered body containing a magnesium silicide as a major component includes: a magnesium silicide phase; and a magnesium oxide layer formed on a surface layer of the magnesium silicide phase, in which an aluminum concentrated layer having an Al concentration higher than an aluminum concentration in an inside of the magnesium silicide phase is formed between the magnesium oxide layer and the magnesium silicide phase, and the aluminum concentrated layer has a metallic aluminum phase including aluminum or an aluminum alloy.