A process for manufacturing a coated metal strip having a metallic corrosion protection coating is provided. The process includes passing a metal strip through a molten metal bath comprising from 2 to 8 wt % aluminum, 0 to 5 wt % magnesium, up to 0.3 wt % additional elements, and a balance including zinc and inevitable impurities, to yield a molten metal coated metal strip, wiping the molten metal coated metal strip with a nozzle spraying a gas on either side of the molten metal coated metal strip and cooling the coating in a controlled manner until the coating has completely solidified, to obtain the coated metal strip. A temperature of the molten metal bath is from 350 to 700° C., and the cooling is conducted at a rate less than 15° C./s between a temperature on leaving a unit where the wiping occurs and a start of solidification of the coating, and then at a rate greater than or equal to 15° C./s between a start and an end of solidification of the coating.

Provided is a plated steel material which can be used for an automobile, a household appliance, a building material, and the like and, more particularly, to a zinc alloy plated steel material having excellent corrosion resistance after being processed and a method for manufacturing the same.

The present invention provides a nickel-plated heat-treated steel sheet for a battery can (1), having a nickel layer with a nickel amount of 4.4 to 26.7 g/m.sup.2 on a steel sheet (11), wherein when the Fe intensity and the Ni intensity are continuously measured along the depth direction from the surface of the nickel-plated heat-treated steel sheet for a battery can, by using a high frequency glow discharge optical emission spectrometric analyzer, the difference (D2-D1) between the depth (D1) at which the Fe intensity exhibits a first predetermined value and the depth (D2) at which the Ni intensity exhibits a second predetermined value is less than 0.04 μm.

A plated steel includes: a steel; and a plating layer that is provided on a surface of the steel, in which the plating layer includes, by mass %, Al: 5.00% to 35.00%, Mg: 2.50% to 13.00%, Fe: 5.00% to 40.00%, Si: 0% to 2.00%, Ca: 0% to 2.00%, and a remainder of Zn and impurities, and in a cross section of the plating layer, the area fraction of a Zn solid-solution Fe.sub.2Al.sub.5 phase in which 5% or more of Zn is solid-soluted is 10% to 60% and the area fraction of a MgZn.sub.2 phase is 10% to 90%.

A flat steel product for hot forming may be produced from a steel substrate that includes a steel comprising 0.1-3% by weight Mn and up to 0.01% by weight B, along with a protective coating that is applied to the steel substrate. The protective coating may be based on Al and may contain up to 20% by weight of other alloy elements. Also disclosed are methods for producing such flat steel products, steel components, and methods for producing steel components. Absorption of hydrogen is minimized during heating necessary for hot forming. This is achieved at least in part through an alloy constituent of 0.1-0.5% by weight of at least one alkaline earth or transition metal in the protective coating, wherein an oxide of the alkaline earth or transition metal is formed on an outer surface of the protective coating during hot forming of the flat steel product.

Provided is a plated steel sheet applicable for various purposes as in construction materials, household electric appliances, automobiles, etc. and, more particularly, to a hot dip plated steel sheet having excellent corrosion resistance and workability and a manufacturing method therefor.

A coated steel material including: a base steel, and a coating layer containing a Zn—Al—Mg alloy layer disposed on a surface of the base steel, wherein the coating layer has a predetermined chemical composition, and, in a backscattered electron image of the Zn—Al—Mg alloy layer that is obtained at a time of observing the surface of the Zn—Al—Mg alloy layer after polishing to ½ of the layer thickness, under a scanning electron microscope at a magnification of 100×, Al crystals are present, and the average value of the cumulative circumferential length of the Al crystals is 88 to 195 mm/mm.sup.2.

An embodiment relates to an ultrasonic additive manufacturing process, comprising joining a foil comprising a bulk metallic glass to a substrate; and forming a cladded composite comprising the foil and the substrate; wherein a thickness of the cladded composite is greater than a critical casting thickness of the bulk metallic glass, wherein the cladded composite comprises a cladding layer of the bulk metallic glass on the substrate and the bulk metallic glass comprises approximately 0% crystallinity, approximately 0% porosity, less than 50 MPa thermal stress, approximately 0% distortion, approximately 0 inch heat affected zone, approximately 0% dilution, and a strength of about 2,000-3,500 MPa.

An Al—Zn—Si—Mg alloy coated strip that has Mg.sub.2Si particles in the coating microstructure is disclosed. The distribution of Mg.sub.2Si particles is such that the surface of the coating has only a small proportion of Mg.sub.2Si particles or is at least substantially free of any Mg.sub.2Si particles.

The present invention relates to a high manganese steel for low temperature applications and a method for manufacturing the same. The high manganese steel contains 0.3 wt % to 0.8 wt % of C, 18 wt % to 26 wt % of Mn, 0.01 wt % to 1 wt % of Si, 0.01 wt % to 0.5 wt % of Al, 0.1 wt % or less of Ti (excluding 0%), 1 wt % to 4.5 wt % of Cr, 0.1 wt % to 0.9 wt % of Cu, 0.03 wt % or less of S (excluding 0%), 0.3 wt % or less of P (excluding 0%), 0.001 wt % to 0.03 wt % of N, 0.004 wt % or less of B (excluding 0%), and a remainder of Fe and other inevitable impurities, wherein a microstructure comprises an austenite single phase structure, and an average grain size of the austenite is 50 μm or less.