A grain-oriented electrical steel sheet having excellent iron loss property is produced from a steel slab containing, by mass %, C: 0.002-0.15%, Si: 2.5-6.0%, Mn: 0.01-0.80%, Al: 0.010-0.050% and N: 0.003-0.020%, when: a heating rate between 500-700° C. in decarburization annealing is not less than 80° C./s, a surface roughness Ra of a work roll in final cold rolling is 0.01-3.0 μm, a total content of alkaline earth metals to MgO in annealing separator is 0-5 mass %, an average length L in rolling direction of passed crystal grains is not more than 25 mm, a ratio of crystal grains having a length in rolling direction of not more than 5 mm is 40-90%, and an existence ratio of alkaline earth metal sulfides having a size corresponding to circle of not less than 0.5 μm in a cross section of forsterite film is not more than 0.2/μm per unit length in sheet width direction.

Provided is a grain-oriented electrical steel sheet having better transformer iron loss property than conventional grain-oriented electrical steel sheets. A grain-oriented electrical steel sheet comprises: a steel substrate; a forsterite film on a surface of the steel substrate; and a Cr-depleted layer at a boundary between the steel substrate and the forsterite film, the Cr-depleted layer having a Cr concentration that is 0.70 times to 0.90 times a Cr concentration of the steel substrate.

Provided is a grain-oriented electrical steel sheet that has excellent magnetic properties and can be manufactured by secondary recrystallization orientation control using coil annealing with high productivity. A grain-oriented electrical steel sheet comprises a specific chemical composition, wherein an average value of a deviation angle (α.sup.2+β.sup.2).sup.1/2 calculated from a deviation angle α from ideal Goss orientation around an ND rotation axis and a deviation angle β from ideal Goss orientation around a TD rotation axis is 5.0° or less, and an area ratio R.sub.β of crystal grains with β≤0.50° is 20% or less.

A grain-oriented electrical steel sheet includes: a base steel sheet having a predetermined chemical composition; a glass coating provided on the surface of the base steel sheet; and a tension-applying insulation coating provided on the surface of the glass coating, in which linear thermal strains having, a predetermined angle (φ) with respect to a transverse direction which is a direction orthogonal to a rolling direction are periodically formed on the surface of the tension-applying insulation coating at predetermined intervals along the rolling direction, a full width at half maximum F1 on the linear thermal strain and a full width at half maximum F2 at an intermediate position between the two linear thermal strains adjacent to each other satisfy 0.00<(F1−F2)/F2≤0.15, the width of the linear thermal strain is 10 μm or more and 300 μm or less, and in the base steel sheet, an orientation distribution angle γ around a rolling direction axis of secondary recrystallization grains, an orientation distribution angle α around an axis parallel to a normal direction, and an orientation distribution angle β around an axis perpendicular to each of the RD axis and the ND axis in units of ° satisfy 1.0≤γ≤8.0 and 0.0≤(α.sup.2+β.sup.2).sup.0.5≤10.0.

Provided is a grain-oriented electrical steel sheet which has been subjected to heat-resistant magnetic domain refining treatment and can effectively suppress carburizing and nitriding during stress relief annealing. The grain-oriented electrical steel sheet has a plurality of grooves on one side that extend linearly across the rolling direction and are lined up at intervals in the rolling direction, and has at least a forsterite film on a surface of the steel sheet, where an average thickness of the forsterite film formed on the floor of the grooves is 0.45 μm or more, and a standard deviation a of the thickness is 0.34 μm or less.

A motor comprising a steel sheet used as a core material of the motor, wherein the steel sheet includes a composition including: by mass %, 0.010% or less of C; 2.0% to 7.0% of Si; 2.0% or less of Al; 0.05% to 1.0% of Mn; 0.005% or less of S; 0.005% or less of N; and balance Fe and inevitable impurities; the steel sheet includes a magnetic flux density changing area where a change ΔB in magnetic flux density to a change ΔH=50 A/m in a magnetic field, is equal to or higher than 0.50 T; a thickness of the steel sheet is 0.05 mm to 0.20 mm; and an eddy-current loss of the steel sheet, at 1000 Hz−1.0 T, is equal to or less than 0.55 of a total iron loss.

Embodiments of the present invention comprise; annealing steel sheets (e.g., hot rolled steel sheets or thin cast strip steel); cold rolling the sheets in one or more cold rolling steps (e.g., with annealing steps between multiple cold rolling steps); and performing one or more of tension leveling, a rough rolling, or a coating process on the sheets after cold rolling, without an intermediate annealing step between the final cold rolling step and the tension leveling, the rough rolling, or the coating process, or the customer stamping or final customer annealing. In order to achieve the desired properties for the steel sheet, stamping and final annealing is performed by the customer. The new process provides an electrical steel with the similar, same, or better magnetic properties than an electrical steel manufactured using the traditional processing that utilizes an intermediate annealing step after cold rolling and before the stamping and final annealing.

A method for manufacturing a non-oriented electrical steel sheet includes a step of performing hot rolling on a steel material having a predetermined chemical composition, a step of performing first cold rolling, a step of performing process annealing, a step of performing second cold rolling, and a step of performing any one or both of final annealing and stress relief annealing. A final pass of finish rolling is performed in a temperature range equal to or higher than an Ar1 temperature, the steel sheet is held for 2 hours or less in a temperature range lower than an Ac1 temperature in the final annealing, and the steel sheet is held for 1200 sec or more in a temperature range equal to or higher than 600° C. and lower than the Ac1 temperature in the stress relief annealing.

According to an exemplary embodiment of the present invention, a method for manufacturing a grain-oriented electrical steel sheet includes: a step of hot-rolling a slab to manufacture a hot-rolled steel sheet; a step of performing hot-rolled sheet annealing on the hot-rolled steel sheet; a step of performing primary cold-rolling on the hot-rolled sheet annealed hot-rolled steel sheet; a step of performing primary decarburization annealing on the primarily cold-rolled steel sheet; a step of performing secondary cold-rolling on the decarburization-annealed steel sheet; a step of performing secondary decarburization annealing on the secondarily cold-rolled steel sheet; and a step of performing continuous annealing on the secondarily decarburization-annealed steel sheet.

An electrical steel sheet (300) is formed such that centerlines of four magnetic poles (salient poles) of a rotor core (111) coincide with a direction of easy magnetization (ED1) or (ED2). In addition, the electrical steel sheets (300) are laminated such that the directions of easy magnetization (ED1) and (ED2) are aligned.