A rare earth sintered magnet is produced by depositing a coating of rare earth-containing particles on the surface of a rare earth magnet body, and heat treating the magnet body for causing absorption and diffusion of rare earth element in the magnet body. The depositing step utilizes a particle impingement phenomenon.

A rare earth sintered magnet is produced by depositing a coating of rare earth-containing particles on the surface of a rare earth magnet body, and heat treating the magnet body for causing absorption and diffusion of rare earth element in the magnet body. The depositing step utilizes a particle impingement phenomenon.

Provide a metal surface reforming method enabling metallic products with superior characteristics such as surface hardness, heat resistance, corrosion resistance, high temperature oxidation, high temperature corrosion, and environmental corrosion and the like.

Halogenation treatment of heating and retaining a base material in an atmosphere containing a halogen based gas is performed on a base material of iron based metal or nickel based metal, then nitride processing of heating and retaining the halogenated base material described above in an atmosphere containing a nitrogen source gas is performed, then chromizing treatment is performed by placing the nitrided base material in a powder containing metal chromium powder to form a surface reformed layer on the base material described above. These metallic products obtained have high hardness, superior heat resistance and corrosion resistance, and exhibit superior performance in high temperature oxidation, high temperature corrosion, erosion, and cavitation and the like environments. Further, the metallic products described above exhibit superior performance in acid or alkali environments, neutral environments, and corrosive environments such as chlorides like salt water.

Treated articles and a process of producing the treated articles, systems having treated articles, and processes incorporating treated articles are disclosed. The treated articles include a metal or metallic substrate, and a surface treatment of the metal or metallic substrate, the surface treatment having fluorine, silicon, and carbon. The systems include a flow path, with the surface treatment being within the flow path. The processes include flowing a fluid through the flow path.

The invention relates to a method for coating a component, which is provided for the hot gas duct of a turbomachine, wherein the coating material is applied onto the uncoated component surface in the form of particles in mixture with a binding agent, and the component with the particle-treated binding agent thereupon then undergoes thermal treatment in such a way that the binding agent is released and the coating material remains on the component.

The invention relates to a method for coating a component, which is provided for the hot gas duct of a turbomachine, wherein the coating material is applied onto the uncoated component surface in the form of particles in mixture with a binding agent, and the component with the particle-treated binding agent thereupon then undergoes thermal treatment in such a way that the binding agent is released and the coating material remains on the component.

A method for producing a surface-hardened material, comprising: an immersion step of immersing an iron steel material having nitrogen attached in the form of a solid solution on the surface thereof in a melt containing a chloride at a temperature ranging from 650° C. to 900° C.; and a cooling step of cooling the immersed iron steel material to a temperature equal to or lower than a martensitic transformation start temperature at a cooling rate equal to or higher than a lower critical cooling rare at which martensitic transformation starts.

An electrode wire for use in an electrical discharge machining apparatus includes a metallic core and a layer of gamma phase brass disposed over the metallic core. Particles of beta phase brass are interspersed within the gamma phase brass layer. An oxide layer including zinc is disposed over the gamma phase brass layer.

An electrode wire for use in an electrical discharge machining apparatus includes a metallic core and a layer of gamma phase brass disposed over the metallic core. Particles of beta phase brass are interspersed within the gamma phase brass layer. An oxide layer including zinc is disposed over the gamma phase brass layer.

A method of hardening a surface of a ferro-alloy object, the method comprising at least partially gasifying a carbon-containing polymer to form a hardening material source; and exposing the object to the hardening material source, such that the hardening material source and the surface of the object react, thereby hardening the surface of the object.