A grain-oriented electrical steel sheet having excellent iron loss property is produced from a steel slab containing, by mass %, C: 0.002-0.15%, Si: 2.5-6.0%, Mn: 0.01-0.80%, Al: 0.010-0.050% and N: 0.003-0.020%, when: a heating rate between 500-700° C. in decarburization annealing is not less than 80° C./s, a surface roughness Ra of a work roll in final cold rolling is 0.01-3.0 μm, a total content of alkaline earth metals to MgO in annealing separator is 0-5 mass %, an average length L in rolling direction of passed crystal grains is not more than 25 mm, a ratio of crystal grains having a length in rolling direction of not more than 5 mm is 40-90%, and an existence ratio of alkaline earth metal sulfides having a size corresponding to circle of not less than 0.5 μm in a cross section of forsterite film is not more than 0.2/μm per unit length in sheet width direction.

A steel sheet has a composition comprising 0.060%≤C≤0.085%, 1.8%≤Mn≤2.0%, 0.4%≤Cr≤0.6%, 0.1%≤Si≤0.5%, 0.010%≤Nb≤0.025%, 3.42N≤Ti≤0.035%, 0≤Mo≤0.030%, 0.020%≤Al≤0.060%, 0.0012%≤B≤0.0030%, S≤0.005%, P≤0.050%, 0.002%≤N≤0.007% and optionally 0.0005%≤Ca≤0.005%, the remainder of the composition being iron and unavoidable impurities. The microstructure consists of 34% to 80% bainite, 10% to 16% martensite, and 10% to 50% of ferrite. The surface fraction of unrecrystallized ferrite, with respect to the whole structure, is of less than 30%. The martensite consists of self-tempered martensite and fresh martensite, the surface fraction of self-tempered martensite being comprised between 4% and 10%.

A method of manufacturing steel strip including the steps of: casting molten steel into slabs; reheating the slabs at 1150° C. or more for 1 hour or more; hot rolling the steel into a strip, preferably with an average F1 slab entry temperature above 1000° C.; coiling the hot rolled steel strip; batch annealing the steel strip: at an intercritical temperature (i.e. between Ac1 and Ac3), preferably below 700° C.; in non-oxidising and non-nitrogenated atmosphere; total annealing time at least 5 hours, preferably at least 10 hours to get Mn enrichment in austenite such that Mn content is at least 1.25 times bulk Mn content of the steel and C enrichment such that C content is at least 1.2 times bulk C content of the steel; cooling the steel after batch annealing in air, forced air or water quench.

A high-strength cold-rolled steel sheet and a hot-dipped galvanized steel sheet with low deviation of material properties and excellent formability, and a method for manufacturing same are provided. The present invention relates to a low-yield-ratio high-strength cold-rolled steel sheet with low deviation of directional material and excellent formability, comprising 0.05-0.15 wt % of C, 0.2-1.5 wt % of Si, 2.2-3.0 wt % of Mn, 0.001-0.10 wt % of P, 0.010 wt % or less of S, 0.01-0.10 wt % of sol.Al, 0.010 wt % or less of N, and the balance of Fe and impurities, satisfying Si/(Mn+Si)≦0.5, wherein the microstructure of the steel sheet includes 40% or more of ferrite, 10% or less of bainite, 3% or less of residual austenite, and a balance of martensite, and the area fraction of a Mn band present in the martensite phase is 5% or less.

A high strength galvanized steel sheet having excellent surface qualities, plating adhesion, and formability is provided, wherein a galvanized layer is formed on a cold-rolled steel sheet comprising 0.1-0.3 wt % of C, 1-2.5 wt % of Si, 2.5-8 wt % of Mn, 0.001-0.5 wt % of sol. Al, at most 0.04 wt % of P, at most 0.015 wt % of S, at most 0.02 wt % of N (excluding 0 wt %), 0.1-0.7 wt % of Cr, at most 0.1 wt % of Mo, (48/14)*[N] to 0.1 wt % of Ti, 0.005-0.5 wt % of Ni, 0.01-0.07 wt % of Sb, at most 0.1 wt % of Nb, and at most 0.005 wt % of B, with the remainder being Fe and other inevitable impurities.

Provided is a steel sheet and a method for manufacturing same, the steel sheet, which can be used for automobile parts and the like, having superb bendability, and excellent balance of strength and ductility and of strength and hole expansion ratio. The steel sheet includes: by wt %, C: 0.25 to 0.75%, Si: 4.0% or less, Mn: 0.9 to 5.0%, Al: 5.0% or less, P: 0.15% or less, S: 0.03% or less, N: 0.03% or less, a balance of Fe, and unavoidable impurities; and as microstructures, ferrite which is a soft structure, and tempered martensite, bainite, and retained austenite which are hard structures.

Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and hole expansion ratio and superior bending formability, and a method for manufacturing same.

A cold-rolled flat steel product for packaging materials has a thickness of less than 0.6 mm, which has been cold-rolled from steel along a rolling direction (0°) and which has an excellent isotropy with respect to its mechanical properties.

An aluminum-based plated steel sheet according to an aspect of the present invention includes: a base material; an aluminum-based plating layer located above the base material; and an intermetallic compound layer that is located between the base material and the aluminum-based plating layer and contains an intermetallic compound of Al and Fe, in which the base material has a chemical component within a predetermined range, the aluminum-based plating layer contains, on average, 80 mass % or more and 97 mass % or less of Al, 3 mass % or more and 15 mass % or less of Si, 0 mass % or more and 5 mass % or less of Zn, 0 mass % or more and 5 mass % or less of Fe, 0 mass % or more and 3 mass % or less in total of one or more selected from the group consisting of Mg and Ca, and impurities so that a total amount thereof is 100 mass %, an average value of a thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less, a maximum value of the thickness of the intermetallic compound layer is 10 μm or more and 25 μm or less, and a standard deviation of the thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less.

A cold-rolled and heat-treated steel sheet having a microstructure of, in surface fraction: between 10% and 30% of retained austenite, said retained austenite being present as films having an aspect ratio of at least 3 and as Martensite Austenite islands, less than 8% of such Martensite Austenite islands having a size above 0.5 μm, at most 10% of fresh martensite and
recovered martensite containing precipitates of at least one element chosen among niobium, titanium and vanadium. A manufacturing method thereof is also provided.