Reinforced structure having continuous fiber reinforced elements and method of making thereof

Abstract

Disclosed are reinforced structures. The structures are comprised of reinforced elements that have continuous fibers embedded in a matrix material. The reinforced elements are combined in a matrix material to form a desired shape of reinforced structure.

Claims

1. A method of forming a reinforced structure with a tubular cross-sectional profile, comprising: forming at least two arc segments of a diameter (D) of a tubular cross-section; wherein each arc segment is a fiber-reinforced element comprising continuous fiber-reinforcing filaments and a first matrix material, wherein the continuous fiber-reinforcing filaments are embedded along a longitudinal axis of the fiber-reinforced element in the first matrix material to form a continuous fiber-reinforced element, forming a tubular arrangement of a reinforced structure with the at least two arc segments; and winding a layer around and on an outer surface of the formed tubular arrangement, wherein the winding layer is unidirectional reinforced thermoplastic tape or unidirectional reinforced thermosetting tape.

2. The method of forming the reinforced structure according to claim 1, wherein edges of adjacent arc segments are in contact and adhered to one another at contact locations.

3. The method of forming the reinforced structure according to claim 1, wherein the arc segments are interlocking elements to adhere to one another.

4. The method of forming the reinforced structure according to claim 1, wherein there is a gap between edges of adjacent arc segments forming the tubular arrangement, and applying a matrix material on an outside surface of the arc segments, the matrix material filling the gaps.

5. The method of forming the reinforced structure according to claim 1, comprising: winding the winding layer under a pretension with a defined winding feed width and rotation; and heating the winding layer to melt a matrix of the tape and heat the tubular arrangement.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 illustrates a cross-sectional profile of a fiber-reinforced element having a circular cross-section.

(2) FIG. 2 illustrates a cross-sectional profile of a fiber-reinforced element having a rectangular cross-section.

(3) FIG. 3 illustrates a cross-section of a woven fiber-reinforced element.

(4) FIGS. 4A-4D illustrate examples of cross-sectional shapes of structural elements comprised of fiber-reinforced elements.

(5) FIG. 5 illustrates a cross-sectional profile of a continuous fiber-reinforced interlocking element.

(6) FIG. 6 illustrates a detail of a cross-sectional shape of a structural tubular element including at least two interlocking fiber-reinforced elements of FIG. 5.

(7) FIG. 7 illustrates a cross-section of a fiber-reinforced element having an arc segment profile.

(8) FIG. 8 illustrates a cross-sectional profile of a first reinforced tubular structure using the elements of FIG. 7 in combination with a layer of reinforcement.

(9) FIG. 9 illustrates a cross-sectional profile of a second reinforced tubular structure using the elements of FIG. 7 in combination with a layer of reinforcement.

(10) FIGS. 10A-10B illustrate a mechanism for applying a hoop layer to fix several fiber-reinforced elements having an arc segment profile to achieve a reinforced tubular structure.

DETAILED DESCRIPTION

(11) Terms “comprising” and “comprises” in this disclosure can mean “including”, “includes” or “having” or can have the meaning commonly given to the term “comprising” or “comprises” in U.S. Patent Law. Terms “consisting essentially of” or “consists essentially of” if used in the claims have the meaning ascribed to them in U.S. Patent Law. Other aspects of the invention are described in or are obvious from (and within the ambit of the invention) the following disclosure.

(12) The terms “threads”, “fibers”, “filaments”, and “yarns” are used interchangeably in the following description. “Threads”, “fibers”, “filaments”, and “yarns” as used herein can refer to monofilaments, multifilament yarns, twisted yarns, multifilament tows, textured yarns, braided yarns, coated yarns, bicomponent yarns, as well as yarns made of any material known to those ordinarily skilled in the art. Yarns can be made of carbon, fiberglass, cotton, aramid, polyamide, polyester, metal, polyethylene, and/or other materials that exhibit desired physical, thermal, chemical or other properties.

(13) The terms “embedded” and “encapsulated” are used interchangeably.

(14) Fiber-reinforced structures according to the disclosure may be characterized in that the profile cross-section is filled with the continuous fiber-reinforced elements in order to enhance mechanical properties such as strength and rigidity. In a particular application, such fiber-reinforced structures can provide a cross-sectional profile for support members such as connecting rods or tension and compression struts, in which a strut with the largest possible external dimensions may be achieved within a predetermined installation space.

(15) FIG. 1 illustrates a cross-sectional profile of a fiber-reinforced element 100. A circular cross-sectional shape is illustrated but other cross-sectional shapes are contemplated including, but not limited to rectangular, triangular, trapezoidal, hexagonal, etc. The continuous fiber-reinforced elements can have a fiber volume content of at least 35%. The fiber-reinforced element includes continuous fiber-reinforcing filaments 105 embedded in matrix 104, are continuous over the length of the fiber-reinforcing element 100, and distributed over the cross-sectional profile. The continuous fiber-reinforced elements 100 can have a diameter of at least 0.40 mm.

(16) Fiber-reinforcing filaments are comprised of materials that include, but are not limited to, textiles, carbon, glass, basalt, plastic, ceramic, aramid, polyester, nylon, and rayon. Matrix material includes, but is not limited to, Polypropylene (PP), Polyamide (PA), Acrylonitrile butadiene styrene (ABS), Polyethylene Imine (PEI), Polyphthalamide (PPA), Polyphenylene sulfide (PPS), Polyaryletherketone (PAEK), Polyetherketoneketone PEKK), or Polyetheretherketone (PEEK). Textiles include single fiber filaments or rovings made of glass, carbon, basalt, ceramic and/or plastic to form woven fabrics, braids, knitted fabrics, and laid fabrics.

(17) A thermoplastic, continuous fiber-reinforced element can be produced, for example, by a pultrusion process to which the continuous fiber-reinforcing filaments are fed.

(18) FIG. 2 illustrates a fiber-reinforced element 200 continuously fiber-reinforced full profile with a rectangular cross-section and having fiber-reinforcing filaments 205 embedded in matrix material 204. The dimensions of the fiber-reinforced element may be equal to or greater than 0.5 inches (12.7 mm) wide by 0.008 inches (0.2 mm) thick.

(19) FIG. 3 illustrates a cross-section of a woven fiber-reinforced element 300, which comprises matrix material 304 and textile reinforcing filaments 307 interwoven with fibers 310. By using semi-finished textile products, additional reinforcements can be achieved transversely to the longitudinal axis of the element 300 with fibers 310. Element 300 is illustrated having a rectangular cross-sectional shape for convenience as any shape is contemplated. Textile reinforcing filaments 307 are illustrated having an oval-shaped cross-section but other shapes are contemplated. Moreover, the shape of textile reinforcing filaments 307 may be altered when subjected to compressive forces.

(20) Woven fiber-reinforced elements 300 can be combined to form reinforced structures having any desired cross-sectional profile as described herein.

(21) FIGS. 4A-4D illustrate non-limiting examples of cross-sectional shapes of structural elements that may be comprised of fiber-reinforced elements described herein above. Circular fiber-reinforced elements are shown for convenience although other shapes are contemplated. The cross-sectional shapes of FIGS. 4A-4C are outer contours that are perimeters of the shapes. That is, the perimeters of the structural elements surround a hollow area H.

(22) FIG. 4A illustrates a circular structural element 400 comprised of fiber-reinforced elements 410 embedded in a matrix material 430. Matrix material 430, discussed above, may be the same or different from the matrix material in fiber-reinforced element 410. FIG. 4B illustrates a rectangular structural element 404 comprised of fiber-reinforced elements 410 embedded in matrix material 430. FIG. 4C illustrates a triangular structural element 406 comprised of fiber-reinforced elements 410 embedded in matrix material 430. FIG. 4D illustrates a T-shaped structural element 408 comprised of fiber-reinforced elements 410 embedded matrix material 430. FIGS. 4A-D illustrate examples of structural element shapes that may be formed from fiber-reinforced elements. Other structural element shapes are contemplated.

(23) FIG. 5 illustrates a section of a continuous fiber-reinforced interlocking element 500 in connection with continuous fiber-reinforcing filaments 510. The fiber-reinforcing filaments may be similar to those described above with respect to FIG. 1. Fiber-reinforcing filaments can lie unidirectionally along the length of element 500 and be embedded in a matrix material 540.

(24) The continuous fiber-reinforcing elements 500 can interlock or intermesh as a result of functional outer contour 502. Interlocking element 500 illustrates one possible interlocking functional outer contour 502 having a head portion 504 and a tail portion 506. Head portion 504 is shaped to interlock or nest in tail portion 506 as illustrated in FIG. 6. Other functional outer contours that interlock that are known to those of ordinary skill in the art are contemplated without departing from the inventive concept of the presently disclosed technique.

(25) FIG. 6 illustrates one implementation of a reinforced structure 600 including at least two interlocking fiber-reinforced elements 500. Fiber-reinforced structure 600 can have any desired external shape, which may be formed by the interlocking of at least two fiber-reinforced elements 500 in matrix material 640, which may be the same or different from the matrix material 540 of the fiber-reinforced interlocking elements, to form a desired external shape 602.

(26) FIG. 7 illustrates a cross-section of another implementation of a fiber-reinforced element 702 comprised of fiber-reinforcing filaments 705 embedded in matrix material 706. Fiber-reinforced elements 702 can be an arc segment of a circle. A thickness W of element 702 can be 1 mm but any desired thickness may be formed.

(27) FIG. 8 illustrates a cross-section of a reinforced tubular structure 801 formed from fiber-reinforced elements 802, 804, 806, 808. Each of fiber-reinforced elements 802, 804, 806, 808 may be an arc segment of a circle formed as discussed above with respect to FIG. 7. The elements 802, 804, 806, 808 form a circle having a diameter D that can be surrounded and contacted on the outside of elements 802, 804, 806, 808 by a winding layer 803. As illustrated, each fiber-reinforced element 802, 804, 806, 808 is a quarter (90 degree) arc segment. The illustration of FIG. 8 is for convenience of explanation as there may two or more fiber-reinforced elements. Moreover, those elements may be any number arc degrees and are not necessarily an equal number of arc degrees.

(28) Elements 802, 804, 806, 808 may be assembled at contact locations 810 to form a tubular structure. Elements 802, 804, 806, 808 may be adhered to one another at contact locations 810 by any known mechanism known to those of ordinary skill in the art. Alternatively, the arc segments may be pre-fixed on a mandrel with adherence points for adhesive or the like, on an inner surface of the arc segments. Moreover, elements 802, 804, 806, 808 may be adhered to one another by being interlocking elements as discussed above with respect to FIG. 5. A winding layer 803 can be formed using unidirectional reinforced thermoplastic tape wound around the formed tubular structure as will be described later.

(29) FIG. 9 illustrates a cross-section of a reinforced tubular structure 901 formed from fiber-reinforced elements 902, 904, 906, 908. Each of fiber-reinforced elements 902, 904, 906, 908 may be an arc segment of a circle formed as discussed above with respect to FIG. 7. The elements 902, 904, 906, 908 form a circle with gaps 910 between the arc segments. A matrix material 914 can fill gaps 910, and also surround and contact the elements on their outside, which may be accomplished by a co-extrusion process or other known means. A winding layer 903 can surround and contact the outside of matrix material 914. Winding layer 903 can be formed using unidirectional reinforced thermoplastic or thermoset tape wound around the formed tubular structure as will be described later. The illustration of FIG. 9 is for convenience of explanation as there may be two or more fiber-reinforced elements. Moreover, those elements may be any number arc degrees and are not necessarily an equal number of arc degrees.

(30) FIG. 10A illustrates a first process step in which arc segment elements 1002, which could be arc segment elements 802, 804, 806, 808 are positioned on a mandrel 1007.

(31) FIG. 10B illustrates a second process step in which arc segment elements 1002 positioned on mandrel 1007 are reinforced by a winding layer 1003 made of unidirectional reinforced thermoplastic tape 1012. Winding layer 1003 is shown as a hoop winding produced for example by thermoplastic winding wherein a heat source 1008 that melts the matrix of the tape 1012 and is wound under pretension 1010 and with a defined winding feed width 1011 and rotation 1009. By the hoop winding, the arc segment elements are fixed and consolidated in the tube body. The winding layer may also be cross-wound layers. With cross-wound layers the winding layers deviate from a hoop winding angle of about 90° to the longitudinal axis of the arc segments. For example, the cross-wound layer of tape may be wound at ±45° to the longitudinal axis of the arc segments. Other winding angles are also contemplated. The winding layer may be one or more than one layer.

(32) The winding process can be discontinuous or continuous. In case of continuous winding, the arc segment elements could be pre-fixed by co-extrusion. Alternatively, the arc segment of the tubular structure can be pultruded directly without an intermediate step of fabricating fiber-reinforced elements. Furthermore, in contrast to discontinuous winding, the winder and not the component would rotate. In the case of continuous winding, pre-fixing may be sufficient to eliminate a mandrel.

(33) Other implementations are within the scope of the following claims.