Polyurethane coating compositions are disclosed that include an isocyanate-reactive component that includes a polycyclic polyether polyol that is the reaction product of a reaction mixture that includes a polycyclic polyol starter, and an alkylene oxide, as well as an isocyanate-functional component that includes a non-aromatic polyisocyanate. The polyurethane coating compositions may be particularly useful as a gel coat in the manufacture of glass fiber reinforced plastics.

Disclosed are HCFO-containing isocyanate-reactive compositions, polyurethane foam-forming compositions containing such isocyanate-reactive compositions, rigid polyurethane foams made using such polyurethane foam-forming compositions, and methods for producing such foams, including use of such foams as insulation in the construction of refrigerated storage devices. The isocyanate-reactive composition can exhibit a long shelf life, be shelf-stable, and produce a foam with good thermal insulation properties.

Aqueous dispersion comprising polyurethane or polyurethane-urea, a preparation method therefor and a use thereof. The polyurethane or polyurethane-urea is prepared by reacting raw materials comprising the following components: a compound having a tertiary amine group and at least one NCO reactive functional group, a polyester polyol having a number average molecular weight of 400 to 5000 and a functionality of 2 to 3, an organic compound having at least two isocyanate groups, a hydrophilic compound having one or more of an ionic group, a potential ionic group and a non-ionic group and having 2 to 3 NCO reactive functional groups, and a mono-functional non-ionic hydrophilic compound having at least one NCO reactive functional group. The aqueous dispersion can be stably stored for a prolonged period of time, and an adhesive prepared from the aqueous dispersion has an improved hydrolysis resistance while maintaining good bonding strength and heat resistance.

The present invention is related to decorative surface coverings, in particular floor or wall coverings, comprising one or more layer(s) and a cured top-layer, combining excellent anti-slip properties and scuff resistance. The invention is further related to a method for the preparation of said surface coverings.

A floor coating, which is prepared from 55-70% by weight of an epoxy-modified polyurethane resin, 5-10% by weight of Al.sub.2O.sub.3, 10-25% by weight of SiC, 0.4-1% by weight of a leveling agent, 0.3-1% by weight of a dispersant, 5-10% by weight of a solvent and 0.2-0.8% by weight of a curing agent. A degree of polymerization of the epoxy-modified polyurethane resin is 80-100. A scratch-resistant floor and a preparation method thereof are also disclosed herein.

Disclosed are a polyol composition using carbon dioxide, a method for preparing a polyurethane foam using the polyol composition, and a polyurethane foam prepared using the method. A method for preparing a polyurethane foam includes reacting isocyanate with a polyol composition containing a polyol compound having a synthetic polyol containing carbon dioxide, a chain extender, and a foaming agent.

An elastomeric composite polyurethane skin having an average flexural modulus, measured in accordance with ASTM D790-03, smaller than 35 MPa is disclosed. The elastomeric composite polyurethane skin includes a first aliphatic polyurethane layer made from a first polyurethane reaction mixture having at least one isocyanate compound with at least two NCO-groups which are not directly attached to an aromatic group, at least one isocyanate-reactive component (B1), and at least one catalyst component (C1) substantially free of lead, and a second aromatic polyurethane layer made from a second polyurethane reaction mixture having at least one aromatic isocyanate compound (A2), and at least one isocyanate-reactive component (B2).

A method for preparing a thermoplastic polyurethane elastomer material with micro air holes is provided. The method comprises the following steps: (1) is feeding liquid raw materials such as diisocyanate molecules and solid additives into a double-screw reactor to trigger a polymerization type chain extension reaction and then obtain a macromolecular weight hot melt. (2) is pushing the macromolecular weight hot melt into a mixing extruder and allowing the reaction to continue to obtain a macromolecular thermoplastic polyurethane melt. (3) is continuously adding the obtained macromolecular thermoplastic polyurethane melt together with polymer particles into a foaming extruder, and extruding the high-pressure hot melt from a mold head into an underwater granulation chamber. (4) is delivering the particles obtained after granulation into a separator by process water via a multi-stage pressure-release process water pipeline, separating, screening and drying the required particles to obtain the target product.

An object of the present invention is to provide a laminated polyester film that has good adhesion to an UV-curable resin, particularly has excellent adhesion to a coating agent such as an UV-curable ink, and has an excellent property to keep the adhesion at a high level over a long period of time. A laminated polyester film comprising: a polyester film; and a coating layer on at least one surface of the polyester film, the coating layer comprising a composition containing a polyurethane resin having a carboxyl group and having an acid value of 30 to 50 mgKOH/g and a crosslinking agent having a carboxyl group and having an acid value of 30 to 50 mgKOH/g.

An object of the present invention is to provide an aqueous coating composition that exhibits a small change in viscosity and can form a coating film having a superior coating film appearance even when the amount of a solvent contained in the aqueous coating composition decreases due to the change of the coating environment. The present invention provides an aqueous coating composition containing a polyurethane resin dispersion (A) and a melamine resin (B), wherein the melamine resin (B) contains a hydrophobic melamine resin, and the polyurethane resin constituting the polyurethane resin dispersion (A) has a viscosity in a range of 101 to 150,000 Pa.Math.s measured at a temperature of 25° C. and a shear rate of 0.1 sec.sup.−1.