Coextruded solar panel backsheet and method of manufacture

Abstract

An improved backsheet used in the construction of solar panels is disclosed. A method of manufacturing the backsheet and solar panel comprising the backsheet, including coextrusion processes are also disclosed. Additionally, a photovoltaic solar panel module comprising the backsheet of the invention is disclosed. The backsheet of the instant invention may comprise an exterior layer having inner and outer surfaces, a middle layer, having inner and outer surfaces, and an interior layer having inner and outer surfaces. In one embodiment of the invention, the outer surface of the middle layer may be adjoined to the inner surface of the exterior layer, and the inner surface of the middle layer may be adjoined to the outer surface of the interior layer. The exterior layer, middle layer, and interior layer may be adjoined via a co-extrusion process, thereby eliminating the need for the use of adhesives for bonding the layers of the backsheet together. The backsheet of the invention improves upon the efficiency, strength, weather resistance, cost, and useful life of the solar panels in which the backsheet is incorporated.

Claims

1. A photovoltaic solar panel backsheet comprising: an exterior layer having substantially planar inner and outer surfaces said exterior layer comprising a non-grafted polyamide and ionomer alloy; a middle layer, having inner and outer surfaces comprising a polyamide; and an interior layer having inner and outer surfaces; wherein said outer surface of said middle layer is directly adjoined to said inner surface of said exterior layer without adhesive, and said inner surface of said middle layer is directly adjoined to said outer surface of said interior layer without adhesive.

2. The photovoltaic solar panel backsheet of claim 1, wherein said interior layer comprises a non-grafted polyamide and ionomer alloy.

3. The photovoltaic solar panel backsheet of claim 1, wherein said interior layer and said exterior layer each have a thickness of between about 0.5 mils and about eight (8) mils.

4. The photovoltaic solar panel backsheet of claim 1, wherein said middle layer has a thickness of between about three (3) mils and about seven (7) mils.

5. The photovoltaic solar panel backsheet of claim 1, wherein said middle layer comprises at least one of a PA11, PA12, PA610, or PA612.

6. The photovoltaic solar panel backsheet of claim 1, wherein said middle layer comprises filler between about five percent (5%) by weight and about forty percent (40%) by weight.

7. The photovoltaic solar panel backsheet of claim 1, wherein said middle layer comprises at least one of a talc filled polyamide, calcium carbonate filled polyamide, or a talc and calcium carbonate filled polyamide.

8. A method for manufacturing a photovoltaic solar panel backsheet, comprising the steps of: drying an exterior layer material comprising a non-grafted polyamide and ionomer alloy, a middle layer material comprising a talc filled polyamide, and an interior layer material comprising a polyamide and ionomer alloy; heating said exterior, middle and interior layer materials to a state wherein each of said materials may be extruded into individual sheets or webs; extruding said exterior, middle and interior layer materials into individual sheets or webs; forming said backsheet comprising a single, three layered sheet or web which comprises said exterior layer material sheet or web having substantially planar inner and outer surfaces, said middle layer material sheet or web having inner and outer surfaces; and said interior layer sheet or web having inner and outer surfaces; wherein said outer surface of said middle layer sheet or web is directly adjoined to said inner surface of said exterior layer sheet or web without adhesive, and said inner surface of said middle layer is directly adjoined to said outer surface of said interior layer sheet or web without adhesive.

9. The method of claim 8, wherein said method comprises a co-extrusion process.

10. The method of claim 9, wherein said co-extrusion process comprises at least one of a co-extruded cast film process and a co-extruded blown film process.

11. A photovoltaic solar panel module comprising: a front cover having inner and outer surfaces; one or more photovoltaic cells substantially encapsulated in an encapsulant having a top outer surface and a bottom outer surface; a backsheet comprising: an exterior layer having substantially planar inner and outer surfaces; a middle layer, having inner and outer surfaces; and an interior layer having inner and outer surfaces; wherein said outer surface of said middle layer is directly adjoined to said inner surface of said exterior layer without adhesive, and said inner surface of said middle layer is directly adjoined to said outer surface of said interior layer without adhesive; and wherein said top outer surface of said encapsulant is adjoined to said inner surface of said front cover, and said bottom outer surface of said encapsulant is adjoined to said inner surface of said interior layer of said backsheet, and wherein one or both of said exterior and interior backsheet layers comprise a non-grafted polyamide and ionomer alloy, and said middle layer comprises a polyamide.

12. The photovoltaic solar panel module of claim 11, wherein said middle layer comprises at least one of a talc filled polyamide, calcium carbonate filled polyamide, or a talc and calcium carbonate filled polyamide.

13. The photovoltaic solar panel module of claim 11, wherein said encapsulant comprises a top portion comprising said top outer surface of said encapsulant, and a bottom portion comprising said bottom outer surface of said encapsulant.

14. The photovoltaic solar panel module of claim 13, wherein said top portion of said encapsulant comprises substantially the same material composition as said bottom portion of said encapsulant.

15. The photovoltaic solar panel module of claim 13, wherein said top portion of said encapsulant comprises a substantially different material composition as said bottom portion of said encapsulant.

16. The photovoltaic solar panel module of claim 13, wherein said top portion of said encapsulant comprises a material composition which permits light to pass through said top portion of said encapsulant sufficient to activate said one or more photovoltaic cells, and said bottom portion of said encapsulant comprises a material composition which reflects at least partially reflects light to increase said one or more photovoltaic cells operating efficiency.

17. A photovoltaic solar panel backsheet comprising: an exterior layer having substantially planar inner and outer surfaces; a middle layer comprising a polyamide and having inner and outer surfaces; and an interior layer having inner and outer surfaces comprising a non-grafted polyamide and ionomer alloy; wherein said outer surface of said middle layer is directly adjoined to said inner surface of said exterior layer without adhesive, and said inner surface of said middle layer is directly adjoined to said outer surface of said interior layer without adhesive.

18. The photovoltaic solar panel backsheet of claim 17, wherein said middle layer comprises a polymeric material.

19. The photovoltaic solar panel backsheet of claim 1, wherein said middle layer comprises a polymeric material.

20. The photovoltaic solar panel module of claim 11, wherein said middle layer of said backsheet comprises a polymeric material.

21. The photovoltaic solar panel backsheet of claim 1, wherein, said outer surface of said inner layer is constructed to be directly adjoined to an outer surface an encapsulant substantially encapsulating one or more photovoltaic cells.

22. The photovoltaic solar panel backsheet of claim 17, wherein said outer surface of said inner layer is constructed to be directly adjoined to an outer surface an encapsulant substantially encapsulating one or more photovoltaic cells.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) Understanding of the present invention will be facilitated by consideration of the following detailed description of the embodiments of the present invention taken in conjunction with the accompanying drawings, in which like numerals refer to like parts, and wherein:

(2) FIG. 1 is a cross sectional schematic of the layers of a prior art embodiment of a solar panel backsheet.

(3) FIG. 2 is a cross sectional schematic of the layers of one embodiment of the solar panel backsheet of the instant invention.

(4) FIG. 3 is a block diagram depicting one embodiment of a method of manufacturing the backsheet of the instant invention via a cast film process.

(5) FIG. 4 is a cross sectional schematic depicting a solar cell construction incorporating one embodiment of the solar panel backsheet of the instant invention.

(6) FIG. 5 is a block diagram depicting one embodiment of a method of manufacturing the backsheet of the instant invention via a blown film process.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(7) It is to be understood that the figures, images and descriptions of the present invention have been simplified to illustrate elements that are relevant for a clear understanding of the present invention, while eliminating, for the purposes of clarity, many other elements which may be found in the present invention. Those of ordinary skill in the pertinent art will recognize that other elements are desirable and/or required in order to implement the present invention. However, because such elements are well known in the art, and because such elements do not facilitate a better understanding of the present invention, a discussion of such elements is not provided herein.

(8) Turning now to FIG. 2, there is shown a cross sectional schematic of backsheet 100 of one embodiment of the instant invention. Backsheet 100 may comprise exterior layer 110 having inner and outer surfaces, middle layer 120 having inner and outer surfaces, and interior layer 130 having inner and outer surfaces. In this embodiment of backsheet 100, the outer surface of middle layer 120 may be adjoined to the inner surface of exterior layer 110, and the inner surface of middle layer 120 may be adjoined to the outer surface of interior layer 130. In one embodiment of the invention, and as discussed below, exterior layer 110, middle layer 120 and interior layer 130 may be adjoined via a co-extrusion process therein eliminating the need for the use of adhesives for bonding the layers of backsheet 100 together.

(9) Backsheet 100 of the instant invention eliminates many of the deficiencies found in known laminated backsheets while reducing the overall cost of producing backsheet 100. Backsheet 100 of this invention utilizes materials which are more cost effective than fluoropolymers used in the exterior layer of known backsheets, and provide better weather resistant properties than those of PET. Moreover, backsheet 100 of this invention is made with no interlayer adhesives.

(10) In one embodiment of the invention, backsheet 100 may be made via a co-extrusion process that enables multiple layers of various materials to be extruded through one die therein producing a final backsheet 100 structure in one step or continuous process. Backsheet 100 may comprise three layers, each providing the functionality needed to perform as a highly durable, cost effective backsheet. The three layer structure of backsheet 100 may comprise a weatherable exterior layer 110, a dimensionally stable insulating solar module encapsulant core layer 120, and the third interior layer 130 which bonds to core layer 120.

(11) In yet another embodiment of the invention, exterior layer 110 of backsheet 100 may comprise Surlyn Reflections. Surlyn Reflections is a polyamide and ionomer alloy available through DuPont, and is manufactured under license from DuPont by LTL compounders in Morrisville, Pa.

(12) Generally, Surlyn Reflections has been used in exterior automotive applications, and offers excellent weather resistance and excellent UV performance. Surlyn Reflections, an alloy of polyamide and ionomer, uses proprietary compatibilizers to result in a resin that is particularly homogenous and stable. Polyamide in the alloy offers the material excellent mechanical properties, and the ionomer offers excellent toughness and UV resistance. The presence of the ionomer in the alloy also greatly reduces the moisture pick up normally seen in available polyamide compositions. In addition, the ionomer present in Surlyn Reflections is a olefinic material that does not absorb moisture and has excellent adhesion to other materials. Thus, the use in of the Surlyn Reflections product in PV applications provides a well engineered exterior layer 110 when compared to exterior backsheet layers currently being employed in PV applications.

(13) In addition, exterior layer 110 comprising Surlyn Reflections may be pigmented to provide any color desired, such as white or black depending on where the solar panel is being deployed and whether or not additional absorption or reflection is desired. Compatibilized alloys of other lower cost olefins such as polyethylene or polypropylene may also be utilized, however, the ionomer offers advantages in the adhesion of junction boxes to the backsheet and higher temperature stability. In one embodiment of the invention, exterior layer 110 may comprise black Surlyn Reflections.

(14) Middle layer 120 may comprise a talc filled polyamide (hereinafter PA). PA610, PA612, PA11, PA12 and PA9T all are acceptable alternative materials to be used for middle layer 120. One of the preferred materials which may be used as middle layer 120 may comprise either PA612, due to its low cost, or PA610, due to it being a bio-based, renewable and environmentally friendly polymer material, also of relatively low cost. In one embodiment, PA610 may comprise up to about sixty-five percent (65%) renewable materials. In one such embodiment of PA610, such renewable materials may be derived from castor bean oil.

(15) Middle layer 120 may also provide excellent dielectric properties, dimensional stability and higher temperature functionality than known backsheets. The nylons can be filled between about ten (10%) and about forty (40%) with talc, with the preferred loading being about twenty-five (25%).

(16) Like exterior layer 110, interior layer 130 of backsheet 100 may also comprise polyamide and ionomer alloy layer, such as Surlyn Reflections. In general, the layer facing the PV cells provides for more efficient operation in the solar panel module when interior layer 130 has enhanced reflectivity. It has been observed improvement in overall solar panel efficiency of up to about five percent (5%) over dark colored backsheets when backsheet 100 of this invention is used.

(17) In this regard, interior layer 130 may comprise a highly reflective white polyamide and ionomer alloy layer, such as Surlyn Reflections, which exhibits good bonding characteristics, and bonds particularly well to EVA encapsulant, providing bond strengths of over about 70 N/cm. Although interior layer 130 may comprise a more traditional clarified PE or EVA, the use of a highly reflective, white, polyamide and ionomer alloy layer, such as Surlyn Reflections, provides an interior layer 130 that has a melting point above about one hundred fifty degrees Celsius (150 C.) and, therefore, does not ooze during the panel lamination process. In this regard, backsheets that incorporate an EVA layer are subject to the EVA layer flowing during the panel lamination inasmuch as EVA has a melting point below the typical one hundred forty degrees Celsius (140 C.) to one hundred fifty degrees Celsius (150 C.) typically used in panel lamination processes. In one embodiment of the invention, interior layer 130 may comprise black Surlyn Reflections.

(18) In yet another embodiment of backsheet 100 of the instant invention, backsheet 100 comprises three coextruded layers for use in a solar module. In this embodiment, backsheet 100 serves, in part, as exterior insulation for a photovoltaic solar panel. In one embodiment of the invention, of backsheet 100 may comprise the following layers:

(19) 1. The Interior Layer

(20) The inner surface of interior layer 130 is in contact with the outer surface or bottom surface of the encapsulant layer of the PV module, and may comprise an ionomer resin intimately alloyed with nylon resin, and may also comprise between about two percent (2%) to about fifteen percent (15%) by weight of titanium dioxide white pigment, or other suitable amount. In this embodiment, interior layer 130 may also contain a UV absorber package, particularly if the encapsulant layer is devoid of such an additive, however such additives my be present in both interior layer 130 and the encapsulant layer of the PV cell. The ionomer resin may be zinc or sodium based, while the nylon may comprise, for example, nylon 6, nylon 66, nylon 610, or nylon 612.

(21) Although interior layer 130 may be of any suitable thickness, in one embodiment of the invention, interior layer 130 may have a thickness of between about twelve microns (12) and about 205 microns (205). Non-conductive carbon black pigment may also be used to make interior layer 130 darker or black. Infrared reflecting pigments may also be used to reduce the temperature to the extent that interior layer 130 is a darker color. Also, specialty pigments may also be used to achieve desired colors in interior layer 130.

(22) Moreover, interior layer 130, positioned next to the bottom layer of encapsulant, may also comprise a suitable amount of EVA resin. In one embodiment of the invention, the percentage of VA may range from about zero percent (0%) to about eight percent (8%) by weight. This composition may also receive the same pigments and other additives as the ionomer/nylon alloy.

(23) 2. The Middle Layer

(24) Middle layer 120 of backsheet 100 may comprise either nylon 11, nylon 12, nylon 610, or nylon 612 and may contain any suitable amount of filler. However, in one embodiment of the invention, middle layer 120 may comprise between about five percent (5%) to about forty percent (40%) filler. The filler may comprise talc, calcium carbonate, any combination of talc and calcium carbonate, or other suitable materials. Middle layer 120 may also contain pigments such as TIO.sub.2 or carbon black. In one embodiment of the invention, middle layer 120 may comprise about one half of one percent (0.5%) to about eight percent (8%) of pigment.

(25) Middle layer 120 may be of any suitable thickness, however in one embodiment of the invention, middle layer 120 may have a thickness of between about seventy-five microns (75) and about one-hundred eighty microns (180).

(26) 3. The Exterior Layer

(27) Exterior layer 110 may comprise an ionomer resin intimately alloyed with nylon resin, and which may also contain a suitable amount of pigment. In one embodiment of the invention, exterior layer 110 may comprise between about four percent (4%) to about fifteen percent (15%) titanium dioxide pigment. A UV absorber may also be added. The ionomer resin may comprise sodium based or zinc based ionomer, while the nylon resin may comprise nylon 6, nylon 66, nylon 610, or nylon 612. Although of exterior layer 110 may be of any suitable thickness, in one embodiment of the invention, of exterior layer 110 may have a thickness of between about twelve microns (12) and about 205 microns (205).

(28) Non-conductive carbon black pigment may also be used to make exterior layer 110 black. Infrared reflecting pigments may also be used to reduce the temperature when exterior layer 110 is a dark color. In addition, specialty pigments to achieve desired colors may also be used.

(29) In at least one embodiment of the method of the instant invention, backsheet 100 may be constructed using a co-extrusion process. To achieve improved bonds between each layer of backsheet 100 of this invention, the materials comprising the layers of backsheet 100 generally may be characteristically compatible and have melting points that are similar enough so that each material is generally contemporaneously molten, and the process temperature at any given time in the process does not cause degradation of the material having the lower melting temperature.

(30) Turning now to FIG. 3, there is shown a block diagram depicting one embodiment of a method for manufacturing backsheet 100 which utilizes a co-extruded cast film process. Backsheets 100 made by the processes described herein have demonstrated excellent performance in actual testing. In one embodiment of the instant invention, when used as exterior layer 110 and interior layer 130 layer, Surlyn Reflections has been found to be compatible with other polyamides, such as a talc filled, thermally stable polyamide which may comprise middle layer 120, although other suitable materials may be used for exterior layer 110, middle layer 120 and interior layer 130.

(31) In a first example of the co-extrusion process of the instant invention depicted in FIG. 3, backsheet 100 was manufactured by utilizing three following three layers of material: (1) an exterior layer 110 (designated as Material A in FIG. 3) of white Surlyn Reflections material comprising about ten percent (10%) TIO.sub.2; (2) a middle layer 120 (designated as Material B in FIG. 3) of PA612 (Dupont 158NC010) comprising about twenty-five percent (25%) talc filler; and (3) an interior layer 130 (designated as Material C in FIG. 3) of the same white Surlyn Reflections, comprising about ten percent (10%) TIO.sub.2, as that of exterior layer 110.

(32) The Surlyn Reflections material utilized for both exterior layer 110 and interior layer 130 was dried for between about 4 to about 6 hours at about seventy degrees Celsius (70 C.) to bring the moisture content in the materials to below about 0.15% by weight in desiccant hopper/dryers 3210 and 3230, respectively. The PA612 material utilized for middle layer 120 was dried for between about 4 to about 6 hours at about eighty degrees Celsius (80 C.) to bring the moisture content in the materials to below about five hundredths of a percent (0.05%) by weight in desiccant hopper/dryer 3220.

(33) Dried pellets of each material were conveyed pneumatically from hopper/dryers 3210, 3220 and 3230, respectively, to the corresponding extruders 3310, 3320 and 3330, respectively. Exterior, middle and interior layers 110, 120 and 130 were then formed into sheets or webs of material as the pellets were passed through extruders 3310, 3320 and 3330, respectively.

(34) Extruders 3310 and 3330 were 2.5 Davis Standard 30/1 L/D single screw units. Extruders 3310 and 3330 were set up with a temperature profile of about 230 C./230 C./240 C. Extruder 3320 was a 3.5 Davis Standard 30/1 L/D single screw unit. Extruder 3320 was set up with a temperature profile of about 235 C./235 C./245 C.

(35) Exterior, middle and interior layers 110, 120 and 130 were then passed through feedblock and flat coat hanger die 3400 to form a single, three layered sheet or web which comprises backsheet 100. Feedblock/Die 3400 was set at a temperature of about two hundred and forty degrees Celsius (240 C.). Molten backsheet 100 was quenched on three-roll stack 3500, which also imparted a micro-texture surface on the film surface. In this configuration, the process of this invention produced backsheet 100 at rates of about 100 to about 300 pounds per hour. Finished backsheet 100 was then rolled up on master roll windup 3600.

(36) In a second example of the co-extrusion process of the instant invention depicted in FIG. 3, backsheet 100 was manufactured by utilizing three following three layers of material: (1) an exterior layer 110 (designated as Material A in FIG. 3) of white Surlyn Reflections material comprising about ten percent (10%) TIO.sub.2; (2) a middle layer 120 (designated as Material B in FIG. 3) of PA610 (Dupont RSLC3090) comprising about twenty-five percent (25%) talc filler; and (3) an interior layer 130 (designated as Material C in FIG. 3) of the same white Surlyn Reflections, comprising about ten percent (10%) TIO.sub.2, as that of exterior layer 110.

(37) The Surlyn Reflections material utilized for both exterior layer 110 and interior layer 130 was dried for between about 4 to about 6 hours at about seventy degrees Celsius (70 C.) to bring the moisture content in the materials to below about fifteen hundredths of a percent (0.15%) by weight in desiccant hopper/dryers 3210 and 3230, respectively. The PA610 material utilized for middle layer 120 was dried for between about 4 to about 6 hours at about eighty degrees Celsius (80 C.) to bring the moisture content in the materials to below about five hundredths of a percent (0.05%) by weight in desiccant hopper/dryer 3220.

(38) Dried pellets of each material were conveyed pneumatically from hopper/dryers 3210, 3220 and 3230, respectively, to the corresponding extruders 3310, 3320 and 3330, respectively. Exterior, middle and interior layers 110, 120 and 130 were then formed into sheets or webs of material as the pellets were passed through extruders 3310, 3320 and 3330, respectively.

(39) Extruders 3310 and 3330 were 2.5 Davis Standard 30/1 L/D single screw units. Extruders 3310 and 3330 were set up with a temperature profile of about 230 C./230 C./240 C. Extruder 3320 was a 3.5 Davis Standard 30/1 L/D single screw unit. Extruder 3320 was set up with a temperature profile of about 240 C./250 C./260 C.

(40) Exterior, middle and interior layers 110, 120 and 130 were then passed through feedblock and flat coat hanger die 3400 to form a single, three layered sheet or web which comprises backsheet 100. Feedblock/Die 3400 was set at a temperature of about two hundred and forty degrees Celsius (240 C.). Molten backsheet 100 was quenched on three-roll stack 3500, which also imparted a micro-texture surface on the film surface. In this configuration, the process of this invention produced backsheet 100 at rates of about 100 to about 300 pounds per hour. Finished backsheet 100 was then rolled up on master roll windup 3600.

(41) In a third example of the co-extrusion process of the instant invention depicted in FIG. 3, backsheet 100 was manufactured by utilizing three following three layers of material: (1) an exterior layer 110 (designated as Material A in FIG. 3) of white Surlyn Reflections material comprising about ten percent (10%) TIO.sub.2; (2) a middle layer 120 (designated as Material B in FIG. 3) of PA11 (ArkemaRilsan) comprising about forty percent (40%) talc filler; and (3) an interior layer 130 (designated as Material C in FIG. 3) of the same white Surlyn Reflections, comprising about ten percent (10%) TIO.sub.2, as that of exterior layer 110.

(42) The Surlyn Reflections material utilized for both exterior layer 110 and interior layer 130 was dried for between about 4 to about 6 hours at about seventy degrees Celsius (70 C.) to bring the moisture content in the materials to below about fifteen hundredths of a percent (0.15%) by weight in desiccant hopper/dryers 3210 and 3230, respectively. The PA11 material utilized for middle layer 120 was dried for between about 4 to about 6 hours at about eighty degrees Celsius (80 C.) to bring the moisture content in the materials to below about five hundredths of a percent (0.05%) by weight in desiccant hopper/dryer 3220.

(43) Dried pellets of each material were conveyed pneumatically from hopper/dryers 3210, 3220 and 3230, respectively, to the corresponding extruders 3310, 3320 and 3330, respectively. Exterior, middle and interior layers 110, 120 and 130 were then formed into sheets or webs of material as the pellets were passed through extruders 3310, 3320 and 3330, respectively.

(44) Extruders 3310 and 3330 were 2.5 Davis Standard 30/1 L/D single screw units. Extruders 3310 and 3330 were set up with a temperature profile of about 230 C./230 C./240 C. Extruder 3320 was a 3.5 Davis Standard 30/1 L/D single screw unit. Extruder 3320 was set up with a temperature profile of about 240 C./250 C./260 C.

(45) Pellets were conveyed pneumatically to the respective extruders. Extruder A and C was 2.5 Davis Standard 30/1 L/D single screw unit. Extruders A & C were setup with a temperature profile of 230 C/230 C/240 C. Extruder B was 3.5 Davis Standard 30/1 L/D single screw unit. Extruders B was setup with a temperature profile of 240 C/250 C/260 C.

(46) Exterior, middle and interior layers 110, 120 and 130 were then passed through feedblock and flat coat hanger die 3400 to form a single, three layered sheet or web which comprises backsheet 100. Feedblock/Die 3400 was set at a temperature of about 250 C. Molten backsheet 100 was quenched on three-roll stack 3500, which also imparted a micro-texture surface on the film surface. In this configuration, the process of this invention produced backsheet 100 at rates of about 100 to about 300 pounds per hour. Finished backsheet 100 was then rolled up on master roll windup 3600.

(47) Feed rates of each extruder were varied to produce backsheets 100 of the following constructions:

(48) TABLE-US-00001 Outer Layers Outer Layers 110 & 130 Middle Layer Material 110 Thickness Middle Layer 120 Thickness Sample & 130 (mils) Material 120 (mils) 1 White Surlyn 1 25% Talc filled 4 Reflections PA610 2 White Surlyn 0.8 25% Talc filled 5 Reflections PA610 3 White Surlyn 2 25% Talc filled 3 Reflections PA610 4 Black Surlyn 0.5 15% Talc filled 6 Reflections PA612 5 White Surlyn 1 25% Talc filled 4 Reflections PA612 6 White Surlyn 1.25 25% Talc filled 3 Reflections PA610 7 White Surlyn 0.75 25% Talc filled 4 Reflections PA612 8 White Surlyn 2 25% Talc filled 5 Reflections PA612 9 White Surlyn 1 15% Talc Filled 5 Reflections PA 612 10 Black Surlyn 0.8 15% Talc Filled 7 Reflections PA 612 11 White Surlyn 1 40% Talc Filled 4 Reflections PA 11 12 White Surlyn 2 40% Talc Filled 6 Reflections PA 11

(49) Other extrusion and/or non-adhesive lamination methods for producing backsheet 100 of the instant invention may also be employed such as, for example, blown film methodologies.

(50) Turning now to FIG. 5, is shown a block diagram depicting another embodiment of a method for manufacturing backsheet 100 which utilizes a co-extruded blown film process. In one embodiment of the instant invention, when used as exterior layer 110 and interior layer 130 layer, Surlyn Reflections has been found to be compatible with other polyamides, such as a talc filled, thermally stable polyamide which may comprise middle layer 120, although other suitable materials may be used for exterior layer 110, middle layer 120 and interior layer 130.

(51) In the blown film process depicted in FIG. 5, the materials utilized for exterior layer 110, middle layer 120 and interior layer 130 are dried in desiccant hopper/dryers 5210, 5220 and 5230, respectively, to bring the moisture content present in each of the materials suitable processing levels.

(52) Dried pellets of each material are then conveyed pneumatically from hopper/dryers 5210, 5220 and 5230, respectively, to corresponding extruders 5310, 5320 and 5330, respectively. Exterior, middle and interior layers 110, 120 and 130 are then formed into sheets or webs of material as the pellets are heated to appropriate temperatures and passed through extruders 5310, 5320 and 5330, respectively. Extruders 5310, 5320 and 5330 may comprise single screw units with temperature profiles being set to suitable levels.

(53) Exterior, middle and interior layers 110, 120 and 130 may then be passed through multi-layered, multi-port blown film die 4400 (which may further comprise an air ring) and collapsing tent 5500 to form a single, three layered sheet or web which comprises backsheet 100. Blown film die 5400 may be set to a suitable temperature which promotes the formation of backsheet 100. Molten backsheet 100 may then be quenched on and a micro-texture surface may also be imparted on surface of backsheet 100. Finished backsheet 100 may then be rolled up on master roll windup 5600.

(54) Although it is preferred that the backsheet of this invention does not utilize adhesives for joining the backsheet layers together, it is possible to employ manufacturing processes which do utilize an amount of suitable adhesive between any two layers of backsheet 100, if desired.

(55) Turning now to FIG. 4, there is shown a cross sectional schematic depicting a solar cell construction 400 which incorporates one embodiment of the solar panel backsheet of the instant invention. Solar cell 400 comprises front cover 410, photovoltaic cells 430 encapsulated in one or more suitable encapsulants 420 and 440, which comprises top encapsulant portion 420 and bottom encapsulant portion 440, and backsheet 100.

(56) Front cover 410 may be constructed from glass or any other suitable material which transmits light to PV cells 430. Encapsulant portions 420 and 440 may comprise a single unitary construction, or may comprise separate encapsulant portions 420 and 440 joined together to encapsulate PV cells 430. Encapsulant portions 420 and 440 may further comprise the same or different material or materials. In one embodiment, top encapsulant portion 420 may comprise a material which protects PV cells 430 but, like front cover 410, also transmits light to PV cells 430. In addition, bottom encapsulant portion 440 may comprise a material which also protects PV cells 430 but also either reflects or absorbs light in a manner which improves the efficiency of PV cells 430.

(57) Also, as shown in the embodiment depicted in FIG. 4, backsheet 100 may comprise three layers: exterior layer 110; middle layer 120; and interior layer 130. Exterior layer 110 may comprise a polyamide and ionomer alloy. Middle layer 120 may comprise a talc filled polyamide. Finally, interior layer 130 may comprise a polyamide and ionomer alloy, which may be the same as or different from the polyamide and ionomer alloy of exterior layer 110.

(58) In this embodiment of backsheet 100, the outer surface of middle layer 120 may be adjoined to the inner surface of exterior layer 110, and the inner surface of middle layer 120 may be adjoined to the outer surface of interior layer 130.

(59) In the embodiment of solar cell 400 depicted in FIG. 4, PV cells 430 are substantially encapsulated in encapsulant 420 and/or 430. The outer surface of encapsulant portion 420 is adjoined to the inner surface of front cover 410. The outer surface of encapsulant portion 440 is adjoined, or otherwise affixed to, the inner surface of backsheet interior layer 130.

(60) The disclosure herein is directed to the variations and modifications of the elements and methods of the invention disclosed and that will be apparent to those skilled in the art in light of the disclosure herein. Thus, it is intended that the present invention covers the modifications and variations of this invention, provided those modifications and variations come within the scope of the appended claims and the equivalents thereof.