Aluminum composite panel containing aerogel and method for manufacturing same

Abstract

An aluminum composite panel, containing an aerogel, includes an aerogel composite using a silica aerogel and a thermoplastic resin. A method for manufacturing the same includes providing an aluminum composite panel containing an aerogel, by molding an aerogel composite from a mixture of 1-90 wt % of a silica aerogel and 10-99 wt % of a thermoplastic resin, and then attaching aluminum plates on an upper surface and a lower surface of the aerogel composite, respectively, while an adhesive resin is coated on the upper surface and the lower surface. The aluminum composite panel containing an aerogel, manufactured according to the present invention, has a lower hygroscopic property than the conventional aluminum composite panel, due to the silica aerogel, and thus has an effect of exhibiting excellent adiabatic property and flame retardancy, retains excellent moldability, is light, and has an effect of facilitating a construction work.

Claims

1. A method for manufacturing an aluminum composite panel containing an aerogel, comprising: (a) preparing a mixture of 10 to 90 wt % of silica aerogel powder having a uniform size of 100 m or less and a density of 0.05 to 0.1 g/cm.sup.3 and 10 to 90 wt % of thermoplastic resin powder having a uniform size of 100 m or less and a density of 0.1 g/cm.sup.3 or less; (b) preparing an aerogel composite by putting the mixture prepared in step (a) in a mold and heating and cooling the resulting mixture, wherein, in step (b), the aerogel composite is compressed under a pressure of 250 to 500 psi and heated for 2 hours at 120 to 200 C.; and (c) attaching an aluminum plate in a state in which an adhesive resin has been applied to each of upper and lower surfaces of the aerogel composite prepared in step (b) so that the aerogel composite containing 10 to 90 wt % of silica aerogel powder extends from the upper surface of the aerogel composite on which the adhesive resin has been applied to the lower surface of the aerogel composition on which the adhesive resin has been applied.

2. The method of claim 1, wherein, in step (a), the silica aerogel powder and the thermoplastic resin powder are mixed at a speed of 10 to 30 rpm using a ribbon mixer.

3. The method of claim 1, wherein, in step (c), the adhesive resin is applied at a thickness of 0.1 mm to each of the upper and lower surfaces of the aerogel composite.

4. The method of claim 1, wherein the aerogel composite is prepared by extrusion molding.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is an exploded perspective view of a structure of an aluminum composite panel containing an aerogel according to the present invention.

(2) FIG. 2 is a process flowchart illustrating a method for manufacturing an aluminum composite panel containing an aerogel according to the present invention.

(3) FIG. 3 is an image obtained by a hygroscopicity test of the aerogel composite constituting the present invention.

(4) FIG. 4 is an image obtained by a fire resistance test of the aerogel composite constituting the present invention.

EXPLANATION OF SYMBOLS

(5) 10: Aerogel composite;

(6) 20: Adhesive resin; and

(7) 30: Aluminum plate.

DETAILED DESCRIPTION

(8) Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings. However, the following embodiments are provided so that those of ordinary skill in the art can fully understand the present invention and thus may be modified into various forms, and the scope of the present invention is not limited to the examples that will be described below.

(9) FIG. 1 is an exploded perspective view of a structure of an aluminum composite panel containing an aerogel according to the present invention.

(10) As shown in FIG. 1, the aluminum composite panel containing an aerogel according to the present invention is composed of an aerogel composite 10, an adhesive resin 20 applied to each of the upper and lower surfaces of the aerogel composite 10, and aluminum plates 30 attached to the adhesive resin 20 (e.g., a first aluminum plate attached to the upper surface of the aerogel composite 10 and a second aluminum plate attached to the lower surface of the aerogel composite 10).

(11) Here, the aerogel composite 10 is composed of a mixture of 1 to 90 wt % of a silica aerogel and 10 to 99 wt % of a thermoplastic resin. The silica aerogel is flame retardant and results in an adiabatic effect due to its structure in which nano-scale pores are formed. When the silica aerogel is contained at less than 1 wt %, the adiabatic effect and the flame-retardant properties of the panel may not be expected. In addition, when the silica aerogel is contained at more than 90 wt %, proportionally, a content of the thermoplastic resin is reduced, and thus extrusion moldability is degraded. Therefore, the contents of silica aerogel and the thermoplastic resin are preferably mixed in the above ranges.

(12) The thermoplastic resin used in the present invention may be any one or a mixture of at least two of ethylene vinyl acetate (EVA), polyethylene (PE), polypropylene (PP), and polyvinyl butyral (PVB). These thermoplastic resins impart extrusion moldability when the aerogel composite 10 is molded in the mixture with the silica aerogel. However, when the content of the thermoplastic resin is less than 10 wt %, the extrusion moldability is insufficient. Moreover, when the content of the thermoplastic resin is more than 99 wt %, due to lack of the silica aerogel, it is difficult to obtain the adiabatic effect and the flame-retardant properties of the panel. Therefore, the thermoplastic resin should be mixed in the range of 10 to 99 wt %.

(13) In the preparation of the aerogel composite 10, the silica aerogel and the thermoplastic resin are preferably mixed in the form of powder for a uniform mixture. Here, for a uniform mixture, the silica aerogel powder most preferably has a uniform size of 100 m or less and a density of 0.05 to 0.1 g/cm.sup.3, and the thermoplastic resin powder also most preferably has a uniform size of 100 m or less and a density of 0.1 g/cm.sup.3 or less.

(14) A method for manufacturing an aluminum composite panel containing an aerogel according to the present invention, constituted as described above, comprises the following steps.

(15) That is, FIG. 2 is a process flowchart illustrating a method for manufacturing an aluminum composite panel containing an aerogel according to the present invention, and the process sequence is as follows.

(16) In the first step of the present invention, step (a), a silica aerogel and a thermoplastic resin are prepared in the form of powder, and 1 to 90 wt % of the silica aerogel powder and 10 to 99 wt % of the thermoplastic resin powder are mixed to form a mixture (S1). Here, the thermoplastic resin may be any one or a mixture of at least two of ethylene vinyl acetate (EVA), polyethylene (PE), polypropylene (PP) and polyvinyl butyral (PVB). In addition, for a uniform mixture, the silica aerogel powder most preferably has a uniform size of 100 m or less and a density of 0.05 to 0.1 g/cm.sup.3, and the thermoplastic resin powder also most preferably has a uniform size of 100 m or less and a density of 0.1 g/cm.sup.3 or less. The silica aerogel powder is preferably mixed with the thermoplastic resin powder at a speed of 10 to 30 rpm using a ribbon mixer. The ribbon mixer, which is also referred to as a screw mixer, may serve to uniformly mix powders with a plurality of ribbon-like (or screw-like) wings. Mixing performance at speeds of less than 10 rpm is decreased. Moreover, speeds of more than 30 rpm cause the silica aerogel to be scattered. Therefore, the mixer needs to be operated at a speed in the range of 10 to 30 rpm.

(17) Subsequently, in the second step, step (b), an aerogel composite is prepared by putting the mixture of the silica aerogel and the thermoplastic resin in a mold (S2-1) for manufacture in a panel form. Thereafter, the second step further includes heating (S2-3), cooling (S2-4) and demolding (S2-5) the resulting mixture. Particularly, heating may be performed for 2 hours at 120 to 200 C., and due to the heating under the temperature and time conditions, the mixture of the silica aerogel and the thermoplastic resin has flowability in a semi-melted or melted state, and thus is easily molded in a mold. Meanwhile, in the preparation of the aerogel composite, the mixture of the silica aerogel and the thermoplastic resin may be compressed under a pressure of 250 to 500 psi before heating and after being put in the mold (S2-2). During the compression, the mixture of the silica aerogel and the thermoplastic resin is easily molded in the mold. However, under a pressure of less than 250 psi or more than 500 psi, molding is disrupted. Therefore the compression is preferably performed under a pressure of 250 to 500 psi.

(18) Afterward, in the third step, step (c), an adhesive resin is applied to each of the upper and lower surfaces of the aerogel composite prepared in step (b) (S3-1), and then the aluminum plates are attached to the applied adhesive resin (S3-2). Particularly, when the adhesive resin is applied to each of the upper and lower surfaces of the aerogel composite, it is preferably applied at a thickness of 0.1 mm.

(19) As the aluminum plates are applied to the adhesive resin as described above, a desired aluminum composite panel containing an aerogel of the present invention is completed.

(20) Meanwhile, FIG. 3 is an image obtained by a hygroscopicity test of the aerogel composite constituting the present invention, and FIG. 4 is an image obtained by a fire resistance test of the aerogel composite constituting the present invention.

(21) First, as shown in FIG. 3, it can be seen that a contact angle is proportional to an increased content of the silica aerogel from less than 10 wt %, to 10 wt %, to 20 wt %, and to 30 wt %. Therefore, as the aerogel composite of the present invention contains up to 90% of the silica aerogel, it can be seen that it has low hygroscopicity, thereby resulting in improved adiabatic properties.

(22) Moreover, as shown in FIG. 4, as the content of the silica aerogel is increased from less than 10 wt %, to 10 wt %, to 20 wt %, and to 30 wt %, it can be seen that the original shape is maintained to the greatest extent possible and the sample is not melted due to high temperatures.

(23) Therefore, the aluminum composite panel containing an aerogel, manufactured according to the present invention, has improved adiabatic properties and flame-retardant properties compared to the conventional aluminum composite panel. Also, since the aluminum composite panel containing an aerogel contains a suitable amount of the thermoplastic resin together with the silica aerogel, it can be molded in various forms using a mold.

(24) While the present invention has been described with reference to the exemplary embodiments, it is not limited to the embodiments, and various modifications is possibly made by those of ordinary skill in the art within the scope of the technical idea of the present invention.