Disclosed is a magnesium-based cementitious material, preparation method and application thereof. The magnesium-based cementitious material, comprising magnesite, sandstone, and water, wherein: the magnesite is provided with CaO, SiO.sub.2, Al.sub.2O.sub.3, Fe.sub.2O.sub.3, and MgO, a mass percentage of the CaO is less than 5%, a mass percentage of SiO.sub.2 is less than 5%, a mass percentage of Al.sub.2O.sub.3 is less than 5%, a mass percentage of Fe.sub.2O.sub.3 is less than 7%, a mass percentage of MgO is between 37% and 50%; the sandstone is provided with SiO.sub.2, CaO, Al.sub.2O.sub.3, and Fe.sub.2O.sub.3, a mass percentage of SiO.sub.2 is greater than 70%. The beneficial effects of this disclosure are: the cementitious material does not contain MgCl.sub.2, which avoids the reduction of the strength of the cementitious material due to the dissolution of MgCl.sub.2 in water; the magnesium-based cementitious material of this disclosure is immiscible with water and has strong water resistance.

Disclosed is a magnesium-based cementitious material, preparation method and application thereof. The magnesium-based cementitious material, comprising magnesite, sandstone, and water, wherein: the magnesite is provided with CaO, SiO.sub.2, Al.sub.2O.sub.3, Fe.sub.2O.sub.3, and MgO, a mass percentage of the CaO is less than 5%, a mass percentage of SiO.sub.2 is less than 5%, a mass percentage of Al.sub.2O.sub.3 is less than 5%, a mass percentage of Fe.sub.2O.sub.3 is less than 7%, a mass percentage of MgO is between 37% and 50%; the sandstone is provided with SiO.sub.2, CaO, Al.sub.2O.sub.3, and Fe.sub.2O.sub.3, a mass percentage of SiO.sub.2 is greater than 70%. The beneficial effects of this disclosure are: the cementitious material does not contain MgCl.sub.2, which avoids the reduction of the strength of the cementitious material due to the dissolution of MgCl.sub.2 in water; the magnesium-based cementitious material of this disclosure is immiscible with water and has strong water resistance.

Disclosed is a magnesium-based cementitious material, preparation method and application thereof. The magnesium-based cementitious material, comprising magnesite, sandstone, and water, wherein: the magnesite is provided with CaO, SiO.sub.2, Al.sub.2O.sub.3, Fe.sub.2 O.sub.3, and MgO, a mass percentage of the CaO is less than 5%, a mass percentage of SiO.sub.2 is less than 5%, a mass percentage of Al.sub.2 O.sub.3 is less than 5%, a mass percentage of Fe.sub.2 O.sub.3 is less than 7%, a mass percentage of MgO is between 37% and 50%; the sandstone is provided with SiO.sub.2, CaO, Al.sub.2 O.sub.3, and Fe.sub.2O.sub.3, a mass percentage of SiO.sub.2 is greater than 70%. The beneficial effects of this disclosure are: the cementitious material does not contain MgCl.sub.2, which avoids the reduction of the strength of the cementitious material due to the dissolution of MgCl.sub.2 in water; the magnesium-based cementitious material of this disclosure is immiscible with water and has strong water resistance.

Disclosed is a magnesium-based cementitious material, preparation method and application thereof. The magnesium-based cementitious material, comprising magnesite, sandstone, and water, wherein: the magnesite is provided with CaO, SiO.sub.2, Al.sub.2O.sub.3, Fe.sub.2 O.sub.3, and MgO, a mass percentage of the CaO is less than 5%, a mass percentage of SiO.sub.2 is less than 5%, a mass percentage of Al.sub.2 O.sub.3 is less than 5%, a mass percentage of Fe.sub.2 O.sub.3 is less than 7%, a mass percentage of MgO is between 37% and 50%; the sandstone is provided with SiO.sub.2, CaO, Al.sub.2 O.sub.3, and Fe.sub.2O.sub.3, a mass percentage of SiO.sub.2 is greater than 70%. The beneficial effects of this disclosure are: the cementitious material does not contain MgCl.sub.2, which avoids the reduction of the strength of the cementitious material due to the dissolution of MgCl.sub.2 in water; the magnesium-based cementitious material of this disclosure is immiscible with water and has strong water resistance.

The invention relates to a calcium sulfoaluminate cement, whereby it contains at least 90% by weight % C4A3$ in crystalline or amorphous form or as a mixture of crystalline and has amorphous parts.

The present invention belongs to the field of composite materials, particularly to an underwater non-dispersible quick-setting and rapid-hardening cement-based composite material and the preparation method and application thereof. The material consists of the following raw materials in percentage by weight: 32%-34% of silicate cement, 8.8%-9% of calcium aluminate, 5%-7% of magnesium oxide, 0.5%-2% of sulfur trioxide, 0.2%-0.3% of polycarboxylate high performance water-reducing agent, 0.3%-0.7% of flocculant, 0.05%-0.2% of setting accelerator, 0.05%-0.2% of air-entraining agent, 0.05%-0.3% of rust inhibitor, 26%-31% of fine aggregate, 13%-18% of coarse aggregate, and 8.4%-8.5% of water. The material can be used for rapid repair of cement buildings in water conservancy projects, the repair material can be quickly set and the initial strength can be guaranteed.

The present invention relates to a hydraulic binder system based on calcined aluminum oxide for use in refractory materials. The invention further relates to a process for producing the hydraulic binder system and also to the use thereof.