In a copper alloy bonding wire for semiconductor devices, the bonding longevity of a ball bonded part under high-temperature and high-humidity environments is improved. The copper alloy bonding wire for semiconductor devices includes in total 0.03% by mass or more to 3% by mass or less of at least one or more kinds of elements selected from Ni, Zn, Ga, Ge, Rh, In, Ir, and Pt (first element), with the balance Cu and inevitable impurities. The inclusion of a predetermined amount of the first element suppresses production of an intermetallic compound susceptible to corrosion under high-temperature and high-humidity environments at the wire bonding interface and improves the bonding longevity of a ball bonded part.

There is provided a bonding wire for semiconductor devices that exhibits a favorable bondability even when being applied to wedge bonding at the room temperature, and also achieves an excellent bond reliability. The bonding wire includes a core material of Cu or Cu alloy (hereinafter referred to as a “Cu core material”), and a coating containing a noble metal formed on a surface of the Cu core material. A concentration of Cu at a surface of the wire is 30 to 80 at%.

An SiC semiconductor device includes an SiC chip having a first main surface at one side and a second main surface at another side, a first main surface electrode including a first Al layer and formed on the first main surface, a pad electrode formed on the first main surface electrode and to be connected to a lead wire, and a second main surface electrode including a second Al layer and formed on the second main surface.

An SiC semiconductor device includes an SiC chip having a first main surface at one side and a second main surface at another side, a first main surface electrode including a first Al layer and formed on the first main surface, a pad electrode formed on the first main surface electrode and to be connected to a lead wire, and a second main surface electrode including a second Al layer and formed on the second main surface.

In a copper alloy bonding wire for semiconductor devices, the bonding longevity of a ball bonded part under high-temperature and high-humidity environments is improved. The copper alloy bonding wire for semiconductor devices includes in total 0.03% by mass or more to 3% by mass or less of at least one or more kinds of elements selected from Ni, Zn, Ga, Ge, Rh, In, Ir, and Pt (first element), with the balance Cu and inevitable impurities. The inclusion of a predetermined amount of the first element suppresses production of an intermetallic compound susceptible to corrosion under high-temperature and high-humidity environments at the wire bonding interface and improves the bonding longevity of a ball bonded part.

A bonding wire for a semiconductor device, characterized in that the bonding wire includes a Cu alloy core material and a Pd coating layer formed on a surface of the Cu alloy core material, the bonding wire contains an element that provides bonding reliability in a high-temperature environment, and a strength ratio defined by the following Equation (1) is 1.1 to 1.6:
Strength ratio=ultimate strength/0.2% offset yield strength.(1)

A bonding wire includes a Cu alloy core material, and a Pd coating layer formed on the Cu alloy core material. The bonding wire contains at least one element selected from Ni, Zn, Rh, In, Ir, and Pt. A concentration of the elements in total relative to the entire wire is 0.03% by mass or more and 2% by mass or less. When measuring crystal orientations on a cross-section of the core material in a direction perpendicular to a wire axis of the bonding wire, a crystal orientation <100> angled at 15 degrees or less to a wire axis direction has a proportion of 50% or more among crystal orientations in the wire axis direction. An average crystal grain size in the cross-section of the core material in the direction perpendicular to the wire axis of the bonding wire is 0.9 m or more and 1.3 m or less.

An SiC semiconductor device includes an SiC chip having a first main surface at one side and a second main surface at another side, a first main surface electrode including a first Al layer and formed on the first main surface, a pad electrode formed on the first main surface electrode and to be connected to a lead wire, and a second main surface electrode including a second Al layer and formed on the second main surface.

An SiC semiconductor device includes an SiC chip having a first main surface at one side and a second main surface at another side, a first main surface electrode including a first Al layer and formed on the first main surface, a pad electrode formed on the first main surface electrode and to be connected to a lead wire, and a second main surface electrode including a second Al layer and formed on the second main surface.

A bonding wire for a semiconductor device includes a Cu alloy core material and a Pd coating layer formed on a surface thereof. Containing an element that provides bonding reliability in a high-temperature environment improves the bonding reliability of the ball bonded part in high temperature. Furthermore, making an orientation proportion of a crystal orientation <100> angled at 15 degrees or less to a wire longitudinal direction among crystal orientations in the wire longitudinal direction 30% or more when measuring crystal orientations on a cross-section of the core material in a direction perpendicular to a wire axis of the bonding wire, and making an average crystal grain size in the cross-section of the core material in the direction perpendicular to the wire axis of the bonding wire 0.9 to 1.5 m provides a strength ratio of 1.6 or less.