Forming a lithium lanthanum zirconate thin film includes disposing zirconium oxide on a substrate to yield a zirconium oxide coating, contacting the zirconium oxide coating with a solution including a lithium salt and a lanthanum salt, heating the substrate to yield a dried salt coating on the zirconium oxide coating, melting the dried salt coating to yield a molten salt mixture, reacting the molten salt mixture with the zirconium oxide coating to yield lithium lanthanum zirconate, and cooling the lithium lanthanum zirconate to yield a lithium lanthanum zirconate coating on the substrate. In some cases, the zirconium oxide coating is contacted with an aqueous molten salt mixture including a lithium salt and a lanthanum salt, the molten salt mixture is reacted with the zirconium oxide coating to yield lithium lanthanum zirconate, and the lithium lanthanum zirconate is cooled to yield a lithium lanthanum zirconate coating on the substrate.

Forming a lithium lanthanum zirconate thin film includes disposing zirconium oxide on a substrate to yield a zirconium oxide coating, contacting the zirconium oxide coating with a solution including a lithium salt and a lanthanum salt, heating the substrate to yield a dried salt coating on the zirconium oxide coating, melting the dried salt coating to yield a molten salt mixture, reacting the molten salt mixture with the zirconium oxide coating to yield lithium lanthanum zirconate, and cooling the lithium lanthanum zirconate to yield a lithium lanthanum zirconate coating on the substrate. In some cases, the zirconium oxide coating is contacted with an aqueous molten salt mixture including a lithium salt and a lanthanum salt, the molten salt mixture is reacted with the zirconium oxide coating to yield lithium lanthanum zirconate, and the lithium lanthanum zirconate is cooled to yield a lithium lanthanum zirconate coating on the substrate.

Forming a lithium lanthanum zirconate thin film includes disposing zirconium oxide on a substrate to yield a zirconium oxide coating, contacting the zirconium oxide coating with a solution including a lithium salt and a lanthanum salt, heating the substrate to yield a dried salt coating on the zirconium oxide coating, melting the dried salt coating to yield a molten salt mixture, reacting the molten salt mixture with the zirconium oxide coating to yield lithium lanthanum zirconate, and cooling the lithium lanthanum zirconate to yield a lithium lanthanum zirconate coating on the substrate. In some cases, the zirconium oxide coating is contacted with an aqueous molten salt mixture including a lithium salt and a lanthanum salt, the molten salt mixture is reacted with the zirconium oxide coating to yield lithium lanthanum zirconate, and the lithium lanthanum zirconate is cooled to yield a lithium lanthanum zirconate coating on the substrate.

Forming a lithium lanthanum zirconate thin film includes disposing zirconium oxide on a substrate to yield a zirconium oxide coating, contacting the zirconium oxide coating with a solution including a lithium salt and a lanthanum salt, heating the substrate to yield a dried salt coating on the zirconium oxide coating, melting the dried salt coating to yield a molten salt mixture, reacting the molten salt mixture with the zirconium oxide coating to yield lithium lanthanum zirconate, and cooling the lithium lanthanum zirconate to yield a lithium lanthanum zirconate coating on the substrate. In some cases, the zirconium oxide coating is contacted with an aqueous molten salt mixture including a lithium salt and a lanthanum salt, the molten salt mixture is reacted with the zirconium oxide coating to yield lithium lanthanum zirconate, and the lithium lanthanum zirconate is cooled to yield a lithium lanthanum zirconate coating on the substrate.

Forming a lithium lanthanum zirconate thin film includes disposing zirconium oxide on a substrate to yield a zirconium oxide coating, contacting the zirconium oxide coating with a solution including a lithium salt and a lanthanum salt, heating the substrate to yield a dried salt coating on the zirconium oxide coating, melting the dried salt coating to yield a molten salt mixture, reacting the molten salt mixture with the zirconium oxide coating to yield lithium lanthanum zirconate, and cooling the lithium lanthanum zirconate to yield a lithium lanthanum zirconate coating on the substrate. In some cases, the zirconium oxide coating is contacted with an aqueous molten salt mixture including a lithium salt and a lanthanum salt, the molten salt mixture is reacted with the zirconium oxide coating to yield lithium lanthanum zirconate, and the lithium lanthanum zirconate is cooled to yield a lithium lanthanum zirconate coating on the substrate.

Forming a lithium lanthanum zirconate thin film includes disposing zirconium oxide on a substrate to yield a zirconium oxide coating, contacting the zirconium oxide coating with a solution including a lithium salt and a lanthanum salt, heating the substrate to yield a dried salt coating on the zirconium oxide coating, melting the dried salt coating to yield a molten salt mixture, reacting the molten salt mixture with the zirconium oxide coating to yield lithium lanthanum zirconate, and cooling the lithium lanthanum zirconate to yield a lithium lanthanum zirconate coating on the substrate. In some cases, the zirconium oxide coating is contacted with an aqueous molten salt mixture including a lithium salt and a lanthanum salt, the molten salt mixture is reacted with the zirconium oxide coating to yield lithium lanthanum zirconate, and the lithium lanthanum zirconate is cooled to yield a lithium lanthanum zirconate coating on the substrate.

A method of forming an airfoil includes the steps of depositing material to form an airfoil in a first layer, and then depositing material in a second layer on the first layer. The first and second layers have distinct densities. An airfoil is also disclosed. The method provides powerful design advantages.

A method of forming an airfoil includes the steps of depositing material to form an airfoil in a first layer, and then depositing material in a second layer on the first layer. The first and second layers have distinct densities. An airfoil is also disclosed. The method provides powerful design advantages.

Forming a lithium lanthanum zirconate thin film includes disposing zirconium oxide on a substrate to yield a zirconium oxide coating, contacting the zirconium oxide coating with a solution including a lithium salt and a lanthanum salt, heating the substrate to yield a dried salt coating on the zirconium oxide coating, melting the dried salt coating to yield a molten salt mixture, reacting the molten salt mixture with the zirconium oxide coating to yield lithium lanthanum zirconate, and cooling the lithium lanthanum zirconate to yield a lithium lanthanum zirconate coating on the substrate. In some cases, the zirconium oxide coating is contacted with an aqueous molten salt mixture including a lithium salt and a lanthanum salt, the molten salt mixture is reacted with the zirconium oxide coating to yield lithium lanthanum zirconate, and the lithium lanthanum zirconate is cooled to yield a lithium lanthanum zirconate coating on the substrate.

A method for enhancing corrosion resistance of a solid material exposed to a liquid. The method includes providing a solid material which can form a solid product layer when exposed to the corrosive liquid, and maintaining the concentration of the solid product material in the liquid either at saturation or elevated level. A materials system containing a solid material capable of forming a solid product layer when exposed to air or a liquid environment containing dissolved oxygen at levels sufficient for oxidation of at least one constituent of the solid material, wherein the solid product layer is in contact with a liquid containing an elevated or saturated concentration of the dissolved solid product layer. A corrosion-resistant device containing a solid material with a solid-product layer exposed to a molten salt solution, wherein the concentration of the solid-product dissolved in the molten salt solution is at saturation or elevated level.