A temporary fixing composition is provided that is used to temporarily fix a first bonding target material and a second bonding target material to each other before the two bonding target materials are bonded to each other. The temporary fixing composition contains a first organic component having a viscosity of less than 70 mPa.Math.s at 25° C. and a boiling point of 200° C. or lower and a second organic component having a viscosity of 70 mPa.Math.s or greater at 25° C. and a boiling point of 210° C. or higher. It is preferable that, when thermogravimetry-differential thermal analysis is performed under the conditions at a temperature increase rate of 10° C./min in a nitrogen atmosphere with a sample mass of 30 mg, the 95% mass reduction temperature is lower than 300° C.

A light-emitting device includes: a light-emitting element including a first surface provided as a light extraction surface, a second surface opposite to the first surface, a plurality of third surfaces between the first surface and the second surface, and a positive electrode and a negative electrode at the second surface; a light-transmissive member disposed at the first surface; and a bonding member disposed between the light-emitting element and the light-transmissive member and covering from the first surface to the plurality of third surfaces of the light-emitting element to bond the light-emitting element and the light-transmissive member. The bonding member is made of a resin that contains nanoparticles. The nanoparticles have a particle diameter of 1 nm or more and 30 nm or less and a content of 10 mass % or more and 20 mass % or less.

A dicing die attach film including a dicing film and a die attach film laminated on the dicing film, in which the die attach film has an arithmetic average roughness Ra1 of from 0.05 to 2.50 μm at a surface in contact with the dicing film, and a value of ratio of Ra1 to an arithmetic average roughness Ra2 at a surface that is of the die attach film and is opposite to the surface in contact with the dicing film is from 1.05 to 28.00.

A silver sintering preparation in the form of a silver sintering paste comprising 70 to 95 wt.-% of coated silver particles (A) and 5 to 30 wt.-% of organic solvent (B) or in the form of a silver sintering preform comprising 74.5 to 100 wt.-% of coated silver particles (A) and 0 to 0.5 wt.-% of organic solvent (B), wherein the coating of the coated silver particles (A) comprises silver acetylacetonate (silver 2,4-pentanedionate) and/or at least one silver salt of the formula C.sub.nH.sub.2n+1COOAg with n being an integer in the range of 7 to 10, and wherein the at least one silver salt is thermally decomposable at >160° C.

A thermosetting sheet according to the present invention includes a thermosetting resin and a thermoplastic resin, in which a thickness change rate when a temperature is changed from 25° C. to 200° C. is 0% or more and 10% or less.

A thermosetting sheet according to the present invention includes: a thermosetting resin; a thermoplastic resin; and conductive particles. The conductive particles includes silver particles having an average particle size D.sub.50 of 0.01 μm or more and 10 μm or less, and having a circularity in cross section of 0.7 or more. The thermosetting sheet has a viscosity at 100° C. of 20 kPa.Math.s or more and 3000 kPa.Math.s or less.

A dicing die bonding film according to the present invention includes: a dicing tape including a base layer and an adhesive layer laminated on the base layer; and a die bonding layer laminated on the adhesive layer of the deicing tape; the die bonding layer including a matrix resin, a thiol-group-containing compound, and conductive particles.

Provided in the present invention is a thermosetting sheet including a thermosetting resin, a thermoplastic resin, a volatile component, and conductive particles. The thermosetting sheet has an arithmetic average roughness Ra of 0.1 μm or more and 1.2 μm or less that is measured in a state before being cured.

There is provided a bonding paste capable of forming a uniform bonding layer by reducing occurrence of voids at edges even when a bonding area is large, and bonding method using the paste, and provides a metal paste for bonding containing at least metal nanoparticles (A) having a number average primary particle size of 10 to 100 nm, wherein a cumulative weight loss value (L.sub.100) when a temperature is raised from 40° C. to 100° C. is 75 or less, and a cumulative weight loss value (L.sub.150) when a temperature is raised from 40° C. to 150° C. is 90 or more, and a cumulative weight loss value (L.sub.200) when a temperature is raised from 40° C. to 200° C. is 98 or more, based on 100 cumulative weight loss value (L.sub.700) when the paste is heated from 40° C. to 700° C. at a heating rate of 3° C./min in a nitrogen atmosphere.

Provided is a metal paste for joints, containing: metal particles; and linear or branched monovalent aliphatic alcohol having 1 to 20 carbon atoms, in which the metal particles include sub-micro copper particles having a volume average particle diameter of 0.12 μm to 0.8 μM.