A pre-coated steel sheet wherein at least a region at the periphery (7) of at least one (6a,6b) of the opposite faces (6a,6b) of said pre-coated sheet (1,1′) is coated with an additional coating (8) selected for increasing the vapor pressure between the pre-coating (2) and said additional coating (8) during a laser welding method up to a critical pressure at which the pre-coating (2) is ejected away from the weld (14). Preferably, the vaporization temperature of the additional coating (8) is greater than the vaporization temperature of the pre-coating (2) and the additional coating includes gammagene elements like carbon and/or nickel. A steel part obtained by laser welding, preferably butt laser welding, of at least a first and second pre-coated steel sheet (1,1′) as above indicated is also provided.

Provided is a surface-treated copper foil in which in order to avoid failures of electronic parts by corrosion, a high bond strength between an electrolytic copper foil and a resin base material can be maintained even when the surface-treated copper foil is exposed to corrosive gases and microparticles, and a method for manufacturing the same. The surface-treated copper foil of the present invention comprises an electrolytic copper foil, a roughened layer covering at least one surface side of the electrolytic copper foil, and a rust preventive layer further covering the roughened layer, wherein the rust preventive layer is at least one surface of the surface-treated copper foil; the rust preventive layer comprises at least a nickel layer; and the thickness of the nickel layer is 0.8 to 4.4 g/m.sup.2 in terms of mass per unit area of nickel; and the noncontact roughness Spd of the rust preventive layer is 1.4 to 2.6 peaks/μm.sup.2 and the surface roughness RzJIS of the rust preventive layer is 1.0 to 2.5 μm. The method for manufacturing the surface-treated copper foil forms the roughened layer having higher roughnesses than the noncontact roughness Spd and surface roughness RzJIS on one surface of the electrolytic copper foil, and thereafter forming the rust preventive layer meeting the predetermined condition.

A method comprising: cold-spraying a surface of a substrate with a bond material to form a bond coating; and cold-spraying a surface of the bond coating with a coating material to form a top coating. The bond material is different from the coating material and harder than the surface of the substrate.

A wind turbine blade includes a base member formed of FRP and having a blade shape, an intermediate layer arranged on the base member and formed of metal, cermet, ceramic, or a mixture of at least one thereof and resin as a major constituent, and an erosion-resistant overcoat arranged on the intermediate layer and formed of a spray film having a porosity of 5% or lower.

Methods of forming memory structures are discussed. Specifically, methods of forming 3D NAND devices are discussed. Some embodiments form memory structures with a metal nitride barrier layer, an α-tungsten layer, and a bulk metal material. The barrier layer comprises a TiXN or TaXN material, where X comprises a metal selected from one or more of aluminum (Al), silicon (Si), tungsten (W), lanthanum (La), yttrium (Yt), strontium (Sr), or magnesium (Mg).

A high-performance thermoformed component provided with a coating, and a manufacturing method therefor. The thermoformed component comprises a substrate and a coating thereon. The substrate comprises the following ingredients in percentage by weight: 0.01-0.8% of C, 0.05-1.0% of Si, 0.1-5% of Mn, 0.001-0.3% of P, 0.001-0.1% of S, 0.001-0.3% of Al, 0.001-0.5% of Ti, 0.0005-0.1% of B, 0.001-0.5% of Nb, 0.001-0.5% of V, and the remainder being Fe and other unavoidable impurities. The appearance of the thermoformed component has no color difference and no mottling. The surface oxygen content of the thermoformed component is 0.1-20 wt. %, and the ratio of the standard deviation to the average value of the surface oxygen content satisfies: 0<standard deviation of oxygen content/average value of oxygen content ≤0.3. In the manufacturing method, a coated steel plate that has undergone heat treatment, transfer processing, and hot stamping is not treated with oil.

A method for manufacturing a laminated tinplate for packaging applications, the laminated tinplate including a tinplate sheet and a thermoplastic laminate layer that covers at least one side of the tinplate steel sheet, to a laminated tinplate produced thereby and use thereof in a process to produce containers for packaging purposes.

The present invention relates to a steel sheet with improved yellowing resistance and phosphatability, wherein the steel sheet contains 0.5% by weight or more of Mn, and contains 0.01 to 10 mg/m.sup.2 of Ca+Mg, 0.01 to 10 mg/m.sup.2 of P, 0.01 to 20 mg/m.sup.2 of C, and 0.05 to 30 mg/m.sup.2 of O as components excluding a steel component on the surface of the steel sheet after pickling, water rinsing, and drying. According to the present invention, in a manufacturing process of the steel sheet, the surface of the steel sheet is subjected to a chemical conversion treatment for improving phosphatability and yellowing resistance in a water-cooling section or a water-washing section, thereby having an effect of improving the surface quality of products using same and various subsequently treated products.

A coated steel sheet has a coating film on at least one side of a plated steel sheet. The coating film contains a binder resin, non-oxide ceramic particles containing V (excluding VC particles), and doped zinc oxide particles. The respective contents of the non-oxide ceramic particles containing V and the doped zinc oxide particles relative to the coating film satisfy the expressions: [(1) C.sub.Zn≥10.0, (2) C.sub.V≤0.5.Math.C.sub.Zn, (3) C.sub.V≤70−C.sub.Zn, (4) C.sub.V≥0.125.Math.C.sub.Zn, and (5) C.sub.V≥2.0], where C.sub.V represents the content (mass %) of the non-oxide ceramic particles containing V, and C.sub.Zn represents the content (mass %) of the doped zinc oxide particles. The coated steel sheet is excellent in both corrosion resistance before electrodeposition coating, and weldability.

To provide a sliding member, such as a piston ring for an internal combustion engine, having low friction and excellent toughness. The above-described problem is solved by a sliding member (10) such as a piston ring coated with a Cr—B—Ti—V—(Mn, Mo)—N-based alloy film (2) on a sliding surface (11) thereof, and configured so that the alloy film (2) contains one or both of Mn and Mo and has a total content of the Mn and the Mo within a range of 2 mass % or less. Preferably, a B content is within a range of 0.1 mass % to 1.5 mass %, inclusive, a V content is within a range of 0.05 mass % to 1 mass %, inclusive, and a Ti content is within a range of 0.05 mass % to 1.5 mass %, inclusive.