Carbon materials formed using various templates of precursor materials are described in addition to method and process for producing the same.

Carbon materials formed using various templates of precursor materials are described in addition to method and process for producing the same.

The present invention relates to a method for preparing a fully ceramic capsulated nuclear fuel material containing three-layer-structured isotropic nuclear fuel particles coated with a ceramic having a composition which has a higher shrinkage than a matrix in order to prevent cracking of ceramic nuclear fuel, wherein the three-layer-structured nuclear fuel particles before coating is included in the range of between 5 and 40 fractions by volume based on after sintering. More specifically, the present invention provides a composition for preparing a fully ceramic capsulated nuclear fuel containing three-layer-structured isotropic particles coated with the substance which includes, as a main ingredient, a silicon carbine derived from a precursor of the silicon carbide wherein a condition of ΔL.sub.c>ΔL.sub.m at normal pressure sintering is created, where the sintering shrinkage of the coating layer of the three-layer-structured isotropic nuclear fuel particles is ΔL.sub.c and the sintering shrinkage of the silicon carbide matrix is ΔL.sub.m; material produced therefrom; and a method for manufacturing the material. The residual porosity of the fully ceramic capsulated nuclear fuel material is 4% or less.

The disclosure relates to a Fe.sub.3C-doped graded porous carbon polymer potassium ion anode material as well as a preparation method and application thereof. In the method, previously prepared Fe.sub.2O.sub.3 is added into phenylamine, pyrrole, thiophene and cellulose acetate solutions, the above mixture is evaporated at the low temperature of 65-100° C., and then the evaporated product is calcinated to obtain a potassium battery anode material. This material consists of carbon nano sheets having different pore diameters, and has a graded porous structure of micropores, mesopores and macropores. Physical characterization results show that this material has the characteristics of large interlayer spacing, high specific surface area, rich defects and the like; electrochemical testing results show that this material has high reversible capacity and excellent cycle stability and rate performance.

The disclosure relates to a Fe.sub.3C-doped graded porous carbon polymer potassium ion anode material as well as a preparation method and application thereof. In the method, previously prepared Fe.sub.2O.sub.3 is added into phenylamine, pyrrole, thiophene and cellulose acetate solutions, the above mixture is evaporated at the low temperature of 65-100° C., and then the evaporated product is calcinated to obtain a potassium battery anode material. This material consists of carbon nano sheets having different pore diameters, and has a graded porous structure of micropores, mesopores and macropores. Physical characterization results show that this material has the characteristics of large interlayer spacing, high specific surface area, rich defects and the like; electrochemical testing results show that this material has high reversible capacity and excellent cycle stability and rate performance.

A crystal of a calcium phosphate that is any one selected from the group consisting of octacalcium phosphate, hydroxyapatite, fluorapatite, chlorapatite and carbonate apatite, in which a part of a plurality of calcium ions in a crystal structure of the crystal are replaced with a silver ion or a copper ion.

A glassy carbon compact according to the present invention has a maximum inscribed sphere diameter of 5 mm or greater, comprises pores having diameters of 500 nm or less dispersed throughout the glassy carbon compact, and has a density of 1.1 g/cm.sup.3 or greater.

A glassy carbon compact according to the present invention has a maximum inscribed sphere diameter of 5 mm or greater, comprises pores having diameters of 500 nm or less dispersed throughout the glassy carbon compact, and has a density of 1.1 g/cm.sup.3 or greater.

A process for preparing a porous carbon material. The process comprises the process steps: providing a carbon source; providing an amphiphilic species; contacting the carbon source and the amphiphilic species to obtain a precursor; and heating the precursor to obtain the porous carbon material; wherein the carbon source comprises a carbon source compound, wherein the carbon source compound comprises an aromatic ring having one or more attached OH groups and an ester link.

A process for preparing a porous carbon material. The process comprises the process steps: providing a carbon source; providing an amphiphilic species; contacting the carbon source and the amphiphilic species to obtain a precursor; and heating the precursor to obtain the porous carbon material; wherein the carbon source comprises a carbon source compound, wherein the carbon source compound comprises an aromatic ring having one or more attached OH groups and an ester link.