Tin-titanium-silicon molecular sieve, preparation method and application thereof

Abstract

A tin-titanium-silicon molecular sieve, a preparation method and an application thereof are provided. The electron binding energy of framework tin active centers in the tin-titanium-silicon molecular sieve is 488.5 eV or less. In the tin-titanium-silicon molecular sieve, the molar ratio of titanium to silicon is preferably 0.005-0.03, and the molar ratio of tin to silicon is preferably 0.005-0.025. The tin-titanium-silicon molecular sieve of the invention has more catalytic active centers, a lower electron binding energy of framework tin active centers, and an excellent catalytic performance.

Claims

1. A tin-titanium-silicon molecular sieve, wherein the electron binding energy of framework tin active centers in the tin-titanium-silicon molecular sieve is 488.5 eV or less.

2. The tin-titanium-silicon molecular sieve according to claim 1, wherein, in the tin-titanium-silicon molecular sieve, the molar ratio of titanium to silicon is 0.005-0.03, preferably 0.005-0.02, and/or the molar ratio of tin to silicon is 0.005-0.025, preferably 0.005-0.02.

3. The tin-titanium-silicon molecular sieve according to claim 1, wherein the electron binding energy of framework tin active centers is 488.0-488.4 eV.

4. The tin-titanium-silicon molecular sieve according to claim 1, wherein the electron binding energy of framework titanium active centers is 460.0-461.2 eV, preferably 460.8-461.2 eV.

5. The tin-titanium-silicon molecular sieve according to claim 1, wherein chemical shift data of phosphorus corresponding to double-quantum nuclear magnetic framework tin species adsorbed by a trimethylphosphine probe molecule are ≤−23 ppm; and/or chemical shift data of phosphorus corresponding to double-quantum nuclear magnetic framework titanium species adsorbed by a trimethylphosphine probe molecule are ≥−34 ppm.

6. The tin-titanium-silicon molecular sieve according to claim 1, which has an external specific surface area of 100-150 m.sup.2/g, and a total pore volume of 0.25-0.35 cm.sup.3/g.

7. The tin-titanium-silicon molecular sieve according to claim 1, which is an Sn—Ti-MFI molecular sieve or an Sn—Ti-MEL molecular sieve.

8. The tin-titanium-silicon molecular sieve according to claim 7, wherein the Sn—Ti-MEL molecular sieve has a structure in which long-strip grains having a length of 10-50 nm and a width of 10-30 nm overlap and stack.

9. A method for preparing the tin-titanium-silicon molecular sieve according to claim 1, said method comprising: S1, mixing an organic silicon source, an organic base, a solvent, a tin source, a titanium source and an alkaline template to obtain a first mixture, wherein the organic base is tetrapropyl ammonium hydroxide and/or tetrabutyl ammonium hydroxide; the molar ratio of the amounts of the organic silicon source, the organic base, the solvent, the tin source and the titanium source is 1:(0.05-0.6):(10-30):(0.005-0.04):(0.005-0.04), wherein the organic silicon source is calculated based on SiO.sub.2, the tin source is calculated based on SnO.sub.2, and the titanium source is calculated based on TiO.sub.2; the molar ratio of the amounts of the tin source and the alkaline template is 1:(1-10), wherein the tin source is calculated based on anion; S2, heating the first mixture at 30-80° C. for 2-10 hours to obtain a second mixture; S3, subjecting the second mixture to a hydrothermal reaction at 120-200° C. for 2-7 days to obtain a third mixture; S4, taking out a solid in the third mixture and subjecting it to drying and calcination.

10. The method according to claim 9, wherein the molar ratio of the amounts of the tin source and the alkaline template is 1:(4-8).

11. The method according to claim 9, wherein the molar ratio of the amounts of the organic silicon source, the organic base, the solvent, the tin source and the titanium source is 1:(0.1-0.4):(15-30):(0.01-0.03):(0.01-0.03).

12. The method according to claim 9, wherein step S1 comprises: mixing the organic silicon source, the organic base, the solvent and the titanium source to obtain a fourth mixture, mixing the resulting fourth mixture with the tin source and stirring for 0.5-2 hours, and then adding the alkaline template to obtain the first mixture.

13. The method according to claim 9, wherein the organic silicon source has a structure shown in formula (I) below, ##STR00009## wherein, R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are each independently selected from C1-C4 alkyl, such as C1-C4 linear alkyl and C3-C4 branched alkyl, preferably one or more of tetramethyl orthosilicate, tetraethyl orthosilicate, tetra-n-propyl orthosilicate and tetra-n-butyl orthosilicate, more preferably tetraethyl orthosilicate and/or tetramethyl orthosilicate; the solvent is selected from deionized water and/or distilled water; the alkaline template is selected from one or more of ammonia, aliphatic amine, aliphatic alcohol amine and quaternary ammonium base, preferably one or more of ammonia, ethylamine, tetrapropyl ammonium hydroxide and triethanolamine; the tin source is selected from one or more of stannic chloride, stannic chloride pentahydrate, stannous chloride, stannous chloride dihydrate, calcium stannate, potassium stannate, sodium stannate, lithium stannate, stannous sulfate and stannous pyrophosphate, preferably stannic chloride pentahydrate; and/or the titanium source has a structure shown in formula (II) below, ##STR00010## wherein, R.sub.1′, R.sub.2′, R.sub.3′ and R.sub.4′ are each independently selected from C1-C6 alkyl, such as C1-C6 linear alkyl and C3-C6 branched alkyl; the titanium source is preferably one or more of tetramethyl titanate, tetraethyl titanate, tetraisopropyl titanate and tetrabutyl titanate.

14. The method according to claim 9, wherein the hydrothermal reaction conditions in S3 include: a temperature of 120-170° C. and time of 2-5 days.

15. Application of the tin-titanium-silicon molecular sieve according to claim 1 in the preparation of lactate from dihydroxyacetone, an ammoximation reaction of aldehydes and ketones, an epoxidation reaction of olefins or an oxidation reaction of aromatics/alkanes.

16. A catalyst comprising the tin-titanium-silicon molecular sieve according to claim 1.

Description

DESCRIPTION OF THE DRAWINGS

[0036] The drawings are used to provide a further understanding of the invention and form a part of the description. They are used to explain the invention together with the following embodiments, but do not constitute a limitation of the invention. In the drawings:

[0037] FIG. 1 is a XPS diagram of the tin-titanium-silicon molecular sieve prepared in Example 1 of the invention;

[0038] FIG. 2 is a XPS diagram of the tin-titanium-silicon molecular sieve prepared in Comparative Example 1 of the invention.

MODE OF CARRYING OUT THE INVENTION

[0039] The embodiments of the present invention will be described in detail below in combination with the drawings. It should be understood that the embodiments described herein are only used to illustrate and explain the invention, not to limit the invention.

[0040] A first aspect of the invention provides a tin-titanium-silicon molecular sieve. The electron binding energy of the framework tin active center in the tin-titanium-silicon molecular sieve is 488.5 eV or less. In the tin-titanium-silicon molecular sieve, the molar ratio of titanium to silicon can be 0.005-0.03, preferably 0.005-0.02, and/or the molar ratio of tin to silicon can be 0.005-0.025, preferably 0.005-0.02.

[0041] According to the invention, the framework tin refers to the tin atom that can be inserted into the molecular sieve framework. The tin-titanium-silicon molecular sieve of the invention also contains a framework titanium on the basis of comprising the framework tin, which can further increase the type and the quantity of Lewis acid of the molecular sieve and increase the catalytic active centers. Moreover, the electron binding energy of the framework tin in the molecular sieve of the invention is lower, and the density of electron cloud is increased, which is beneficial to improve the catalytic performance, especially to improve the catalytic performance of molecular sieves for the preparation of lactate from dihydroxyacetone, the ammoximation reaction of aldehydes and ketones, the epoxidation reaction of olefins, or the oxidation reaction of aromatics/alkanes.

[0042] In an embodiment of the invention, the electron binding energy of the active center of the framework tin is 488.0-488.4 eV.

[0043] In an embodiment of the invention, the electron binding energy of the active center of the framework titanium is 460.8-461.2 eV.

[0044] According to the invention, the external specific surface area of the tin-titanium-silicon molecular sieve can be 100-150 m.sup.2/g, and the total pore volume can be 0.25-0.35 cm.sup.3/g. Preferably, the external specific surface area is 100-140 m.sup.2/g, and the total pore volume is 0.27-0.32 cm.sup.3/g. The external specific surface area refers to the total area of the molecular sieve per unit mass of material (except microporous surface area).

[0045] According to the invention, the tin-titanium-silicon molecular sieve can be an Sn—Ti-MFI molecular sieve or an Sn—Ti-MEL molecular sieve.

[0046] In an embodiment, the Sn—Ti-MEL molecular sieve has a structure in which long-strip grains overlap and stack, wherein the length of the grains may be 10-50 nm, and the width may be 10-30 nm. The long-strip shape means that the length-diameter ratio of the molecular sieve grains is greater than 1, preferably greater than 1.5, more preferably greater than 2. The overlapped and stacked structure of the grains refers to the irregularly stacked and overlapped morphology of the grains of the Sn-MEL molecular sieve observed by a high-resolution transmission electron microscope.

[0047] A second aspect of the invention provides a method for preparing the tin-titanium-silicon molecular sieve provided by the first aspect of the invention, said method comprising: [0048] S1, mixing an organic silicon source, an organic base, a solvent, a tin source, a titanium source and an alkaline template to obtain a first mixture, wherein the organic base is tetrapropyl ammonium hydroxide and/or tetrabutyl ammonium hydroxide; the molar ratio of the amounts of the organic silicon source, the organic base, the solvent, the tin source and the titanium source is 1:(0.05-0.6):(10-30):(0.005-0.04):(0.005-0.04), wherein the organic silicon source is calculated based on SiO.sub.2, the tin source is calculated based on SnO.sub.2, and the titanium source is calculated based on TiO.sub.2; the molar ratio of the amounts of the tin source and the alkaline template is 1:(1-10), wherein the tin source is calculated based on anion; [0049] S2, heating the first mixture at 30-80° C. for 2-10 hours to obtain a second mixture; [0050] S3, subjecting the second mixture to a hydrothermal reaction at 120-200° C. for 2-7 days to obtain a third mixture; [0051] S4, taking out a solid in the third mixture and subjecting it to drying and calcination.

[0052] The method of the invention can increase the molar ratio of tin to silicon and the molar ratio of titanium to silicon in the tin-titanium-silicon molecular sieve, make the electron binding energy of the framework tin shift to a lower level, and increase the density of the electron cloud. The prepared tin-titanium-silicon molecular sieve has an excellent catalytic performance for the preparation of lactate from dihydroxyacetone, the ammoximation reaction of aldehydes and ketones, the epoxidation reaction of olefins or the oxidation reaction of aromatics/alkanes.

[0053] According to the invention, in step S1, the molar ratio of the amounts of the organic silicon source, the organic base, the solvent, the tin source and the titanium source can be 1:(0.1-0.4):(15-30):(0.01-0.03):(0.01-0.03), wherein the organic silicon source is calculated based on SiO.sub.2, the tin source is calculated based on SnO.sub.2, and the titanium source is calculated based on TiO.sub.2.

[0054] According to the invention, the molar ratio of the amounts of the tin source and the alkaline template is preferably 1:(4-8), and more preferably, the molar ratio of the amounts of the tin source and the alkaline template is 1:(4-6), wherein the tin source is calculated based on anion.

[0055] In a preferred embodiment, step S1 can comprise: mixing the organic silicon source, the organic base, the solvent and the titanium source to obtain a fourth mixture, mixing the resulting fourth mixture with the tin source and stirring for 0.5-2 hours, and then adding the alkaline template to obtain the first mixture.

[0056] According to the invention, step S2 can comprise: heating the first mixture at 50-80° C. for 5-8 hours under stirring conditions to obtain a second mixture. Stirring can be a conventional means adopted by those skilled in the art, such as mechanical stirring, electromagnetic stirring, etc.

[0057] According to the invention, in step S4, the method of taking out the solid in the third mixture is not specifically limited. For instance, filtration, centrifugation and the like may be used. Preferably, the solid as taken out is washed before drying and calcination. There is no restriction on the solution used for washing. It can be any liquid that does not react with the solid, such as deionized water. Drying and calcination are operations familiar to those skilled in the art. In an embodiment, drying can be carried out in a constant temperature drying oven, and the drying conditions can include: a temperature of 50-150° C., time of 2-10 hours, preferably 3-10 hours; the calcination can be conducted in a muffle furnace or a tubular furnace, and the calcination conditions can include: a temperature of 550-750° C., time of 3-10 hours. The atmosphere is air or inert atmosphere, wherein the inert atmosphere contains nitrogen and/or inert gas that can be argon, helium, etc.

[0058] According to the invention, the organic silicon source can have a structure shown in formula (I) below,

##STR00003##

[0059] In formula (I), R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are each independently selected from C1-C4 alkyl that can comprise C1-C4 linear alkyl and C3-C4 branched alkyl, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl or tert-butyl. In a preferred embodiment, the organic silicon source is one or more of tetramethyl orthosilicate, tetraethyl orthosilicate, tetra-n-propyl orthosilicate and tetra-n-butyl orthosilicate, more preferably tetraethyl orthosilicate and/or tetramethyl orthosilicate.

[0060] According to the invention, the titanium source can have a structure shown in formula (II) below,

##STR00004##

[0061] In formula (II), R.sub.1′, R.sub.2′, R.sub.3′ and R.sub.4′ are each independently selected from C1-C6 alkyl that can comprise C1-C6 linear alkyl and C3-C6 branched alkyl; in a preferred embodiment, the titanium source is one or more of tetramethyl titanate, tetraethyl titanate, tetraisopropyl titanate and tetrabutyl titanate.

[0062] According to the invention, the alkaline template may be selected from one or more of ammonia, aliphatic amine, aliphatic alcohol amine and quaternary ammonium base, preferably one or more of ammonia, ethylamine, tetrapropyl ammonium hydroxide and triethanolamine. Therein the aliphatic amine can be a compound formed after at least one hydrogen in various NH.sub.3 is substituted with an aliphatic hydrocarbon group (preferably alkyl), the aliphatic alcohol amine can be a compound formed after at least one hydrogen in various NH.sub.3 is substituted with a hydroxyl-containing aliphatic hydrocarbon group (preferably alkyl).

[0063] In an embodiment, the quaternary ammonium base can be an organic quaternary ammonium base, which has the structure shown in formula (III)

##STR00005##

wherein R.sub.5, R.sub.6, R.sub.7 and R.sub.8 are each independently alkyl with a carbon atom number of 1-4, which can include a linear alkyl with a carbon atom number of 1-4 and a branched alkyl with a carbon atom number of 3-4, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl or tert-butyl.

[0064] In an embodiment, the aliphatic amine has the structure shown in formula (IV), R.sub.9(NH.sub.2).sub.n formula (IV), wherein n is 1 or 2. When n is 1, R.sup.9 can be alkyl with a carbon atom number of 1-6, which can include a linear alkyl with a carbon atom number of 1-6 and a branched alkyl with a carbon atom number of 3-6, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, n-amyl, neopentyl, isopentyl. When n is 2, R.sup.9 can be alkylene with a carbon atom number of 1-6, which can include a linear alkylene with a carbon atom number of 1-6 and a branched alkylene with a carbon atom number of 3-6, such as methylene, n-propylene, n-butylene, n-pentylene. In a preferred embodiment, the aliphatic amine compound is one or more of ethylamine, n-butylamine and butanediamine.

[0065] In an embodiment, the aliphatic alcohol amine has the structure shown in formula (V), (HOR.sup.10).sub.m(NH).sub.3m formula (V), wherein m is 1, 2 or 3, and m R.sup.10 can be the same or different, each independently selected from alkylene with 1-4 carbon atoms. The alkylene can include a linear alkylene with 1-4 carbon atoms and a branched alkylene with 3-4 carbon atoms, such as methylene, ethylene, n-propylene and n-butylene. In a preferred embodiment, the aliphatic alcohol amine compound is one or more of monoethanolamine, diethanolamine and triethanolamine.

[0066] According to the invention, the solvent can be selected from deionized water and/or distilled water.

[0067] According to the invention, the tin source can be any water-soluble inorganic tin salt, preferably one or more of stannic chloride, stannic chloride pentahydrate, stannous chloride, stannous chloride dihydrate, calcium stannate, potassium stannate, sodium stannate, lithium stannate, stannous sulfate and stannous pyrophosphate, more preferably stannic chloride pentahydrate.

[0068] According to the present invention, the hydrothermal reaction is well known to those skilled in the art. For example, it can be carried out in an autoclave. There is no specific restriction on the pressure of the hydrothermal reaction, which can be either a self-generated pressure of the reaction or a pressure added additionally to the reaction system. In an embodiment, the hydrothermal reaction conditions can include: the temperature of 120-170° C., the time of 2-5 days.

[0069] A third aspect of the invention provides an application of the tin-titanium-silicon molecular sieve provided in the first aspect of the invention in the preparation of lactate from dihydroxyacetone, the ammoximation reaction of aldehydes and ketones, the epoxidation reaction of olefins or the oxidation reaction of aromatics/alkanes.

[0070] According to the present invention, lactate is prepared using dihydroxyacetone in the presence of a solvent and the tin-titanium-silicon molecular sieve. The solvent used to prepare lactate from dihydroxyacetone is well known to those skilled in the art. For example, it can be a lower alcohol, and more specifically, it can be methanol, ethanol, propanol, butanol, etc.

[0071] In an embodiment, the invention provides an application of the tin-titanium-silicon molecular sieve in the preparation of methyl lactate from dihydroxyacetone, and the solvent is methanol. For the ammoximation reaction of aldehydes and ketones, the solvent used is well known to those skilled in the art. For example, it can be a lower alcohol, more specifically methanol, ethanol, isopropanol, tert-butanol, etc.

[0072] For the epoxidation reaction of olefins, the solvent used is familiar to those skilled in the art. For example, it can be a lower alcohol, more specifically methanol, ethanol, isopropanol, tert-butanol, etc.

[0073] For the oxidation reaction of aromatics/alkanes, the solvent used is familiar to those skilled in the art. For example, it can be a lower alcohol, more specifically methanol, ethanol, isopropanol, tert-butanol, etc.

[0074] A fourth aspect of the invention provides a catalyst containing the tin-titanium-silicon molecular sieve provided by the first aspect of the invention.

[0075] The present invention is further illustrated by the following examples, but the present invention is not limited thereto.

[0076] Unless otherwise specified, the raw materials used in the examples and the comparative examples are all chemically pure reagents. Tetraethyl orthosilicate is purchased from Hunan Jianchang Petrochemical Co., Ltd., tetrabutyl titanate from Hunan Jianchang Petrochemical Co., Ltd., tetrabutyl ammonium hydroxide from Beijing Innochem Science & Technology Co., Ltd., stannic chloride pentahydrate from Beijing Innochem Science & Technology Co., Ltd., tetrapropyl ammonium hydroxide from Beijing Innochem Science & Technology Co., Ltd., dihydroxyacetone from Beijing Innochem Science & Technology Co., Ltd., methanol from Beijing Innochem Science & Technology Co., Ltd., stannous chloride from Beijing Innochem Science & Technology Co., Ltd., stannous chloride dihydrate from Beijing Innochem Science & Technology Co., Ltd., triethanolamine from Beijing Innochem Science & Technology Co., Ltd., and ethylamine from Beijing Innochem Science & Technology Co., Ltd.

[0077] The electron binding energy of the framework tin active center in the molecular sieve can be obtained by XPS characterization;

[0078] The electron binding energy of the framework titanium active center in the molecular sieve can be obtained by XPS characterization;

[0079] The double-quantum nuclear magnetic analysis uses trimethylphosphine as a probe molecule.

[0080] After a sample is pretreated, trimethylphosphine is adsorbed on the molecular sieve, and then a measurement is performed through .sup.31P and .sup.1H nuclear magnetic resonance spectrogram. The obtained spectrogram is correlated with .sup.31P—-.sup.31P or .sup.31P—.sup.1H to obtain said double-quantum nuclear magnetic analysis spectrogram;

[0081] The molar ratio of titanium to silicon and the molar ratio of tin to silicon in the molecular sieve are measured by XRF method;

[0082] The external specific surface area and the total pore volume of the molecular sieve are measured using BET characterization;

[0083] The length and the width of grains are characterized by a transmission electron microscope with high resolution (resolution of 50 nm).

[0084] The yield of methyl lactate in the test examples is analyzed by gas chromatography. The analysis results are quantified by an internal standard method and the internal standard is naphthalene. The analysis conditions of chromatography are: Agilent-6890 type chromatograph, HP-5 capillary column, injection volume of 0.5 μL, and injection port temperature of 280° C.; the column temperature is maintained at 100° C. for 2 min, then increased to 200° C. at a rate of 15° C./min and maintained for 3 min; FID detector, detector temperature of 300° C.

[0085] The yield of methyl lactate is calculated using the following formula:

Yield of methyl lactate %=mole number of methyl lactate in the product/mole number of dihydroxyacetone in the raw material×100%, i.e., methyl lactate yield %=methyl lactate selectivity %×dihydroxyacetone conversion %.

[0086] The conversion and the selectivity are calculated by the following formulae:

conversion (%)=mole number of converted organic matters/mole number of input organic matters×100%,

selectivity (%)=mole number of target product/total mole number of generated product×100%.

Example 1

[0087] S1, tetraethyl orthosilicate:tetrabutyl titanate:tetrapropylammonium hydroxide:deionized water were mixed in a molar ratio of 1:0.02:0.2:20, and stirred at room temperature; during stirring of the above mixture, stannic chloride pentahydrate was added and stirred for 1 hour to obtain a colorless transparent solution (the molar ratio of tetraethyl orthosilicate to stannic chloride pentahydrate is 1:0.02), in which tetraethyl orthosilicate was calculated based on SiO.sub.2, stannic chloride pentahydrate was calculated based on SnO.sub.2, and tetrabutyl titanate was calculated based on TiO.sub.2; then tetrapropyl ammonium hydroxide with the same molar amount of chloride ion in stannic chloride pentahydrate was added to obtain a first mixture; [0088] S2, the first mixture was placed on a magnetic stirrer with a reaction temperature of 70° C. and heated to remove alcohol for 6 hours to obtain a second mixture; [0089] S3, the second mixture was placed in a stainless-steel sealed reactor and crystallized at 160° C. and the self-generated pressure for 3 days to obtain a third mixture; [0090] S4, the third mixture was filtered to take out the solid, and the solid substance obtained was washed with water followed by drying at 110° C. for 2 hours, and then calcination in air atmosphere at 550° C. for 6 hours, thereby obtaining the tin-titanium-silicon molecular sieve of the present invention, i.e., the Sn—Ti-MFI molecular sieve, whose XPS diagram is shown in FIG. 1.

[0091] The specific reaction conditions for the synthesis of the tin-titanium-silicon molecular sieve are listed in Table 1. The physicochemical characterization and the activity evaluation result of the tin-titanium-silicon molecular sieve are shown in Table 2.

Examples 2-21

[0092] The Sn—Ti-MFI molecular sieve was prepared according to the method of Example 1. Its ratio, synthesis condition and material ratio are shown in Table 1; the physicochemical characterization and the activity evaluation result of the tin-titanium-silicon molecular sieve are shown in Table 2, and refer to Example 1 for synthesis conditions if not involved in Table 1.

Example 22

[0093] S1, tetraethyl orthosilicate:tetrabutyl titanate:tetrapropylammonium hydroxide:deionized water were mixed in a molar ratio of 1:0.02:0.2:20, and stirred at room temperature; during stirring of the above mixture, stannic chloride pentahydrate was added and stirred for 1 hour to obtain a colorless transparent solution (the molar ratio of tetraethyl orthosilicate to stannous chloride pentahydrate is 1:0.01), in which tetraethyl orthosilicate was calculated based on SiO.sub.2, stannous chloride pentahydrate was calculated based on SnO.sub.2, and tetrabutyl titanate was calculated based on TiO.sub.2; then tetrapropyl ammonium hydroxide with the same amount of chloride ion in stannic chloride pentahydrate was added to obtain a first mixture; [0094] S2, the first mixture was placed on a magnetic stirrer with a reaction temperature of 70° C. and heated to remove alcohol for 6 hours to obtain a second mixture; [0095] S3, the second mixture was placed in a stainless-steel sealed reactor and crystallized at 160° C. and the self-generated pressure for 3 days to obtain a third mixture; [0096] S4, the third mixture was filtered to take out the solid, and the solid substance obtained was washed with water followed by drying at 110° C. for 2 hours, and then calcination in air atmosphere at 550° C. for 6 hours, thereby obtaining the tin-titanium-silicon molecular sieve of the present invention, i.e., the Sn—Ti-MFI molecular sieve.

[0097] The specific reaction conditions for the synthesis of the tin-titanium-silicon molecular sieve are listed in Table 1. The physicochemical characterization and the activity evaluation result of the tin-titanium-silicon molecular sieve are shown in Table 2.

Examples 23-24

[0098] The Sn—Ti-MFI molecular sieve was prepared according to the method of Example 22. Its ratio, synthesis condition and material ratio are shown in Table 1; the physicochemical characterization and the activity evaluation result of the tin-titanium-silicon molecular sieve are shown in Table 2, and refer to Example 22 for synthesis conditions if not involved in Table 1.

Comparative Example 1

[0099] The Sn—Ti-MFI molecular sieve was prepared by hydrothermal method in this comparative example.

[0100] Stannic tetrachloride pentahydrate (SnCl.sub.4.Math.5H.sub.2O) was dissolved in water. The aqueous solution was added with tetraethyl orthosilicate (TEOS) and stirred, followed by addition of tetrabutyl titanate (TBOT), addition of tetrapropyl ammonium hydroxide (TPAOH, 20% aqueous solution) and water under stirring, stirred continuously for 30 min to obtain a clear liquid with a chemical composition of 0.015 TiO.sub.2:0.03 SnO.sub.2:SiO.sub.2:0.45 TPA:35 H.sub.2O, aged at 70° C. for 6 hours, and then crystallized at 433 K for 2 days. After that, the obtained solid was filtered, washed with distilled water, dried at 393 K for 5 hours, and then calcined at 823 K for 10 hours to obtain a molecular sieve sample. Therein the amount of TEOS was 15.31 g, the amount of TPAOH was 33.67 g, the amount of SnCl.sub.4.Math.5H.sub.2O was 0.38 g, the amount of TBOT was 0.38 g, and the amount of water was 39.64 g. The XPS diagram of the prepared Sn—Ti-MFI molecular sieve is shown in FIG. 2.

Comparative Example 2

[0101] The Sn—Ti-MFI molecular sieve was prepared by a hydrothermal method in this comparative example.

[0102] Stannic tetrachloride pentahydrate (SnCl.sub.4.Math.5H.sub.2O) was dissolved in water. The aqueous solution was added with tetraethyl orthosilicate (TEOS) and stirred, followed by addition of tetrabutyl titanate (TBOT), addition of tetrapropyl ammonium hydroxide (TPAOH, 20% aqueous solution) and water under stirring, stirred continuously for 30 min to obtain a clear liquid with a chemical composition of 0.015 TiO.sub.2:0.03 SnO.sub.2:SiO.sub.2:0.45 TPA:35 H.sub.2O, aged at 70° C. for 6 hours, and then crystallized at 433 K for 2 days. After that, the obtained solid was filtered, washed with distilled water, dried at 393 K for 5 hours, and then calcined at 733 K for 10 hours to obtain a molecular sieve sample. Therein the amount of TEOS was 15.31 g, the amount of TPAOH was 42.96 g, the amount of SnCl.sub.4.Math.5H.sub.2O was 0.38 g, the amount of TBOT was 0.38 g, and the amount of water was 39.64 g.

Comparative Examples 3-10

[0103] The Sn—Ti-MFI molecular sieve was prepared according to the method of Comparative Example 1. Its ratio, synthesis condition and material ratio are shown in Table 1; the physicochemical characterization and activity evaluation result of the tin-titanium-silicon molecular sieve are shown in Table 2, and refer to Comparative Example 1 for synthesis conditions if not involved in Table 1.

Test Examples

[0104] (1) Preparation of Methyl Lactate from Catalysis of Dihydroxyacetone

[0105] The samples obtained in the examples and the comparative examples were used as catalysts for the catalysis reaction of dihydroxyacetone to prepare methyl lactate. The specific reaction conditions were as follows: in the slurry bed reactor, the reactant of dihydroxyacetone and the solvent of methanol were reacted at 60° C. and the self-generated pressure at a molar ratio of 1:200, the amount of the catalyst being 3.0% by weight of the total reaction solution, and samples were taken every hour of reaction to determine the composition of the product. The calculation results are shown in Table 2.

[0106] (2) Ammoximation Reaction of Aldehydes and Ketones

[0107] The samples obtained in the examples and comparative examples were used as catalysts, and reacted according to the formula of

##STR00006##

wherein R is selected from alkyl and aryl, such as phenyl; R.sub.1 is selected from hydrogen and alkyl; or R and R.sub.1 are combined to form a ring.

[0108] The specific reaction conditions were as follows: in the slurry bed reactor, the reactants of aldehydes and ketones, hydrogen peroxide and the solvent (such as tert-butyl alcohol) were reacted at 80° C. and the self-generated pressure at a molar ratio of 1:1:200, the amount of catalyst being 5.0% by weight of the total reaction solution, and samples were taken every hour of reaction to determine the composition of the product. The results are shown in Table 3.

[0109] (3) Epoxidation Reaction of Olefins

[0110] The samples obtained in the examples and comparative examples were used as catalysts, and reacted according to the formula of

##STR00007##

wherein R.sub.1 and R.sub.2 are respectively selected from hydrogen and alkyl optionally containing heteroatoms (such as oxygen), or R.sub.1 and R.sub.2 are combined to form a ring.

[0111] The specific reaction conditions were as follows: in the slurry bed reactor, the reactants of olefin, hydrogen peroxide and the solvent (such as tert-butyl alcohol) were reacted at 50° C. and the self-generated pressure at a molar ratio of 1:1:200, the amount of catalyst being 5.0% by weight of the total reaction solution, and samples were taken every hour of reaction to determine the composition of the product. The results are shown in Table 3.

[0112] (4) Oxidation Reaction of Aromatics/Alkanes

[0113] The samples obtained in the examples and comparative examples were used as catalysts, and reacted according to the formula of

##STR00008##

wherein R is selected from hydrogen, alkyl and hydroxyl, and R can represent two substituents; R.sub.1 and R.sub.2 are respectively selected from hydrogen and alkyl, or R.sub.1 and R.sub.2 are combined to form an optionally alkyl-substituted ring.

[0114] The specific reaction conditions were as follows: in the slurry bed reactor, the reactants (aromatics/alkanes), hydrogen peroxide and the solvent (such as tert-butyl alcohol) were reacted at 80° C. and self-generated pressure at a molar ratio of 1:1:200, the amount of catalyst being 5.0% by weight of the total reaction solution, and samples were taken every hour of reaction to determine the composition of the product. The results are shown in Table 3.

TABLE-US-00001 TABLE 1 organic temper- silicon organic temper- ature source: silicon tin ature and and time organic inorganic titanium source: source: time of of hydro- silicon titanium tin alkaline organic source:organic tin alkaline heating in thermal sources sources sources template bases base:solvent source template step S2 reaction Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 1 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 2 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannous tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 3 orthosilicate titanate chloride ammonium ammonium 6 h 3 days hydroxide hydroxide Ex- tetraethyl tetrabutyl stannous tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 4 orthosilicate titanate chloride ammonium ammonium 6 h 3 days dihydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic ammonia tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 5 orthosilicate titanate chloride ammonium 6 h 3 days pentahydrate hydroxide Ex- tetraethyl tetrabutyl stannic ethylamine tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 6 orthosilicate titanate chloride ammonium 6 h 3 days pentahydrate hydroxide Ex- tetraethyl tetrabutyl stannic triethanol- tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 7 orthosilicate titanate chloride amine ammonium 6 h 3 days pentahydrate hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.1:20 1:0.02 1:1 70° C., 160° C., ample 8 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.4:20 1:0.02 1:1 70° C., 160° C., ample 9 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:15 1:0.02 1:1 70° C., 160° C., ample 10 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:30 1:0.02 1:1 70° C., 160° C., ample 11 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.01 1:1 70° C., 160° C., ample 12 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.03 1:1 70° C., 160° C., ample 13 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 50° C., 160° C., ample 14 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 80° C., 160° C., ample 15 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 16 orthosilicate titanate chloride ammonium ammonium 5 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 17 orthosilicate titanate chloride ammonium ammonium 8 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 120° C., ample 18 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 170° C., ample 19 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 20 orthosilicate titanate chloride ammonium ammonium 6 h 2 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., ample 21 orthosilicate titanate chloride ammonium ammonium 6 h 5 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.01 1:1 70° C., 160° C., ample 22 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:21 1:0.03 1:1 70° C., 160° C., ample 23 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:22 1:0.02 1:1 70° C., 160° C., ample 24 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:9 70° C., 160° C., ample 25 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Ex- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.04:0.5:32  1:0.035 1:1 70° C., 160° C., ample 26 orthosilicate titanate chloride ammonium ammonium 6 h 3 days pentahydrate hydroxide hydroxide Com- tetraethyl tetrabutyl stannic — tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., parative orthosilicate titanate chloride ammonium 6 h 3 days Ex- pentahydrate hydroxide ample 1 Com- tetraethyl tetrabutyl stannic — tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., parative orthosilicate titanate chloride ammonium 6 h 3 days Ex- pentahydrate hydroxide ample 2 Com- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.01:20 1:0.02 1:1 70° C., 160° C., parative orthosilicate titanate chloride ammonium ammonium 6 h 3 days Ex- pentahydrate hydroxide hydroxide ample 3 Com- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:5 1:0.02 1:1 70° C., 160° C., parative orthosilicate titanate chloride ammonium ammonium 6 h 3 days Ex- pentahydrate hydroxide hydroxide ample 4 Com- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20  1:0.001 1:1 70° C., 160° C., parative orthosilicate titanate chloride ammonium ammonium 6 h 3 days Ex- pentahydrate hydroxide hydroxide ample 5 Com- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.06 1:1 70° C., 160° C., parative orthosilicate titanate chloride ammonium ammonium 6 h 3 days Ex- pentahydrate hydroxide hydroxide ample 6 Com- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 10° C., 160° C., parative orthosilicate titanate chloride ammonium ammonium 6 h 3 days Ex- pentahydrate hydroxide hydroxide ample 7 Com- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., parative orthosilicate titanate chloride ammonium ammonium 1 h 3 days Ex- pentahydrate hydroxide hydroxide ample 8 Com- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 100° C., parative orthosilicate titanate chloride ammonium ammonium 6 h 3 days Ex- pentahydrate hydroxide hydroxide ample 9 Com- tetraethyl tetrabutyl stannic tetrapropyl tetrapropyl 1:0.02:0.2:20 1:0.02 1:1 70° C., 160° C., parative orthosilicate titanate chloride ammonium ammonium 6 h 1 days Ex- pentahydrate hydroxide hydroxide ample 10

[0115] In Table 1, organic silicon source:titanium source:organic base:solvent refers to the molar ratio of the amounts of the organic silicon source, the titanium source, the organic base and the solvent; organic silicon source:tin source refers to the molar ratio of the amounts of the organic silicon source and the tin source; tin source:alkaline template refers to the molar ratio of the amounts of the tin source and the alkaline template.

TABLE-US-00002 TABLE 2 electron double- double- electron binding quantum quantum binding energy of nuclear nuclear molar molar external energy of frame- magnetic magnetic ratio of ratio of specific total long-strip yield of frame- work frame- framework tin to titanium surface pore grains methyl work titanium/ work tin titanium silicon, to silicon, area, volume, length, width, lactate/ tin/eV eV species/ppm species/ppm ×10.sup.−2 ×10.sup.−2 m.sup.2/g cm.sup.3/g nm nm % Example 488.33 460.2 −23.1 −33.9 1.9 2.0 123 0.26 25 15 97 1 Example 488.35 460.3 −24.1 −33.1 1.8 2.0 125 0.28 14 14 98 2 Example 488.39 460.1 −23.9 −33.6 2.0 1.9 113 0.26 17 15 97 3 Example 488.36 460.4 −24.5 −33.7 1.6 1.8 126 0.25 20 18 96 4 Example 488.32 460.5 −23.8 −33.2 1.8 1.8 131 0.27 22 23 97 5 Example 488.33 460.9 −23.2 −32.9 2.1 1.7 124 0.29 26 24 97 6 Example 488.37 460.3 −24.5 −32.8 2.3 1.8 126 0.27 19 23 98 7 Example 488.25 460.4 −23.8 −33.5 2.1 1.9 136 0.28 18 21 95 8 Example 488.43 460.1 −23.4 −33.1 2.0 1.9 133 0.31 21 10 99 9 Example 488.27 460.5 −23.5 −32.8 1.9 1.8 117 0.33 26 14 96 10 Example 488.44 460.9 −24.5 −33.1 1.8 1.7 119 0.29 27 17 98 11 Example 488.26 460.6 −23.4 −33.5 1.7 1.7 123 0.29 31 12 95 12 Example 488.41 460.5 −23.9 −33.9 1.8 1.8 129 0.3 34 13 97 13 Example 488.27 460.1 −24.1 −33.1 1.9 1.9 121 0.31 42 16 95 14 Example 488.43 460.5 −23.5 −33.6 1.9 2.0 125 0.32 44 18 97 15 Example 488.22 460.9 −24.5 −33.7 2.0 2.2 116 0.26 42 19 95 16 Example 488.44 460.3 −23.4 −33.2 2.1 2.1 134 0.25 40 17 98 17 Example 488.25 460.8 −23.9 −32.9 2.2 2.0 125 0.28 38 23 95 18 Example 488.45 460.4 −24.3 −32.8 2.0 2.0 127 0.29 28 24 98 19 Example 488.26 460.3 −24.3 −33.5 2.0 1.9 124 0.33 29 24 95 20 Example 488.43 460.9 −23.7 −33.1 1.9 1.8 123 0.31 31 22 98 21 Example 488.28 461.1 −23.4 −33.5 2.0 1.9 127 0.3 33 21 95 22 Example 488.46 460.7 −24.2 −33.1 2.0 2.8 122 0.3 36 20 97 23 Example 488.33 460.5 −23.8 −32.8 1.9 1.9 131 0.32 38 20 96 24 Example 488.50 460.6 −24.3 −33.1 1.8 1.8 110 0.22 26 29 93 25 Example 488.45 460.8 −23.9 −33.5 1.9 2.9 123 0.26 25 28 92 26 Com- 488.69 459.2 −22.8 −34.2 1.9 1.9 125 0.24 12 2 75 parative Example 1 Com- 488.7 459.3 −22.6 −34.7 1.8 1.8 127 0.23 13 3 81 parative Example 2 Com- 488.59 459.4 −22.4 −34.5 1.8 1.9 121 0.25 18 6 78 parative Example 3 Com- 488.56 459.1 −21.6 −35 1.9 1.8 114 0.22 14 8 77 parative Example 4 Com- 488.58 459.6 −21.8 −34.6 2.0 0.09 115 0.26 11 10 72 parative Example 5 Com- 488.52 459.3 −22.1 −34.9 1.9 2.2 111 0.27 12 6 79 parative Example 6 Com- 488.57 459.2 −21.9 −34.8 1.8 1.8 107 0.26 14 7 73 parative Example 7 Com- 488.58 459.5 −21.4 −34.6 1.9 1.9 109 0.25 13 8 74 parative Example 8 Com- 488.59 459.1 −22.2 −34.6 1.7 1.8 104 0.25 13 6 73 parative Example 9 Com- 488.58 459.6 −21.8 −34.4 1.8 1.8 106 0.25 14 9 75 parative Example 10

TABLE-US-00003 TABLE 3 ammoximation reaction epoxidation reaction oxidation reaction of of aldehydes and ketones of olefins aromatics/alkanes raw raw raw raw material product raw material product raw material product material conversion selectivity material conversion selectivity material conversion selectivity name (%) (%) name (%) (%) name (%) (%) Example acetalde- 96.4 97.4 propyle 94.9 97.4 phenol 74.0 96.4 1 hyde Example benzalde- 99.6 100.0 ethylene 98.0 98.6 benzene 74.9 97.6 2 hyde Example aceto- 98.3 99.3 1-hexene 96.7 99.3 cyclo- 75.5 98.3 3 phenone hexane Example cyclo- 99.1 100.1 1-octene 97.5 97.8 toluene 74.3 96.8 4 hexanone Example cyclo- 98.4 99.4 cyclo- 96.8 99.4 cyclo- 75.5 98.4 5 hexanone hexene octane Example cyclo- 97.5 98.5 propylene 95.9 98.5 ethyl- 74.8 97.5 6 pentanone benzene Example cyclo- 96.8 97.8 propylene 95.3 97.8 methyl- 74.3 96.8 7 octanone cyclo- hexene Example methyl 99.2 98.2 cyclo- 97.6 98.2 phenol 74.6 97.2 8 ethyl octene ketone Example acetone 98.7 99.7 methyl- 97.1 99.7 cresol 75.8 98.7 9 oleate Example cyclo- 99.1 97.6 1-pentene 97.5 99.1 1-hexane 75.3 98.1 10 hexanone Example cyclo- 97.9 98.9 propylene 96.3 98.9 phenol 75.1 97.9 11 hexanone Example cyclo- 95.7 96.7 ethylene 94.2 96.7 cyclo- 73.5 95.7 12 octanone octane Example acetone 98.4 99.4 1-hexene 96.8 99.4 ethyl- 75.5 98.4 13 benzene Example acetalde- 95.4 96.4 1-octene 93.9 96.4 phenol 73.3 95.4 14 hyde Example benzalde- 98.6 99.6 cyclo- 97.0 99.6 benzene 75.7 98.6 15 hyde hexene Example aceto- 97.3 98.3 propylene 95.8 98.3 cyclo- 74.7 97.3 16 phenone hexane Example cyclo- 98.1 99.1 propylene 96.5 99.1 toluene 75.3 98.1 17 hexanone Example cyclo- 97.4 98.4 1-butene 95.9 98.4 cyclo- 74.8 97.4 18 hexanone octane Example cyclo- 96.5 97.5 propylene 95.0 97.5 ethyl- 74.1 96.5 19 pentanone benzene Example cyclo- 95.8 96.8 cyclo- 94.3 96.8 methyl- 73.6 95.8 20 octanone octene cyclo- hexene Example methyl 98.2 99.2 methyl 96.6 99.2 phenol 75.4 98.2 21 ethyl oleate ketone Example acetone 97.7 98.7 1-pentene 96.1 98.7 cresol 75.0 97.7 22 Example cyclo- 98.1 99.1 propylene 96.5 99.1 1-hexane 75.3 98.1 23 hexanone Example cyclo- 96.9 97.9 1-butene 95.4 97.9 phenol 74.4 96.9 24 hexanone Example methyl 98.9 99.9 1-pentene 97.3 99.9 cresol 75.9 98.9 25 ethyl ketone Example aceto- 99.5 95.3 cyclo- 97.9 97.5 cyclo- 55.6 96.5 26 phenone hexene hexane Com- acetalde- 87.7 88.6 propylene 86.3 88.6 phenol 50.5 87.7 parative hyde Example 1 Com- benzalde- 90.6 91.5 ethylene 89.2 91.5 benzene 52.2 90.6 parative hyde Example 2 Com- aceto- 89.5 90.3 1-hexene 88.0 90.3 cyclo- 51.5 87.6 parative phenone hexane Example 3 Com- cyclo- 90.2 91.1 1-octene 88.7 91.1 toluene 51.9 88.4 parative hexanone Example 4 Com- cyclo- 89.5 90.4 cyclo- 88.1 90.4 cyclo- 51.6 87.7 parative hexanone hexene octane Example 5 Com- cyclo- 88.7 89.6 propylene 87.3 89.6 ethyl- 51.1 86.9 parative pentanone benzene Example 6 Com- cyclo- 88.1 89.0 propylene 86.7 89.0 methyl- 50.7 86.3 parative octanone cyclo- Example hexene 7 Com- methyl 90.3 91.2 cyclo- 88.8 91.2 phenol 52.0 88.4 parative ethyl octene Example ketone 8 Com- acetone 89.8 90.7 methyl- 88.4 90.7 cresol 51.7 88.0 parative oleate Example 9 Com- cyclo- 90.2 91.1 1-pentene 88.7 91.1 1-hexane 51.9 88.4 parative hexanone Example 10

[0116] The tin-titanium-silicon molecular sieve of the invention has more active centers, a low electron binding energy of the framework tin, and a high catalytic activity.

[0117] The preferred embodiments of the invention are described above in detail in combination with the drawings. However, the invention is not limited to the specific details in the above embodiments. Within the scope of the technical concept of the invention, a variety of simple variations of the technical solutions of the invention can be made, and these simple variations are all within the scope of protection of the invention.

[0118] In addition, it should be noted that the specific technical features described in the above embodiments can be combined in any suitable way if not contradictory. To avoid unnecessary repetition, the present invention will not further explain the various possible combinations.

[0119] Besides, various embodiments of the invention can also be combined arbitrarily. As long as they do not violate the idea of the invention, they should also be considered as the contents of the invention.