An interior trim part made by a method that includes the steps of bringing a fiber web onto a conveyor, needlepunching the fiber web to form a base in contact with the conveyor, and introducing a binder component on the base. The binder component introduced on the base is a thermoplastic polymer in solid form. The method includes a step for heating the base to cause the thermoplastic polymer making up the binder component to penetrate the base over a thickness smaller than the thickness of the base.

An interior trim part made by a method that includes the steps of bringing a fiber web onto a conveyor, needlepunching the fiber web to form a base in contact with the conveyor, and introducing a binder component on the base. The binder component introduced on the base is a thermoplastic polymer in solid form. The method includes a step for heating the base to cause the thermoplastic polymer making up the binder component to penetrate the base over a thickness smaller than the thickness of the base.

Articles, such as sanitary tissue products, including fibrous structures, and more particularly articles including fibrous structures having a plurality of fibrous elements wherein the article exhibits differential cellulose content throughout the thickness of the article and methods for making same are provided.

Articles, such as sanitary tissue products, including fibrous structures, and more particularly articles including fibrous structures having a plurality of fibrous elements wherein the article exhibits differential cellulose content throughout the thickness of the article and methods for making same are provided.

A sheet manufacturing method includes: a defibrating step of defibrating a raw material containing a fiber in air; a mixing step of mixing a defibrated material defibrated in the defibrating step and a resin in air; a web forming step of forming a web by accumulating the mixture mixed in the mixing step on a moving body; a transporting step of transporting the web; a sheet forming step of forming a sheet from the web; a setting step of setting a thickness of the sheet; and a control step of controlling a moving speed of the moving body and a transporting speed of the web in the transporting step, in accordance with the thickness of the sheet set in the setting step.

A sheet manufacturing method includes: a defibrating step of defibrating a raw material containing a fiber in air; a mixing step of mixing a defibrated material defibrated in the defibrating step and a resin in air; a web forming step of forming a web by accumulating the mixture mixed in the mixing step on a moving body; a transporting step of transporting the web; a sheet forming step of forming a sheet from the web; a setting step of setting a thickness of the sheet; and a control step of controlling a moving speed of the moving body and a transporting speed of the web in the transporting step, in accordance with the thickness of the sheet set in the setting step.

A method for manufacturing a compact includes a mixing step of mixing a fiber and a powder of a binder to obtain a mixture; an accumulating step of accumulating the mixture to form a web; a humidifying step of adding water to the web; and a forming step of heating and pressurizing the water-added web to obtain a compact. The binder binds between fiber molecules by the addition of water. The powder has an average particle diameter (D50) of 20.0 μm or less.

A method for manufacturing a compact includes a mixing step of mixing a fiber and a powder of a binder to obtain a mixture; an accumulating step of accumulating the mixture to form a web; a humidifying step of adding water to the web; and a forming step of heating and pressurizing the water-added web to obtain a compact. The binder binds between fiber molecules by the addition of water. The powder has an average particle diameter (D50) of 20.0 μm or less.

An insulating product includes mineral fibers of aluminosilicate glass including aluminum oxide, Al.sub.2O.sub.3, in a fraction by weight of between 14% and 28%, that are sized with a sizing composition including the following constituents within the limits defined below, expressed as fractions by weight with respect to the total weight of the composition: from 80% to 98% of water, from 2% to 20% of water-soluble poly(furfuryl alcohol), which is obtained by polycondensation of furfuryl alcohol, and less than 0.5% of furfuryl alcohol, wherein a sum of the fractions by weight of the poly (furfuryl alcohol) and of the water is at least 95%, and wherein the sizing composition applied to the mineral fibres has a pH in a range from 5 to 8.

Articles, such as sanitary tissue products, including fibrous structures, and more particularly articles including fibrous structures having a plurality of fibrous elements wherein the article exhibits differential cellulose content throughout the thickness of the article and methods for making same are provided.