The present invention relates to a molding made of expanded bead foam, wherein at least one fiber (F) is partly within the molding, i.e. is surrounded by the expanded bead foam. The two ends of the respective fibers (F) that are not surrounded by the expanded bead foam thus each project from one side of the corresponding molding. The present invention further provides a panel comprising at least one such molding and at least one further layer (S1). The present invention further provides processes for producing the moldings of the invention from expanded bead foam or the panels of the invention and for the use thereof, for example as rotor blade in wind turbines.

A reclaiming agent is formed by grafting thiol groups onto styrene-butadiene rubber (SBR). The reclaiming agent has a weight average molecular weight of 1000 to 120000, which can be a random copolymer or a block copolymer. 100 parts by weight of styrene-butadiene rubber can be reacted with 0.1 to 50 parts by weight of the reclaiming agent to form a reclaimed rubber.

A foamed article formed by foam injection molding or foam extrusion of a composition is disclosed. The article is formed from a molding composition consisting essentially of: 100 phr of at least two different hydrogenated styrenic block copolymers (HSBC), a first HSBC and a second HSBC, having different molecular weights, a molecular weight ratio of at least 1.2:1, respectively; and a weight ratio of ranging from 5:95 to 95:5, respectively; 10-55 phr of a polypropylene having a melt flow of at least 2 g10/min; and optionally up to 55 phr of a plasticizer, selected from hydrocarbon based oils, fatty acids, triglyceride oils, and mixtures thereof. The composition has a melt flow rate of 2-50 g/10 min, a Shore A hardness of 60-90, a melt strength (F) of at least 0.010 N, and a melt strength (V) of at least 10.

The present invention provides a process of catalytic depolymerization of polystyrene involving a spherical catalyst, an apparatus for carrying out the depolymerization, recovering the aromatic rich liquid product and recycling the catalyst without any decrease in the catalytic performance. Further, the present invention provides that the aromatic rich liquid product includes styrene, xylene, benzene, ethyl benzene, with styrene content greater than 65%. Additionally, the catalyst involved in the depolymerization process is a spherical catalyst that is easily recovered from coke/char formed during the process and is recycled and reused without any decrease in the catalytic performance.

An anion-exchange membrane of the present invention includes a substrate made of polyolefin-based woven fabric and an anion-exchange resin, and has an electrical resistance measured using 0.5 M NaCl solution at 25° C. of 1.0 Ω•cm.sup.2 or more to 2.5 Ω•cm.sup.2 or less, a bursting strength of 0.7 MPa or more to 1.2 MPa or less, a water permeation rate measured using pressured water at 0.1 MPa of 300 ml/(m.sup.2•hr) or less, a thickness of the substrate of 90 .Math.m or more to 160 .Math.m or less, and an open area ratio of the substrate of 35% or more to 55% or less.

The invention relates to a molding composed of extruded foam, wherein at least one fiber (F) is present with a fiber region (FB2) within the molding and is surrounded by the extruded foam, while a fiber region (FB1) of the fiber (F) projects from a first side of the molding and a fiber region (FB3) of the fiber (F) projects from a second side of the molding, and the extruded foam is produced by an extrusion process comprising the following steps: I) providing a polymer melt in an extruder, II) introducing at least one blowing agent into the polymer melt provided in step I) to obtain a foamable polymer melt, III) extruding the foamable polymer melt obtained in step II) from the extruder through at least one die aperture into an area at lower pressure, with expansion of the foamable polymer melt to obtain an expanded foam, and IV) calibrating the expanded foam from step III) by conducting the expanded foam through a shaping tool to obtain the extruded foam.

Cationic polymers are provided that comprise monomeric units of Formula (V). (V) Each asterisk (*) indicates an attachment position to another monomeric unit; R is hydrogen or methyl; each R.sup.2 is each independently an alkyl, aryl, or a combination thereof; L is a linking group comprising an alkylene group; and +R.sup.3 is a cationic nitrogen-containing group free of any N—H bonds. Membranes formed from said cationic polymers, devices including such membranes, and methods of making such cationic polymers are also provided.

##STR00001##

The present invention relates to a molding made from foam, wherein at least one fiber (F) is partly within the molding, i.e. is surrounded by the foam. The two ends of the respective fibers (F) that are not surrounded by the foam thus each project from one side of the corresponding molding. The foam comprises at least two mutually bonded foam segments.

Disclosed is a fiber structure including a halogen-free polymer layer such as a styrenic block (SBC) copolymer. The fiber structure has environmentally-friendly properties and reduced weight, as compared to conventional materials such as PVC and has improved low temperature stability, fixing ability and resistance to deformation.

A process for producing a styrene-butadiene diblock copolymer-containing blend that is not an agglomeration, that involves mixing a styrene-butadiene multiblock thermoplastic elastomer solution with a styrene-butadiene diblock copolymer solution. Blends comprising a styrene-butadiene diblock copolymer and a styrene-butadiene multiblock thermoplastic elastomer, which blends are not an agglomeration.